CN102899577B - 不锈钢合金电阻材料 - Google Patents
不锈钢合金电阻材料 Download PDFInfo
- Publication number
- CN102899577B CN102899577B CN201210154634.3A CN201210154634A CN102899577B CN 102899577 B CN102899577 B CN 102899577B CN 201210154634 A CN201210154634 A CN 201210154634A CN 102899577 B CN102899577 B CN 102899577B
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- steel alloy
- resistive material
- alloy resistive
- mass percent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种不锈钢合金电阻材料，包括化学成分满足C0～0.05％，P0～0.025％，S0～0.020％，Mn0～0.05％，Si0～0.05％，Cr17.0％～19.0％，Ni0.20％～0.60％，Al1.5％～2.2％，Ti0～0.50％，余量为Fe（均为质量百分比）。通过上述方式，本发明不锈钢合金电阻材料用于配电系统中性点接地电阻器，在保证强度高、韧性好、抗氧化性好和阻值稳定的同时，具有电阻率高和电阻温度系数低的优点。
Description
技术领域
本发明涉及电力电网系统领域，尤其涉及一种用于配电系统中性点接地电阻器的不锈钢合金电阻材料。
背景技术
电阻器是电子电路中应用数量最多的元件，通常按功率和阻值形成不同系列，供电路设计者选用。电阻器在电路中主要用来调节和稳定电流与电压，可作为分流器和分压器，也可作电路匹配负载。
配电系统中性点接地电阻器接地的方式在欧美、东亚及南亚等国家已经被广泛的采用。在我国以电缆线路为主的城市配电系统、发电系统，如北京、天津、长三角、珠三角地区等大中型城市的配电网系统，普遍采用了中性点接地电阻器接地方式。现有的中性点接地电阻器其电阻材料通常采用的不同成分组成的不锈钢合金，都具有强度高、韧性好、抗氧化性好和阻值稳定的优点，在整个中性点接地电阻器的工作运行过程中不同成分的不锈钢合金电阻材料呈现出的效果不一样。而现在对其中性点接地电阻器的电阻材料提出更高的要求，在保证强度高、韧性好、抗氧化性好和阻值稳定的同时，电阻率高和电阻温度系数低显得尤为重要，在环境温度变化的情况下，更好的稳定电流与电压，而现有的不锈钢合金电阻材料并不能满足这样的要求。
发明内容
本发明要解决的技术问题是针对现有技术中存在的缺陷，提供了一种电阻率高和电阻温度系数低的不锈钢合金电阻材料。
为了克服背景技术中存在的缺陷，本发明解决其技术问题所采用的技术方案是：一种不锈钢合金电阻材料，包括化学成分满足C 0～0.05％，P 0～0.025％，S 0～0.020％，Mn 0～0.05％，Si 0～0.05％，Cr 17.0％～19.0％，Ni 0.20％～0.60％，Al 1.5％～2.2％，Ti 0～0.50％，余量为Fe（均为质量百分比）。
在本发明的一较佳实施例中，所述Al的含量为1.7％～1.8％。
在本发明的一较佳实施例中，所述不锈钢合金电阻材料热锻成板材结构，表面经喷砂处理。
本发明解决了背景技术中存在的缺陷，使用最佳成分配比，尤其是铝的含量为1.7％～1.8％的情况下，在热处理条件下和冷处理后具有好的组织稳定性，提高了不锈钢合金电阻材料的电阻率和降低了电阻温度系数，更好的稳定电流和电压。
具体实施方式
本实施例中介绍的一种用于配电系统中性点接地电阻器的不锈钢合金电阻材料，包括化学成分满足C 0～0.05％，P 0～0.025％，S 0～0.020％，Mn 0～0.05％，Si 0～0.05％，Cr 17.0％～19.0％，Ni 0.20％～0.60％，Al 1.5％～2.2％，Ti 0～0.50％，余量为Fe（均为质量百分比），其中Al的最佳含量为1.7％～1.8％。不锈钢合金电阻材料热锻成板材结构，边长为240 mm，厚度为3.5 mm的正方形板材，表面经喷砂处理，检测电阻率ρ≧0.8μΩ·m。
实施例1，根据设计的成分配方：C 0.01％，P 0.02％，S 0.01％，Mn 0.03％，Si 0.02％，Cr 17％，Ni 0.3％，Al 1.5％，Ti 0.20％，余量为Fe（均为质量百分比）。经熔炼、油淬和空冷，制成边长为240 mm，厚度为3.5 mm的正方形板材，检测电阻率ρ为0.81μΩ·m。
实施例2，根据设计的成分配方：C 0.03％，P 0.02％，S 0.02％，Mn 0.02％，Si 0.03％，Cr 19％，Ni 0.5％，Al 1.8％，Ti 0.30％，余量为Fe（均为质量百分比）。经熔炼、油淬和空冷，制成边长为240 mm，厚度为3.5 mm的正方形板材，检测电阻率ρ为0.83μΩ·m。
实施例3，根据设计的成分配方：C 0.03％，P 0.02％，S 0.01％，Mn 0.04％，Si 0.05％，Cr 19％，Ni 0.5％，Al 1.7％，Ti 0.50％，余量为Fe（均为质量百分比）。经熔炼、油淬和空冷，制成边长为240 mm，厚度为3.5 mm的正方形板材，检测电阻率ρ为0.085μΩ·m。
实施例4，根据设计的成分配方：C 0.04％，P 0.01％，S 0.02％，Mn 0.04％，Si 0.03％，Cr 17％，Ni 0.6％，Al 1.7％，Ti 0.20％，余量为Fe（均为质量百分比）。经熔炼、油淬和空冷，制成边长为240 mm，厚度为3.5 mm的正方形板材，检测电阻率ρ为1.02μΩ·m。
实施例5，根据设计的成分配方：C 0.05％，P 0.02％，S 0.02％，Mn 0.03％，Si 0.04％，Cr 17％，Ni 0.5％，Al 1.8％，Ti 0.30％，余量为Fe（均为质量百分比）。经熔炼、油淬和空冷，制成边长为240 mm，厚度为3.5 mm的正方形板材，检测电阻率ρ为1.00μΩ·m。
本发明不锈钢合金电阻材料在热处理和冷处理后，具有较好的组织稳定性和良好的机械性能，在保证强度高、韧性好、抗氧化性好和阻值稳定的同时，提高了不锈钢合金电阻材料的电阻率和降低了电阻温度系数，应用在配电系统中性点接地电阻器中可以更好的稳定电流和电压。
以上述依据本发明的理想实施例为启示，通过上述的说明内容，相关工作人员完全可以在不偏离本项发明技术思想的范围内，进行多样的变更以及修改。本项发明的技术性范围并不局限于说明书上的内容，必须要根据权利要求范围来确定其技术性范围。
Claims (2)
1.一种不锈钢合金电阻材料，其特征在于：包括质量百分比的化学成分满足C 0～0.05％，P 0～0.025％，S 0～0.020％，Mn 0～0.05％，Si 0～0.05％，Cr 17.0％～19.0％，Ni 0.20％～0.60％，Al 1.5％～2.2％，Ti 0～0.50％，余量为Fe，
上述中，所述不锈钢合金电阻材料热锻成板材结构，经熔炼、油淬和空冷，制成边长为 240 mm，厚度为 3.5 mm 的正方形板材，表面经喷砂处理，进行冷处理和热处理后检测电阻率ρ≧0.8μΩ·m。
2.根据权利要求1所述的不锈钢合金电阻材料，其特征在于：所述Al质量百分比的含量为1.7％～1.8％。