CN1100671C

CN1100671C - A method of manufacturing a reflector

Info

Publication number: CN1100671C
Application number: CN99105958A
Authority: CN
Inventors: 李美琴
Original assignee: Individual
Current assignee: Individual
Priority date: 1999-05-04
Filing date: 1999-05-04
Publication date: 2003-02-05
Anticipated expiration: 2019-05-04
Also published as: CN1272426A

Abstract

The invention discloses a method for manufacturing a reflecting piece, which comprises the steps of carrying out vacuum electroplating processing on the surface of a base material, automatically spraying a coating layer of colloid on the coating layer through a processing machine to form a coating layer, standing for a period of time to enable the coating layer to be in a semi-dry state with a dry surface and an inner layer not yet dried, directly spraying glass bead particles with the diameter of 0.06mm-0.15mm on the coating layer in the semi-dry state through a spray gun device to form uniformly distributed reflecting bead surfaces with the same refraction curvature, wherein the thickness of the coating layer is smaller than the diameter of the glass bead particles. It can maintain the reflecting function for a long time and the reflecting part is not affected by the erosion of sunlight and water.

Description

A kind of manufacture method of reflecting component

The present invention relates to the reflecting component field, on especially a kind of object that can be applicable to any moulding and can reach the manufacture method of the reflecting component of special aesthetic feeling with reflecting effect.

With traditional reflection function, be that reflective dose or fluorescent material etc. are painted on object surfaces substantially, present reflective dose of chemical pigment gay colours own, or the chemical characteristic of performance fluorescent material, by the very dazzling color that is observed visually of human body, the what is called that promptly it has often been said " reflecting effect ".

Yet reflective dose attached to body surface is waited pigment because of wherein adding binding agent, curing agent, the thickness of spray liniment material is difficult to evenly distribute, the quality of reflective material is soft glue-line, enamelled coating, the long-term use down owing to wiping repeatedly is worn, cause reflective dose of layer to take off, and reflective dose of layer is because of often exposing to the open air in the sun, in the moisture, also will forming gradually and fading or the rotten deterioration that makes it, so traditional reflective object exists the shortcoming that can't keep the stability of effect for a long time.

Purpose of the present invention is exactly will provide a kind of to make the manufacture method of reflecting component with bead, and it makes reflection function keep the long period, the influence that reflecting component is not corroded by sunlight and moisture content can.

The object of the present invention is achieved like this: a kind of manufacture method of reflecting component comprises following procedure of processing: the object of one, getting a suitable shape is a base material; Two, the surface of base material is carried out vacuum plating processing and handle, form the surface as the plating layer of cure process excessively; Three, the plating layer is sprayed the cover layer that forms a colloid automatically by processing equipment; Four, tectal colloid is stagnated placement a period of time, make it be in the surface and do and the dried yet leather hard of internal layer; Five, cut-off directly is the bead particle of 0.06mm-0.15mm, injects directly on by lance driving device on the cover layer of leather hard; Six, make on the cover layer of each bead particle bond attached to colloid, and be the stickup contact-making surface of minute surface substrate, form the identical reflecting beads face of uniform refractive power curvature with platingization layer; The cover layer of spraying colloid, its thickness is less than the diameter of bead particle, each bead particle is when embedding cover layer, a part of sphere height will be protruded, each bead particle is that contact-making surface is pasted in substrate with the higher plating layer of hardness, the height of each pearl body becomes individual layer evenly to distribute and arranges unanimity, constitutes a splendid light source reflecting surface.

The present invention is owing to adopt the manufacture method of the reflecting component of innovation, can improve the processing that various relevant needs are used the body surface of reflection function, have high-definition reflection function and unique visual sensory effect, regular washing, grooming does not all damage the special-effect of its reflection source, not sunkissed influence, the effect of reflecting effect and the reflective equipment of tradition are than keeping the longer time, the refractive surface minute surface reflection curvature unanimity of reflecting component, can reach the maximum reflection effect of light source, the extreme hardness of bead, also than reflective dose of traditional glue face height, make reflecting component more wear-resisting, improved service life, be fit to use on various different occasions or the product.

Fig. 1 is that the present invention is applied in the schematic diagram of making the sole reflecting piece;

Fig. 2 is the A partial enlarged drawing among Fig. 1;

Fig. 3 is the 3-3 cutaway view among Fig. 1;

Fig. 4 is the procedure of processing schematic diagram that the present invention makes reflecting component;

Describe method of the present invention and principle in detail below in conjunction with accompanying drawing.

As shown in Figure 1, the present invention is applied in the embodiment that makes the sole reflecting piece, and the reflecting component 2 in footwear body 1 bottom has the outline of a moulding, and the reflecting beads face is set on the surface of outline.

Shown in Fig. 2-4, the preparation method of the reflecting beads face of reflecting component, the object of at first getting a suitable shape is a base material 3; Vacuum plating processing is carried out on the surface of base material 3 handled, form the plating layer 4 that a surperficial cure process is crossed; The surface of platingization layer 4 has higher hardness number, will spray the cover layer 5 that forms a colloid automatically by processing equipment on the platingization layer 4; The cover layer 5 that will contain bonding jelly is placed a period of time, make it be in surperficial doing but the dried yet leather hard of internal layer, naked eyes see it is body of powder, cut-off directly is about the bead particle 6 of 0.06mm-0.15mm, by lance driving device 7 directly with bead particle 6 pressurized jet on half-dried cover layer 5; The coating thickness of cover layer 5 is less than the diameter of each bead 6, when making each bead particle 6 under high pressure inject in the cover layer 5, because of the hardness of bottom platingization layer 4 bigger, with platingization layer 4 stickup contact-making surface as the mirror surface substrate, so each bead 6 will form individual layer and consistent evenly distribution, the colloid bonding of each bead 6 lining cap rock 5 is adhered to fixing simultaneously, the bead 6a that repeats to spray will form reflecting beads face equally distributed and that refractive power curvature is identical at last because of the tripping that runs foul of each other of pearl body.By this technical method, can make with platingization layer 4 easily is the reflective surface of minute surface substrate, the exposed parts of each clear glass pearl particle produces reflection and refraction to light source, and the hardness of bead is higher, and the daily wearing and tearing of wiping repeatedly are less, reflective effect between can keeping often, and filled up colloid cover layer 5 in the gap of 6 of each beades, it belongs to the good material of water proofing property, therefore is not subjected to the erosion of moisture, all the curvature of reflective particles is identical, can reach splendid light source reflecting effect.

Claims

1. A manufacturing method of a reflective member, characterized in that: comprising the following processing steps: one, taking an object of an appropriate shape as the base material; The same plating layer; 3. The plating layer is automatically sprayed by a processing machine to form a colloidal covering layer; 4. The covering layer is stagnated for a period of time so that the surface is dry and the inner layer is still not dry. Semi-dry state; 5. Take glass bead particles with a diameter of 0.06mm-0.15mm, and spray them directly on the semi-dry state covering layer through spray gun equipment; 6. Make each glass bead particle adhere to the colloidal covering layer , and the plating layer is used as the paste contact surface of the mirror substrate to form a uniformly distributed reflective bead surface with the same refractive curvature; the thickness of the sprayed colloid covering layer is less than the diameter of the glass bead particles, and each glass bead particle is embedded in the cover When layering, it will protrude a part of the spherical height, and each glass bead particle is based on the plating layer with higher hardness to stick the contact surface. The light source reflects off the surface.