CN102311858A - Lubricant for assembling rubber articles and metal parts, and manufacturing method thereof - Google Patents
Lubricant for assembling rubber articles and metal parts, and manufacturing method thereof Download PDFInfo
- Publication number
- CN102311858A CN102311858A CN201110241903A CN201110241903A CN102311858A CN 102311858 A CN102311858 A CN 102311858A CN 201110241903 A CN201110241903 A CN 201110241903A CN 201110241903 A CN201110241903 A CN 201110241903A CN 102311858 A CN102311858 A CN 102311858A
- Authority
- CN
- China
- Prior art keywords
- parts
- lubricant
- metalwork
- weight parts
- ppm
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a lubricant for assembling rubber articles and metal parts, and a manufacturing method thereof. The lubricant comprises the following raw materials, by weight, 10-60 parts of phytic acid, 40-70 parts of triethanolamine, and 200-500 parts of distilled water. The manufacturing method of the lubricant comprises the following steps: 1, proportionally mixing the phytic acid, triethanolamine and distilled water; 2, heating the phytic acid, triethanolamine and distilled water which are well mixed in step 1 to 75-85DEG C, fully and uniformly stirring manually or with a small mixer to prepare the lubricant, wherein the artificial stirring time is 25-35min, and the stirring time of the small mixer is 15-20min; and 3, cooling to normal temperature for later use after fully and uniformly stirring the lubricant. The lubricant which has the characteristics of good lubricity and anticorrosion and antirust property can provide lubrication for the rubber articles and the metal parts, so assembling the rubber articles and the metal parts is convenient; and the lubricant also can provide anticorrosion and antirust property for the rubber articles and the metal parts.
Description
Technical field
The present invention relates to the assembling of rubber parts and metalwork with lubricator and preparation method thereof.
Background technology
Automobile vibration isolation piece, rubber bushing rubber parts such as (vulcanizations of rubber) assemble with metalwork usually; Play shockproof effect, frictional force is bigger during owing to rubber parts and metalwork relative movement, for ease of installing; For preventing the rubber parts wearing and tearing, must make with lubricator auxiliary when press-fiting simultaneously.When making with lubricator, lubricant can not have side effects when being convenient to the assembling of rubber parts and metalwork, promptly must not corroding metal spare, as cause that metalwork gets rusty etc.
Rubber parts material general and the metalwork assembling is tree elastomer (a NR rubber), and the lubricant of selecting for use has following two kinds: the one, and, directly do lubricant and use with machinery oil; The 2nd, do lubricant with liquid detergent and use; Machinery oil is that tree elastomer spare does not possess the oil resistant function as the defective of lubricant, can corrode rubber parts with machinery oil, influences the assembling stability of rubber parts and metalwork, and then influences the product shockproof properties; Liquid detergent has solved not oil resistant problem of rubber as lubricant, but the easy corroding metal spare of the moisture that contains in the liquid detergent causes that the metallic surface is oxidized gets rusty, and influences the work-ing life and the use properties of metalwork.
Summary of the invention
The objective of the invention is to overcome the deficiency of prior art, a kind of rubber parts and metalwork assembling of both being convenient to is provided, the rubber parts that effective protection can be provided again and metalwork assemble with lubricator and preparation method thereof.
To achieve these goals, the technical scheme of the present invention's employing is:
Described rubber parts and metalwork assemble with lubricator, and said lubricant is made up of following raw material: vegetable oil acid 10～60 weight parts, trolamine 40～70 weight parts, zero(ppm) water 200～500 weight parts.
Said rubber parts and metalwork assembling making method with lubricator may further comprise the steps;
(1) with vegetable oil acid, trolamine, zero(ppm) water proportional mixing;
(2) vegetable oil acid, trolamine and the zero(ppm) water that step (1) is mixed is heated to 75～85 ℃; Craft is stirred or is utilized pony mixer to stir then; Process lubricant, the hand mixing time is 25～35 minutes, and the pony mixer churning time is 15～20 minutes;
(3) after lubricant stirred, it was for use to be cooled to normal temperature.
Vegetable oil acid and trolamine Hybrid Heating and stir after make trihydroxy ethylamine oleate soap; The trihydroxy ethylamine oleate soap that trolamine and vegetable oil acid mix has characteristic: be the tawny paste; Solubilized, be scattered in the water; The back pH value that is dissolved in the water is 8-9, and content can reach more than 99% in the water; Trihydroxy ethylamine oleate soap has good emulsifying property, and is antiseptic and rustproof effective.
The invention has the advantages that: the assembling of said rubber parts and metalwork with lubricator and preparation method thereof; By making after vegetable oil acid and the trolamine Hybrid Heating; Oil-containing and water do not have good lubricity and antiseptic and rustproof property, on the one hand; Can provide lubricated for the assembling of metalwork and rubber parts, be convenient to the two assembling; Can good protection be provided for metalwork and rubber parts on the other hand, can guarantee the assembling stability of rubber parts and metalwork, guarantee the shockproof properties of product; Said lubricant ME is simple simultaneously, is convenient to control, convenient in application.
Embodiment
Through the description to embodiment, specific embodiments of the invention is done further detailed explanation below.
Embodiment one
Said rubber parts and metalwork assemble with lubricator, and said lubricant is made up of following raw material: 10 parts of vegetable oil acids, 40 parts of trolamines, 200 parts of zero(ppm) water.
Said rubber parts and metalwork assembling making method with lubricator are at first with 10 parts of vegetable oil acids, 40 parts of trolamines, 200 parts of zero(ppm) water proportional mixing; Again the vegetable oil acid that mixes, trolamine and zero(ppm) water are heated to 75 ℃, craft is stirred or is utilized pony mixer to stir then, processes lubricant, and the hand mixing time is 25 minutes, and the pony mixer churning time is 15 minutes; After lubricant stirred, it was for use to be cooled to normal temperature.
Embodiment two
Said rubber parts and metalwork assemble with lubricator, and said lubricant is made up of following raw material: 60 parts of vegetable oil acids, 70 parts of trolamines, 500 parts of zero(ppm) water.
Said rubber parts and metalwork assembling making method with lubricator are at first with 60 parts of vegetable oil acids, 70 parts of trolamines, 500 parts of zero(ppm) water proportional mixing; Again the vegetable oil acid that mixes, trolamine and zero(ppm) water are heated to 85 ℃, craft is stirred or is utilized pony mixer to stir then, processes lubricant, and the hand mixing time is 35 minutes, and the pony mixer churning time is 20 minutes; After lubricant stirred, it was for use to be cooled to normal temperature.
Embodiment three
Said rubber parts and metalwork assemble with lubricator, and said lubricant is made up of following raw material: 30 parts of vegetable oil acids, 55 parts of trolamines, 350 parts of zero(ppm) water.
Said rubber parts and metalwork assembling making method with lubricator are at first with 30 parts of vegetable oil acids, 55 parts of trolamines, 350 parts of zero(ppm) water proportional mixing; Again the vegetable oil acid that mixes, trolamine and zero(ppm) water are heated to 80 ℃, craft is stirred or is utilized pony mixer to stir then, processes lubricant, and the hand mixing time is 30 minutes, and the pony mixer churning time is 18 minutes; After lubricant stirred, it was for use to be cooled to normal temperature.
Embodiment four
Said rubber parts and metalwork assemble with lubricator, and said lubricant is made up of following raw material: 48 parts of vegetable oil acids, 52 parts of trolamines, 300 parts of zero(ppm) water.
Said rubber parts and metalwork assembling making method with lubricator are at first with 48 parts of vegetable oil acids, 52 parts of trolamines, 300 parts of zero(ppm) water proportional mixing; Again the vegetable oil acid that mixes, trolamine and zero(ppm) water are heated to 79 ℃, craft is stirred or is utilized pony mixer to stir then, processes lubricant, and the hand mixing time is 28 minutes, and the pony mixer churning time is 20 minutes; After lubricant stirred, it was for use to be cooled to normal temperature.
The rubber parts and the metalwork assembling that are made by embodiment one to embodiment four with lubricator all have good antiseptic and rustproof effect, and be best with the lubricant result of use that embodiment four makes, and not only be convenient to the assembling of rubber parts and metalwork, and antiseptic and rustproof effect is best.
Above the present invention has been carried out exemplary description; Obviously the concrete realization of the present invention does not receive the restriction of aforesaid way; As long as adopted the improvement of the various unsubstantialities that method of the present invention design and technical scheme carry out; Or design of the present invention and technical scheme are directly applied to other occasion without improving, all within protection scope of the present invention.
Claims (5)
1. rubber parts and metalwork assemble with lubricator, and it is characterized in that: said lubricant is made up of following raw material: vegetable oil acid 10～60 weight parts, trolamine 40～70 weight parts, zero(ppm) water 200～500 weight parts.
2. assemble with lubricator according to described rubber parts of claim 1 and metalwork, it is characterized in that: said vegetable oil acid is 10～30 weight parts, and said trolamine is 40～55 weight parts, and said zero(ppm) water is 200～350 weight parts.
3. assemble with lubricator according to described rubber parts of claim 1 and metalwork, it is characterized in that: said vegetable oil acid is 30～60 weight parts, and said trolamine is 55～70 weight parts, and said zero(ppm) water is 350～500 weight parts.
4. assemble with lubricator according to described rubber parts of claim 1 and metalwork, it is characterized in that: said vegetable oil acid is 30～48 weight parts, and said trolamine is 40～52 weight parts, and said zero(ppm) water is 200～300 weight parts.
5. any one described rubber parts of claim 1 to 4 and metalwork assembling making method with lubricator is characterized in that: may further comprise the steps;
(1) with vegetable oil acid, trolamine, zero(ppm) water proportional mixing;
(2) vegetable oil acid, trolamine and the zero(ppm) water that step (1) is mixed is heated to 75～85 ℃; Craft is stirred or is utilized pony mixer to stir then; Process lubricant, the hand mixing time is 25～35 minutes, and the pony mixer churning time is 15～20 minutes;
(3) after lubricant stirred, it was for use to be cooled to normal temperature.