CN1249325A - 防火阻燃剂 - Google Patents
防火阻燃剂 Download PDFInfo
- Publication number
- CN1249325A CN1249325A CN 98121478 CN98121478A CN1249325A CN 1249325 A CN1249325 A CN 1249325A CN 98121478 CN98121478 CN 98121478 CN 98121478 A CN98121478 A CN 98121478A CN 1249325 A CN1249325 A CN 1249325A
- Authority
- CN
- China
- Prior art keywords
- urea
- water
- boric acid
- borax
- phosphoric acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种适用于棉布、化纤、纸张、木料等易燃物的防火阻燃剂。它是由尿素、磷酸、硼砂、硼酸和水组成。各组分称好后,先将水、尿素和磷酸放入夹层反应釜中,加热直至混合物完全溶解,待冷却后加入硼砂和硼酸,调至pH为7制成。它具有无色、透明、无毒、无味、无污染、无腐蚀、使用方便、被处理物的性质、光泽、手感、柔软性均不变等优点。
Description
本发明涉及一种防火阻燃剂，特别适用于布料、化纤、纸张、地毯、木料等易燃物的防火阻燃处理。
现有的水剂防火阻燃剂，具有无毒、不污染环境、无腐蚀等优点，但透明度差，使用后留有水印，影响装饰效果，喷涂或浸渍在门帘、窗帘、窗帷等上面，会使布料变硬。
本发明的目的在于克服背景技术中的不足之处而提供一种无色、透明、无毒、无味、无腐蚀、处理后的材料柔软性不变、防火性能好、使用方便的防火阻燃剂。
本发明的目的是这样实现的：该防火阻燃剂是由尿素、磷酸、硼砂、硼酸和水组成，其重量百分比分别为尿素10.5-14.5％、磷酸3-7％、硼砂1-5％、硼酸2.5-6.5％、水70-80％。将各组分按比例称好，先将水、尿素和磷酸放入夹层反应釜中加热至100℃，直至混合物完全溶解，待冷却后加入硼砂和硼酸，调至PH值为7，过滤制成。
本发明的目的还可以通过以下技术措施来实现：各组分的最佳配比(重量百分比)为尿素12.5％、磷酸5.0％、硼砂3.0％、硼酸4.5％、水75％。所需的水以无离子水为最佳。
本发明与现有技术相比具有如下优点：
1、该产品无色透明、无毒、无味、无污染；
2、因本产品为中性，因此无腐蚀；
3、使用方便，喷、涂、浸渍均可，被处理物的性质、光泽、手感、柔软性均不改变。
4、防火性能好，能耐700℃的高温，也可防明火；
5、成本低，仅为同类产品的二分之一。
下面结合实施例详述本发明：例1、取尿素25份、磷酸10份、硼砂6份、硼酸9份、水150份，合计200份，每份以1公斤计算，即尿素25公斤占总量的12.5％，磷酸10公斤，占5.0％，硼砂6公斤，占3％，硼酸9公斤，占4.5％，水150公斤，占75％，各组分按上述比例称好后，先将水、尿素和磷酸放入夹层反应釜中加热至100℃，直至混合物完全溶解，待冷却后加入硼砂和硼酸，搅拌均匀使其充分反应，用硼酸调至PH值为7后，再过滤包装制得成品。
以配料100公斤防火阻燃剂为例，备组分配比例表说明，制备方法同上。
| 尿素 | 磷酸 | 硼砂 | 硼酸 | 水 | ||||||
| 重量Kg | 百分比％ | 重量Kg | 百分比％ | 重量Kg | 百分比％ | 重量Kg | 百分比％ | 重量Kg | 百分比％ | |
| 例2 | 12.5 | 12.5 | 5 | 5 | 3 | 3 | 4.5 | 4.5 | 75 | 75 |
| 例3 | 11 | 11 | 5.5 | 5.5 | 4 | 4 | 5 | 5 | 74.5 | 74.5 |
| 例4 | 14 | 14 | 3 | 3 | 1 | 1 | 6.5 | 6.5 | 75.5 | 75.5 |
| 例5 | 13 | 13 | 7 | 7 | 2 | 2 | 2.5 | 2.5 | 75.5 | 75.5 |
| 例6 | 13.5 | 13.5 | 4 | 4 | 2.5 | 2.5 | 3.5 | 3.5 | 76.5 | 76.5 |
| 例7 | 10 | 10 | 3.5 | 3.5 | 5 | 5 | 6.5 | 6.5 | 75 | 75 |
| 例8 | 12 | 12 | 4.5 | 4.5 | 1.5 | 1.5 | 2.5 | 2.5 | 79.5 | 79.5 |
| 例9 | 11.5 | 11.5 | 3 | 3 | 3 | 3 | 2.5 | 2.5 | 80 | 80 |
| 例10 | 14 | 14 | 6 | 6 | 5 | 5 | 5 | 5 | 70 | 70 |
| 例11 | 13 | 13 | 6.5 | 6.5 | 4 | 4 | 3.5 | 3.5 | 73 | 73 |
| 例12 | 12.5 | 12.5 | 5.5 | 5.5 | 3.5 | 3.5 | 4 | 4 | 74.5 | 74.5 |
Claims (3)
1、一种防火阻燃剂，其特征在于：它是由尿素、磷酸、硼砂、硼酸和水组成，其重量百分比分别为尿素10.5-14.5％、磷酸3-7％、硼砂1-5％、硼酸2.5-6.5％、水70-80％。
2、根据权利要求1所述的防火阻燃剂，其特征在于各组分的最佳重量百分比为尿素12.5％、磷酸5.0％、硼砂3.0％、硼酸4.5％、水75％。
3、根据权利要求1所述的防火阻燃剂，其特征在于以无离子水为最佳。