CN1273487C - Collagen and method for preparing collagen from skins of birds - Google Patents
Collagen and method for preparing collagen from skins of birds Download PDFInfo
- Publication number
- CN1273487C CN1273487C CN 200510038809 CN200510038809A CN1273487C CN 1273487 C CN1273487 C CN 1273487C CN 200510038809 CN200510038809 CN 200510038809 CN 200510038809 A CN200510038809 A CN 200510038809A CN 1273487 C CN1273487 C CN 1273487C
- Authority
- CN
- China
- Prior art keywords
- birds
- skins
- collagen
- collagen protein
- preparing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention discloses collagen protein prepared by that poultry skin is used as raw materials, which is composed of an alpha chain group and a beta chain group. A method for preparing the collagen protein from poultry skin is used for preparing the collagen protein and comprises the following steps that poultry skin which is washed clearly is soaked and processed in an alkaline solution, and the poultry skin which is processed in the alkaline solution is washed in deionized water; the poultry skin which is processed is soaked in an acidic buffer solution, is filtered and is centrifugated, and then supernatant liquid is collected and is dialyzed until the dialyzed liquid is in neutrality. The present invention does not contain a gamma chain, and has high content of an alpha chain and low content of a beta chain; furthermore, the non-spiral end in collagen with immunogenic performance is cut off; the present invention has the advantages of good biocompatibility, convenient method, high purity, low preparation cost, simple and practical working procedure, etc.
Description
Technical field
The present invention relates to a kind of bird used in tissue engineering collagen protein and preparation method.The skin that utilizes bird extracts type i collagen albumen as raw material.Specifically, the present invention relates to utilize alkaline solution to handle the skins of birds that cleans, utilize the molten method of acid to handle above-mentioned skin again, purify the molten supernatant liquor of acid and promptly obtain I type skins of birds collagen protein.
Background technology
Collagen protein is a kind of structural protein, has multiple biological function.Collagen protein is the upholder and the weighting material of tissue, initiatively participates in migration, differentiation and the propagation of cell, and relevant with the reparation of wound and embryo's growth.The biological substitution thing that with the collagen protein is feedstock production obtains effect preferably in experimentation on animals and clinical experiment.
At present, having occurred a collection of in the world is the biological products of main component with the collagen protein, comprises soluble collagen, insoluble collagen and the mixture of being made up of collagen and non-collagen stroma.These materials can be used for preparing collagen solution, collagen paste, collagen film, collagen suture line etc., thus the reparation of the wound of being widely used in and burn, shaping and beauty, neurotization and blood valve surgery etc.
The collagen protein of the collagen formulations of using clinically mainly is a Mammals at present, as the collagen protein of pig, ox-hide skin.The pre-treatment of the extraction of this class collagen protein is cumbersome, and for obtaining the skin starting material of clean hygiene, the required workload of cleaning skin is big before and after butchering, and the cost that needs is also just corresponding to be improved.In addition, use ox-hide collagen may in indivedual cases, cause in various degree immune response clinically.Particularly the danger of mad cow disease extensively is familiar with recently, has limited the source of collagen protein greatly.
In recent years, the research in collagen protein field became a focus at home and abroad gradually.At present, it all is to focus on to extract dissimilar collagen that a lot of researchs are arranged, and to its structure, function, etc. characteristic inquire into.Skins of birds collagen protein, particularly quail collagen, To Be Protected from Heat owing to quail natural disposition, and the denaturation temperature of collagen protein is quite low, does not resemble the propagation of restrictive cell the cow leather collagen.Because the difference of raw material, the pre-treatment during preparation skins of birds collagen also just is different from the pre-treatment of mammal skin.The pre-treatment of skins of birds comprises unhairing, degrease, discolor etc., removes the composition of noncollagen protein in the skins of birds with organic solvent, also has part fat can not remove, and should handle the method cost height of skins of birds, contaminate environment.Shimizu et.al. (US 6,271,350) utilizes the method for the pickled skin of salt, can effectively remove the non-collagen tissue in the skins of birds.This method salt marsh is handled needs a week, length consuming time; Only supply the needs of industry and food with the collagen protein of 70-90 ℃ distilled water extraction.Ho1zer (US 5,484,888) utilizes the alkali of 1.6-12.5% to soak raw material 3-60 days, and the weakly acid soln with pH5 is used for food weighting material, filmstrip and pharmaceutical capsule in 45-55 ℃ of extraction preparation high strength gelatinum again.When Hadden (US 5,162,506) makes collegen filament that foodstuff additive and nutrition amino acid uses in preparation, utilize saturated alkaline solution to remove residual solubility noncollagen protein and polysaccharide in the raw material.The unspiralized region of the proteic β of type i collagen, γ chain is the antigenic determinant of collagen protein.If as biomaterial, the individual possibility that produces immunne response of acceptor increases greatly.In addition, the degree of purification of collagen protein is not high also can limit prepared Application of Collagen.
Summary of the invention
The invention provides the low type i collagen albumen of a kind of good biocompatibility, purity height and preparation cost and reach the method for preparing collagen protein by skins of birds.
The present invention adopts following technical scheme:
Collagen protein of the present invention, that is:
A kind of is the collagen protein of feedstock production with the skins of birds, and prepared bird collagen is made up of α, β chain, and the mass content of α chain is 70%-90%, and the mass content of β chain is 10%-30%.
Of the present inventionly prepare the method for collagen protein, that is: by skins of birds
A kind of be used to prepare above-mentioned collagen protein prepare former proteic method by the bird hide glue, follow these steps to successively carry out:
1. with the skins of birds that cleans up with the alkaline solution of 0.5%-10% 0-16 ℃ of immersion treatment, the weightmeasurement ratio of skins of birds and dilute alkaline soln is 1: 1-10, use the skins of birds after the washed with de-ionized water alkaline purification again, till pH6.5-7.5;
2. the skins of birds after the above-mentioned processing is soaked in the acidic buffer of 0.1-2.0M pH1.0-6.8 under 0-16 ℃ of condition, after 1-4 days, filters;
3. with the filtrate of above-mentioned pH1.0-6.8 in 2,000-10,000rpm and in 0-10 ℃ centrifugal down, collect supernatant, with the acidic buffer dialysis of pH1.0-6.8, at last with the pure water dialysis, till dialyzate is neutrality.
Collagen liquid through dialysis can 0-16 ℃ of preservation, also can dry back in 0-16 ℃ of preservation.
The above-mentioned skins of birds that cleans up is that the skins of birds of fresh or stored frozen is clean with 0-16 ℃ tap water soaking flushing, uses deionized water soaking flushing 3-5 time again.Described skins of birds can be the skin of quail, pigeon, chicken, duck etc.Described Na
+, K
+, Ca
2+, Mg
2+Deng salt of weak acid, can be phosphoric acid salt, carbonate, Citrate trianion, acetate.
Compared with prior art, the present invention has following advantage:
Skins of birds collagen protein of the present invention is compared with other collagen protein (ox), does not only contain the γ chain, and the content height of α chain, and the content of β chain is low, has excised the non-helical end that has in the immunogenic collagen, good biocompatibility.Method of the present invention is easy, only needs immersion and centrifugal treating the tropocollagen molecule dissolving can be extracted, and also solubilized contains the collegen filament of aldehyde amines cross-link bond.Through the skins of birds type i collagen purity of protein height that the present invention makes, preparation cost is low, and operation is simple and easy to do.
Description of drawings
Fig. 1 is the quail collagen electrophoretogram that the present invention prepares.
Reference numeral explanation: 1-standard protein marker; The 2-procollagen.
The collagen protein electrophoretogram of the present invention's preparation illustrates that the collagen protein 2 of the present invention's preparation does not contain the γ chain as shown in Figure 1, and the content height of α chain, and the content of β chain is relatively low.
Embodiment
To help to understand the present invention by following embodiment, but not limit content of the present invention.
Embodiment 1: the preparation of quail collagen
1. clean the quail skin.The quail skin of stored frozen is clean with the tap water soaking flushing of 4 ℃ of 100ml, reject quail hair and subcutis, in soak solution, except that monoblock quail skin, do not have to use the deionized water soaking flushing again 5 times till other fine hair thing.
2. alkaline purification quail skin.With the quail skin of 0.1M NaOH solution 100ml after 4 ℃ of immersions (1) are handled 2-3 days, change 0.1M NaOH solution every day one time.Fully clean quail skin after the alkaline purification with deionized water again, till about pH7.
3. procollagen.Quail skin after (2) processing is dissolved in acetic acid-sodium-acetate (1: 1/V: V) in the damping fluid, under 4 ℃ of conditions, extracted 3 days continuously, use filtered through gauze of 40ml 0.5M.The residue molten extraction of hypo acid again, step is the same, merges filtrate twice.
4. purification collagen protein.In 10, the 000rpm low-temperature centrifugation is collected supernatant with above-mentioned filtrate, with the dialysis of acetate buffer tonsure, at last with the pure water dialysis, till dialyzate is neutrality.
The refining proteic SDS-PAGE electrophoretogram of collagen as shown in Figure 1.
Embodiment 2: the preparation of quail collagen
1. clean the quail skin.The quail skin of stored frozen is clean with the tap water soaking flushing of 1-10 ℃ of 100ml, reject quail hair and subcutis, in soak solution, except that monoblock quail skin, do not have to use the deionized water soaking flushing again 5 times till other fine hair thing.
2. alkaline purification quail skin.With 3%Ca (OH)
2The quail skin of solution 100ml after 1-10 ℃ of immersion (1) handled 3-4 days changed a 3%Ca (OH) sooner or later
2Solution.Fully clean quail skin after the alkaline purification with deionized water again, till about pH7.
3. procollagen.Quail skin after (2) processing is dissolved in acetic acid-sodium-acetate (1: 1/V: V) in the damping fluid, under 4 ℃ of conditions, extracted 3 days continuously, use filtered through gauze of 40ml 0.5M.The residue molten extraction of hypo acid again, step is the same, merges filtrate twice.
4. purification collagen protein.In 10, the 000rpm low-temperature centrifugation is collected supernatant with above-mentioned filtrate, with the dialysis of acetate buffer tonsure, at last with the pure water dialysis, till dialyzate is neutrality.
Embodiment 3: the preparation of salt marsh cock skin collagen protein
1. cleaning cock skin.The cock skin of stored frozen is clean with the tap water soaking flushing of 5 ℃ of 200ml, reject chicken feather and subcutis, in soak solution, except that the monoblock cock skin, do not have to use the deionized water soaking flushing again 5 times till other fine hair thing.
2. alkaline purification cock skin.With NaCl salt marsh cock skin (1: 1w/w) 7 days, fully clean cock skin after the alkaline purification with deionized water again, till about pH7.
3. procollagen.Cock skin after (2) processing is dissolved in acetic acid-sodium-acetate (1: 1/V: V) in the damping fluid, under 4 ℃ of conditions, extracted 3-4 days, use filtered through gauze of 100ml 0.5M.The residue molten extraction of hypo acid again, step is the same, merges filtrate twice.
4. purification collagen protein.In 10, the 000rpm low-temperature centrifugation is collected supernatant with above-mentioned filtrate, with the dialysis of acetate buffer tonsure, at last with the pure water dialysis, till dialyzate is neutrality.
Embodiment 4
A kind of is the collagen protein of feedstock production with the skins of birds, and prepared bird collagen is made up of α, β chain, and the mass content of α chain is 70%-90%, and the mass content of β chain is 10%-30%.
Embodiment 5
A kind ofly prepare the method for collagen protein, follow these steps to successively carry out by the bird hide glue:
1. with the skins of birds that cleans up with the alkaline solution of 0.5%-10% 0-16 ℃ of immersion treatment, the weightmeasurement ratio of skins of birds and dilute alkaline soln is 1: 1-10, use the skins of birds after the washed with de-ionized water alkaline purification again, till pH6.5-7.5;
2. the skins of birds after the above-mentioned processing is soaked in the acidic buffer of 0.1-2.0M pH1.0-6.8 under 0-16 ℃ of condition, after 1-4 days, filters;
3. with the filtrate of above-mentioned pH1.0-6.8 in 2,000-10,000rpm and in 0-10 ℃ centrifugal down, collect supernatant, with the acidic buffer dialysis of pH1.0-6.8, at last with the pure water dialysis, till dialyzate is neutrality,
The cleaning of above-mentioned clean skins of birds is the skins of birds of fresh or stored frozen is soaked with 0-16 ℃ tap water and to rinse well, uses deionized water soaking flushing 3-5 time again; Skins of birds can be the skin of quail, pigeon, chicken or duck; The alkaline solution that is used to soak skins of birds is Ca (OH)
2, NaOH, Na
+, K
+, Ca
2+, Mg
2+Salt of weak acid solution in a kind of, what the damping fluid that is used for soaking the bird hide glue was pH at acetic acid-acetic acid sodium salt, phosphoric acid salt, phthalic acid potassium-sodium hydroxide, citric acid-sodium citrate, citric acid-sodium hydroxide-hydrochloric acid or the SODIUM PHOSPHATE, MONOBASIC-citrate buffer solution of 1.0-6.8 is a kind of, damping fluid can be prepared by existing method, by adjusting component, the pH that makes damping fluid is between 1.0-6.8, in the present embodiment, the filtration residue molten processing of hypo acid again, and merge with preceding first-time filtrate.
Claims (7)
1. one kind is the collagen protein of feedstock production with the skins of birds, it is characterized in that prepared bird collagen is made up of α, β chain, and the mass content of α chain is 70%-90%, and the mass content of β chain is 10%-30%.
2. method for preparing the described collagen protein of claim 1 is characterized in that following these steps to successively carry out:
1. with the skins of birds that cleans up with the alkaline solution of 0.5%-10% 0-16 ℃ of immersion treatment, the weightmeasurement ratio of skins of birds and dilute alkaline soln is 1: 1-10, use the skins of birds after the washed with de-ionized water alkaline purification again, till pH6.5-7.5;
2. the skins of birds after the above-mentioned processing is soaked in the acidic buffer of 0.1-2.0M pH1.0-6.8 under 0-16 ℃ of condition, after 1-4 days, filters;
3. with the filtrate of above-mentioned pH1.0-6.8 in 2,000-10,000rpm and in 0-10 ℃ centrifugal down, collect supernatant, with the acidic buffer dialysis of pH1.0-6.8, at last with the pure water dialysis, till dialyzate is neutrality.
3. as preparing the method for collagen protein as described in the claim 2, the cleaning that it is characterized in that clean skins of birds is the skins of birds of fresh or stored frozen is soaked with 0-16 ℃ tap water and to rinse well, uses deionized water soaking flushing 3-5 time again.
4. as preparing the method for collagen protein as described in the claim 2, it is characterized in that described skins of birds is the skin of quail, pigeon, chicken or duck.
5. as preparing the method for collagen protein as described in the claim 2, it is characterized in that the alkaline solution that uses is Ca (OH)
2, NaOH, Na
+, K
+, Ca
2+, Mg
2+Salt of weak acid solution in a kind of.
6. as preparing the method for collagen protein as described in the claim 2, what the damping fluid that it is characterized in that being used for dissolving the bird hide glue was pH at acetic acid-acetic acid sodium salt, phosphoric acid salt, phthalic acid potassium-sodium hydroxide, citric acid-sodium citrate, citric acid-sodium hydroxide-hydrochloric acid or the SODIUM PHOSPHATE, MONOBASIC-citrate buffer solution of 1.0-6.8 is a kind of.
7. by the described method for preparing collagen protein of claim 2, it is characterized in that the filtration residue molten processing of hypo acid again, and merge with preceding first-time filtrate.