CN102817152A - Combed polyester-cotton ring spinning abrasive band base fabric - Google Patents
Combed polyester-cotton ring spinning abrasive band base fabric Download PDFInfo
- Publication number
- CN102817152A CN102817152A CN2012102915398A CN201210291539A CN102817152A CN 102817152 A CN102817152 A CN 102817152A CN 2012102915398 A CN2012102915398 A CN 2012102915398A CN 201210291539 A CN201210291539 A CN 201210291539A CN 102817152 A CN102817152 A CN 102817152A
- Authority
- CN
- China
- Prior art keywords
- polyester
- abrasive band
- ring spinning
- band base
- polyester fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a combed polyester-cotton ring spinning abrasive band base fabric, which comprises a plurality of polyester-cotton fiber warp yarns, wherein the polyester-cotton fiber warp yarns are interwove with a plurality of polyester-cotton fiber weft yarns; the polyester-cotton fiber warp yarns and the polyester-cotton fiber weft yarns are interwoven to form a twill weave; and the twill weave is characterized by two-upward and one-downward twills; the warp density is 86-108 pcs/10cm; and the weft density is 48-68 pcs/10cm.The yarn evenness is uniform, the strength is uniform, a fabric face is smooth, the adhesiveness is strong, and the domestic market share and the international competitiveness of the high-end products are effectively improved.
Description
Technical field
The weaving technology field that the present invention relates to spin particularly relates to a kind of combing polyester-cotton blend ring spinning abrasive band base cloth.
Background technology
Scientific and technical innovation, autonomous innovation is fabricated onto China from China and creates, and is the most important thing in the economic work during 12, and scientific and technical innovation, autonomous innovation at first will be carried out intellectual property protection, and protection of Intellectual Property Rights, unique channel are applied for national international monopoly exactly.
Coated abrasive tool, this industry before more than ten years for strange vocabulary of general Chinese Lai Shuoshi; Even the past, there was this respect product demand in some units; Also to rely on import; Because the at that time few of top-grade furniture of common people and the high-grade automobile of China, let alone high standard, high request and high bright and clean luxury goods.Through our industry people unremitting effort during the last ten years, grow out of nothing and expand from small to large, from having to excellent, uninterruptedly researches and develops new product together, not only satisfy domestic demand now, and 20% products export arrives some developed countries in addition, for country strives foreign exchange and honor.Particularly during the 11th Five-Year and after getting into 12.Can use high speed development, swift and violent expansion is represented.
Improving constantly of Along with people's living standard; With people the live closely bound up various service for life articles for use and the various products of all trades and professions, little inside and outside surface finally all needs grinding, cutting and polishing from each parts to entire equipment to train, automobile, aircraft, artillery, guided missile, rocket, artificial satellite, airship, warship, aircraft carrier etc. greatly to family expenses soup ladle, chopsticks.Metal material as; Gold, silver, copper, iron, tin, aluminium, lead etc., alloy material as; Steel alloys such as manganese, nickel, chromium, cobalt, tungsten, nonmetallic materials as; Furniture, wall, leather, glass, stone material, timber, diamond, jewel, diamond, crystal product, oily seven goods or the like all need just can reach accuracy and fineness standard after grinding, cutting and the polishing; And for example each parts is in contact with one another face; Without high-precision grinding, cutting and polishing; Be the accuracy that can't reach desirable, otherwise be not gas leakage, to leak be exactly leakage of oil, can't guarantee normally using and running well of machinery.And cut, grinding, polishing; Understand fully that at first what requirement is the workpiece material that needs to cut, grind, polish have and then select the abrasive band of corresponding cutting, grinding, polishing material, specification, institutional framework and standard to suit the remedy to the case according to the flintiness of material, standard-required; Carry out processed, could realize expected effect and QUALITY STANDARD.
Decision abrasive band quality and standard depend primarily on the technology manufacturing in abrasive band base material and abrasive band.And the base material in abrasive band generally is made up of four major parts, and promptly matrix, binding agent, abrasive material (sand grains) and structure are formed.In the manufacture process in abrasive band, base cloth is one of crucial base material, and its thickness, thin and thick, tearing power, density, intensity, flatness be decisive role all; Base cloth is the foundation in abrasive band, is the supporting body of abrasive band adhesive and abrasive material, also is the supporter in grinding, cutting, the polishing process; Therefore must possess certain TENSILE STRENGTH; Well scratch resistance, less retractility, its performance guarantee the important preceding topic of abrasive band grinding tool quality.
Polyester-cotton blend is meant the general designation of terylene and cotton BLENDED FABRIC, and the textiles that adopts the cotton mixed yarn of 65%-67% terylene and 33%-35% to be made into is commonly called as cotton dacron terylene.Polyester-cotton blend had not only been given prominence to the style of terylene but also the strong point of COTTON FABRIC had been arranged, do, elasticity and ABRASION RESISTANCE are all better under the wet situation, dimensionally stable, washing shrinkage is little, have tall and straight, be difficult for fold, be prone to the characteristics of washing, doing soon, can not use the immersion of hot iron and boiling water.
According to the characteristic of polyester fiber, combing polyester-cotton blend ring spinning abrasive band base cloth should have advantages such as sliver is done evenly, brute force is even, cloth cover is smooth, cohesiveness is strong.But, do not see the announcement of Related product and production Technology both at home and abroad as yet.
Summary of the invention
One of them technical problem to be solved by this invention provides the combing polyester-cotton blend ring spinning abrasive band base cloth that a kind of sliver is done evenly, brute force is even, cloth cover is smooth, cohesiveness is strong.
A kind of combing polyester-cotton blend ring spinning abrasive band base cloth, it comprises:
A plurality of polyester fiber warp thread, said a plurality of polyester fiber warp thread and a plurality of polyester fiber weft yarns interweave,
Said polyester fiber warp thread and said polyester fiber weft yarn are woven into twill-weave,
Said twill-weave is twill once on two;
Its warp-wise density is 86-108/10cm, 48-68/10cm of latitudinal density.
As a kind of preferred version of combing polyester-cotton blend ring spinning according to the invention abrasive band base cloth, wherein said polyester fiber is formed through the RING SPINNING spinning after combing is removed impurity, short flannel, contrary fine adding terylene short fiber by cotton again.
As a kind of preferred version of combing polyester-cotton blend ring spinning according to the invention abrasive band base cloth, wherein said polyester fiber warp thread and said polyester fiber weft yarn are woven into the angle that interweaves of certain angle.
As a kind of preferred version of combing polyester-cotton blend ring spinning according to the invention abrasive band base cloth, the angle that interweaves of wherein said certain angle is 30 °～60 °.
The combing polyester-cotton blend ring spinning abrasive band base cloth that the present invention adopts polyester fiber to carry out processing has the incomparable advantage of other types base cloth: sliver is done evenly, brute force is even, cloth cover is smooth, cohesiveness is strong.This invention is applied widely, is metal material, alloy material, hard alloy material, the grinding of high-grade stone product, cutting, the desirable selection of polishing.The present invention has filled up domestic and international blank, has solved the U.S. and European Union's high-tech product and such base cloth product restricted problem to China's outlet, has effectively improved high-end product occupation rate of market and international competitiveness at home.
Description of drawings
Fig. 1 be combing polyester-cotton blend ring according to the invention spinning abrasive band base cloth two on once the twill base cloth organize sketch map.
Fig. 2 be combing polyester-cotton blend ring according to the invention spinning abrasive band base cloth two on the cross-sectional view of twill base cloth once.
The specific embodiment
Below in conjunction with concrete embodiment production method according to the invention is elaborated.
Like Fig. 1～shown in Figure 2, among the figure, 1, warp thread; 1a, through interlacing point; 2, weft yarn; 3, the angle that interweaves.
Alleged here " embodiment " or " embodiment " are meant special characteristic, structure or the characteristic that can be contained at least one implementation of the present invention.Different in this manual local " in one embodiment " that occur not are all to refer to same embodiment, neither be independent or optionally mutually exclusive with other embodiment embodiment.
As shown in Figure 1, Fig. 1 for combing polyester-cotton blend ring according to the invention spinning abrasive band base cloth two on once the twill base cloth organize sketch map.In this embodiment; This combing polyester-cotton blend ring spinning abrasive band base cloth comprises a plurality of polyester fiber warp thread 1, and said a plurality of polyester fiber warp thread 1 interweave with a plurality of polyester fiber weft yarns 2, and said polyester fiber warp thread 1 is woven into twill-weave with said polyester fiber weft yarn 2; When polyester fiber warp thread 1 is on fiber weft yarn 2, be through interlacing point 1a; And this twill-weave is twill once on two, and its warp-wise density is 86-108/10cm, 48-68/10cm of latitudinal density.
As shown in Figure 2, Fig. 2 is the cross-sectional view of combing polyester-cotton blend ring spinning according to the invention abrasive band base cloth.In this embodiment, polyester fiber warp thread 1 and said polyester fiber weft yarn 2 are woven on two twill-weave once, and polyester fiber warp thread 1 and said polyester fiber weft yarn 2 are woven into the angle 3 that interweaves of certain angle.
Preferably, polyester fiber warp thread 1 and said polyester fiber weft yarn 2 are woven into 30 °～60 ° the angle 3 that interweaves.
Method for simplifying flow process in its actual production is: the cotton vanning, and----------------------------------------------weaving cotton cloth,----check is dispatched from the factory--supplies to make the abrasive band base cloth to sizing to warping to spun yarn to rove to drafting three to drafting two to drafting one to blowing to blowing to go up axle to wear palm fibre in the winder packing in comb and parallel cotton fibers prior to spinning for bar and the vanning of volume+terylene short fiber in combing in comb and parallel cotton fibers prior to spinning.
The main specifications of this kind combing polyester-cotton blend ring spinning abrasive band base cloth is in the actual production:
J: after the cotton combing of combing spinning process JT/C with big chemical fibre blending
Standard proportional 65 is washed 35 cottons
Utilize this production method to adopt the combing spinning process; Impurity, short flannel, different fibre, contrary fibre in the cotton are removed and the terylene short fiber blending, and prepared combing polyester-cotton blend ring spinning abrasive band base cloth has the incomparable advantage of other types base cloth: sliver is dried evenly, powerful evenly, cloth cover is smooth, cohesive is strong.This invention is applied widely, is metal material, alloy material, hard alloy material, the grinding of high-grade stone product, cutting, the desirable selection of polishing.The present invention has filled up domestic and international blank, has solved the U.S. and European Union's high-tech product and such base cloth product restricted problem to China's outlet, has effectively improved high-end product occupation rate of market and international competitiveness at home.
What should explain is; Above embodiment is only unrestricted in order to technical scheme of the present invention to be described; Although with reference to preferred embodiment the present invention is specified, those of ordinary skill in the art should be appreciated that and can make amendment or be equal to replacement technical scheme of the present invention; And not breaking away from the spirit and the scope of technical scheme of the present invention, it all should be encompassed in the middle of the claim scope of the present invention.
Claims (4)
1. combing polyester-cotton blend ring spinning abrasive band base cloth; It is characterized in that: said combing polyester-cotton blend ring spinning abrasive band base cloth comprises: a plurality of polyester fiber warp thread; Said a plurality of polyester fiber warp thread and a plurality of polyester fiber weft yarns interweave; Said polyester fiber warp thread and said polyester fiber weft yarn are woven into twill-weave, and said twill-weave is twill once on two; Its warp-wise density is 86-108/10cm, 48-68/10cm of latitudinal density.
2. combing polyester-cotton blend ring spinning as claimed in claim 1 abrasive band base cloth is characterized in that: said polyester fiber is formed through the RING SPINNING spinning after combing is removed impurity, short flannel, contrary fine adding terylene short fiber by cotton again.
3. combing polyester-cotton blend ring spinning as claimed in claim 1 abrasive band base cloth, it is characterized in that: said polyester fiber warp thread and said polyester fiber weft yarn are woven into the angle that interweaves of certain angle.
4. combing polyester-cotton blend ring spinning as claimed in claim 2 abrasive band base cloth, it is characterized in that: the angle that interweaves of said certain angle is 30 °～60 °.