CN101716701A - 利用激光-gma电弧复合焊接装置实现摆动焊接的方法 - Google Patents

利用激光-gma电弧复合焊接装置实现摆动焊接的方法 Download PDF

Info

Publication number
CN101716701A
CN101716701A CN200910311165A CN200910311165A CN101716701A CN 101716701 A CN101716701 A CN 101716701A CN 200910311165 A CN200910311165 A CN 200910311165A CN 200910311165 A CN200910311165 A CN 200910311165A CN 101716701 A CN101716701 A CN 101716701A
Authority
CN
China
Prior art keywords
welding
laser
gma
arc
electric arc
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN200910311165A
Other languages
English (en)
Inventor
陈彦宾
雷正龙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Harbin Institute of Technology Shenzhen
Original Assignee
Harbin Institute of Technology Shenzhen
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Harbin Institute of Technology Shenzhen filed Critical Harbin Institute of Technology Shenzhen
Priority to CN200910311165A priority Critical patent/CN101716701A/zh
Publication of CN101716701A publication Critical patent/CN101716701A/zh
Pending legal-status Critical Current

Abstract

利用激光-GMA电弧复合焊接装置实现摆动焊接的方法，它涉及一种激光-熔化极气体保护焊复合焊接方法。本发明为解决利用激光-GMA电弧复合焊接装置焊接中、厚板过程中，易出现侧壁和层间未熔合、气孔、夹渣等缺陷的问题。方法：步骤一：开坡口；步骤二：装夹待焊工件；步骤三：确定电弧与激光束的位置：激光束垂直入射于待焊工件表面，电弧与激光束之间夹角为15～60°，激光束与GMA电弧焊丝尖端之间间距为2～6mm；步骤四：设定焊接工艺参数；步骤五：实施焊接：焊接时，电弧焊枪保持不动，激光束聚焦焊枪呈“S”形来回摆动焊接。本发明用于造船、石油管道、高压容器、战车及核装置等国防与民用领域中10mm以上厚板的对接焊。

Description

利用激光-GMA电弧复合焊接装置实现摆动焊接的方法
技术领域
本发明涉及一种激光-熔化极气体保护焊复合焊接方法。
背景技术
以往在舰船、石油管道、高压容器、铁路车辆、国防与民用工业领域大量使用的中、厚板高强钢的焊接均采用传统的电弧焊接方法，不仅焊接效率低，而且焊缝强度低，热输入大，焊接变形大。激光-GMA电弧复合焊接装置(GMA为熔化极气体保护焊)是实现中、厚壁构件高效、低成本的有效途径，激光-GMA电弧复合焊接装置可焊各种金属材料，由于采用激光-GMA电弧复合焊接装置具有焊接速度快(是传统弧焊的几倍以上)、焊接变形小、通过光束距离长、柔性传输容易实现遥控和全位置焊接优点而被广泛用于中、厚板的焊接中。但是利用激光-GMA电弧复合焊接装置在焊接中、厚板过程中，通常激光束在待焊工件1上呈直线移动，焊道侧壁和层间会产生未熔合、气孔、夹渣等焊接缺陷；为了解决中、厚板复合多层焊接过程中出现的上述缺陷，国内外学者进行了大量研究，提出了窄间隙引导路径式激光电弧复合焊接(LPLAC)技术、窄间隙U形坡口设计等方法。虽然上述方法在一定程度上改善了中、厚板激光-GMA电弧复合多层焊焊接过程中出现气孔、夹渣的缺陷，但是仍然会有气孔和夹渣等缺陷，而且产生的焊道歪斜、焊接的稳定性难以保证。
发明内容
本发明的目的是为解决利用激光-GMA电弧复合焊接装置在焊接中、厚板过程中，容易出现的侧壁和层间未熔合、气孔、夹渣等缺陷的问题，提供一种利用激光-GMA电弧复合焊接装置实现摆动焊接的方法。
本发明的方法是通过以下步骤实现的：步骤一：开坡口：在待焊工件的焊接部位开坡口；步骤二：装夹待焊工件：将待焊工件固定在夹具上；步骤三：确定电弧与激光束的位置：调整激光-GMA电弧复合焊接装置的位置，使激光束垂直入射于待焊工件的表面，电弧与激光束之间的夹角为15～60°，激光束与GMA电弧焊丝尖端之间的间距为2～6mm；步骤四：设定焊接工艺参数：激光功率为800～5000W，焊接电流为60～300A，GMA电弧焊枪气体流量为10～30L/min，GMA电弧焊丝的干伸长度为15～20mm，GMA电弧焊丝的直径为1.0～1.6mm，焊接速度为0.5～3.0m/min；步骤五：实施焊接：启动激光-GMA电弧复合焊接装置上的激光器和焊接电源，启动引弧开关和激光焊接电子光闸，焊接时，电弧焊枪保持不动，激光束聚焦焊枪呈“S”形来回摆动，激光束聚焦焊枪的摆动频率为2～100Hz，摆动幅度为0～10mm，GMA电弧与激光束共同作用在焊缝同一熔池并随激光焊接产生的匙孔移动，完成摆动焊接。
本发明具有以下优点：一、利用激光-GMA电弧复合焊接装置，在中、厚板焊接过程中，实施激光束在待焊工件1上呈“S”形摆动焊接，使焊接能量作用在焊缝坡口的两侧壁上，改变了熔池流动，扩大了焊缝熔池，增加了焊缝熔宽，有效避免了激光-GMA电弧复合焊接过程中出现的侧壁未熔合现象；由于焊缝熔池增加了，所以降低了焊缝冷却速率，有利于气体逸出，由此避免了焊接气孔及夹渣等缺陷。二、由于激光的摆动，避免了复合焊接过程中电弧等离子体对激光能量的损耗，提高了激光能量利用率和焊接匙孔的稳定性，有利于焊接过程的稳定。同时，对于一定尺寸的焊缝坡口，采用激光-GMA电弧复合焊接技术每一层可能需要多道焊接才能完成；而采用摆动激光-GMA电弧复合焊接技术由于增加了熔池宽度，因此，可以相应地减少焊接道数，提高焊接效率，保证了焊缝质量和焊接稳定性，降低生产成本。
附图说明
图1是利用激光-GMA电弧复合焊接装置在待焊工件1上实施摆动激光焊接的焊接部位立体图，图2是电弧2与激光束3之间的位置示意图，图中标记5为GMA电弧焊枪喷嘴、标记7为聚焦镜，图3是焊接时，激光束聚焦焊枪呈“S”形来回摆动焊接示意图(图中标记8为激光束呈“S”形摆动的路线，标记9为焊接方向)。
具体实施方式
具体实施方式一：结合图1～图3说明本实施方式，本实施方式是通过以下步骤实现的：步骤一：开坡口：在待焊工件1的焊接部位开坡口1-1；步骤二：装夹待焊工件1：将待焊工件1固定在夹具上；步骤三：确定电弧2与激光束3的位置：调整激光-GMA电弧复合焊接装置的位置，使激光束3垂直入射于待焊工件1的表面，电弧2与激光束3之间的夹角β为15～60°，激光束3与GMA电弧焊丝6尖端之间的间距D为2～6mm；步骤四：设定焊接工艺参数：激光功率为800～5000W，焊接电流为60～300A，GMA电弧焊枪气体流量为10～30L/min，GMA电弧焊丝6的干伸长度为15～20mm，GMA电弧焊丝6的直径为1.0～1.6mm，焊接速度为0.5～3.0m/min；步骤五：实施焊接：启动激光-GMA电弧复合焊接装置上的激光器和焊接电源，启动引弧开关和激光焊接电子光闸，焊接时，电弧焊枪保持不动，激光束聚焦焊枪呈“S”形来回摆动，激光束聚焦焊枪的摆动频率为2～100Hz，摆动幅度L为0～10mm，GMA电弧与激光束共同作用在焊缝同一熔池并随激光焊接产生的匙孔移动，完成摆动焊接。本发明主要针对10mm以上的厚板对接焊缝进行焊接。实验结果表明：利用激光-GMA电弧复合焊接装置在实施摆动焊接的过程中，激光焊接的锁孔作用能够吸引、压缩GMA焊接电弧，因此，利用激光-GMA电弧复合焊接装置在实施摆动焊接可以提高电弧稳定性和作用于工件的能量密度。
具体实施方式二：结合图1说明本实施方式，本实施方式的步骤一中的坡口形状为U形或Y形。这样设计一方面有利于复合焊接过程中激光能量的吸收；另一方面有利于避免侧壁未熔合缺陷的产生。其它步骤与具体实施方式一相同。
具体实施方式三：结合图1说明本实施方式，本实施方式的步骤三中的电弧2与激光束3之间的夹角β为45°。电弧2与激光束3之间的夹角β为45°时是激光束在待焊工件1摆动焊接的最佳角度。其它步骤与具体实施方式一相同。
具体实施方式四：结合图1说明本实施方式，本实施方式的步骤三中的激光束3与GMA电弧焊丝6尖端之间的间距D为4mm。激光束3与GMA电弧焊丝6尖端之间的间距D为4mm时，能够保证激光与电弧之间相互作用和焊缝熔宽在最佳范围内。其它步骤与具体实施方式一相同。
具体实施方式五：结合图1说明本实施方式，本实施方式的步骤四中的激光功率为3000W。激光功率为3000W时是实施焊接的最佳功率。其它步骤与具体实施方式一相同。
具体实施方式六：结合图1说明本实施方式，本实施方式的步骤四中的焊接电流为200A。焊接电流为200A时是实施焊接的最佳焊接电流。其它步骤与具体实施方式一相同。
具体实施方式七：结合图1说明本实施方式，本实施方式的步骤四中的GMA电弧焊枪气体流量为20L/min。GMA电弧焊枪气体流量为20L/min时是实施焊接的最佳焊枪气体流量。其它步骤与具体实施方式一相同。
具体实施方式八：结合图1说明本实施方式，本实施方式的步骤四中的GMA电弧焊丝6的干伸长度为18mm，GMA电弧焊丝6的直径为1.2mm。上述数值能够保证焊缝熔池达到要求，避免了焊接时出现气孔及夹渣等缺陷。其它步骤与具体实施方式一相同。
具体实施方式九：结合图1说明本实施方式，本实施方式的步骤四中的焊接速度为2.0m/min。焊接速度为2.0m/min时是实施焊接的最佳焊接速度。其它步骤与具体实施方式一相同。
具体实施方式十：结合图1说明本实施方式，本实施方式的步骤四中的激光采用CO2激光、YAG激光、半导体激光或光纤激光。根据不同的工件尺寸和焊接材料可以选择不同的激光器产生的激光进行摆动激光-GMA电弧复合焊接，以便提高焊接的适应性和加工效率。其它步骤与具体实施方式一相同。

Claims (10)

1.一种利用激光-GMA电弧复合焊接装置实现摆动焊接的方法，其特征在于：所述方法是通过以下步骤实现的：步骤一：开坡口：在待焊工件(1)的焊接部位开坡口(1-1)；步骤二：装夹待焊工件(1)：将待焊工件(1)固定在夹具上；步骤三：确定电弧(2)与激光束(3)的位置：调整激光-GMA电弧复合焊接装置的位置，使激光束(3)垂直入射于待焊工件(1)的表面，电弧(2)与激光束(3)之间的夹角(β)为15～60°，激光束(3)与GMA电弧焊丝(6)尖端之间的间距(D)为2～6mm；步骤四：设定焊接工艺参数：激光功率为800～5000W，焊接电流为60～300A，GMA电弧焊枪气体流量为10～30L/min，GMA电弧焊丝(6)的干伸长度为15～20mm，GMA电弧焊丝(6)的直径为1.0～1.6mm，焊接速度为0.5～3.0m/min；步骤五：实施焊接：启动激光-GMA电弧复合焊接装置上的激光器和焊接电源，启动引弧开关和激光焊接电子光闸，焊接时，电弧焊枪保持不动，激光束聚焦焊枪呈“S”形来回摆动，激光束聚焦焊枪的摆动频率为2～100Hz，摆动幅度(L)为0～10mm，GMA电弧与激光束共同作用在焊缝同一熔池并随激光焊接产生的匙孔移动，完成摆动焊接。
2.根据权利要求1所述利用激光-GMA电弧复合焊接装置实现摆动焊接的方法，其特征在于：所述步骤一中的坡口形状为U形或Y形。
3.根据权利要求1所述利用激光-GMA电弧复合焊接装置实现摆动焊接的方法，其特征在于：所述步骤三中的电弧(2)与激光束(3)之间的夹角(β)为45°。
4.根据权利要求1所述利用激光-GMA电弧复合焊接装置实现摆动焊接的方法，其特征在于：所述步骤三中的激光束(3)与GMA电弧焊丝(6)尖端之间的间距(D)为4mm。
5.根据权利要求1所述利用激光-GMA电弧复合焊接装置实现摆动焊接的方法，其特征在于：所述步骤四中的激光功率为3000W。
6.根据权利要求1所述利用激光-GMA电弧复合焊接装置实现摆动焊接的方法，其特征在于：所述步骤四中的焊接电流为200A。
7.根据权利要求1所述利用激光-GMA电弧复合焊接装置实现摆动焊接的方法，其特征在于：所述步骤四中的GMA电弧焊枪气体流量为20L/min。
8.根据权利要求1所述利用激光-GMA电弧复合焊接装置实现摆动焊接的方法，其特征在于：所述步骤四中的GMA电弧焊丝(6)的干伸长度为18mm，GMA电弧焊丝(6)的直径为1.2mm。
9.根据权利要求1所述利用激光-GMA电弧复合焊接装置实现摆动焊接的方法，其特征在于：所述步骤四中的焊接速度为2.0m/min。
10.根据权利要求1所述利用激光-GMA电弧复合焊接装置实现摆动焊接的方法，其特征在于：所述步骤五中的激光采用CO2激光、YAG激光、半导体激光或光纤激光。
CN200910311165A 2009-12-10 2009-12-10 利用激光-gma电弧复合焊接装置实现摆动焊接的方法 Pending CN101716701A (zh)