CN109909137A - A kind of plate timber UV coating construction process - Google Patents
A kind of plate timber UV coating construction process Download PDFInfo
- Publication number
- CN109909137A CN109909137A CN201711327023.3A CN201711327023A CN109909137A CN 109909137 A CN109909137 A CN 109909137A CN 201711327023 A CN201711327023 A CN 201711327023A CN 109909137 A CN109909137 A CN 109909137A
- Authority
- CN
- China
- Prior art keywords
- coating
- roller
- drying
- coat
- transparent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明提供了一种平板木门UV涂装施工工艺，依次进行三遍的辊涂UV透明腻子、双辊涂UV透明底漆和砂磨，之后进行辊涂UV修色面漆和镭射辊涂UV哑光面漆，这样能有效解决平板木门UV底漆在涂装过程中产生的不易砂光、不环保的问题。本发明的平板木门UV涂装施工工艺，使用自动化的辊涂设备，没有漆雾，而且大批量生产，由于是UV辊涂于基材表面，漆膜涂布非常均匀平整，附着力强，效果好，最主要的是使用此工艺进行平板木门加工，有效提高了生产效率，节省人力成本，而且油漆不断循环，无油漆浪费，真正做到降低成本及环保高效。The invention provides a UV coating construction process for a flat wooden door. The UV transparent putty is applied by rollers, the UV transparent primer is applied by double rollers, and sanding is performed three times in sequence, and then the UV refinishing topcoat by rollers and the UV laser rollers are applied. Matte finish, which can effectively solve the problem of not easy sanding and environmental protection caused by UV primer for flat wooden doors during the painting process. The UV coating construction process for flat wooden doors of the present invention uses automated roller coating equipment, has no paint mist, and is mass-produced. Because UV rollers are applied to the surface of the substrate, the paint film is very uniform and smooth, with strong adhesion and excellent effect. Well, the most important thing is to use this process to process flat wooden doors, which effectively improves production efficiency and saves labor costs. Moreover, the paint is continuously circulated, and there is no paint waste, which truly reduces costs and is environmentally friendly and efficient.
Description
Technical field
The present invention relates to the technical field of chemistry painting industry construction method more particularly to a kind of plate timber UV coating decoration works
Skill.
Background technique
UV paint is photocureable coating, it is current using more extensive furniture lacquer, and main feature has: by intensive ultraviolet
Photocuring is handled, color stability, for a long time Chang Xin.UV paint film spatially shape structure, hardness is big, wearability is good, transparency is good, produces
The resistance to scraping collision of product, rub resistance, stand the test of time.UV paint in terms of be widely used.
The main technique of coating plate timber is that the first artificial big groove PE that carries out mends soil currently on the market, then polished,
Spraying twice or multiple PE/PU transparent priming carry out priming paint polishing again, finally carry out PU and repair color and finishing coat coating.It is such to apply
The problem of work technique will appear harmful substance volatilization in production process, influence health, and the production cycle is long, occupied ground
Greatly, coating product easily occurs to split cruelly, plays the problems such as pinprick tangerine peel, and polishing difficulty is very big.
Therefore, it is necessary to a kind of easy plate timber UV coating decoration method polished and paint film is smooth be developed, with solution
The certainly demand in market.
Summary of the invention
The present invention provides a kind of plate timber UV coating construction process for the deficiency of product on the market at present, successively into
Row three times roller coating UV compound type transparent putties, double roller painting UV transparent priming and sand millings, carry out roller coating UV later and repair color finishing coat and radium-shine roller
UV dull finishing coat is applied, can effectively solve that plate timber UV priming paint generates in coating process in this way is not easy sanding, not environmentally
Problem, the film thickness and paint film planarization which forms all are very significantly improved.
In order to solve the above-mentioned technical problem, the present invention realizes by the following technical programs:
A kind of plate timber UV coating construction process, comprising the following steps:
(1) plate timber substrate the processing of substrate: is subjected to the processing of sand hair using plane sander；
(2) roller coating first pass UV compound type transparent putty: the coating weight of the roller coating first pass UV compound type transparent putty is 30 ~ 35 g/m2, roller
It is in semi-cured state that mono- mercury lamp of Tu Houyong, which carries out UV curing,；
(3) double roller applies first pass UV transparent priming: the coating weight that the double roller applies first pass UV transparent priming is 40 ~ 45 g/
m2, carrying out UV curing with double mercury lamps after roller coating is in all solidstate state；
(4) light weight sand polishing is carried out using plane sander；
(5) second time UV compound type transparent putty of roller coating: the coating weight of second time UV compound type transparent putty of roller coating is 30 ~ 35 g/m2, roller
It is in semi-cured state that mono- mercury lamp of Tu Houyong, which carries out UV curing,；
(6) double roller applies second time UV transparent priming: the coating weight that the double roller applies second time UV transparent priming is 40 ~ 45 g/
m2, carrying out UV curing with double mercury lamps after roller coating is in all solidstate state；
(7) light weight sand polishing is carried out using plane sander；
(8) roller coating third is all over UV compound type transparent putty: the roller coating third is 30 ~ 35 g/m all over the coating weight of UV compound type transparent putty2, roller
It is in semi-cured state that mono- mercury lamp of Tu Houyong, which carries out UV curing,；
(9) double roller applies third all over UV transparent priming: it is 40 ~ 45 g/ that the double roller, which applies third all over the coating weight of UV transparent priming,
m2, carrying out UV curing with double mercury lamps after roller coating is in all solidstate state；
(10) light weight sand is carried out using plane sander and is polishing to no bright spot；
(11) roller coating UV repairs color finishing coat: the coating weight that the roller coating UV repairs color finishing coat is 12 ~ 15 g/m2, then use half mercury
It is in semi-cured state that lamp half gallium lamp, which carries out UV curing,；
(12) radium-shine roller coating UV dull finishing coat: 35 ~ 40 g/m of coating weight of the radium-shine roller coating UV dull finishing coat2, then use
It is in all solidstate state that one mercury lamp, one gallium lamp, which carries out UV curing,；
(13) construction production is completed in offline processing, packing.
As further describing for technical solution of the present invention, the UV of the roller coating first pass, second time and third time
In compound type transparent putty step, the dry tenacity that a mercury lamp carries out UV curing is 100mJ, and drying time is 1 ~ 3 second.
As further describing for technical solution of the present invention, the double roller applies first pass, second time and third time
In UV transparent priming step, the dry tenacity that double mercury lamps carry out UV curing is 250mJ, and drying time is 1 ~ 3 second.
As further describing for technical solution of the present invention, the roller coating UV is repaired in color finishing coat step, half mercury lamp
The dry tenacity that half gallium lamp carries out UV curing is 200mJ, and drying time is 1 ~ 3 second.
As further describing for technical solution of the present invention, in the radium-shine roller coating UV dull finishing coat step, a mercury
The dry tenacity that one gallium lamp of lamp carries out UV curing is 300mJ, and drying time is 1 ~ 3 second.
Plate timber UV coating construction process of the invention is added plate timber surface by mechanization roller coating production equipment
Work is painted well, and packing use can directly be carried out by forming good paint；Plate timber is filled by roller coating UV putty, UV clear bottom,
UV repairs the completion of the processes such as color face and UV radium-shine roll surface paint, and surface effect is flat and smooth, and gloss is stablized, and has than traditional paint technique
Superior surface effect.
Based on above-mentioned technical solution, technical effect that the present invention has are as follows:
(1) plate timber UV coating construction process provided by the invention, plate timber carry out processable difference when roller coating UV construction
The plate of gauge height, improves the utilization rate of material, to improve the working efficiency of equipment.
(2) plate timber UV coating construction process of the invention carries out the processing of timber plate by roller coating UV, this is overturned
Woodwork painting technology solves the PE in traditional handicraft and mends soil, and minimum continuous spray painting more than three times, polishing consume several days
The production cycle of time occupies the above problem in a large amount of recruitment places.
(3) plate timber UV coating construction process of the invention, using the roll coating apparatus of automation, without coating cloud, and
Produce in enormous quantities, due to being UV roller coating in substrate surface, paint film coating is highly uniform smooth, and adhesive force is strong, and effect is good, main
Be to carry out the processing of plate timber using this technique, effectively increase production efficiency, save human cost, and paint constantly follows
Ring, no paint waste, being truly realized reduces cost and environment-friendly high-efficiency.
Specific embodiment
To facilitate the understanding of the present invention, below in conjunction with specific embodiments to invention is more fully described.Though
So The present invention gives better embodiments, but the invention can be realized in many different forms, however it is not limited to herein
Described embodiment.On the contrary, the purpose of providing these embodiments is that making to understand more the disclosure
Add thorough and comprehensive.
Unless otherwise defined, all technical and scientific terms used herein and belong to technical field of the invention
The normally understood meaning of technical staff is identical.Term as used herein in the specification of the present invention is intended merely to description tool
The purpose of the embodiment of body, it is not intended that in the limitation present invention.
Embodiment 1
A kind of plate timber UV coating construction process, comprising the following steps:
(1) plate timber substrate the processing of substrate: is subjected to the processing of sand hair using plane sander；
(2) roller coating first pass UV compound type transparent putty: the coating weight of roller coating first pass UV compound type transparent putty is 33 g/m2, with one after roller coating
It is in semi-cured state that mercury lamp, which carries out UV curing, and dry tenacity 100mJ, drying time is 3 seconds；
(3) double roller applies first pass UV transparent priming: the coating weight that the double roller applies first pass UV transparent priming is 45 g/m2,
UV curing is carried out in all solidstate state with double mercury lamps after roller coating, and dry tenacity 250mJ, drying time is 3 seconds；
(4) light weight sand polishing is carried out using plane sander；
(5) second time UV compound type transparent putty of roller coating: the coating weight of second time UV compound type transparent putty of roller coating is 33g/m2, after roller coating
UV curing is carried out in semi-cured state with a mercury lamp, and dry tenacity 100mJ, drying time is 3 seconds；
(6) double roller applies second time UV transparent priming: the coating weight that the double roller applies second time UV transparent priming is 45 g/m2,
UV curing is carried out in all solidstate state with double mercury lamps after roller coating, and dry tenacity 250mJ, drying time is 3 seconds；
(7) light weight sand polishing is carried out using plane sander；
(8) roller coating third is all over UV compound type transparent putty: the roller coating third is 33g/m all over the coating weight of UV compound type transparent putty2, after roller coating
UV curing is carried out in semi-cured state with a mercury lamp, and dry tenacity 100mJ, drying time is 3 seconds；
(9) double roller applies third all over UV transparent priming: it is 45 g/m that the double roller, which applies third all over the coating weight of UV transparent priming,2,
UV curing is carried out in all solidstate state with double mercury lamps after roller coating, and dry tenacity 250mJ, drying time is 3 seconds；
(10) light weight sand is carried out using plane sander and is polishing to no bright spot；
(11) roller coating UV repairs color finishing coat: the coating weight that the roller coating UV repairs color finishing coat is 15 g/m2, then use half mercury lamp one
It is in semi-cured state that half gallium lamp, which carries out UV curing, and dry tenacity 200mJ, drying time is 3 seconds；
(12) radium-shine roller coating UV dull finishing coat: 40 g/m of coating weight of the radium-shine roller coating UV dull finishing coat2, then with a mercury
It is in all solidstate state that one gallium lamp of lamp, which carries out UV curing, and dry tenacity 300mJ, drying time is 3 seconds；
(13) construction production is completed in offline processing, packing.
Plate timber UV coating construction process provided in this embodiment, using the roll coating apparatus of automation, without coating cloud, and
And produce in enormous quantities, due to being UV roller coating in substrate surface, paint film coating is highly uniform smooth, and adhesive force is strong, and effect is good, most main
What is wanted is to carry out the processing of plate timber using this technique, effectively increases production efficiency, saves human cost, and is painted continuous
Circulation, no paint waste, being truly realized reduces cost and environment-friendly high-efficiency.
Embodiment 2
A kind of plate timber UV coating construction process, comprising the following steps:
(1) plate timber substrate the processing of substrate: is subjected to the processing of sand hair using plane sander；
(2) roller coating first pass UV compound type transparent putty: the coating weight of roller coating first pass UV compound type transparent putty is 30 g/m2, with one after roller coating
It is in semi-cured state that mercury lamp, which carries out UV curing, and dry tenacity 100mJ, drying time is 2 seconds；
(3) double roller applies first pass UV transparent priming: the coating weight that the double roller applies first pass UV transparent priming is 40 g/m2,
UV curing is carried out in all solidstate state with double mercury lamps after roller coating, and dry tenacity 250mJ, drying time is 2 seconds；
(4) light weight sand polishing is carried out using plane sander；
(5) second time UV compound type transparent putty of roller coating: the coating weight of second time UV compound type transparent putty of roller coating is 30g/m2, after roller coating
UV curing is carried out in semi-cured state with a mercury lamp, and dry tenacity 100mJ, drying time is 2 seconds；
(6) double roller applies second time UV transparent priming: the coating weight that the double roller applies second time UV transparent priming is 40 g/m2,
UV curing is carried out in all solidstate state with double mercury lamps after roller coating, and dry tenacity 250mJ, drying time is 2 seconds；
(7) light weight sand polishing is carried out using plane sander；
(8) roller coating third is all over UV compound type transparent putty: the roller coating third is 30g/m all over the coating weight of UV compound type transparent putty2, after roller coating
UV curing is carried out in semi-cured state with a mercury lamp, and dry tenacity 100mJ, drying time is 2 seconds；
(9) double roller applies third all over UV transparent priming: it is 40 g/m that the double roller, which applies third all over the coating weight of UV transparent priming,2,
UV curing is carried out in all solidstate state with double mercury lamps after roller coating, and dry tenacity 250mJ, drying time is 2 seconds；
(10) light weight sand is carried out using plane sander and is polishing to no bright spot；
(11) roller coating UV repairs color finishing coat: the coating weight that the roller coating UV repairs color finishing coat is 12 g/m2, then use half mercury lamp one
It is in semi-cured state that half gallium lamp, which carries out UV curing, and dry tenacity 200mJ, drying time is 2 seconds；
(12) radium-shine roller coating UV dull finishing coat: the coating weight 35g/m of the radium-shine roller coating UV dull finishing coat2, then with a mercury
It is in all solidstate state that one gallium lamp of lamp, which carries out UV curing, and dry tenacity 300mJ, drying time is 2 seconds；
(13) construction production is completed in offline processing, packing.
Plate timber UV coating construction process provided in this embodiment, using the roll coating apparatus of automation, without coating cloud, and
And produce in enormous quantities, due to being UV roller coating in substrate surface, paint film coating is highly uniform smooth, and adhesive force is strong, and effect is good, most main
What is wanted is to carry out the processing of plate timber using this technique, effectively increases production efficiency, saves human cost, and is painted continuous
Circulation, no paint waste, being truly realized reduces cost and environment-friendly high-efficiency.
Embodiment 3
A kind of plate timber UV coating construction process, comprising the following steps:
(1) plate timber substrate the processing of substrate: is subjected to the processing of sand hair using plane sander；
(2) roller coating first pass UV compound type transparent putty: the coating weight of roller coating first pass UV compound type transparent putty is 31 g/m2, with one after roller coating
It is in semi-cured state that mercury lamp, which carries out UV curing, and dry tenacity 100mJ, drying time is 2 seconds；
(3) double roller applies first pass UV transparent priming: the coating weight that the double roller applies first pass UV transparent priming is 42g/m2, roller
UV curing is carried out in all solidstate state with double mercury lamps after painting, and dry tenacity 250mJ, drying time is 3 seconds；
(4) light weight sand polishing is carried out using plane sander；
(5) second time UV compound type transparent putty of roller coating: the coating weight of second time UV compound type transparent putty of roller coating is 31g/m2, after roller coating
UV curing is carried out in semi-cured state with a mercury lamp, and dry tenacity 100mJ, drying time is 2 seconds；
(6) double roller applies second time UV transparent priming: the coating weight that the double roller applies second time UV transparent priming is 42 g/m2,
UV curing is carried out in all solidstate state with double mercury lamps after roller coating, and dry tenacity 250mJ, drying time is 3 seconds；
(7) light weight sand polishing is carried out using plane sander；
(8) roller coating third is all over UV compound type transparent putty: the roller coating third is 31g/m all over the coating weight of UV compound type transparent putty2, after roller coating
UV curing is carried out in semi-cured state with a mercury lamp, and dry tenacity 100mJ, drying time is 2 seconds；
(9) double roller applies third all over UV transparent priming: it is 42 g/m that the double roller, which applies third all over the coating weight of UV transparent priming,2,
UV curing is carried out in all solidstate state with double mercury lamps after roller coating, and dry tenacity 250mJ, drying time is 3 seconds；
(10) light weight sand is carried out using plane sander and is polishing to no bright spot；
(11) roller coating UV repairs color finishing coat: the coating weight that the roller coating UV repairs color finishing coat is 13 g/m2, then use half mercury lamp one
It is in semi-cured state that half gallium lamp, which carries out UV curing, and dry tenacity 200mJ, drying time is 2 seconds；
(12) radium-shine roller coating UV dull finishing coat: 37 g/m of coating weight of the radium-shine roller coating UV dull finishing coat2, then with a mercury
It is in all solidstate state that one gallium lamp of lamp, which carries out UV curing, and dry tenacity 300mJ, drying time is 2 seconds；
(13) construction production is completed in offline processing, packing.
Plate timber UV coating construction process provided in this embodiment, using the roll coating apparatus of automation, without coating cloud, and
And produce in enormous quantities, due to being UV roller coating in substrate surface, paint film coating is highly uniform smooth, and adhesive force is strong, and effect is good, most main
What is wanted is to carry out the processing of plate timber using this technique, effectively increases production efficiency, saves human cost, and is painted continuous
Circulation, no paint waste, being truly realized reduces cost and environment-friendly high-efficiency.
Embodiments of the present invention above described embodiment only expresses, the description thereof is more specific and detailed, but can not
Therefore limitations on the scope of the patent of the present invention are interpreted as, as long as skill obtained in the form of equivalent substitutions or equivalent transformations
Art scheme should all be fallen within the scope and spirit of the invention.
Claims (5)