CN102039328A - 一种白铜合金冷凝管热型连铸-连续拉伸方法 - Google Patents
一种白铜合金冷凝管热型连铸-连续拉伸方法 Download PDFInfo
- Publication number
- CN102039328A CN102039328A CN 201010569484 CN201010569484A CN102039328A CN 102039328 A CN102039328 A CN 102039328A CN 201010569484 CN201010569484 CN 201010569484 CN 201010569484 A CN201010569484 A CN 201010569484A CN 102039328 A CN102039328 A CN 102039328A
- Authority
- CN
- China
- Prior art keywords
- pipe
- equal
- diameter
- carrying
- continuous
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种白铜合金冷凝管热型连铸-连续拉伸方法，其特征在于，所述方法包括以下步骤：1)通过热型连铸得到白铜管坯；2)对管坯进行拉伸处理；3)进行3道次拉伸；4)最后进行联拉、精整、清洗和成品退火得到成品。对直径大于等于1mm小于等于50mm的管坯进行联拉，并进行3道次盘拉伸。对直径大于50mm小于等于108mm的管坯进行联拉，并进行3道次直条拉伸。对直径大于108mm小于等于319mm的管坯进行联拉，并进行3道次扩径拉伸。本发明可以减少工艺环节、提高铸造成材率、降低铸锭加热-挤压工序能耗、大幅降低成本。
Description
技术领域
本发明涉及一种白铜合金管材的制备方法，尤其涉及一种白铜合金冷凝管热型连铸-连续拉伸方法。
背景技术
现有铜合金冷凝管生产工艺流程参见图1，可见，现有技术采用立式半连铸工艺生产实心铸锭，定尺锯切为400-600mm长的短锭，将短锭加热至800-1000℃（视合金种类不同而不同），在双动挤压机上进行穿孔挤压得到空心管坯。对管坯进行定尺锯切、矫直、酸洗后进行皮尔格轧制。对轧制管坯需要裁切为4-6m的短管，随后退火、酸洗、制头、拉伸；拉伸后的管坯还需要裁切为4-6m的短管，随后再次退火、酸洗、制头、拉伸；如此反复3-5次，工艺流程长，生产道次多；挤压加热、反复退火，能耗极高；挤压工序工装损耗大、成本高；酸洗工序金属损耗大。特别是制品品质低、无法生产超长铜合金冷凝管。
发明内容
有鉴于此，本发明的目的是提供一种白铜合金冷凝管热型连铸-连续拉伸方法，其能够解决上述问题。
上述目的是通过下述方案实现的：
一种白铜合金冷凝管热型连铸-连续拉伸方法，其特征在于，所述方法包括以下步骤：
1)通过热型连铸得到白铜管坯；
2)对管坯进行拉伸处理；
3)进行3道次拉伸；
4)最后进行联拉、精整、清洗和成品退火得到成品。
根据上述方法，其特征在于，在步骤2)中是对直径大于等于1mm小于等于50mm的管坯进行联拉，并在步骤3)中进行的3道次拉伸为盘拉伸。
根据上述方法，其特征在于，在步骤2)中是对直径大于50mm小于等于108mm的管坯进行联拉，并在步骤3)中进行的3道次拉伸为直条拉伸。
根据上述方法，其特征在于，在步骤2)中是对直径大于108mm小于等于319mm的管坯进行联拉，并在步骤3)中进行的3道次拉伸为扩径拉伸。
本发明的生产工艺较传统工艺减少工艺环节60%；提高铸造成材率9%左右；省略了铸锭加热-穿孔挤压工序，相当于提高工序成材率10-12%；降低铸锭加热-挤压工序能耗800KWh/t，降低挤压工具损耗和人员工资成本；减少中间裁切、中间退火、中间酸洗和中间转运工序，有效防止制品转运磕碰伤，制品品质大幅度提高，生产效率成倍增加，消除了酸洗金属损耗，生产成本大幅度降低。
附图说明
图1为本发明的现有技术的铜合金冷凝管生产工艺流程图。
具体实施方式
本发明的方法包括以下步骤：
1)通过热型连铸得到白铜管坯；
2)对管坯进行拉伸处理；
3)进行3道次拉伸；
4)最后进行联拉、精整、清洗和成品退火得到成品。
其中的热型连铸是日本于上世纪七十年代提出的一种铸造方法，用于生产直径在15-25mm以下的管棒坯料,通过拉拔加工后生产出直径在6mm以下的管棒材,用作电信领域的高保真传输线。热型连铸过程是在铸造之前对铸模进行加热，在整个铸造过程中，铸模内壁始终维持在被铸合金的熔点以上，确保铸模内壁始终不能形成晶核。冷却水直接对牵引出铸模外的金属进行冷却，通过热传导对铸模中部的液态金属进行冷却而首先形核、结晶，靠近铸模的金属只能在离开铸模后才会凝固，铸坯表面没有受到铸模摩擦作用影响，铸坯表面光洁如镜。由于热传导在轴线上进行，晶粒沿轴线由内向外生长，利于铸锭排气补缩。形成的铸坯内外质量很高。
实施例1
在步骤2)中对直径大于等于1mm小于等于50mm的管坯进行联拉，并在步骤3)中进行的3道次拉伸为盘拉伸。
实施例2
在步骤2)中是对直径大于50mm小于等于108mm的管坯进行联拉，并在步骤3)中进行的3道次拉伸为直条拉伸。
实施例3
在步骤2)中是对直径大于108mm小于等于319mm的管坯进行联拉，并在步骤3)中进行的3道次拉伸为扩径拉伸。
Claims (4)
1.一种白铜合金冷凝管热型连铸-连续拉伸方法，其特征在于，所述方法包括以下步骤：
1)通过热型连铸得到白铜管坯；
2)对管坯进行拉伸处理；
3)进行3道次拉伸；
4)最后进行联拉、精整、清洗和成品退火得到成品。
2.根据权利要求1所述的方法，其特征在于，在步骤2)中是对直径大于等于1mm小于等于50mm的管坯进行联拉，并在步骤3)中进行的3道次拉伸为盘拉伸。
3.根据权利要求1所述的方法，其特征在于，在步骤2)中是对直径大于50mm小于等于108mm的管坯进行联拉，并在步骤3)中进行的3道次拉伸为直条拉伸。
4.根据权利要求1所述的方法，其特征在于，在步骤2)中是对直径大于108mm小于等于319mm的管坯进行联拉，并在步骤3)中进行的3道次拉伸为扩经拉伸。