CN1028375C - 一种钛镍合金箔及板材的制取工艺 - Google Patents
一种钛镍合金箔及板材的制取工艺 Download PDFInfo
- Publication number
- CN1028375C CN1028375C CN 91106230 CN91106230A CN1028375C CN 1028375 C CN1028375 C CN 1028375C CN 91106230 CN91106230 CN 91106230 CN 91106230 A CN91106230 A CN 91106230A CN 1028375 C CN1028375 C CN 1028375C
- Authority
- CN
- China
- Prior art keywords
- titanium
- nickel
- plate
- alloy foil
- nickel alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种钛镍合金箔及板材的制取工艺，其特征在于，制取工艺的步骤如下：将钛、镍板相间叠放，置于金属盒内用真空电子束焊封接；采用热压焊或扩散焊将钛板与镍板焊接起来；热轧减薄；扩散处理，温度800-940℃，保温时间：1个小时以上。本发明可提高成品率，简化生产工艺，降低成本。
Description
本发明系属于合金领域，即提供了一种钛镍合金箔及板材的制取工艺。
钛镍合金除具有形状记忆功能外，还具有超弹性、高阻尼减振性能以及优良的耐腐蚀、抗磨损性能，因此钛镍合金在许多领域中得到了广泛的应用。但是到目前为止，该合金的生产均是采用传统的生产工艺，即：冶炼-锻造-轧制法，这种传统工艺所获得的成品率低、成本高、制取的钛镍箔成本则更高。
为提高成品率，简化生产工艺，降低成本，本发明提供了一种钛镍合金箔及板材的制取工艺。
本发明的主要特征在于将钛和镍板相间叠放、焊合、轧制到每层厚度小于0.05mm，再进行扩散处理，利用镍向钛扩散后形成的连片孔沿揭层获得钛镍合金箔;若想得到钛镍合金板，经扩散处理后再进行一次或多次中间轧制-扩散处理，即可获得钛镍合金板材。
本发明所提供的钛镍合金箔和板材制取工艺流程如下：
（1）将钛、镍板相间叠放，置于金属盒内用真空电子束焊封接;
（2）采用热压焊或扩散焊将钛板与镍板焊接起来;
（3）热轧减薄;
（4）扩散处理，温度：800-940℃
保温时间：1个小时以上。
当制取钛镍合金箔时，热轧减薄每层钛和镍的厚度应减薄到50μm以下，扩散处理后需揭层成箔。当制取钛镍合金板材时，需进行多次扩散-轧制，每次轧制变形量为5-30%。
下面给出本发明所提供的实施例1-一种钛镍合金箔的抽取工艺
将多层的钛板和镍板相间放入金属盒中，同真空电子来焊封，再用真空热压扩散法使钛和镍板之间实现焊接的同时进行热轧减薄，使每层的厚度不大于50μm，然后经900℃，8小时的扩散处理。最后利用扩散形成的连片孔洞分层，得到100μm以下的近等原子比的钛镍合金箔。
实施例2-一种钛镍合金板材制取工艺
将多层等厚度的钛板和镍板相间地放入金属盒中，用真空电子束焊接密封，再用真空热压焊使钛和镍板之间实现焊接，在扩散处理温度为900℃，时间为8小时的条件下进行多次扩散-轧制，得到近等原子比的钛镍合金板，每次轧制变形量为10%。轧制的作用在于消除扩散孔洞，以便扩散过程继续进行。
由本发明所提供的制取工艺生产出的近等原子比的钛镍合金箔与传统的冶炼-锻造-轧制方法相比，不仅工艺简单，成品率高，而且成本仅为传统方法的1/10左右，生产出的钛镍板成本也仅为传统工艺的1/3左右。
Claims (3)
1、一种钛镍合金箔及板材的制取工艺，其特征在于制取工艺的步骤如下：
(1)将钛、镍板相间叠放，置于金属盒内用真空电子束焊封接；
(2)采用热压焊或扩散焊将钛板与镍板焊接起来；
(3)热轧减薄；
(4)扩散处理，温度：800-940℃
保温时间：1个小时以上。
2、按照权利要求1所述钛镍合金箔及板材的制取工艺，其特征在于：当制取钛镍合金箔时，热轧减薄每层钛和镍的厚度应减薄到50μm以下，扩散处理后需揭层成箔。
3、按权利要求1所述钛镍合金箔及板材的制取工艺，其特征在于：当制取钛镍合金板材时，需进行多次扩散-轧制，每次轧制变形量为5～30%。