CN103009855A - 一种淋膜转印菲尼尔透镜的制备方法及其制得的产品 - Google Patents
一种淋膜转印菲尼尔透镜的制备方法及其制得的产品 Download PDFInfo
- Publication number
- CN103009855A CN103009855A CN2012105685379A CN201210568537A CN103009855A CN 103009855 A CN103009855 A CN 103009855A CN 2012105685379 A CN2012105685379 A CN 2012105685379A CN 201210568537 A CN201210568537 A CN 201210568537A CN 103009855 A CN103009855 A CN 103009855A
- Authority
- CN
- China
- Prior art keywords
- preparation
- film
- coating
- lens
- thickness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种淋膜转印菲尼尔透镜膜的制备方法及其制得的产品。现有工艺制备菲尼尔透镜一般采用在PVC膜上直接模压或PET膜涂UV层再模压的方法。本发明淋膜转印菲尼尔透镜膜的制备方法采用如下步骤：选择膜载体；喷覆高温熔融的PE材料；压印成型菲尼尔透镜膜。本发明的方法较现有方法相比，成本更低，效率更高。本发明生产的透镜膜经镀铝后，用于高档烟包和出口灯具及化妆品的高档防伪复合膜包装，兼具美观和防伪的特效。
Description
技术领域
本发明属于包装印刷技术领域，具体地说是一种淋膜转印菲尼尔透镜的制备方法及用该方法制得的菲尼尔透镜光学膜。
背景技术
菲尼尔透镜膜又叫猫眼膜、3D冷裱膜，是一种国际新潮装饰包装材料。菲尼尔透镜膜为一种光学透镜阵列成像薄膜，立体感强，透明度高，具有透镜广角效应，缩小图像，扩大视野，能反映观察物数个缩小的图像，因观看效果类似猫眼，故称猫眼膜。菲尼尔透镜属于深纹路压印光学图案，纹路深度达到2.5μm，具有良好的包装美观及防伪效果。
传统工艺制备菲尼尔透镜方法，其一为直接在厚度40-50μm 的PVC薄膜上压印；其二为在PET或BOPP膜上涂覆UV胶，压印后再通过UV光照固化。
发明内容
本发明所要解决的技术问题是克服上述现有菲尼尔透镜制备工艺存在的缺陷，提供一种淋膜转印菲尼尔透镜的制备方法，其用PE淋膜代替PVC膜直接压印或UV光固，以简化生产工序，提高生产效率，降低生产成本。
为此，本发明采用如下的技术方案：一种淋膜转印菲尼尔透镜的制备方法，其步骤如下：
1）选择膜载体：选择厚度为12~20μm的PET电晕膜，电晕面表面张力值≥50dyn；选择PET电晕膜的原因是由于PET具有良好的耐高温性能及拉伸强度，电晕面≥50dyn是为了更好的使PE涂层与PET电晕膜表面贴合。
2）喷淋PE涂层：在PET电晕膜电晕面喷淋熔融指数为2~8的挤塑涂覆型PE材料，形成PE涂层；选用熔融指数2~8的PE材料，而非其他PE材料，是取其良好的挤塑涂覆性能。
3）压印固化：用包覆菲尼尔透镜光学微雕镍版的冷却辊压印并冷却固化PE涂层。
进一步，PE材料的熔融温度为120~130℃；PE涂层厚度为4~5μm；PET电晕膜的厚度为115μm。
进一步，所述冷却辊与PET电晕膜的贴合压力为0.4~0.5Mpa，冷却辊中通温度为20~25℃的冷却水，也可通过其他方式来实现。
本发明所述方法相比第一种现有方法，由于本发明采用厚度12~20μm的PET电晕膜，厚度减小，成本降低，而且本发明能通用于PET、BOPP或其他基膜上制作菲尼尔透镜膜，适用范围广。相比第二种现有方法，本发明无需采用高昂的UV胶及其UV光照设备，而且相比UV光固方式，生产时车速能由15-20m/min提高到80-100m/min，效率也随之提高。
本发明所述制备方法制得的菲尼尔透镜光学膜，其分上、下两层，其中PE涂层的厚度为4~5μm，PET电晕膜的厚度为12~20μm。本发明制得的菲尼尔透镜光学膜主要应用在高档香烟、出口灯具及化妆品等的包装上，包括但不限于以上几方面。
附图说明
图1是本发明的工艺流程图。
图2 是本发明制备的菲尼尔透镜光学膜的结构示意图。
具体实施方式
下面结合说明书附图和具体实施方式对本发明作进一步说明。
如图1所示的淋膜转印菲尼尔透镜的制备方法，其步骤如下：
A.选择膜载体：选择厚度为15μm的PET电晕膜（简称PET膜），电晕面表面张力值≥50dyn。
B.喷淋PE涂层：淋膜通过常用淋膜机加装压印辊来实现，PE涂层涂覆在PET电晕膜的电晕面上，厚度控制在4~5μm，车速为80-100m/min，具体根据熔融PE流速调节。
C.压印固化：用包覆菲尼尔透镜光学微雕镍版的冷却辊压印并冷却固化PE涂层，冷却辊中通循环冷却水，水温为20~25℃为宜。
如图2所示，通过上述方法制备的菲尼尔透镜膜分上下两层，其中PE涂层1厚为4~5μm，PET电晕膜2厚度为15μm，此透镜膜可直接用于制作菲尼尔透镜复合膜。
Claims (5)
1.一种淋膜转印菲尼尔透镜的制备方法，其步骤如下：
1）选择膜载体：选择厚度为12~20μm的PET电晕膜，电晕面表面张力值≥50dyn；
2）喷淋PE涂层：在PET电晕膜电晕面喷淋熔融指数为2~8的挤塑涂覆型PE材料，形成PE涂层；
3）压印固化：用包覆菲尼尔透镜光学微雕镍版的冷却辊压印并冷却固化PE涂层。
2.根据权利要求1所述的制备方法，其特征在于，PE材料的熔融温度为120~130℃，PE涂层厚度为4~5μm。
3.根据权利要求1所述的制备方法，其特征在于，所述冷却辊与PET电晕膜的贴合压力为0.4~0.5Mpa，冷却辊中通温度为20~25℃的冷却水。
4.根据权利要求1所述的制备方法，其特征在于，所述PET电晕膜的厚度为15μm。
5.权利要求1-4任一项所述制备方法制得的菲尼尔透镜光学膜，其特征在于，其分上、下两层，其中PE涂层的厚度为4~5μm，PET电晕膜的厚度为12~20μm。