CN103756566A - 环保内墙乳胶漆 - Google Patents
环保内墙乳胶漆 Download PDFInfo
- Publication number
- CN103756566A CN103756566A CN201110383983.8A CN201110383983A CN103756566A CN 103756566 A CN103756566 A CN 103756566A CN 201110383983 A CN201110383983 A CN 201110383983A CN 103756566 A CN103756566 A CN 103756566A
- Authority
- CN
- China
- Prior art keywords
- environmentally
- emulsion paint
- paint
- wall emulsion
- emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明的环保内墙乳胶漆是乳液性涂料，乳胶漆以水为稀释剂，是一种施工方便、安全、耐水洗、透气性好的漆种，它可根据不同的配色方案调配出不同的色泽，乳胶漆的制作成分中基本上由水、颜料、乳液、填充剂和各种助剂组成，这些原材料是不含什么毒性，是环保型内墙漆种。
Description
一、技术领域
本发明涉及一种内墙漆的制作工艺，特别是环保内墙乳胶漆的制作。
二、背景技术
内墙漆品种繁多，但是各有特点，有的内墙漆存在抗污性弱，耐水耐碱性差；还有的外墙漆缺乏弹性，抗裂性差；有的防霉防藻能力差，容易滋生霉菌和藻类，严重影响墙的外观和使用寿命。还有的内墙漆使用挥发物质，对人的健康不利，不够安全。
一、 发明内容
发明的环保内墙乳胶漆是乳液性涂料，乳胶漆以水为稀释剂，是一种施工方便、安全、耐水洗、透气性好的的漆种，它可根据不同的配色方案调配出不同的色泽，乳胶漆的制作成分中基本上由水、颜料、乳液、填充剂和各种助剂组成，这些原材料是不含什么毒性，是环保型内墙漆种。
本发明具有遮盖力强，附着力大，耐水刷洗，漆膜色泽亮丽持久，抗污染性作用持久的优点。
二、 具体实施方式
1、全过程应按配方准确称量，严格按配方次序添加，
2、称好水，加入消泡剂、AP-95，继续高速搅拌3分钟。
3、在低速搅拌下依次加入4-8，搅拌2分钟，至混合均匀。
4、在高速搅拌下（1200转/分）依次加入9-14，每袋粉剂加入时应
等完全润湿后再加入下一袋。
5、粉剂加完后，高速搅拌30分钟，检查漆浆无异常，停止搅拌。
6、漆浆过40目萝，打入中转罐。
7、经砂磨机研磨一遍，研磨温度不得高于55℃，至细度≤70um。
8、在搅拌罐中加入水，在搅拌下缓慢乳液搅拌10分钟后，加AP-95继续搅拌30分钟，至均匀。
9、在低速搅拌下依次加入20--23，继续搅拌15分钟，至均匀。
10、在低速搅拌下将研磨好的漆浆打入兑稀罐中。
11、在搅拌下缓慢加入混合好的增稠剂。
12、利用后期余水顶车、调整漆的黏度，检测细度。
13、合格后，在漆的温度低于50℃时过80目绢，包装。
要求 细度 黏度 PH值 ≤70um 95±1KU 7--9 。
Claims (2)
1.本发明的环保内墙乳胶漆，其特征在于材料为：去离子水、消泡剂、AP-95、OP-10、分散剂、防腐剂、增白剂、群青、轻钙、高岭土、钛白粉、赛钛白、滑石粉、重钙、乳液。
2. 根据权利要求1所述的环保内墙乳胶漆，其特征在于，各种材料配比为：
去离子水 215 消泡剂 DFC-17 1 AP-95 0.5 OP-10 1 分散剂 5040 5 防腐剂 DECI15 1 增白剂0.5 群青 0.05
轻钙 200 高岭土 50 钛白粉 35 赛钛白 10
滑石粉 325目 70 重钙 400目 200 乳液 TL-615B 120 。