[go: up one dir, main page]

CN102634105A - 柔软型无卤阻燃电缆料 - Google Patents

柔软型无卤阻燃电缆料 Download PDF

Info

Publication number
CN102634105A
CN102634105A CN2011100361699A CN201110036169A CN102634105A CN 102634105 A CN102634105 A CN 102634105A CN 2011100361699 A CN2011100361699 A CN 2011100361699A CN 201110036169 A CN201110036169 A CN 201110036169A CN 102634105 A CN102634105 A CN 102634105A
Authority
CN
China
Prior art keywords
parts
retardant cable
type non
halogen flame
soft type
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2011100361699A
Other languages
English (en)
Other versions
CN102634105B (zh
Inventor
吴彤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Hanyang Precision Electronics Co Ltd
Original Assignee
Suzhou Hanyang Precision Electronics Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Hanyang Precision Electronics Co Ltd filed Critical Suzhou Hanyang Precision Electronics Co Ltd
Priority to CN201110036169.9A priority Critical patent/CN102634105B/zh
Publication of CN102634105A publication Critical patent/CN102634105A/zh
Application granted granted Critical
Publication of CN102634105B publication Critical patent/CN102634105B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种柔软型无卤阻燃电缆料，其成分按重量份数表示包括：聚烯烃树脂20～40份，热塑性弹性体1～10份，填充油1～10份，相容剂2～10份，无机阻燃剂40～60份，协效阻燃剂3～10份，润滑剂1～5份，偶联剂0.4～1.2份，抗氧剂0.1～0.5份。本发明的柔软型无卤阻燃电缆料通过采用低硬度热塑性弹性体与聚烯烃类树脂共混，在保持其良好的机械性能外，使该电缆料的柔软度得到很大提高，从而扩大了电缆料的使用范围。

Description

柔软型无卤阻燃电缆料
【技术领域】
本发明涉及一种电缆料，具体涉及一种柔软型无卤阻燃电缆料。
【背景技术】
由于聚烯烃具有相对密度小、耐化学药品性、耐水性好、良好的机械强度、电绝缘性等特点，具有弹性同时能保持良好热塑性能的聚烯烃组合物已经广泛应用于各种领域中，例如可用于薄膜、管材、板材、各种成型制品、电线电缆中等。
当聚烯烃应用于电线电缆中时，聚烯烃无卤阻燃电缆料为了增加其阻燃性，会填充大量的无机型阻燃材料，如氢氧化镁、氢氧化铝等用来阻燃，但填入大量无机阻燃材料的同时，导致电缆线材料硬度增加，不适用于要求电缆线柔软的场合。
有鉴于此，实有必要开发一种柔软型无卤阻燃电缆料，该柔软型无卤阻燃电缆料在保持良好的机械性能外，提高了其柔软度，扩大了电缆料的使用范围。
【发明内容】
因此，本发明的目的是提供一种柔软型无卤阻燃电缆料，该柔软型无卤阻燃电缆料在保持良好的机械性能外，提高了其柔软度，扩大了电缆料的使用范围。
为了达到上述目的，本发明的柔软型无卤阻燃电缆料，其成分按重量份数表示包括：
聚烯烃树脂    20～40份
热塑性弹性体  1～10份
填充油        1～10份
相容剂        2～10份
无机阻燃剂    40～60份
协效阻燃剂    3～10份
润滑剂        1～5份
偶联剂        0.4～1.2份
抗氧剂        0.1～0.5份。
较佳的，上述聚烯烃树脂为乙烯-醋酸乙烯共聚物、乙烯-丙烯酸乙酯共聚物、乙烯-辛烯共聚物中的一种或多种混合物。
较佳的，上述热塑性弹性体为苯乙烯类热塑性弹性体、聚乙烯类热塑性弹性体中的一种或其混合物。
较佳的，上述填充油为石蜡油、环烷油中的一种或其混合物。
较佳的，上述相容剂为POE-g-MAH(马来酸酐官能团接枝乙烯-辛烯共聚物)、EVA-g-MAH(马来酸酐官能团接枝乙烯-醋酸乙烯共聚物)中的一种或其混合物。
较佳的，上述无机阻燃剂为氢氧化镁、氢氧化铝中的一种或其混合物。
较佳的，上述协效阻燃剂为硼酸锌、氧化锌、红磷中的一种或多种混合物。
较佳的，上述润滑剂为EBS(乙撑双硬脂酸酰胺)、硬脂酸锌、硬脂酸钙、聚乙烯蜡中的一种或多种混合物。
较佳的，上述偶联剂为硅烷偶联剂KH172、硅烷偶联剂KH550、硅烷偶联剂KH171中的一种或多种混合物。
较佳的，上述抗氧剂为抗氧剂1010、抗氧剂1076、抗氧剂168中的一种或多种混合物。
较佳的，该柔软型无卤阻燃电缆料其成分按重量份数表示包括：
乙烯-醋酸乙烯共聚物    23份
苯乙烯类热塑性弹性体   5份
石蜡油                 5份
POE-g-MAH              3.5份
氢氧化镁               57份
硼酸锌                 3.5份
EBS                    2份
KH172                  0.5份
抗氧剂1010             0.5份。
较佳的，该柔软型无卤阻燃电缆料其成分按重量份数表示包括：
乙烯-辛烯共聚物        31份
苯乙烯类热塑性弹性体   5份
石蜡油                 5份
POE-g-MAH              3份
氢氧化镁               25份
氢氧化铝               25份
硼酸锌                 3份
EBS                    2份
KH172                  0.5份
抗氧剂1010             0.5份。
本发明的柔软型无卤阻燃电缆料，通过采用低硬度热塑性弹性体与聚烯烃类树脂共混，在保持良好的机械性能外，其柔软性得到大大提升，扩大了电缆料的使用范围。
【具体实施方式】
以下结合实施例对本发明作出进一步说明。
实施例1
取各种添加成分，于本实施例中，聚烯烃树脂采用乙烯-醋酸乙烯共聚物，热塑性弹性体采用苯乙烯类热塑性弹性体，填充油采用石蜡油，相容剂采用POE-g-MAH，无机阻燃剂采用氢氧化镁，协效阻燃剂采用硼酸锌，润滑剂采用EBS，偶联剂采用硅烷偶联剂KH172，抗氧剂采用抗氧剂1010，按下述组成配方将所有原料进行共混：
乙烯-醋酸乙烯共聚物       23份
苯乙烯类热塑性弹性体      5份
石蜡油                    5份
POE-g-MAH                 3.5份
氢氧化镁                  57份
硼酸锌                    3.5份
EBS                       2份
KH172                     0.5份
抗氧剂1010                0.5份
再将该共混料通过挤出机混炼造粒，所得混炼造粒经注射成型制成成品，最后按国家标准测试所得成品的机械性能、氧指数、邵氏硬度，结果如表1所示：
表1：实施例1提供的柔软型无卤阻燃电缆料的性能数据表
  性能   测试方法   测试结果
  拉伸强度/MPa(200mm/min)   GB/T1040-2006   10.6
  断裂伸长率/(200mm/min)   GB/T1040-2006   187
  氧指数   GB/T2408-2009   37
  邵氏硬度   -   92A
实施例2
取各种添加成分，于本实施例中，聚烯烃树脂采用乙烯-醋酸乙烯共聚物，热塑性弹性体采用苯乙烯类热塑性弹性体，填充油采用石蜡油，相容剂采用POE-g-MAH，无机阻燃剂采用氢氧化镁和氢氧化铝的混合物，协效阻燃剂采用硼酸锌，润滑剂采用EBS，偶联剂采用硅烷偶联剂KH172，抗氧剂采用抗氧剂1010，按下述组成配方将所有原料进行共混：
乙烯-辛烯共聚物         31份
苯乙烯类热塑性弹性体    5份
石蜡油                  5份
POE-g-MAH               3份
氢氧化镁                25份
氢氧化铝                25份
硼酸锌         3份
EBS            2份
KH172          0.5份
抗氧剂1010     0.5份
再将该共混料通过挤出机混炼造粒，所得混炼造粒经注射成型制成成品，最后按国家标准测试所得成品的机械性能、氧指数、邵氏硬度，结果如表2所示：
表2：实施例2提供的柔软型无卤阻燃电缆料的性能数据表
  性能   测试方法   测试结果
  拉伸强度/MPa(200mm/min)   GB/T1040-2006   9.5
  断裂伸长率/(200mm/min)   GB/T1040-2006   220
  氧指数   GB/T2408-2009   30
  邵氏硬度   -   88A
相较于现有技术，本发明的柔软型无卤阻燃电缆料通过采用低硬度热塑性弹性体与聚烯烃类树脂共混，在保持其良好的机械性能外，使该电缆料的柔软度得到很大提高，从而扩大了电缆料的使用范围。

Claims (12)

1.一种柔软型无卤阻燃电缆料，其特征在于，该柔软型无卤阻燃电缆料其成分按重量份数表示包括：
聚烯烃树脂    20～40份
热塑性弹性体  1～10份
填充油        1～10份
相容剂        2～10份
无机阻燃剂    40～60份
协效阻燃剂    3～10份
润滑剂        1～5份
偶联剂        0.4～1.2份
抗氧剂        0.1～0.5份。
2.根据权利要求1所述的柔软型无卤阻燃电缆料，其特征在于，所述的聚烯烃树脂为乙烯-醋酸乙烯共聚物、乙烯-丙烯酸乙酯共聚物、乙烯-辛烯共聚物中的一种或多种混合物。
3.根据权利要求1所述的柔软型无卤阻燃电缆料，其特征在于，所述的热塑性弹性体为苯乙烯类热塑性弹性体、聚乙烯类热塑性弹性体中的一种或其混合物。
4.根据权利要求1所述的柔软型无卤阻燃电缆料，其特征在于，所述的填充油为石蜡油、环烷油中的一种或其混合物。
5.根据权利要求1所述的柔软型无卤阻燃电缆料，其特征在于，所述的相容剂为POE-g-MAH、EVA-g-MAH中的一种或其混合物。
6.根据权利要求1所述的柔软型无卤阻燃电缆料，其特征在于，所述的无机阻燃剂为氢氧化镁、氢氧化铝中的一种或其混合物。
7.根据权利要求1所述的柔软型无卤阻燃电缆料，其特征在于，所述的协效阻燃剂为硼酸锌、氧化锌、红磷中的一种或多种混合物。
8.根据权利要求1所述的柔软型无卤阻燃电缆料，其特征在于，所述的润滑剂为EBS、硬脂酸锌、硬脂酸钙、聚乙烯蜡中的一种或多种混合物。
9.根据权利要求1所述的柔软型无卤阻燃电缆料，其特征在于，所述的偶联剂为硅烷偶联剂KH172、硅烷偶联剂KH550、硅烷偶联剂KH171中的一种或多种混合物。
10.根据权利要求1所述的柔软型无卤阻燃电缆料，其特征在于，所述的抗氧剂为抗氧剂1010、抗氧剂1076、抗氧剂168中的一种或多种混合物。
11.根据权利要求1至10中任一项所述的柔软型无卤阻燃电缆料，其特征在于，该柔软型无卤阻燃电缆料其成分按重量份数表示包括：
乙烯-醋酸乙烯共聚物      23份
苯乙烯类热塑性弹性体     5份
石蜡油                   5份
POE-g-MAH                3.5份
氢氧化镁                 57份
硼酸锌                   3.5份
EBS                      2份
KH172                    0.5份
抗氧剂1010               0.5份。
12.根据权利要求1至10中任一项所述的柔软型无卤阻燃电缆料，其特征在于，该柔软型无卤阻燃电缆料其成分按重量份数表示包括：
乙烯-辛烯共聚物        31份
苯乙烯类热塑性弹性体   5份
石蜡油                 5份
POE-g-MAH              3份
氢氧化镁               25份
氢氧化铝               25份
硼酸锌                 3份
EBS                    2份
KH172                  0.5份
抗氧剂1010             0.5份。
CN201110036169.9A 2011-02-11 2011-02-11 柔软型无卤阻燃电缆料 Expired - Fee Related CN102634105B (zh)