CN116814129A - 一种蚯蚓纹雅晶石涂料及其制备方法 - Google Patents
一种蚯蚓纹雅晶石涂料及其制备方法 Download PDFInfo
- Publication number
- CN116814129A CN116814129A CN202310757907.1A CN202310757907A CN116814129A CN 116814129 A CN116814129 A CN 116814129A CN 202310757907 A CN202310757907 A CN 202310757907A CN 116814129 A CN116814129 A CN 116814129A
- Authority
- CN
- China
- Prior art keywords
- parts
- earthworm
- pattern
- component
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种蚯蚓纹雅晶石涂料及其制备方法，该涂料包括如下重量份数的原料：聚乙烯醇5‑10份，成膜助剂5‑15份，分散剂3‑8份，丙烯酸酯共聚乳液100‑150份，重钙60‑90份，碳酸钙粉末混合物250‑500份，二氧化硅1‑3份，膨润土5‑7份，润湿剂1‑10份，消泡剂3‑8份，防腐剂1‑10份，增稠剂1‑8份和水100‑200份。该涂料涂覆后具有清晰立体蚯蚓纹装饰效果，并具有良好的耐磨性，可满足消费者多样化的装饰需求。
Description
技术领域
本发明属于涂料技术领域，具体涉及一种蚯蚓纹雅晶石涂料及其制备方法。
背景技术
墙面涂料是指用于建筑墙面起装饰、保护、掩饰墙面缺陷和其他特殊作用的材料，这种材料可以用不同的施工工艺涂覆在物件表面，形成粘附牢固、具有一定强度、连续的固态薄膜。在当下“轻装修、重装饰”盛行的主流装饰意识下，消费者己经不再满足于涂料单调的光泽或颜色变化了，人们希望装饰效果不拘一格，所以要求墙面涂料除了本身的装饰和保护作用外，也要向丰富多彩、时尚健康发展。
艺术涂料是一种新型的墙面装饰艺术材料，其以其新颖的装饰风格，不同寻常的装饰效果，倍受人们的欢迎和推崇，解决了人们个性化审美的需求。艺术型涂料使涂膜表面具有美观清晰的花纹，并且还具有无污染环保的特点。
蚯蚓走泥纹是钧瓷釉面上所形成的类似蚯蚓在泥地上爬过的痕迹，这种痕迹作为钧窑的一种纹饰特征，形状蜿蜒曲折、自然天成，具有独特的技术性。
但现有的艺术涂料并不能很好呈现蚯蚓纹的纹路，大多数纹路模糊，视觉效果差。因此，如何提供一种蚯蚓纹纹理更加清晰的涂料是本领域技术人员急需解决的技术问题。
发明内容
本发明的目的在于提供一种仿蚯蚓纹的雅晶石涂料，其涂覆后具有清晰立体蚯蚓纹装饰效果，并具有良好的耐磨性，可满足消费者多样化的装饰需求。
为了达到上述目的，本发明采用如下技术方案：
一种蚯蚓纹雅晶石涂料，包括如下重量份数的原料：聚乙烯醇5-10份，成膜助剂5-15份，分散剂3-8份，丙烯酸酯共聚乳液100-150份，重钙60-90份，碳酸钙粉末混合物250-500份，二氧化硅1-3份，膨润土5-7份，润湿剂1-10份，消泡剂3-8份，防腐剂1-10份，增稠剂1-8份和水100-200份。
优选的，所述成膜助剂为醇醚酯类成膜助剂。包括但不限于己二醇丁醚醋酸酯、3-乙氧基丙酸乙酯EEP。
优选的，所述分散剂为聚丙烯酸钠和均聚羧酸盐任意比例的组合物。如DISPERSANT8420、DISPERSANT8450等。
优选的，所述碳酸钙粉末混合物物由粒径为50-60目与120-150目的碳酸钙粉末按照1:1-2组成。
优选的，所述表面活性剂选自阴离子表面活性剂、非离子表面活性剂或两性离子表面活性剂。优选阴离子表面活性剂和/或非离子表面活性剂，进一步优选AES、AEO-9、LAS、AEO-7、BS-12、水性卵磷脂、阴离子聚羧酸钠盐、油酸基环氧烷共聚物、聚硅氧烷、聚丙烯酸钠、聚丙烯酸胺、或APG中的1种或至少2种的组合。
优选的，消泡剂为磷酸三丁醋或有机硅。
优选的，所述防腐剂为异噻唑啉酮类杀菌剂。
优选的，所述增稠剂为SL681、1332、TT230、TT9350-100中的任一种，
本发明还公开了上述所述的一种蚯蚓纹雅晶石涂料的制备方法，包括以下步骤：
步骤一：将上述重量份的成膜助剂和膨润土进行预先搅拌混合，获得组分A；
步骤二：将组分A加入等离子差速搅拌机中，按顺序向组分A中依次加入上述重量份数的聚乙烯醇、水、分散剂、润湿剂、防腐剂、丙烯酸酯共聚乳液，搅拌均匀，得组分B；
步骤三：按顺序向组分B中依次加入重钙、二氧化硅，搅拌混合均匀，得组分C；
步骤四：将上述重量份数的增稠剂和水预混合制得混合液，然后将混合液和消泡剂加入组分C中，搅拌混合均匀，得组分D；
步骤五：对组分D进行过滤，加入上述重量份数的碳酸钙砂粉组合物，搅拌均匀，得蚯蚓纹雅晶石涂料。
进一步的，所述步骤一至步骤五中搅拌速度为600-1500r/min，搅拌时间为5-15分钟。
本发明的有益效果：
1、碳酸钙粉末混合物由两种不同粒径大小的碳酸钙颗粒组成，选用两种粒径不同的碳酸钙颗粒能够使蚯蚓纹纹理，花纹更加逼真，装饰效果更好。
2、等离子搅拌机能够将各组分进行充分搅合，消除分子间隙，可以使蚯蚓纹纹理凸显的更加清晰。
3、本发明制备的涂料给墙面创造出生动非凡的艺术效果，立体时尚的纹理效果、多选择的个性搭配，为人们装饰装修提供了宽泛的选择。
4、本发明制备的涂料符合现行国家建筑涂料标准要求及其它环保指标标准要求；而且其施工性好、强度高、高耐刮、抗龟裂、防水耐污。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
一种蚯蚓纹雅晶石涂料，包括如下重量份数的原料：聚乙烯醇5份，成膜助剂己二醇丁醚醋酸酯5份，分散剂DISPERSANT84203份，丙烯酸酯共聚乳液100份，重钙60份，碳酸钙粉末混合物(由粒径为60目与150目的碳酸钙粉末按照1:1组成)250份，二氧化硅1份，膨润土5份，润湿剂AES 1份，消泡剂磷酸三丁醋3份，防腐剂上海环巨科技HO-8811份，增稠剂SL6811份和水100份。
实施例2
一种蚯蚓纹雅晶石涂料，包括如下重量份数的原料：聚乙烯醇10份，成膜助剂3-乙氧基丙酸乙酯EEP15份，分散剂DISPERSANT84508份，丙烯酸酯共聚乳液150份，重钙90份，碳酸钙粉末混合物(由粒径为50目与120目的碳酸钙粉末按照1:2组成)500份，二氧化硅3份，膨润土7份，润湿剂聚丙烯酸钠10份，消泡剂有机硅8份，防腐剂上海环巨科技HO-88110份，增稠剂TT2308份和水200份。
实施例3
一种蚯蚓纹雅晶石涂料，包括如下重量份数的原料：聚乙烯醇7份，成膜助剂己二醇丁醚醋酸酯10份，分散剂DISPERSANT84205份，丙烯酸酯共聚乳液120份，重钙75份，碳酸钙粉末混合物(由粒径为55目与130目的碳酸钙粉末按照1:1.5组成)350份，二氧化硅2份，膨润土6份，润湿剂水性卵磷脂5份，消泡剂磷酸三丁醋5份，防腐剂BIT-205份，增稠剂TT9350-1004份和水150份。
实施例4
一种蚯蚓纹雅晶石涂料，包括如下重量份数的原料：聚乙烯醇8份，成膜助剂3-乙氧基丙酸乙酯EEP12份，分散剂DISPERSANT84504份，丙烯酸酯共聚乳液120份，重钙70份，碳酸钙粉末混合物(由粒径为60目与150目的碳酸钙粉末按照1:1组成)400份，二氧化硅1份，膨润土7份，润湿剂AES1份、APG1份，消泡剂磷酸三丁醋6份，防腐剂BIT-204份，增稠剂SL6812份、13323份和水180份。
实施例5
一种采用实施例1-4任一项配方制备蚯蚓纹雅晶石涂料的方法，包括以下步骤：
步骤一：将上述重量份的成膜助剂和膨润土进行预先搅拌混合，获得组分A；
步骤二：将组分A加入等离子差速搅拌机中，按顺序向组分A中依次加入上述重量份数的聚乙烯醇、水、分散剂、润湿剂、防腐剂、丙烯酸酯共聚乳液，搅拌均匀，得组分B；
步骤三：按顺序向组分B中依次加入重钙、二氧化硅，搅拌混合均匀，得组分C；
步骤四：将上述重量份数的增稠剂和水预混合制得混合液，然后将混合液和消泡剂加入组分C中，搅拌混合均匀，得组分D；
步骤五：对组分D进行过滤，加入上述重量份数的碳酸钙砂粉组合物，搅拌均匀，得蚯蚓纹雅晶石涂料；
步骤一至步骤五中搅拌速度为600-1500r/min，搅拌时间为5-15分钟。
本发明制备的蚯蚓纹雅晶石涂料的涂刷方法：均匀批刮腻子一遍，厚度以有效覆盖基面为宜，要求厚薄均匀。滚涂底漆后不同方向平批蚯蚓纹雅晶石涂料二遍，待表面5成干时，用木刮板打圈方式搓出纹理，约7-8成干再次搓纹理使表面手感平整。
本说明书中各个实施例采用递进的方式描述，每个实施例重点说明的都是与其他实施例的不同之处，各个实施例之间相同相似部分互相参见即可。对所公开的实施例的上述说明，使本领域专业技术人员能够实现或使用本发明。对这些实施例的多种修改对本领域的专业技术人员来说将是显而易见的，本文中所定义的一般原理可以在不脱离本发明的精神或范围的情况下，在其它实施例中实现。因此，本发明将不会被限制于本文所示的这些实施例，而是要符合与本文所公开的原理和新颖特点相一致的最宽的范围。
Claims (10)
1.一种蚯蚓纹雅晶石涂料，其特征在于，包括如下重量份数的原料：聚乙烯醇5-10份，成膜助剂5-15份，分散剂3-8份，丙烯酸酯共聚乳液100-150份，重钙60-90份，碳酸钙粉末混合物250-500份，二氧化硅1-3份，膨润土5-7份，润湿剂1-10份，消泡剂3-8份，防腐剂1-10份，增稠剂1-8份和水100-200份。
2.根据权利要求1所述的一种蚯蚓纹雅晶石涂料，其特征在于，所述成膜助剂为醇醚酯类成膜助剂。
3.根据权利要求1所述一种蚯蚓纹雅晶石涂料，其特征在于，所述分散剂为聚丙烯酸钠和均聚羧酸盐任意比例的组合物。
4.根据权利要求1所述一种蚯蚓纹雅晶石涂料，其特征在于，所述碳酸钙粉末混合物物由粒径为50-60目与120-150目的碳酸钙粉末按照1:1-2组成。
5.根据权利要求1所述的一种蚯蚓纹雅晶石涂料，其特征在于，所述表面活性剂选自阴离子表面活性剂、非离子表面活性剂或两性离子表面活性剂。
6.根据权利要求1所述的一种蚯蚓纹雅晶石涂料，其特征在于，所述消泡剂为磷酸三丁醋或有机硅。
7.根据权利要求1所述的一种蚯蚓纹雅晶石涂料，其特征在于，所述防腐剂为异噻唑啉酮类杀菌剂。
8.根据权利要求1～7任一项所述的一种蚯蚓纹雅晶石涂料，其特征在于，所述增稠剂为SL681、1332、TT230、TT9350-100中的任一种。
9.根据权利要求1～8任一项所述的一种蚯蚓纹雅晶石涂料的制备方法，其特征在于，包括以下步骤：
步骤一：将上述重量份的成膜助剂和膨润土进行预先搅拌混合，获得组分A；
步骤二：将组分A加入等离子差速搅拌机中，按顺序向组分A中依次加入上述重量份数的聚乙烯醇、水、分散剂、润湿剂、防腐剂、丙烯酸酯共聚乳液，搅拌均匀，得组分B；
步骤三：按顺序向组分B中依次加入重钙、二氧化硅，搅拌混合均匀，得组分C；
步骤四：将上述重量份数的增稠剂和水预混合制得混合液，然后将混合液和消泡剂加入组分C中，搅拌混合均匀，得组分D；
步骤五：对组分D进行过滤，加入上述重量份数的碳酸钙砂粉组合物，搅拌均匀，得蚯蚓纹雅晶石涂料。
10.根据权利要求9所述的一种蚯蚓纹雅晶石涂料的制备方法，其特征在于，所述步骤一至步骤五中搅拌速度为600-1500r/min，搅拌时间为5-15分钟。