CN103275411A - 一种超薄壁汽车电线用pvc - Google Patents
一种超薄壁汽车电线用pvc Download PDFInfo
- Publication number
- CN103275411A CN103275411A CN2013100633480A CN201310063348A CN103275411A CN 103275411 A CN103275411 A CN 103275411A CN 2013100633480 A CN2013100633480 A CN 2013100633480A CN 201310063348 A CN201310063348 A CN 201310063348A CN 103275411 A CN103275411 A CN 103275411A
- Authority
- CN
- China
- Prior art keywords
- percentage composition
- cent
- calcium carbonate
- pvc
- molecular weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种超薄壁汽车电线用PVC，包括高聚合度PVC树脂含量百分比为60～62％；高分子量增塑剂含量百分比为19～21％；单链高分子量增塑剂含量百分比为3～5％；钙锌稳定剂含量百分比为5～6％；超细微碳酸钙含量百分比为5～6％；纳米碳酸钙含量百分比为5～6％；改性剂含量百分比为1％，采用高聚合度的PVC树脂，高分子量的增塑剂和部分线性高分子量增塑剂，纳米级的碳酸钙做为填充，在保证低温性能的同时满足耐磨性能的要求。
Description
技术领域
本发明涉及一种超薄壁汽车电线用PVC。
背景技术
由于超薄壁汽车电线使用的PVC需要耐105摄氏度，低温-40摄氏度，耐磨性能要求较高，而厚度只有0.2mm，普通的汽车电线PVC无法满足要求。
发明内容
针对上述技术缺陷，本发明提出一种超薄壁汽车电线用PVC。
为了解决上述技术问题，本发明的技术方案如下：
一种超薄壁汽车电线用PVC，包括高聚合度PVC树脂含量百分比为60～62％；高分子量增塑剂含量百分比为19～21％；单链高分子量增塑剂含量百分比为3～5％；钙锌稳定剂含量百分比为5～6％；超细微碳酸钙含量百分比为5～6％；纳米碳酸钙含量百分比为5～6％；改性剂含量百分比为1％。
进一步的，所述高聚合度PVC树脂含量百分比为60％；高分子量增塑剂含量百分比为20％；单链高分子量增塑剂含量百分比为3％；钙锌稳定剂含量百分比为5％；超细微碳酸钙含量百分比为6％；纳米碳酸钙含量百分比为5％；改性剂含量百分比为1％。
进一步的，所述高聚合度PVC树脂含量百分比为62％；高分子量增塑剂含量百分比为19％；单链高分子量增塑剂含量百分比为3％；钙锌稳定剂含量百分比为5％；超细微碳酸钙含量百分比为5％；纳米碳酸钙含量百分比为5％；改性剂含量百分比为1％。
进一步的，所述高聚合度PVC树脂含量百分比为61％；高分子量增塑剂含量 百分比为19％；单链高分子量增塑剂含量百分比为3％；钙锌稳定剂含量百分比为5％；超细微碳酸钙含量百分比为6％；纳米碳酸钙含量百分比为5％；改性剂含量百分比为1％。
本发明的有益效果在于；采用高聚合度的PVC树脂，高分子量的增塑剂和部分线性高分子量增塑剂，纳米级的碳酸钙做为填充，在保证低温性能的同时满足耐磨性能的要求。另外由于该产品中增塑剂含量较少，而且电线产品的绝缘很薄，不需要像普通PVC一样加入三氧化二锑等阻燃剂就能够使电线满足ISO6722的阻燃性能要求。这样既降低了材料的成本，又减少了重金属元素的加入。该产品完全符合RoHS指令要求。该PVC生产出的电线完全满足ISO6722标准中的超薄壁电线的绝缘要求。
具体实施方式
下面将结合具体实施例对本发明做进一步的说明。
一种超薄壁汽车电线用PVC，包括高聚合度PVC树脂含量百分比为60～62％；高分子量增塑剂含量百分比为19～21％；单链高分子量增塑剂含量百分比为3～5％；钙锌稳定剂含量百分比为5～6％；超细微碳酸钙含量百分比为5～6％；纳米碳酸钙含量百分比为5～6％；改性剂含量百分比为1％。
实施例一：
所述高聚合度PVC树脂含量百分比为60％；高分子量增塑剂含量百分比为20％；单链高分子量增塑剂含量百分比为3％；钙锌稳定剂含量百分比为5％；超细微碳酸钙含量百分比为6％；纳米碳酸钙含量百分比为5％；改性剂含量百分比为1％。
实施例二：
所述高聚合度PVC树脂含量百分比为62％；高分子量增塑剂含量百分比为19％；单链高分子量增塑剂含量百分比为3％；钙锌稳定剂含量百分比为5％；超细微碳酸钙含量百分比为5％；纳米碳酸钙含量百分比为5％；改性剂含量百分比为1％。
实施例三：
所述高聚合度PVC树脂含量百分比为61％；高分子量增塑剂含量百分比为19％；单链高分子量增塑剂含量百分比为3％；钙锌稳定剂含量百分比为5％；超细微碳酸钙含量百分比为6％；纳米碳酸钙含量百分比为5％；改性剂含量百分比为1％。
按照实施例一、二或者三任意一种比例制成汽车电线用PVC，其耐磨使用寿命一般为普通pvc的1倍以上，阻燃性能和普通pvc相同。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员，在不脱离本发明构思的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明保护范围内。
Claims (4)
1.一种超薄壁汽车电线用PVC，其特征在于，包括高聚合度PVC树脂含量百分比为60～62％；高分子量增塑剂含量百分比为19～21％；单链高分子量增塑剂含量百分比为3～5％；钙锌稳定剂含量百分比为5～6％；超细微碳酸钙含量百分比为5～6％；纳米碳酸钙含量百分比为5～6％；改性剂含量百分比为1％。
2.根据权利要求1所述的一种超薄壁汽车电线用PVC，其特征在于，所述高聚合度PVC树脂含量百分比为60％；高分子量增塑剂含量百分比为20％；单链高分子量增塑剂含量百分比为3％；钙锌稳定剂含量百分比为5％；超细微碳酸钙含量百分比为6％；纳米碳酸钙含量百分比为5％；改性剂含量百分比为1％。
3.根据权利要求1所述的一种超薄壁汽车电线用PVC，其特征在于，所述高聚合度PVC树脂含量百分比为62％；高分子量增塑剂含量百分比为19％；单链高分子量增塑剂含量百分比为3％；钙锌稳定剂含量百分比为5％；超细微碳酸钙含量百分比为5％；纳米碳酸钙含量百分比为5％；改性剂含量百分比为1％。
4.根据权利要求1所述的一种超薄壁汽车电线用PVC，其特征在于，所述高聚合度PVC树脂含量百分比为61％；高分子量增塑剂含量百分比为19％；单链高分子量增塑剂含量百分比为3％；钙锌稳定剂含量百分比为5％；超细微碳酸钙含量百分比为6％；纳米碳酸钙含量百分比为5％；改性剂含量百分比为1％。