CN1109774C - Refractory alloy composition - Google Patents
Refractory alloy composition Download PDFInfo
- Publication number
- CN1109774C CN1109774C CN00129326A CN00129326A CN1109774C CN 1109774 C CN1109774 C CN 1109774C CN 00129326 A CN00129326 A CN 00129326A CN 00129326 A CN00129326 A CN 00129326A CN 1109774 C CN1109774 C CN 1109774C
- Authority
- CN
- China
- Prior art keywords
- chromium
- alloy
- alloy composition
- silicon
- manganese
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及冶炼技术，是一种耐热合金组合物。其组份及含量是：0.02～0.8%碳，0.2～1.5%锰，3～15%铬，0.5～3%硅，0.2～3.5%铝，0.01～0.5%钼，0.001～0.006%硼，0.01～1.5%的添加剂及余量铁。使其保持合金综合性能不变的前提下，大幅度降低合金成本。The invention relates to smelting technology, and is a heat-resistant alloy composition. Its components and contents are: 0.02-0.8% carbon, 0.2-1.5% manganese, 3-15% chromium, 0.5-3% silicon, 0.2-3.5% aluminum, 0.01-0.5% molybdenum, 0.001-0.006% boron, 0.01 ~1.5% additives and balance iron. Under the premise of keeping the overall performance of the alloy unchanged, the cost of the alloy is greatly reduced.
Description
Technical field
The present invention relates to smelting technology, is a kind of refractory alloy composition.
Background technology
Existing heat-resisting allay material, some alloy adding is higher, and for example: the add-on of chromium is generally about 30% usually.This just causes smelting cycle lengthening, complex process, and deficiencies such as cost up in addition, must add nickel (Ni) in traditional refractory alloy component, and the costing an arm and a leg of nickel, institute is so that cost of alloy is higher.
Summary of the invention
The purpose of this invention is to provide a kind of refractory alloy composition, make it keep reducing cost of alloy significantly under the constant prerequisite of alloy over-all properties.
The present invention for the technical scheme of finishing the foregoing invention purpose and providing is, a kind of refractory alloy composition, its component and content are: 0.02-0.15% carbon, 0.2-1.5% manganese, 6-8% chromium, 0.5-3% silicon, 0.2-3.5% aluminium, the 0.01-0.5% molybdenum, 0.001-0.006% boron, the niobium of 0.01-1.5%, titanium additives and balance iron.Described additive generally is the combination of at least two kinds of materials in niobium, titanium, the vanadium.Described a kind of refractory alloy composition, its component and content are: 0.15% carbon, 0.45% manganese, 7% chromium, 2.5% silicon, 1% aluminium, 0.02% molybdenum, 0.002% boron, 0.05% niobium, titanium and balance iron.Content in the each component of the present invention all by weight percentage.
Alloy of the present invention proves to have good comprehensive performances through commerical test, and has good welding property, high tenacity, good anti-Quench, sharp thermal characteristics etc., and technology is simple, cost of alloy reduces significantly.
Contribution of the present invention is, the content of alloying element is significantly reduced than prior art,, utilize its interaction to replace nickel element simultaneously with element combinations such as chromium, aluminium, silicon, manganese, and obtain performances such as high temperature resistant, that oxidation-resistance is strong equally, cost is reduced significantly.The present invention adds chromium, aluminium, element silicon in iron after, can improve the appearance temperature of ferric oxide.When containing these elements in the steel, interaction can take place between them, form alloy oxide film, as: Cr
2O
3, Al
2O
3, FeO-Cr
2O
3, FeO-Al
2O
3, Fe
2SrO
4Deng, these alloy oxide films have good protective action.Alloy of the present invention step manufacturing as follows: 1, the blast-melted processing rear converter that gives adds waste materials such as steel scrap, fluorite, ore when inferior.2, carry out deoxidation alloying; 3, molten steel furnace external refining; 4, continuous casting or ingot casting, foundry goods, foundry goods is 900-1200 ℃ of normalizing treatment; 5, controlled rolling, cooling.Metallographic structure of the present invention is based on ferrite and a small amount of troostite or bainite.Evidence, solderability is good, does not undergo phase transition, and profile does not change under Quench, sharp enthusiasm condition.
Embodiment
The embodiment of component content of the present invention is as follows: each component content all by weight percentage.
Embodiment 1:0.5% carbon, 0.45% manganese, 7% chromium, 1.5% silicon, 1.2% aluminium, 0.02% molybdenum, 0.002% boron, 0.05% niobium, titanium, vanadium and balance iron.
Embodiment 2:0.02% carbon, 0.3% manganese, 10% chromium, 2% silicon, 1.5% aluminium, 0.05% molybdenum, 0.002% boron, 0.07% niobium, titanium and balance iron.
Embodiment 3:0.15% carbon, 0.45% manganese, 8% chromium, 2.5% silicon, 3% aluminium, 0.06% molybdenum, 0.005% boron, 1.0% titanium, vanadium and balance iron.
Embodiment 4:0.12% carbon, 1.5% manganese, 12% chromium, 3% silicon, 3.5% aluminium, 0.05% molybdenum, 0.006% boron, 1.2% niobium, vanadium and balance iron.
Embodiment 5:0.15% carbon, 0.45% manganese, 7% chromium, 2.5% silicon, 1% aluminium, 0.02% molybdenum, 0.002% boron, 0.05% niobium, titanium and balance iron.
The not detailed description technique content of the present invention is a known technology.
Claims (2)
1, a kind of refractory alloy composition, it is characterized in that: its component and content are: 0.02-0.15% carbon, 0.2-1.5% manganese, 6-8% chromium, 0.5-3% silicon, 0.2-3.5% aluminium, the 0.01-0.5% molybdenum, 0.001-0.006% boron, the niobium of 0.01-1.5%, titanium additives and balance iron.
2, a kind of refractory alloy composition according to claim 1, it is characterized in that: its component and content are: 0.15% carbon, 0.45% manganese, 7% chromium, 2.5% silicon, 1% aluminium, 0.02% molybdenum, 0.002% boron, 0.05% niobium, titanium and balance iron.