CN109810574A

CN109810574A - Inorganic nano material prints ink and its preparation method and application

Info

Publication number: CN109810574A
Application number: CN201711163437.7A
Authority: CN
Inventors: 李雪
Original assignee: Shenzhen TCL Industry Research Institute Co Ltd
Current assignee: Shenzhen TCL Industry Research Institute Co Ltd
Priority date: 2017-11-21
Filing date: 2017-11-21
Publication date: 2019-05-28

Abstract

The present invention provides a kind of inorganic nano materials to print ink, solvent in the inorganic nano material printing ink is organic solvent, the inorganic nano material printing ink includes at least one inorganic nano material and at least one fluorine silicon alkanes organic solvent, and the structure of the fluorine silicon alkanes organic solvent is as shown in general structure I: (R^b’)_n’‑(R_f ^b)_n‑(R_f ^a)_m‑(R^a’)_m’‑SiR₁(R₂)(R₃) in Formulas I Formulas I, the R_f ^a、R_f ^bIndependently selected from partially fluorinated or perfluorinated alkyl, aryl；The R^b’Aliphatic, aromatic group, F, Cl independently selected from H, C1-30, Br, I, sulfonate group, sulfonyl ester group, methoxyl group；The R^a’Aliphatic, aromatic group, sulfonate group selected from C1-30, sulfonyl ester group, methoxyl group；The R₁、R₂、R₃Independently selected from H, alkyl or substituted hydrocarbon radical, aryl or substituted aryl；Described m, n, m ', the value range of n ' meets: m, n are respectively 0 or 1, and m, n are not 0 simultaneously；M ', n ' are respectively 0 or 1.

Description

Inorganic nano material prints ink and its preparation method and application

Technical field

The invention belongs to electroluminescent diode field of display technology more particularly to a kind of inorganic nano material to print ink And preparation method thereof.

Background technique

Quantum dot (quantum dot, QD), but can be described as it is nanocrystalline, be one kind by II-VI group or iii-v element The nano particle of composition.Quantum dot is the nano semiconductor material of zero dimension (zero-dimensional), the ruler of three of them dimension Twice of the very little exciton Bohr radius for being all not more than its corresponding semiconductor material, the performance of quantum dot is generally imitated by quantum confinement Answer the influence of (quantum confinement effect), skin effect and doping.The partial size of quantum dot is typically in the range of 1~ Between 10nm, since electrons and holes are by quantum confinement, continuous band structure becomes the discrete energy levels knot with molecular characterization Structure can emit fluorescence after being excited.Quantum dot has the performances such as novel electronics and optics, and the chemical component of quantum dot ensures Luminescent color can cover the entire visual field from blue light to feux rouges, and excitation purity is high, continuously adjustable, is to have breakthrough work The material of industry application.In recent years, quantum dot light emitting material is playing very big effect in fields such as LED illumination, liquid crystal displays, Quantum dot substitutes traditional fluorescent powder, effectively improves the colour gamut of LED and liquid crystal display.Recently, luminescent material is as hair The light emitting diode with quantum dots (QLED) of photosphere is with a wide range of applications in fields such as solid-state lighting, FPD, by The extensive concern of academia and industrial circle.

The solution processing properties of quantum dot allow quantum dot light emitting layer to pass through spin coating, blade coating, injection, inkjet printing etc. Various ways preparation.Opposite front several method, inkjet printing technology can be accurately in the desired amount by quantum dot light emitting material Deposit it is in place, allow semiconductor material uniform deposition formed film layer.Quantum dot light emitting layer, material are prepared by inkjet printing The utilization rate of material is very high, and manufacturer can reduce production cost, simplifies manufacture craft, is easy universal volume production, reduces cost.Spray Black printing technique is the effective ways of the manufacture problem that can solve large scale QLED screen generally acknowledged at present.

However, inkjet printing technology needs to prepare suitable ink, ink needs sufficiently stable.Firstly, ink-jet print Water needs enough dispersibilities and hydrophobicity, nanoparticle is uniformly dispersed under solution state, while avoiding solvent Hydrone is absorbed, the ligand environment of quantum dot surface is destroyed.Secondly, ink-jet printing ink also needs to have viscosity appropriate, table Face tension.Suitable viscosity and surface tension not only may be implemented printer and stablize ink-jet, it is also possible that ink is in pixel square Stabilization is sprawled in battle array, is improved wetability, is effectively prevent excessive and avoid sprawling not in place.Meanwhile suitable viscosity and surface Tension can also realize that solvent is uniformly spread in ink curing processes, prevent from forming the non-uniform ink droplet film such as coffee ring.And For quantum dot ink, there is an urgent need to research and develop one kind to have preferably dispersibility and hydrophobicity, and have controllable viscous Degree, surface tension, and the solvent of removal can be facilitated in last handling process, it is wanted so that quantum dot ink can satisfy inkjet printing It asks, stablizes out of ink, high wettability, stabilization is sprawled, and uniform drying forms a film uniform.

Summary of the invention

The purpose of the present invention is to provide a kind of inorganic nano material printing ink and preparation method thereof, it is intended to solve existing Inorganic nano material print ink comprehensive stability (including hydrophobic stability, dispersibility, viscosity, surface tension and volatility) It is difficult to the problem of taking into account.

Another object of the present invention is to provide a kind of preparation methods of inorganic nano material film.

The invention is realized in this way a kind of inorganic nano material prints ink, the inorganic nano material prints ink In solvent be organic solvent, inorganic nano material printing ink includes at least one inorganic nano material and at least one Fluorine silicon alkanes organic solvent, the structure of the fluorine silicon alkanes organic solvent is as shown in general structure I:

(R^b’)_n’-(R_f ^b)_n-(R_f ^a)_m-(R^a’)_m’-SiR₁(R₂)(R₃) Formulas I

In Formulas I, the R_f ^a、R_f ^bIndependently selected from partially fluorinated or perfluorinated alkyl, aryl；

The R^b’Aliphatic, aromatic group independently selected from H, C1-30, F, Cl, Br, I, sulfonate group, sulfonyl Ester group, methoxyl group；

The R^a’Aliphatic, aromatic group, sulfonate group selected from C1-30, sulfonyl ester group, methoxyl group；

The R₁、R₂、R₃Independently selected from H, alkyl or substituted hydrocarbon radical, aryl or substituted aryl；

Described m, n, m ', the value range of n ' meets: m, n are respectively 0 or 1, and m, n are not 0 simultaneously；M ', n ' are respectively 0 Or 1.

Correspondingly, a kind of preparation method of inorganic nano material printing ink, comprising the following steps:

Inorganic nano material and organic solvent are provided, it is organic molten at least to contain a kind of fluorine silicon alkanes in the organic solvent Agent；

Inorganic nano material is dissolved in organic solvent and forms the inorganic nano material printing ink.

And a kind of preparation method of inorganic nano material film, comprising the following steps:

Inorganic nano material printing ink is prepared according to the method described above；

Ink is printed in deposited on supports inorganic nano using inkjet printing, by being dried, obtains inorganic nano material Expect film.

Inorganic nano material provided by the invention prints ink, has using with fluorine silicon alkanes shown in general structure I Solvent, containing Si-C key, the interior Rotation energy barrier is low, and molecular volume is big, and cohesion energy density is low, assigns the fluorine silicon alkanes The excellent hydrophobicity of organic solvent.Further, fluorine-containing in the fluorine silicon alkanes organic solvent, fluorine atom has maximum electricity negative Property (3.98), radius are smallWith characteristics such as high oxidative, high ionization energy, this characteristic makes fluorine carbon key bond energy high, Structural stability (structure is than hydrocarbon stable structure) with higher, fluorine atom is difficult to be polarized, so that fluorocarbon chain has The excellent performances such as high surface-active, chemical stability, excellent compatibility.

Using the inorganic nano material with fluorine silicon alkanes organic solvent shown in general structure I as organic solvent constituent Material printing ink can not only make inorganic nano material be uniformly dispersed in printing ink, storage-stable.Moreover, containing upper The inorganic nano material printing ink of the fluorine silicon alkanes organic solvent of specific structure is stated, surface tension is in 20-50mN/m model In enclosing, viscosity under the conditions of 25-35 DEG C is 0.5-50.0mPa.s, can satisfy current ink-jet printer to viscosity and surface The inkjet printing mode of inorganic nano material layer is realized in the requirement of tension, realize in print procedure stablize it is out of ink, stablize sprawl, High wettability, uniform drying, film forming are uniform, obtain the inorganic nano material hair with pixel-matrix, high-resolution, electroexcitation Photosphere.Meanwhile inorganic nano material printing ink provided by the invention has volatile performance appropriate, and printing can be made to prepare Inorganic nano material layer in organic molecule volatilization completely, obtain the film layer without ink organic solvent and fine and close arrangement, from And charge transmits between inorganic nano material is effectively ensured, and reduces threshold voltage, improves efficiency.

To sum up, inorganic nano material provided by the invention printing ink have preferable hydrophobic stability and dispersion performance, Suitable viscosity and surface tension, volatile performance, particularly suitable inkjet printing prepare inorganic nano material layer, are such as beaten by ink-jet Impression method prepares the inorganic nano material luminescent layer in light emitting diode.

The preparation method of inorganic nano material provided by the invention printing ink, inorganic nano material need to be only dissolved in containing It is easy to operate easily-controllable in the organic solvent of the fluorine silicon alkanes solvent of specific structure, do not need harsh condition, it can be achieved that Produce in enormous quantities.

The preparation method of inorganic nano material film provided by the invention, only need to be by inorganic nano material in organic solvent It is fully dispersed, inorganic nano material is made and prints ink, and then progress inkjet printing, drying can be obtained on carrier, method Simply, it is easy to accomplish standardization control.

Specific embodiment

In order to which technical problems, technical solutions and advantageous effects to be solved by the present invention are more clearly understood, below in conjunction with Embodiment, the present invention will be described in further detail.It should be appreciated that specific embodiment described herein is only used to explain The present invention is not intended to limit the present invention.

In the description of the present invention, it is to be understood that, term " first ", " second " are used for description purposes only, and cannot It is interpreted as indication or suggestion relative importance or implicitly indicates the quantity of indicated technical characteristic.Define as a result, " the One ", the feature of " second " can explicitly or implicitly include one or more of the features.In the description of the present invention, The meaning of " plurality " is two or more, unless otherwise specifically defined.

The embodiment of the invention provides a kind of inorganic nano materials to print ink, and the inorganic nano material prints in ink Solvent be organic solvent, inorganic nano material printing ink includes that at least one inorganic nano material and at least one contain Fluorine organic solvent.It is fluorine-containing in the fluorine-containing organic solvent, structural stability (structure is than hydrocarbon stable structure) with higher, fluorine Atom is difficult to be polarized, so that fluorocarbon chain has the Optimalities such as high surface-active, chemical stability, excellent compatibility Energy.

Situation is preferably implemented as the first, the fluorine-containing organic solvent is fluorine silicon alkanes organic solvent, i.e., the described nothing Machine nano material prints ink, including at least one inorganic nano material and at least one fluorine silicon alkanes organic solvent, and institute The structure of fluorine silicon alkanes organic solvent is stated as shown in general structure I:

(R^b’)_n’-(R_f ^b)_n-(R_f ^a)_m-(R^a’)_m’-SiR₁(R₂)(R₃) Formulas I

The R^b’Aliphatic, aromatic group, F, Cl selected from H, C1-30, Br, I, sulfonate group, sulfonyl ester group, first Oxygroup；

Inorganic nano material provided in an embodiment of the present invention prints ink, using with fluorine silicon shown in general structure I Alkanes organic solvent, containing Si-C key, the interior Rotation energy barrier is low, and molecular volume is big, and cohesion energy density is low, assigns described fluorine-containing The excellent hydrophobicity of silanes organic solvent.Further, fluorine-containing in the fluorine silicon alkanes organic solvent, fluorine atom has most Big electronegativity (3.98), radius are smallMake fluorine carbon key with characteristics, this characteristics such as high oxidative, high ionization energy Bond energy is high, and structural stability (structure is than hydrocarbon stable structure) with higher, fluorine atom is difficult to be polarized, so that fluorine carbon Chain has the excellent performances such as high surface-active, chemical stability, excellent compatibility.

Specifically, in the embodiment of the present invention, it is preferred that the partially fluorinated or perfluorinated alkyl, aryl include- CF₂-、-C_kF_2k+1、-CFC_kF_2k+1-、-CF₂C_kF_2k+1、-C₆F_jH_5-j, wherein j is the positive integer of 1-4, and k is the positive integer of 1-10. Preferred partially fluorinated or perfluorinated alkyl, aryl, have suitable carbon atom number and number of fluorine atoms, can assign described contain The excellent hydrophobic stability of silicon fluoride class organic solvent, high surface-active, chemical stability, excellent compatibility.

The R₁、R₂、R₃Selection do not limit clearly, independently selected from H, alkyl or substituted hydrocarbon radical, aryl or can take For aryl.

It is specific preferred, the fluorine silicon alkanes organic solvent include dimethoxy-methyl (3,3,3- trifluoro propyl) silicon, (3,3,3- trifluoro propyl) dichloro methyl silane, Chlorodimethyl -3,3,3- fluoropropyl silane, triethoxy -1H, 1H, 2H, 2H- 13 fluoro- N- octyl silane, trifluoro propyl methyl cyclotrisiloxane, trimethylsilyl 2- (fluorosulfonyl) difluoro acetate, Bis- (fluoroform sulfonylamino acid) di-t-butyl silicon substrate esters, tert-butyl dimethyl silyl triflate, dimethoxy-methyl (3,3,3- Trifluoro propyl) silicon, the fluoro- 4- of 1- (trimethyl silicon substrate) benzene, 1H, 1H, 2H, the bis- (3,3,3- of 2H- perfluoro decyl trichlorosilane, 1,3- Trifluoro propyl) -1,1,3,3- tetramethyl-disilazane, bis- (trimethyl silicon substrate) phenyl tetrafluorides of 1,4-, (trimethyl silicon substrate) methyl three Fluoromethane sulphonic acid ester, (heptafluoropropyl) trimethyl silane, bis- (nine fluorine hexyl dimethylsilyl bis) methyl-monosilanes, 1H, 1H, 2H, 2H- perfluoro decyl triethoxysilane.The fluorine silicon alkanes organic solvent can be one of selected from above-mentioned solvent, can also be with It is combined using a variety of in above-mentioned solvent, forms mixed solvent.Preferred fluorine silicon alkanes type of organic solvent have compared with Good hydrophobic stability and dispersion performance, suitable viscosity and surface tension, volatile performance, can be in the post-processing after film forming It is completely removed by modes such as heating, cooling, decompressions, will not influence the inorganic nano material film layer that inkjet printing is prepared, Particularly suitable inkjet printing prepares inorganic nano material layer, such as quantum dot light emitting layer.

As second of preferred implementation situation, the fluorine-containing organic solvent is fluorine-containing based organic solvent, i.e., described inorganic Nano material prints ink, including at least one inorganic nano material and at least one fluorine-containing based organic solvent, and described contains The structure of fluorine based organic solvent is as shown in general formula II:

(R^b’)_n’-(R_f ^b)_n-COO-(R_f ^a)_m-(R^a’)_m’Formula II

In formula II, the R_f ^a、R_f ^bIndependently selected from partially fluorinated or perfluorinated alkyl, aryl；

The R^a’、R^b’Aliphatic, aromatic group independently selected from H, C1-30, F, Cl, Br, I；

Inorganic nano material provided in an embodiment of the present invention prints ink, using with fluorinated ester shown in general formula II Class organic solvent.The fluorine-containing based organic solvent has high viscosity, can effectively overcome ink droplet gravity, is convenient for inkjet printing, Stabilization out of ink；Ink droplet compensation flowing can also be overcome, so that film forming is uniformly, no coffee ring, good film-forming property.Meanwhile fluorine atom has The characteristics such as there are high oxidative, high ionization energy, be difficult to be polarized, so that fluorine carbon key bond energy is high, structural stability (knot with higher Structure is than hydrocarbon stable structure) so that fluorocarbon chain has high surface-active, chemical stability, excellent compatibility etc. excellent Benign energy.In addition, the fluorine-containing based organic solvent is readily dissolved in fat-soluble solvent, it is not soluble in water, therefore hinder hydrone Intrusion, to reach preferable waterproof effect.

Specifically, in the embodiment of the present invention, it is preferred that the partially fluorinated or perfluorinated alkyl, aryl include- CF₂-、-C_kF_2k+1、-CFC_kF_2k+1-、-CF₂C_kF_2k+1、-C₆F_jH_5-j, wherein j is the positive integer of 1-4, and k is the positive integer of 1-10. Preferred partially fluorinated or perfluorinated alkyl, aryl, have suitable carbon atom number and number of fluorine atoms, can assign described contain The suitable viscosity of silicon fluoride class organic solvent is conducive to the working performance for improving inkjet printing, and improves and prepared by inkjet printing Film performance.

Specific preferred, the fluorine-containing based organic solvent includes fluoro propionyl ethyl, fluoroacetic acid butyl ester, fluorine second Acetoacetic ester, chlorine ethyl fluoroacetate, ethyl bromide fluoride, the fluoro- 2- propyl -3- oxy butyrate ethyl ester of 4,4,4- tri-, fluorine (benzene sulfydryl) second Acetoacetic ester, fluorine dimethyl malenate, 2,3,3,3- tetrafluoro methyl propionate, Trifluoroacetic Acid Ethyl Ester, fluorine ethyl hexanoate, 2,2,3,3- tetra- Fluoropropyl methacrylate, 2- (perfluoro butyl) ethylmethyl acrylate, trifluoroethyl methacrylate, (perfluor is pungent by 2- Base) ethylmethyl acrylate, methacrylic acid octafluoro pentyl ester, the fluoro- 3- oxygen pentyl ester of methyl 2-, acrylic acid trifluoro ethyl ester, methyl Hexafluorobutyl acrylate, n-butyric acie 2,2,2- trifluoro ethyl ester, 2- fluorine diethyl malonate, 4,4- difluoro ethyl acetoacetate, third Olefin(e) acid octafluoro pentyl ester, 4- fluorophenyl acetate, chloro-carbonic acid -4- fluorobenzene ester, 3- fluorophenyl acetate, pentafluorobenzyl caprylic acid ester, Dimethyl -4- (trifluoromethyl) phthalic acid ester, trifluoroacetic acid phenyl ester, naphthenic acid -3- fluorobenzene ester, ethyl 2,4,5- tri- Fluoro- 3- iodo-benzoic acid ester, trans- -4- ethyl-fluoro- phenyl ester of cyclohexane-carboxylic acid -4-, dimethoxyethyl phthalate.It is described to contain Fluorine based organic solvent can also be combined, shape one of selected from above-mentioned solvent using a variety of in above-mentioned solvent At mixed solvent.The preferred fluorine-containing esters type of organic solvent has more suitable viscosity, can better adapt to ink-jet and beat Print requirement to viscosity, and in the post-processing after film forming, the fluorine-containing based organic solvent can by heating, cool down, subtract The modes such as pressure completely remove, and will not influence the inorganic nano material film layer that inkjet printing is prepared, and are particularly suitable for inkjet printing Prepare inorganic nano material layer, such as quantum dot light emitting layer.

Situation is preferably implemented as the third, the fluorine-containing organic solvent is fluorine-containing organic solvent of ketone, i.e., described inorganic Nano material prints ink, including at least one inorganic nano material and at least one fluorine-containing organic solvent of ketone, and described contains The structure of fluorine organic solvent of ketone is as shown in general structure III:

(R^b’)_n’-(R_f ^b)_n-CO-(R_f ^a)_m-(R^a’)_mFormula III

In formula III, the R_f ^a、R_f ^bIndependently selected from partially fluorinated or perfluorinated alkyl, aryl；

Inorganic nano material provided in an embodiment of the present invention prints ink, using with fluorinated ketones contained shown in general structure III Class organic solvent.It is highest in all elements since the electronegativity of fluorine atom is 3.98；Meanwhile van der Waals radius is 0.135, be it is the smallest in addition to hydrogen, therefore, fluorine atom combination electronics it is very capable, polarizable rate is low.In addition fluorine-containing ketone Group does not have the proton (such as hydrogen) of high reaction activity, and therefore, the fluorine-containing organic solvent of ketone containing fluorine atom is chemically Matter is stablized, and with excellent chemically-resistant reactivity, oxidative resistance and low-corrosiveness, carrier or lower one functional layer to deposition are (such as Electronic work ergosphere or hole functional layer in QLED device) influence it is small, so as to guarantee preparation device function-stable Property.In addition, the fluorine-containing organic solvent of ketone and the compatibility of other solvents are good, it is easy to get the quantum dot ink of stable uniform Solution.

Specifically, in the embodiment of the present invention, it is preferred that the partially fluorinated or perfluorinated alkyl, aryl include- CF₂-、-C_kF_2k+1、-CFC_kF_2k+1-、-CF₂C_kF_2k+1、-C₆F_jH_5-j, wherein j is the positive integer of 1-4, and k is the positive integer of 1-10. Preferred partially fluorinated or perfluorinated alkyl, aryl, have suitable carbon atom number and number of fluorine atoms, can assign described contain The better chemical stability of silicon fluoride class organic solvent is conducive to the working performance for improving inkjet printing, and improves and beaten by ink-jet Print standby film performance.

Specific preferred, the fluorine-containing organic solvent of ketone includes the fluoro- 3- phenyl-propane -2- ketone of 1-, 3,3,3- tri- fluoro- 1- Phenylpropyl alcohol alkane -1,2- diketone, the fluoro- 3- phenylacetone of 1,1,1- tri-, the fluoro- 3- phenyl-propane -2- ketone of 1-, fluoro- phenyl -1 1- 2,2- bis-, 3- diacetyl, the fluoro- 1,3- diphenyl -1,3- propanedione of 2,2- bis-, the fluoro- 1- phenyl -1,3- diacetyl of 4,4- bis-, 2,2- bis- are fluoro- 1- phenyl -1,3- diacetyl, the fluoro- 2,4- acetyl butyryl of 1,1,1- tri-, 2- (trifluoroacetyl group) cyclopentanone, 2- (trifluoroacetyl group) ring Hexanone, the fluoro- 6- methyl -2,4- heptadione of 1,1,1- tri-, 2- (trifluoroacetyl group) cyclohexanone, the fluoro- 5- methyl -2,4- of 1,1,1- tri- Acetyl butyryl, the fluoro- 2,4- heptadione of 1,1,1- tri-, the fluoro- 1,3- diacetyl of 1- cyclopropyl -4,4,4- three, the fluoro- 5,5- bis- of 1,1,1- tri- Methyl -2,4- acetyl butyryl, the fluoro- 3- methyl -2,4- acetyl butyryl of 1,1,1- tri-, the fluoro- 5- methyl -2,4- heptadione of 1,1,1- tri-, first Base perfluor nonyl ketone, (TrifluoroMethyl)acetophenone, 4'- fluoro- 3'- (trifluoromethyl) acetophenone, 4- fluoro- 3- (trifluoromethyl) phenylpropyl alcohol Ketone, 1- [2,4- bis- fluoro- 3- (trifluoromethyl) phenyl] ethyl ketone, 2- fluoro- 6- (trifluoromethyl) acetophenone, the fluoro- 5- (fluoroform of 3- Base) acetophenone, the fluoro- 2- trifluoromethyl acetophenone of 4-, the bromo- 2- of 2- (2- fluorophenyl) -1- cyclopropyl ethyl ketone, 1- cyclopropyl -2- (2- Fluorophenyl) ethyl ketone, o-trifluoromethyl acetophenone, methyl perfluoro amyl ketone, 2,2- dimethyl -6,6,7,7,8,8,8- seven fluoro- 3, 5- acetyl caproyl.The fluorine-containing organic solvent of ketone can be selected from one of above-mentioned solvent, can also be using in above-mentioned solvent It is a variety of to be combined, form mixed solvent.The preferred fluorine-containing ketone type of organic solvent has better chemical stability, Requirement of the inkjet printing to viscosity can be better adapted to, and in the post-processing after film forming, the fluorine-containing organic solvent of ketone can It is completely removed in a manner of through heating, cooling, decompression etc., will not influence the inorganic nano material film that inkjet printing is prepared Layer, particularly suitable inkjet printing prepare inorganic nano material layer, such as quantum dot light emitting layer.

As the 4th kind of preferred implementation situation, the fluorine-containing organic solvent is fluorine-containing ether organic solvent, i.e., described inorganic Nano material prints ink, including at least one inorganic nano material and at least one fluorine-containing ether organic solvent, and described contains The structure of fluorine ether organic solvent is as shown in general structure IV:

(R^b’)_n’-(R_f ^b)_n-O-(R_f ^a)_m-(R^a’)_m’Formula IV

In formula IV, the R_f ^a、R_f ^bIndependently selected from partially fluorinated or perfluorinated alkyl, aryl；

Inorganic nano material provided in an embodiment of the present invention prints ink, using with fluorine-containing ether shown in general structure IV Class organic solvent.The fluorine-containing ethers surface of organic solvent tension is low, can more effective spreading wetting lower film.And fluorine ether compared with Ether water absorption rate is lower, can effectively reduce the adsorpting water quantity of the inorganic nano material film to be formed such as quantum dot film, reduces quantum dot Film post-processing difficulty.Meanwhile the polarity of fluorine ether is weak, can reduce the destruction to lower layer function transport layer film relatively.In addition, institute Stating fluorine-containing ether organic solvent also has significant anti-flammability, and inorganic nano material ink such as quantum dot ink can be improved and store Safety.The fluorine-containing ether organic solvent non-toxic and safe environmental protection, global warming potential (GWP) is low, the latent value of ozone-depleting It (ODP) is O, effective protection environment.

Specifically, in the embodiment of the present invention, it is preferred that the partially fluorinated or perfluorinated alkyl, aryl include- CF₂-、-C_kF_2k+1、-CFC_kF_2k+1-、-CF₂C_kF_2k+1、-C₆F_jH_5-j, wherein j is the positive integer of 1-4, and k is the positive integer of 1-10. Preferred partially fluorinated or perfluorinated alkyl, aryl, have suitable carbon atom number and number of fluorine atoms, can assign described contain The more suitable surface tension of fluorine ether organic solvent is conducive to the working performance for improving inkjet printing, and improves by inkjet printing The film performance of preparation.

Specific preferred, the fluorine-containing ether organic solvent includes bromo- 1,1,2- trifluoroethyl ether of 2-, the bromo- 5- fluorine of 3- Methyl phenyl ethers anisole, tetra- fluoroanisole of 2,3,5,6-, methyl fluoride perfluor isopropenyl ethers, 2- (4- bromine difluoromethoxy phenyl) -2- methyl-prop Base 3- phenoxy benzyl ether, bis- (4- fluorophenyl) ethers, bis- (the trifluoromethyl) -4,4- diamino-phenyl ethers of 2,2-, 3- (2,2,3,3- Tetrafluoro propoxyl group) -1,2- propylene oxide, four fluoro ethyl trifluoro vinyl ether of 2- bromine, perfluoroethylvinyl ether, ethylperfluoro fourth Base ether, 1,1,2,2- tetrafluoro phenetole, tetra- fluoro ethyl -4- methyl phenyl ether of 1,1,2,2-, shrinks at 1,2,2- tetrafluoro ethyl etherate Ten hexafluoro nonyl ethers of glycerin ether, 2,3- difluorobenzene hexyl ether.The fluorine-containing ether organic solvent can be selected from one in above-mentioned solvent Kind, it can also be combined using a variety of in above-mentioned solvent, form mixed solvent.The preferred fluorine-containing ether organic solvent Type has better surface tension, can better adapt to requirement of the inkjet printing to viscosity, and in the post-processing after film forming, The fluorine-containing ether organic solvent can be completely removed by modes such as heating, cooling, decompressions, will not influence inkjet printing preparation Obtained inorganic nano material film layer, particularly suitable inkjet printing prepare inorganic nano material layer, such as quantum dot light emitting layer.

As the 5th kind of preferred implementation situation, the fluorine-containing organic solvent is fluorine-containing aromatic hydrocarbons organic solvent, i.e., the described nothing Machine nano material prints ink, including at least one inorganic nano material and at least one fluorine-containing aromatic hydrocarbons organic solvent, and institute The structure of fluorine-containing aromatic hydrocarbons organic solvent is stated as shown in general structure V:

(R^b’)_n’-(R_f ^b)_n-(R_f ^a)_m-(R^a’)_m’Formula V

In formula V, the R_f ^aSelected from partially fluorinated or perfluorinated alkyl；

The R_f ^bSelected from partially fluorinated, perfluorinated or nonfluorinated aromatic hydrocarbons；

The R^a’、R^b’Aromatic group, F, Cl, Br, I of aliphatic group, C5-30 independently selected from H, C1-30；

Described m, n, m ', the value range of n ' meets: m, n are respectively 0 or 1, and m, n are not 0 simultaneously；M ', n ' be respectively 0 or 1；And when n is 0, the R^a’、R^b’In at least one be C5-30 aromatic group；When m is 0, the R_f ^bSelected from portion Divide fluorination or fluoridized aromatic hydrocarbons.

Inorganic nano material provided in an embodiment of the present invention prints ink, using with fluorine-containing virtue shown in general structure V Hydrocarbon organic solvent.In the fluorine-containing aromatic hydrocarbons organic solvent, on the one hand, fluorine atom van der Waals radius is small, leads to intermolecular draw Power is small, thus has very low surface tension, is easy to the levelling in film forming procedure and sprawls.On the other hand, the fluorine-containing aromatic hydrocarbons Organic solvent has the property of aromatic compound, has biggish polarity, is easy to carry out with other function solvent molecule in ink Good mixing of dissolving each other prevents inorganic nano material such as quantum dot from reuniting in other function adjusting solvent and settles out, maintains ink The stability of water；The use scope for having expanded function point analysis solvent simultaneously, effectively has adjusted the performance parameters such as the viscosity of ink, increases Strong ink is printed as film property etc..In addition, the fluorine-containing aromatic hydrocarbons organic solvent fluorine-containing alkane solvent tool more identical than carbon number There is higher boiling point, therefore the boiling point of ink can be improved, suitably reduction rate of volatilization, is suitble to preparation large scale display base plate.

Specifically, in the embodiment of the present invention, it is preferred that the partially fluorinated or perfluorinated alkyl includes-CF₂-、- C_kF_2k+1、-CFC_kF_2k+1-、-CF₂C_kF_2k+1, described partially fluorinated or perfluorinated including-C₆F_jH_5-j, the nonfluorinated aromatic hydrocarbons do not have Stringent limitation, wherein j is the positive integer of 1-4, and k is the positive integer of 1-10.Preferred functional group has suitable carbon atom number And number of fluorine atoms, the fluorine-containing more suitable surface tension of aromatic hydrocarbons organic solvent can be assigned, is easy to flow in film forming procedure Tiling exhibition is conducive to the working performance for improving inkjet printing, and improves the film performance prepared by inkjet printing.

Specific preferred, the fluorine-containing aromatic hydrocarbons organic solvent includes fluorobenzene, 4- methyl trifluoro toluene, 4- fluorine bromoethyl The bromo- 5- fluoride trifluoro toluene of benzene, 3-, the fluoro- 4- *-methoxy acetophenone of 2,2,2- tri-, the bromo- 2- fluoride trifluoro toluene of 5-, the chloro- 6- fluorine three of 2- Toluene fluoride, 2-bromo-5-fluorobenzotrifluoride, 1,2- bis- bromo- 5- fluoro- 3- (trifluoromethyl) benzene, the chloro- 4- fluoride trifluoro toluene of 3-, 4- are chloro- The bromo- 2- fluoride trifluoro toluene of 2- fluoride trifluoro toluene, 5-, the chloro- 2- fluoride trifluoro toluene of 5-, 4- (difluoro-methoxy) iodobenzene, 3- fluorine trifluoro Toluene, 2- fluorine benzotrichloride, the bromo- 2- fluoride trifluoro toluene of 3-, 3,5- bistrifluoromethylbenzyl bromine, 4- fluoro- 2- (trifluoromethyl) bromine Benzyl, 4- (trifluoromethyl) benzyl chloride, 4- (trifluoromethyl) benzyl chloride, 3- fluoro- 4- (trifluoromethyl) bromobenzyl, the fluoro- 5- (fluoroform of 2- Base) bromobenzyl, 3- fluorine bromobenzyl, 3- (trifluoromethyl) bromobenzyl, 2- (trifluoromethyl) benzyl bromine, bis- (trifluoromethyl) bromobenzenes of 2,4-, 3,5- Two fluoro- 4- methyl bromobenzene trifluorides, (±) -4- fluorobenzene ethene epoxides.The fluorine-containing aromatic hydrocarbons organic solvent can be selected from above-mentioned One of solvent can also be combined using a variety of in above-mentioned solvent, form mixed solvent.The preferred fluorine-containing virtue Hydrocarbon organic solvent type has better surface tension, is easy to the levelling in film forming procedure and sprawls, and the rear place after film forming In reason, the fluorine-containing aromatic hydrocarbons organic solvent can be completely removed by modes such as heating, cooling, decompressions, will not influence ink-jet The inorganic nano material film layer being prepared is printed, particularly suitable inkjet printing prepares inorganic nano material layer, as quantum dot is sent out Photosphere.

As the 6th kind of preferred implementation situation, the fluorine-containing organic solvent is fluorine-containing alkanes organic solvent, i.e., the described nothing Machine nano material prints ink, including at least one inorganic nano material and at least one fluorine-containing alkanes organic solvent, and institute The structure of fluorine-containing alkanes organic solvent is stated as shown in general structure VI:

(R^b’)_n’-(R_f ^b)_n-(R_f ^a)_m-(R^a’)_m’Formula VI

In formula VI, the R_f ^a、R_f ^bIndependently selected from partially fluorinated or perfluorinated alkyl；

The R^a’、R^b’Aliphatic, F, Cl, Br, I independently selected from H, C1-30；

Inorganic nano material provided in an embodiment of the present invention prints ink, using with containing fluothane shown in general structure VI Hydrocarbon organic solvent.In the fluorine-containing alkanes organic solvent, fluorine atom electronegativity is big, and radius is small, and C-F key is short, bond energy is big.One Aspect, the fluorine atom connected in the fluorine-containing alkanes organic solvent on fluorine-containing alkane main chain make spiral along zigzag carbon-carbon bond Shape distribution, is shielded fluorine-containing alkane main chain, avoids being influenced by extraneous factor (light, water, oxygen and chemical substance), keeps Good chemical stability.On the other hand, to inorganic nano material especially quantum dot in the fluorine-containing alkanes organic solvent With good dispersibility, the main dispersion solvent of inorganic nano material ink such as quantum dot ink can be used as, have preferable Dispersion stabilization.And there is preferable compatibility with other solvents in the fluorine-containing alkanes organic solvent, therefore, even if will The fluorine-containing alkanes organic solvent and other main solvents, still can be with collectively as the organic solvent of inorganic nano material ink Keep the dispersion stabilization of quantum dot ink.In addition, fluorine carbon key bond energy is high, structure ratio in the fluorine-containing alkanes organic solvent Hydrocarbon stable structure, fluorine atom are very difficult to be polarized, and alkane is to lower layer's dissolubility inherently very little in addition, so that described inorganic Nano material ink fluorine-containing alkanes organic solvent as described in quantum dot ink is to carrier or lower layer function such as hole transmission layer Or the active force of electron transfer layer is small, it is possible to reduce infiltration and removing to lower one functional layer avoid inorganic nano material layer such as Quantum dot layer and function transmission bed boundary are unclear, can keep the stability of function transport layer.

Specifically, in the embodiment of the present invention, it is preferred that the partially fluorinated or perfluorinated alkyl include-CF- ,- CF₂-、-C_kF_2k+1、-CFC_kF_2k+1-、-CF₂C_kF_2k+1, wherein k is the positive integer of 1-10.It is preferred partially fluorinated or perfluorinated Alkyl has suitable carbon atom number and number of fluorine atoms, it is preferably dispersed can to assign the fluorine-containing alkanes organic solvent Energy and chemical stability are conducive to the working performance for improving inkjet printing, and improve the film performance prepared by inkjet printing.

Specific preferred, the fluorine-containing alkanes organic solvent includes 1,1,1,2,2,3,4,5,5,5- Decafluoropentane, 1, The chloro- 2- bromoethane of the fluoro- 2- of 1,1- tri-, the chloro- 2- bromoethane of the fluoro- 2- of 1,1,1- tri-, the bromo- 1,2,2,2- tetrafluoroethane of 1-, tetrafluoro second Pentafluoroiodoethane telomer, bis- iodo of 1,6-, ten difluoro hexane, perfluoro-hexyl iodide alkane, the perfluoro octyl iodide alkane, 1- bromine perfluor of alkene Ethane, ten trifluorohexane of 1H-, perfluoro bromide octane, perflexane, 15 fluorine iodine heptane, 1- fluorine heptane, the 12 fluoro- 1,9- last of the ten Heavenly stems two Alkene, nine fluorine heptyl iodide of 4,4,5,5,6,6,7,7,7-, perfluor perhydro fluorenes, 1H, 1H, 2H, the seven bis- (fluoroforms of fluoro- 3,3- of 2H- Base) -1- iodohexane, bis- (trifluoromethyl) hexanes of the fluoro- 3,3- of the bromo- 4,4,5,5,6,6,6- seven of 1-, 1,3- bis- bromo- 1,1- difluoro heptan Alkane, 1,6- dibromo perflexane, nine fluorine hexane of 1,1,3,5,6- pentachloro-, 1H, the iodo- 1h of 6H- perflexane, 1-, 1H- perfluor oneself Alkane, the chloro- 1,1,2- trifluorohexane of the bromo- 2- of 1,6- bis-, 1,6- dichloro perflexane, the fluoro- 7- iodine heptane of 1,1,1,2,2,3,3- seven, 1H-6- bromine perflexane, the bromo- nine fluorine hexane of 1,6- dichloro of 1,3,5- tri-, the fluoro- 3- iodine heptane of 1,1,1- tri-, the bromo- 6- of 1- it is fluoro- oneself Alkane, 1,1,1,3,5,6- chlordene octafluoro hexane, 1,1,2,2- tetrahydro perfluoro-hexyl iodide, PF 5070, fluorine pentamethylene, fluoro hexamethylene Alkane.The fluorine-containing alkanes organic solvent can be selected from one of above-mentioned solvent, can also be using a variety of in above-mentioned solvent It is combined, forms mixed solvent.The preferred fluorine-containing alkanes type of organic solvent has better dispersion performance and change Stability is learned, and in the post-processing after film forming, the fluorine-containing alkanes organic solvent can pass through heating, cooling, decompression etc. Mode completely removes, and will not influence the inorganic nano material film layer that inkjet printing is prepared, and is particularly suitable for inkjet printing preparation Inorganic nano material layer, such as quantum dot light emitting layer.

As the 7th kind of preferred implementation situation, the fluorine-containing organic solvent is fluorine-containing alcohol organic solvent, i.e., described inorganic Nano material prints ink, including at least one inorganic nano material and at least one fluorine-containing alcohol organic solvent, and described contains The structure of fluorine alcohol organic solvent is as shown in general structure VIII:

[(R^b’)_n’-(R_f ^b)_n-(R_f ^a)_m-(R^a’)_m’]-OH formula VIII

In formula VIII, the R_f ^a、R_f ^bIndependently selected from partially fluorinated or perfluorinated alkyl, aryl；

- the OH is connected with carbon atom, and is not connected directly with phenyl ring carbon；

Inorganic nano material provided in an embodiment of the present invention prints ink, using with fluorine-containing alcohol shown in general structure VIII Class organic solvent.In the fluorine-containing alcohol organic solvent, on the one hand, fluorine alcohol is similar to alcohol property, and the viscosity of ink can be improved, Improve film forming；On the other hand, for opposite alcohol, fluorine alcohol has fat-soluble and hydrophobicity, therefore can reduce the introducing of steam, Avoid influencing the photoelectric properties of inorganic nano material such as quantum dot.In addition, fluorine atom has stronger electronegativity, the fluorine-containing alcohol The compatibility with quantum dot ligand can be improved in class organic solvent, enhances the dispersion stabilization of quantum dot；And it is described at room temperature Fluorine-containing alcohol organic solvent can dissolve the organic matters for being much typically difficult to dissolution, can expand the use model of other solvents in ink It encloses；The fluorine-containing alcohol organic solvent can also be formed effectively with other solvents and be interacted, and improve ink viscosity, be improved out of ink Stability.

It is worth noting that-OH is connected in carbon atom in fluorine-containing aromatic hydrocarbons organic solvent structure described in the embodiment of the present invention On, but when the carbon on-OH and phenyl ring is connected directly, the fluorine-containing aromatic hydrocarbons organic solvent is to inorganic nano material such as quantum dot Dissolubility it is poor, cannot function as inorganic nano material printing ink solvent.Therefore ,-the OH not with the direct phase of phenyl ring carbon Even.

Specifically, in the embodiment of the present invention, it is preferred that the partially fluorinated or perfluorinated alkyl includes-CF₂-、- C_kF_2k+1、-CFC_kF_2k+1-、-CF₂C_kF_2k+1, described partially fluorinated or perfluorinated including-C₆F_jH_5-j, the nonfluorinated aromatic hydrocarbons do not have Stringent limitation, wherein j is the positive integer of 1-4, and k is the positive integer of 1-10.Preferred partially fluorinated or perfluorinated alkyl, virtue Base has suitable carbon atom number and number of fluorine atoms, can assign the more suitable viscosity of fluorine-containing alcohol organic solvent, be easy to Film forming is improved in film forming procedure, is conducive to the working performance for improving inkjet printing, and improve the film prepared by inkjet printing Layer performance.

Specific preferred, the fluorine-containing alcohol organic solvent includes 3,3,4,4,5,5,5- hexafluoro amylalcohols, 4,4,5,5,5- Pentafluorobenzyl pentanol, perfluoro hexyl ethyl alcohol, 6- perfluoro butyl hexanol, 6- perfluoro hexyl hexanol, octafluoropentanol, 2- (perfluoro butyl) second Alcohol, fluorine hexane -1- alcohol in heptan, the fluoro- sec-n-octyl alcohol of 1,1,1- tri-, the fluoro- 1- hexanol of 6-, the fluoro- 2- nonyl alcohol of 1,1,1- tri-, 5- bromo- 4,4,5, The fluoro- 1- amylalcohol of 5- tetra-, 1H, 1H, the amyl- 1- alcohol of 5H- octafluoro, five fluorine dodecyl -3- alcohol of 1,1,1,2,2-, 2,2,3,3,4,4,5, 5- octafluoro -1- amylalcohol, 1H, 1H, 2H, 2H- perfluor -1- decyl alcohol, 1H, the fluoro- 1- amylalcohol of 1H- nine, trans- -2- fluorine cyclohexanol, fluorine beauty Western promise, 3,5- bis trifluoromethyl benzylalcohol, 4- (trifluoromethyl) benzylalcohol, 4- (trifluoromethyl) cyclohexanol, 2- (trifluoromethyl) hexamethylene Alcohol, 2- (trifluoromethyl) benzyl alcohol, 2,3,4,5- tetrafluorobenzyl alcohol, to fluorophenyl methanol, to fluorobenzene ethyl alcohol, the bromo- 3- fluorobenzene first of 4- Alcohol, 1- [4- (trifluoromethyl) phenyl] ethyl alcohol, m-phenoxy are to fluoro benzyl alcohol, 5- chloro- 2- (trifluoromethyl) -3- fluorobenzene ethyl alcohol, 4- The fluoro- 3- methoxy benzyl alcohol of methoxyl group -2,3,5,6- tetrafluorobenzyl alcohol, 4-, 2- fluoro- 3- (trifluoromethyl) benzyl alcohol, the fluoro- 5- of 3- (trifluoromethyl) benzyl alcohol, 2- fluoro- 5- (trifluoromethyl) benzyl alcohol, 2- fluoro- 4- (trifluoromethyl) benzyl alcohol, the fluoro- 4- (trifluoro of 3- Methyl) benzyl alcohol, 3,5- difluoro-benzyl alcohol, the fluoro- 4- chlorobenzyl alcohol of 3-, 4- (difluoro-methoxy) benzylalcohol, 1- (4- fluorophenyl) -1- second Alcohol, 2,4- dibromo benzylalcohol, 4- (difluoro-methoxy) benzyl alcohol, 5- fluoro-2-methylbenzene methanol, the bromo- 5- fluoro benzyl alcohol of 3-, 1- [3,5- Bis- (trifluoromethyl) phenyl] ethyl alcohol, α-cyclopropyl -4- fluorophenyl methanol, 4- fluoro-2-methylbenzene methanol, 3- (difluoro-methoxy) benzene Methanol, 3- fluoro benzyl alcohol, 2,5- difluoro-benzyl alcohol, 2,3- difluoro-benzyl alcohol.The fluorine-containing alcohol organic solvent can be selected from above-mentioned solvent One of, it can also be combined using a variety of in above-mentioned solvent, form mixed solvent.The preferred fluorine-containing alcohols has Solvent type has more suitable viscosity, is easy to improve film forming in film forming procedure, and in the post-processing after film forming, institute Stating fluorine-containing alcohol organic solvent can be completely removed by modes such as heating, cooling, decompressions, be will not influence inkjet printing and be prepared into The inorganic nano material film layer arrived, particularly suitable inkjet printing prepare inorganic nano material layer, such as quantum dot light emitting layer.

In the embodiment of the present invention, the needs based on inkjet printing, solvent temperature is too high or too low all to be unfavorable for forming densification The film layer of arrangement.Specifically, printing ink during inkjet printing prepares film layer, wave by solvent when solvent boiling point is too low Hair is unable to satisfy inkjet printing requirement to influence the overall performance (such as dispersion performance, viscosity, surface tension) of printing ink； It when solvent boiling point is excessively high, need to could remove, will affect in this way molten in printing ink by high temperature in subsequent film forming procedure The performance of matter ingredient such as inorganic nano material, such as causes the fluorescent quenching of quantum dot.Specifically, in the embodiment of the present invention, it is described The boiling point of fluorine silicon alkanes organic solvent is 80 DEG C -350 DEG C；The boiling point of the fluorine-containing based organic solvent is 140 DEG C -380 DEG C； The boiling point of the fluorine-containing organic solvent of ketone is 120 DEG C -360 DEG C；The boiling point of the fluorine-containing ether organic solvent is 120 DEG C -380 ℃；The boiling point of the fluorine-containing aromatic hydrocarbons organic solvent is 120 DEG C -400 DEG C；The boiling point of the fluorine-containing alkanes organic solvent is 120℃-350℃；The boiling point of the fluorine-containing alcohol organic solvent is 130 DEG C -400 DEG C.It is provided in an embodiment of the present invention above-mentioned to contain Fluorine organic solvent all has suitable boiling point, and inkjet printing prepares suitable volatile performance, Ke Yicong when inorganic nano material layer Evaporation is completed in dicyandiamide solution, to form the film layer of fine and close arrangement.

In the embodiment of the present invention, the fluorine-containing organic solvent for meeting above-mentioned specific structure has suitable viscosity and surface Tension.Specifically, range of viscosities of the fluorine silicon alkanes organic solvent at 25 DEG C is 0.5cPs-50cPs, at 25 DEG C Surface tension is 20-50mN/m, and range of viscosities of the fluorine-containing based organic solvent at 25 DEG C is 0.5cPs-50cPs, 25 Surface tension at DEG C is 20-60mN/m；Range of viscosities of the fluorine-containing organic solvent of ketone at 25 DEG C is 0.5cPs- 50cPs, the surface tension at 25 DEG C are 20-60mN/m；Range of viscosities of the fluorine-containing ether organic solvent at 25 DEG C be 0.5cPs-50cPs, the surface tension at 25 DEG C are 20-50mN/m；The fluorine-containing aromatic hydrocarbons organic solvent is viscous at 25 DEG C Degree range is 0.5cPs-50cPs, and the surface tension at 25 DEG C is 20-60mN/m；The fluorine-containing alkanes organic solvent is 25 Range of viscosities at DEG C is 0.5cPs-50cPs, and the surface tension at 25 DEG C is 20-50mN/m；The fluorine-containing alcohols is organic molten Range of viscosities of the agent at 25 DEG C is 0.5cPs-60cPs, and the surface tension at 25 DEG C is 20-80mN/m.The embodiment of the present invention The above-mentioned fluorine-containing organic solvent provided all has suitable viscosity and surface tension, can satisfy current ink-jet printer to viscosity With the requirement of surface tension, realize inorganic nano material layer inkjet printing mode, obtain with pixel-matrix, high-resolution, The inorganic nano material luminescent layer of electroexcitation.

In the embodiment of the present invention, the organic solvent of the inorganic nano material printing ink can be contained only above-mentioned fluorine-containing One of class organic solvent type, or what two kinds in above-mentioned fluorinated organic solvent or type more than two were formed Combination solvent, the mixing that can also be that at least one of above-mentioned fluorinated organic solvent type and other organic solvents are formed are molten Agent, to adjust the dispersion performance of inorganic nano material printing ink and the balance of viscosity.Further, each described fluorinated Type of organic solvent can select one or more according to actual needs.

In the embodiment of the present invention, organic and/or inorganic materials, the inorganic nano material are contained in the inorganic nano material ink It can use one or more.

Specifically, matrix component of the inorganic nano material as inorganic nano material printing ink, can be IV race, II-VI group, II-V race, iii-v, III-VI race, group IV-VI, I-III-VI race, II-IV-VI race, II-IV-V race At least one of binary or polynary semiconducting compound.Specifically, the inorganic nano material can be selected from but not limited to At least one of CdSe, CdS, CdTe, ZnO, ZnSe, ZnS, ZnTe, HgS, HgSe, HgTe, CdZnSe；Be also selected from but Be not limited to InAs, InP, InN, GaN, InSb, InAsP, InGaAs, GaAs, GaP, GaSb, AlP, AlN, AlAs, AlSb, At least one of CdSeTe, ZnCdSe.In addition, the inorganic nano material can also be perovskite nanometer particle material, it is special Not preferably do not shine perovskite nanoparticle, metal nano particle material, metal oxide nanoparticles material and combinations thereof.

The composition form of the inorganic nano material is unrestricted, can be doped or non-doped inorganic nano material, Wherein, doping refers to that other doped chemicals are also contained in the inside of the inorganic nano material.Specifically, the inorganic nano material Material can be quanta point material.Wherein, the ligand of the quantum dot include sour ligand, mercaptan ligand, amine ligand, (oxygen) Phosphine ligands, At least one of phosphatide, soft phosphatide, polyvinylpyridine etc..As specific embodiment, the acid ligand is ten acid, hendecene At least one of acid, tetradecylic acid, oleic acid, stearic acid；The mercaptan ligand is eight alkyl hydrosulfides, lauryl mercaptan, 18 At least one of alkyl hydrosulfide；The amine ligand includes at least one of oleyl amine, octadecylamine, eight amine；(oxygen) phosphine is matched Body is at least one of tri octyl phosphine, trioctylphosphine oxide (TOPO).

In the embodiment of the present invention, the structure type of the quantum dot is unrestricted, and it is mixed that uniform mixed type, gradient can be used Close type, core-shell structure copolymer type or union type.

The printing of inorganic nano material described in the embodiment of the present invention is suitable for inkjet printing quantum dot light emitting layer, when described inorganic When water content is higher in nano material printing ink, since shipwreck is in volatilization or removal, it is easy residual in the quantum dot ink It stays, and then influences the performance of the quantum dot light emitting layer formed.In view of this, quantum dot described in the embodiment of the present invention is preferably Oil-soluble quantum dot.

As particular preferred embodiment, the average-size of the quantum dot is 2-20nm.

Preferably, in the embodiment of the present invention, the total weight by inorganic nano material printing ink is packet in terms of 100% Include the following component of following weight percentage:

Inorganic nano material 0.01-20.0%；

Organic solvent 0.01-99.9%；

The mass ratio of the i.e. described inorganic nano material and the organic solvent is 0.01-20.0:80-99.9；

Wherein, in the organic solvent contain the fluorine-containing organic solvent, and the fluorine-containing organic solvent account for it is described organic The 1-90% of solvent gross weight.

In a particular embodiment, the fluorine silicon alkanes organic solvent accounts for the 1-90% of the organic solvent gross weight；Or institute State the 1-90% that fluorine-containing based organic solvent accounts for the organic solvent gross weight；Or the fluorine-containing organic solvent of ketone account for it is described organic The 1-90% of solvent gross weight；Or the fluorine-containing ether organic solvent accounts for the 1-90% of the organic solvent gross weight；Or it is described fluorine-containing Aromatic hydrocarbons organic solvent accounts for the 1-90% of the organic solvent gross weight；Or the fluorine-containing ether organic solvent accounts for the organic solvent The 1-90% of gross weight；Or the fluorine-containing aromatic hydrocarbons organic solvent accounts for the 1-90% of the organic solvent gross weight.It should be appreciated that described In organic solvent, in addition to the fluorine-containing organic solvent, other organic solvents can also be contained.

Specifically, above-mentioned fluorine-containing organic solvent account for the organic solvent gross weight weight percentage can for 1%, 5%, 10%, 20%, 30%, 40%, 50%, 60%, 70%, 80%, 90%.It should be appreciated that the inorganic nano material off-set oil The content of Mo Zhong, the fluorine-containing organic solvent are higher, and the performance that corresponding fluorine-containing organic solvent plays is better, the inorganic nano material The comprehensive performance of material printing ink is higher, and (inorganic nano material prints ink as described in making the fluorine silicon alkanes organic solvent Hydrophobic stability it is more preferable, the fluorine-containing based organic solvent has inorganic nano material printing ink to be more suitable for spraying The viscosity of ink printing, the fluorine-containing organic solvent of ketone make the chemical stability of the inorganic nano material printing ink more It is good；The fluorine-containing ether organic solvent makes the inorganic nano material printing ink have more suitable surface tension；It is described Fluorine-containing aromatic hydrocarbons organic solvent makes the inorganic nano material printing ink have adjustable surface tension；The fluorine-containing ethers Organic solvent makes the inorganic nano material printing ink have better dispersion performance and chemical stability；Or it is described fluorine-containing Aromatic hydrocarbons organic solvent makes the inorganic nano material printing ink have adjustable viscosity), it is more able to satisfy inkjet printing and wants It asks.

Gross weight by inorganic nano material printing ink is the weight percent of the inorganic nano material in terms of 100% Content is 0.1-20.0%, as specific embodiment, the dosage of the inorganic nano material can for 0.1%, 0.2%, 0.5%, 0.8%, 1.0%, 2.0%, 4.0%, 5.0%, 8.0%, 10.0%, 12.0%, 15.0%, 18.0%, 20.0% etc. is specific Numerical value content.Further, as a preferred embodiment, the dosage of the inorganic nano material is 4-15%.As a kind of preferred Mode, the inorganic nano material printing ink are made of the inorganic nano material and the organic solvent, by weight, The mass ratio of the inorganic nano material and the organic solvent is 4-15:85-96, and the fluorine-containing based organic solvent accounts for institute State the 1-50% of organic solvent gross weight.In addition to the inorganic nano material and described i.e. in inorganic nano material printing ink Outside organic solvent, other auxiliary reagents are not contained.

As another preferred embodiment, the mass ratio of the inorganic nano material and organic solvent is 4-15:85-96, and The fluorine-containing based organic solvent accounts for the 1-50% of the organic solvent gross weight.Further, in the embodiment of the present invention, the nothing Machine nano material, which prints ink, to include auxiliary reagent, and the auxiliary reagent includes but is not limited to: charge transfer agent, viscosity Regulator and dispersing agent.

Wherein, inorganic nano material can be prepared in inorganic nano material printing ink by the charge conveyer After the bed of material such as quantum dot light emitting layer, charge transport properties are improved, so that charge transmission is more smooth effectively, reduce threshold voltage, So that electronics, hole may be coextruded radioluminescence.Specific preferred, the charge transfer agent can be polycarbazole, gather Fluorenes, polyaniline gather to styrene support (to phenylacetylene), polyacetylene, gather to benzene, polythiophene, polypyridine, polypyrrole and its derivative At least one of or in which at least two formed copolymers or blend, but not limited to this.

When to make the quantum dot ink carry out inkjet printing, ink is suitably discharged from the nozzle of inkjet print head without sending out Raw blocking, while there is preferable film forming characteristics, it can be printed in ink in the inorganic nano material and viscosity modifier is added. The viscosity modifier be preferably polyhydroxy-alcohol, alkyl glycol ether or trimethylolpropane, trimethylolethane, casein, At least one of carboxymethyl cellulose.Specifically, the polyhydroxy-alcohol is ethylene glycol, diethylene glycol (DEG), diethylene glycol, three second two Alcohol, propylene glycol, dipropylene glycol, hexylene glycol, 1,3 butylene glycol, 1,4- butanediol, 1,5- pentanediol, 2- butylene-1,4-diol and At least one of 2- methyl -2- pentanediol, 1,2,6- hexanetriol, glycerine, polyethylene glycol and dipropylene glycol, polyvinyl alcohol.Institute Stating alkyl glycol ether is in polyethylene glycol monobutyl ether, diethylene glycol monoethyl ether, dipropylene glycol monomethyl ether and Propylene glycol n-propyl ether At least one.

The dispersing agent can effectively be such that the quantum dot is dispersed in the solvent and protect the dispersion It is fixed to keep steady.Specifically, the dispersing agent can be one or more surfactants.The surfactant can be anion Type, cationic, non-ionic or amphoteric surfactant.

As specific embodiment, the nonionic surfactant includes but is not limited to straight chain or second level alcohol ethoxylates Object, alkyl phenol polyoxyethylene ether, fluorine-containing surfactant, polyoxyethylene carboxylate, aliphatic amine polyoxyethylene ether, polyoxyethylene Block copolymer and propoxylated block copolymers, polyoxyethylene and propyl silica resin based surfactants, alkyl polysaccharide At least one of glycosides and acetylenic polyethylene oxides surfactant.The anionic surfactant includes but is not limited to Carboxylate (for example, ether carboxylate and sulfosuccinate), sulfate (for example, lauryl sodium sulfate), sulfonate (for example, Dodecyl benzene sulfonate, α olefin sulfonate, p alkylphenylaceticacid, fatty acid taurides, alkyl naphthalene sulfonic acid Salt), phosphate (for example, alkyl and aryl alcohol phosphate), phosphonate and amine oxide surfactant and Anionic fluorinated table At least one of face activating agent.The amphoteric surfactant include but is not limited to trimethylamine second lactones, sulfobetaines with And at least one of alanine rouge.The cationic surfactant includes but is not limited to quaternary ammonium compound, cationic amine At least one of oxide, ethoxy fatty amine and imidazoline surfactant.

In order to sufficiently realize in the inorganic nano material printing ink, inorganic nano material prints fully dispersed, can Other organic solvents are added in inorganic nano material printing ink.Preferably, the weight of other organic solvents Account for 50% or more of the organic solvent total weight.

Further, other organic solvents are chlorobenzene, o-dichlorohenzene, tetrahydrofuran, methyl phenyl ethers anisole, morpholine, toluene, neighbour Dimethylbenzene, meta-xylene, paraxylene, n-hexane, methylene chloride, chloroform, 1,4- dioxane, 1,2 2 chloroethenes Alkane, 1,1,1- trichloroethanes, 1,1,2,2- tetrachloroethanes, naphthane, naphthalane, phenoxytoluene, dodecane, 1- methoxynaphthalene, 1- dibutyl naphthalene, o-dimethoxybenzene, 1- methyl naphthalene, 1,2- dimethylnaphthalene, cyclohexyl benzene, 1,2,4- trimethoxy-benzene, benzene hexane, In the tetradecane, 1,2- dimethylnaphthalene, 4- isopropyl biphenyl, 2- isopropyl naphthalene, 1-ethylnaphthalene and 1,2,3,4-tetralin extremely Few one kind.

As a kind of specific preferred embodiment, inorganic nano material printing ink is by the inorganic nano material, described Organic solvent and auxiliary reagent composition.

The viscosity of inorganic nano material printing ink provided in an embodiment of the present invention, it is organic molten by the fluorine silicon alkanes The dosage and concrete type of agent are regulated and controled.Inorganic nano material provided in an embodiment of the present invention prints ink, in 25-35 DEG C of item Viscosity under part is 0.5-60.0mPa.s, concretely 1mPa.s, 5mPa.s, 10mPa.s, 15mPa.s, 20mPa.s, 25mPa.s,30mPa.s,35mPa.s,40mPa.s,45mPa.s,50mPa.s,55mPa.s,60mPa.s；Further, described The viscosity of quantum dot ink is preferably that 25 DEG C of viscosity is preferably 1-30.0mPa.s, more preferably viscous under the conditions of 25-35 DEG C Degree is 1-15.0mPa.s.The surface tension of the inorganic nano material printing ink is 20.0-80.0mN/m, thus in ink-jet It can be discharged glibly from printing head in print procedure, and there is preferable film forming characteristics.Specifically, stating inorganic nano material Print ink surface tension can for 20.0mN/m, 30.0mN/m, 40.0mN/m, 50.0mN/m, 60.0mN/m, 70.0mN/m, 80.0mN/m。

It is provided in an embodiment of the present invention using above-mentioned several fluorine-containing organic solvents with specific structure general formula as organic The inorganic nano material of solvent composition prints ink, inorganic nano material can not only be made to be uniformly dispersed in printing ink, Storage-stable.Moreover, the inorganic nano material prints the surface tension of ink within the scope of 20-80mN/m, in 25-35 DEG C of item Viscosity under part is 0.5-60.0mPa.s, can satisfy requirement of the current ink-jet printer to viscosity and surface tension, realizes nothing The inkjet printing mode of machine layer of nanomaterial, realize in print procedure stablize it is out of ink, stablize sprawl, high wettability, uniform drying, It forms a film uniform, obtains the inorganic nano material luminescent layer with pixel-matrix, high-resolution, electroexcitation.Meanwhile the present invention is real The inorganic nano material printing ink for applying example offer has volatile performance appropriate, the inorganic nano material that printing can be made to prepare Organic molecule volatilization in the bed of material completely, obtains the film layer without ink organic solvent and fine and close arrangement, so that nothing be effectively ensured Charge transmits between machine nano material, reduces threshold voltage, improves efficiency.To sum up, inorganic nano material provided in an embodiment of the present invention Material printing ink has preferable hydrophobic stability and dispersion performance, suitable viscosity and surface tension, volatile performance, especially suitable It closes inkjet printing and prepares inorganic nano material layer, the inorganic nano material in light emitting diode is such as prepared by inkjet printing methods Luminescent layer.

Inorganic nano material provided in an embodiment of the present invention prints ink, can be prepared by following methods.

Correspondingly, the embodiment of the invention provides a kind of preparation method of inorganic nano material printing ink, including it is following Step:

S01. inorganic nano material and organic solvent are provided, it is organic molten at least to contain a kind of fluorinated in the organic solvent Agent；

S02. inorganic nano material is dissolved in organic solvent and forms the inorganic nano material printing ink.

The preparation method of inorganic nano material printing ink provided in an embodiment of the present invention, only need to be molten by inorganic nano material It is easy to operate easily-controllable in the organic solvent of the fluorinated solvent containing specific structure, harsh condition is not needed, it can be real Now produce in enormous quantities.

Specifically, the type of the fluorinated organic solvent can be found in above in above-mentioned steps S01, specifically, as described At least contain a kind of fluorine silicon alkanes organic solvent in organic solvent；Or at least contain a kind of fluorine-containing esters in the organic solvent Organic solvent；Or at least contain a kind of fluorine-containing organic solvent of ketone in the organic solvent；Or at least contain in the organic solvent There is a kind of fluorine-containing ether organic solvent；Or at least contain a kind of fluorine-containing aromatic hydrocarbons organic solvent in the organic solvent；Or it is described At least contain a kind of fluorine-containing ether organic solvent in organic solvent；Or at least contain a kind of fluorine-containing aromatic hydrocarbons in the organic solvent Organic solvent.Of course it is to be understood that the organic solvent can also contain other non-fluorinated organic solvents, and described fluorine-containing Class organic solvent can also contain two or more in above-mentioned solvent.

The inorganic nano material prints the formula of ink and its preferred ingredient, content have hereinbefore been stated, in order to Length is saved, details are not described herein again.

In above-mentioned steps S02, inorganic nano material is dissolved in organic solvent, discrete form is unrestricted, can be used and stirs The mode of mixing is realized.

And the embodiment of the invention also provides a kind of preparation methods of inorganic nano material film, comprising the following steps:

E01. inorganic nano material printing ink is prepared according to the method described above；

E02. ink is printed in deposited on supports inorganic nano using inkjet printing, by being dried, obtains inorganic receive Rice material film.

The preparation method of inorganic nano material film provided in an embodiment of the present invention, only need to be by inorganic nano material organic It is fully dispersed in solvent, inorganic nano material is made and prints ink, and then progress inkjet printing, drying can obtain on carrier , method is simple, it is easy to accomplish standardization control.

The method that above-mentioned steps E01 prepares inorganic nano material printing ink is as described above, in order to save length, herein It repeats no more.

In above-mentioned steps E02, by selecting suitable ink-jet printer to carry out inkjet printing, receive deposited on supports is inorganic Then solvent flashing is dried to inorganic nano printing ink in rice printing ink.Specifically, the inkjet printing It is preferred that being realized using piezoelectric ink jet printing or thermal inkjet-printing.It is described to be dried as heating drying, cooling and drying, be dried under reduced pressure At least one of.As an implementation, individually using heating drying, cooling and drying, one of be dried under reduced pressure progress It is dried.As another embodiment, dry using heating and be dried under reduced pressure or cooling and drying and being dried under reduced pressure is done Dry processing.Preferably, the dry temperature of the heating is 30-180 DEG C, time 0-30min；Preferably, the cooling processing Temperature be 0-20 DEG C；Preferably, the vacuum degree of the reduced pressure treatment is 1 × 10^-6Torr is to normal pressure.

It is dried to obtain inorganic nano material film, such as quantum dot film.It is suitable to be dried mode, it can be efficient Under the premise of removing the fluorine silicon alkanes organic solvent, guarantee that the inorganic nano material such as quanta point material is not damaged.

The inorganic nano material film dry film formed through inkjet printing, thickness is preferably 10-100nm；Further, through spraying The inorganic nano material film thickness of dry film that ink printing is formed is 20-50nm.

It is illustrated combined with specific embodiments below.

Embodiment 1

A kind of inorganic nano material prints ink, including the stable quantum dot of oleyl amine, organic solvent and auxiliary reagent, In, the mass ratio of the stable quantum dot of the oleyl amine and organic solvent is 10:90；The organic solvent is by weight percentage Dimethoxy-methyl (3,3,3- trifluoro propyl) siloxane solvent group that 80% 1- dibutyl naphthalene solvent and weight percentage is 20% At, and 1- dibutyl naphthalene and dimethoxy-methyl (3,3,3- trifluoro propyl) silicon are refined to purity and are greater than through water removal, deoxygenation 99.9%；The auxiliary reagent is polypyrrole.

A kind of preparation method of inorganic nano material film, comprising the following steps:

S11. each component is weighed according to the formula of above-mentioned inorganic nano material printing ink；

S12., 500mL single-necked flask is provided, in the case of stirring, the stable red CdSe/ZnS quantum of addition oleyl amine Point, 1- dibutyl naphthalene, polypyrrole and dimethoxy-methyl (3,3,3- trifluoro propyl) siloxane solvent, are stirred 30min, obtain quantum Point printing ink composition；

S13. the quantum dot printing ink composition is injected into printing ink-jet printer cartridge, by ink-jet printer in carrier Upper inkjet printing is printed as 20 × 30um, the red quantum dot layer of 200 × 200ppi of resolution ratio.120 are heated on hot plate ℃、1×10^-4Volatile dry 30min under Torr obtains monochromatic quantum dot luminescent layer.

Embodiment 2

A kind of inorganic nano material printing ink, including the quantum dot and organic solvent that oleyl amine is stable, wherein the oleyl amine The mass ratio of stable quantum dot and organic solvent is 8:92；1- (the first that the organic solvent is 55% by weight percentage Oxymethoxy) naphthalene, weight percentage be 30% cyclohexyl benzene and weight percentage be 15% triethoxy -1H, The fluoro- N- octyl silane solution of 1H, 2H, 2H- 13 composition, and 1- (methoxymethoxy) naphthalene, cyclohexyl benzene, triethoxy -1H, The fluoro- N- octyl silane solution of 1H, 2H, 2H- 13 is refined to purity greater than 99.9% through water removal, deoxygenation.

S21. each component is weighed according to the formula of above-mentioned inorganic nano material printing ink；

S22., 500mL high-density polyethylene bottle is provided, in the case of stirring, successively adds the stable green of oleyl amine CdZnSe/CdZnS, 1- (methoxymethoxy) naphthalene, cyclohexyl benzene, the fluoro- N- octyl silicon of triethoxy -1H, 1H, 2H, 2H- 13 Alkane solvents are stirred 30min, obtain quantum dot printing ink composition；

S23. by the quantum dot printing ink composition by ink-jet printer inkjet printing on carrier, it is printed as 20 × The green quantum dot layer of 30um, 200 × 200ppi of resolution ratio.110 DEG C, 1 × 10 are heated on hot plate^-6Volatile dry under Torr 30min obtains monochromatic quantum dot luminescent layer.

Embodiment 3

A kind of inorganic nano material printing ink, the weight percentage with inorganic nano material printing ink are 100% meter, each component comprising following weight percentage:

The stable quantum dot 9% of oleyl amine；

Organic solvent 91%；

Wherein, the stable quantum dot of the oleyl amine blue CdS/CdZnS stable for oleyl amine, (green CdZnSe/CdZnS, Red CdSe/ZnS quantum dot)；3- phenoxytoluene that the organic solvent is 55% by weight percentage, weight percent contains Measure the decahydronaphthalenes for 25%, the bis- (front threes of 1,4- that the dodecane that weight percentage is 17% and weight percentage are 3% Base silicon substrate) phenyl tetrafluoride composition, and 3- phenoxytoluene, decahydronaphthalenes, dodecane and bis- (trimethyl silicon substrate) phenyl tetrafluorides of Isosorbide-5-Nitrae-are equal Purity is refined to greater than 99.9% through water removal, deoxygenation.

S31. each component is weighed according to the formula of above-mentioned inorganic nano material printing ink；

S32., 500mL high-density polyethylene bottle is provided, in the case of stirring, successively adds 3- phenoxytoluene, decahydro The stable blue CdS/CdZnS of change naphthalene, oleyl amine, (green CdZnSe/CdZnS, red CdSe/ZnS quantum dot), dodecane, 1, Bis- (trimethyl silicon substrate) phenyl tetrafluorides of 4-, are stirred 30min, obtain quantum dot printing ink composition；

S33. by the quantum dot printing ink composition by ink-jet printer inkjet printing on carrier, it is printed as 20 × Blue, green, the red side-by-side quantum dot layer of 30um, 200 × 200ppi of resolution ratio.160 DEG C, 1 are heated on hot plate ×10^-5Volatile dry 30min under Torr obtains three primary colours quantum dot light emitting layer.

Embodiment 4

A kind of inorganic nano material prints ink, including the stable quantum dot of oleyl amine, organic solvent and auxiliary reagent, In, the mass ratio of the stable quantum dot of the oleyl amine and organic solvent is 4:96；The organic solvent is by weight percentage The methacrylic acid octafluoro pentyl ester solvent that 50% 1- dibutyl naphthalene solvent and weight percentage is 50% forms, and 1- dibutyl naphthalene Purity is refined to greater than 99.9% through water removal, deoxygenation with methacrylic acid octafluoro pentyl ester solvent；The auxiliary reagent is poly- pair Styrene support and 1,4- butanediol.

S41. each component is weighed according to the formula of above-mentioned inorganic nano material printing ink；

S42., 500mL single-necked flask is provided, in the case of stirring, the stable red CdSe/ZnS quantum of addition oleyl amine Point, methacrylic acid octafluoro pentyl ester solvent, gathers to styrene support and 1,4-butanediol 1- dibutyl naphthalene solvent, is stirred 30min obtains quantum dot printing ink composition；

S43. the quantum dot printing ink composition is injected into printing ink-jet printer cartridge, by ink-jet printer in carrier Upper inkjet printing is printed as 20 × 30um, the red quantum dot layer of 200 × 200ppi of resolution ratio.130 are heated on hot plate ℃、1×10^-4Volatile dry 30min under Torr obtains monochromatic quantum dot luminescent layer.

Embodiment 5

The stable green CdZnSe/CdZnS 10% of oleyl amine；

Organic solvent 90%；

Wherein, 1,2,4- trimethoxy-benzenes, weight percentage of the organic solvent by weight percentage for 55% Fluorine (benzene sulfydryl) the ethyl acetate solvent composition that cyclohexyl benzene and weight percentage for 30% are 15%, and 1,2,4- front threes Oxygroup benzene, cyclohexyl benzene, fluorine (benzene sulfydryl) ethyl acetate solvent are refined to purity greater than 99.9% through water removal, deoxygenation.

S51. each component is weighed according to the formula of above-mentioned inorganic nano material printing ink；

S52., 500mL high-density polyethylene bottle is provided, in the case of stirring, successively adds the stable green of oleyl amine CdZnSe/CdZnS, 1,2,4- trimethoxy-benzenes, cyclohexyl benzene, fluorine (benzene sulfydryl) ethyl acetate solvent, are stirred 30min, Obtain quantum dot printing ink composition；

S53. by the quantum dot printing ink composition by ink-jet printer inkjet printing on carrier, it is printed as 20 × The green quantum dot layer of 30um, 200 × 200ppi of resolution ratio.120 DEG C, 1 × 10 are heated on hot plate^-6Volatile dry under Torr 30min obtains monochromatic quantum dot luminescent layer.

Embodiment 6

A kind of inorganic nano material printing ink, including the quantum dot and organic solvent that oleyl amine is stable, wherein the oleyl amine The mass ratio of stable quantum dot and organic solvent is 15:85；Wherein, the stable quantum dot of the oleyl amine is the stable indigo plant of oleyl amine Color CdS/CdZnS, (green CdZnSe/CdZnS, red CdSe/ZnS quantum dot)；The organic solvent is by weight percentage For 50% 3- phenoxytoluene, weight percentage be 25% 2- isopropyl naphthalene, 12 that weight percentage is 22% The 4- fluorophenyl acetate that alkane and weight percentage are 3% forms, and 3- phenoxytoluene, 2- isopropyl naphthalene, dodecane and 4- fluorophenyl acetate is refined to purity greater than 99.9% through water removal, deoxygenation.

S61. each component is weighed according to the formula of above-mentioned inorganic nano material printing ink；

S62., 500mL high-density polyethylene bottle is provided, in the case of stirring, it is different successively to add 3- phenoxytoluene, 2- The stable blue CdS/CdZnS of propyl naphthalene, oleyl amine, (green CdZnSe/CdZnS, red CdSe/ZnS quantum dot), dodecane and 4- fluorophenyl acetate, is stirred 30min, obtains quantum dot printing ink composition；

S63. by the quantum dot printing ink composition by ink-jet printer inkjet printing on carrier, it is printed as 20 × Blue, green, the red side-by-side quantum dot layer of 30um, 200 × 200ppi of resolution ratio.160 DEG C, 1 are heated on hot plate ×10^-5Volatile dry 30min under Torr obtains three primary colours quantum dot light emitting layer.

Embodiment 7

A kind of inorganic nano material prints ink, including the stable quantum dot of oleyl amine, organic solvent and auxiliary reagent, In, the mass ratio of the stable quantum dot of the oleyl amine and organic solvent is 5:95；The organic solvent is by weight percentage The methyl perfluoro nonyl ketone that 75% 1,2- dimethylnaphthalene and weight percentage is 25% forms, and 1,2- dimethylnaphthalene and first Base perfluor nonyl ketone solvent is refined to purity greater than 99.9% through water removal, deoxygenation；The auxiliary reagent be carboxymethyl cellulose, Polypyridine and polyoxyethylene.

S71. each component is weighed according to the formula of above-mentioned inorganic nano material printing ink；

S72., 500mL single-necked flask is provided, in the case of stirring, the stable red CdSe/ZnS quantum of addition oleyl amine Point, 1,2- dimethylnaphthalene, methyl perfluoro nonyl ketone solvent, carboxymethyl cellulose, polypyridine and polyoxyethylene, are stirred 30min obtains quantum dot printing ink composition；

S73. the quantum dot printing ink composition is injected into printing ink-jet printer cartridge, by ink-jet printer in carrier Upper inkjet printing is printed as 20 × 30um, the red quantum dot layer of 200 × 200ppi of resolution ratio.150 are heated on hot plate ℃、1×10^-4Volatile dry 30min under Torr obtains monochromatic quantum dot luminescent layer.

Embodiment 8

The stable green CdZnSe/CdZnS 10% of oleyl amine；

Organic solvent 90%；

Wherein, the organic solvent is 55% by weight percentage 4- isopropyl biphenyl, weight percentage are The fluoro- 2- trifluoromethyl acetophenone solvent composition of the 4- that 40% cyclohexyl benzene and weight percentage is 5%, and 4- isopropyl joins The fluoro- 2- trifluoromethyl acetophenone solvent of benzene, cyclohexyl benzene, 4- is refined to purity greater than 99.9% through water removal, deoxygenation.

S81. each component is weighed according to the formula of above-mentioned inorganic nano material printing ink；

S82., 500mL high-density polyethylene bottle is provided, in the case of stirring, successively adds the stable green of oleyl amine The fluoro- 2- trifluoromethyl acetophenone of CdZnSe/CdZnS, 4- isopropyl biphenyl, cyclohexyl benzene, 4-, is stirred 30min, the amount of obtaining Son point printing ink composition；

S83. by the quantum dot printing ink composition by ink-jet printer inkjet printing on carrier, it is printed as 20 × The green quantum dot layer of 30um, 200 × 200ppi of resolution ratio.115 DEG C, 1 × 10 are heated on hot plate^-6Volatile dry under Torr 30min obtains monochromatic quantum dot luminescent layer.

Embodiment 9

A kind of inorganic nano material printing ink, including the quantum dot and organic solvent that oleyl amine is stable, wherein the oleyl amine The mass ratio of stable quantum dot and organic solvent is 6:94；The stable quantum dot of the oleyl amine is the stable blue CdS/ of oleyl amine CdZnS, (green CdZnSe/CdZnS, red CdSe/ZnS quantum dot)；The organic solvent is 55% by weight percentage 3- phenoxytoluene, weight percentage be 25% 1,2,3,4- naphthane, weight percentage be 19% diphenyl ether The bromo- 2- of 2- (2- the fluorophenyl) -1- cyclopropyl ethyl ketone for being 1% with weight percentage forms, and 3- phenoxytoluene, 1, and 2,3, 4- naphthane, diphenyl ether and the bromo- 2- of 2- (2- fluorophenyl) -1- cyclopropyl ethyl ketone are refined to purity and are greater than through water removal, deoxygenation 99.9%.

S91. each component is weighed according to the formula of above-mentioned inorganic nano material printing ink；

S92. provide 500mL high-density polyethylene bottle, in the case of stirring, successively add 3- phenoxytoluene, 1,2, The stable blue CdS/CdZnS of 3,4- naphthane, oleyl amine, (green CdZnSe/CdZnS, red CdSe/ZnS quantum dot), hexichol Ether and the bromo- 2- of 2- (2- fluorophenyl) -1- cyclopropyl ethyl ketone, are stirred 30min, obtain quantum dot printing ink composition；

S93. by the quantum dot printing ink composition by ink-jet printer inkjet printing on carrier, it is printed as 20 × Blue, green, the red side-by-side quantum dot layer of 30um, 200 × 200ppi of resolution ratio.170 DEG C, 1 are heated on hot plate ×10^-5Volatile dry 30min under Torr obtains three primary colours quantum dot light emitting layer.

Embodiment 10

A kind of inorganic nano material prints ink, including the stable quantum dot of oleyl amine, organic solvent and auxiliary reagent, In, the mass ratio of the stable quantum dot of the oleyl amine and organic solvent is 4:96；The organic solvent is by weight percentage Bis- (4- fluorophenyl) ethers that 70% tetradecane and weight percentage is 30% form, and the tetradecane and bis- (4- fluorophenyl) ethers Purity is refined to greater than 99.9% through water removal, deoxygenation；The auxiliary reagent is polyoxyethylene carboxylate.

S101. each component is weighed according to the formula of above-mentioned inorganic nano material printing ink；

S102., 500mL single-necked flask is provided, in the case of stirring, the stable red CdSe/ZnS quantum of addition oleyl amine Point, tetradecane solvent, bis- (4- fluorophenyl) ethers and polyoxyethylene carboxylate, are stirred 30min, obtain quantum dot ink group Close object；

S103. the quantum dot printing ink composition is injected into printing ink-jet printer cartridge, is being carried by ink-jet printer Inkjet printing on body is printed as 20 × 30um, the red quantum dot layer of 200 × 200ppi of resolution ratio.160 are heated on hot plate ℃、1×10^-4Volatile dry 30min under Torr obtains monochromatic quantum dot luminescent layer.

Embodiment 11

A kind of inorganic nano material printing ink, including the quantum dot and organic solvent that oleyl amine is stable, wherein the oleyl amine The mass ratio of stable quantum dot and organic solvent is 10:90；The 1- first that the organic solvent is 50% by weight percentage The ten hexafluoro nonyl of glycidol ether that the cyclohexyl benzene and weight percentage that oxygroup naphthalene, weight percentage are 45% are 5% Ether composition, and 1- methoxynaphthalene, cyclohexyl benzene, ten hexafluoro nonyl ether solvents of glycidol ether through water removal, deoxygenation be refined to it is pure Degree is greater than 99.9%.

S111. each component is weighed according to the formula of above-mentioned inorganic nano material printing ink；

S112., 500mL high-density polyethylene bottle is provided, in the case of stirring, successively adds the stable green of oleyl amine CdZnSe/CdZnS, 1- methoxynaphthalene, cyclohexyl benzene, ten hexafluoro nonyl ethers of glycidol ether, are stirred 30min, the amount of obtaining Son point printing ink composition；

S113. by the quantum dot printing ink composition by ink-jet printer inkjet printing on carrier, it is printed as 20 × The green quantum dot layer of 30um, 200 × 200ppi of resolution ratio.120 DEG C, 1 × 10 are heated on hot plate^-6Volatile dry under Torr 30min obtains monochromatic quantum dot luminescent layer.

Embodiment 12

The stable quantum dot 10% of oleyl amine；

Organic solvent 90%；

Wherein, the stable quantum dot of the oleyl amine blue CdS/CdZnS stable for oleyl amine, (green CdZnSe/CdZnS, Red CdSe/ZnS quantum dot)；3- phenoxytoluene that the organic solvent is 30% by weight percentage, weight percent contains Measure the decahydronaphthalenes for 45%, the 2,3- bis- that the benzene hexane that weight percentage is 24.5% and weight percentage are 0.5% Fluorobenzene hexyl ether composition, and 3- phenoxytoluene, decahydronaphthalenes, benzene hexane and 2,3- difluorobenzene hexyl ether are refined through water removal, deoxygenation It is greater than 99.9% to purity.

S121. each component is weighed according to the formula of above-mentioned inorganic nano material printing ink；

S122., 500mL high-density polyethylene bottle is provided, in the case of stirring, successively adds 3- phenoxytoluene, decahydro The stable blue CdS/CdZnS of change naphthalene, oleyl amine, (green CdZnSe/CdZnS, red CdSe/ZnS quantum dot), benzene hexane and 2, 3- difluorobenzene hexyl ether, is stirred 30min, obtains quantum dot printing ink composition；

S123. by the quantum dot printing ink composition by ink-jet printer inkjet printing on carrier, it is printed as 20 × Blue, green, the red side-by-side quantum dot layer of 30um, 200 × 200ppi of resolution ratio.160 DEG C, 1 are heated on hot plate ×10^-5Volatile dry 30min under Torr obtains three primary colours quantum dot light emitting layer.

Embodiment 13

A kind of inorganic nano material prints ink, including the stable quantum dot of oleyl amine, organic solvent and auxiliary reagent, In, the mass ratio of the stable quantum dot of the oleyl amine and organic solvent is 6:94；The organic solvent is by weight percentage 75% 1,2- dimethylnaphthalene and weight percentage be 25% 2- fluorine trifluomethoxybenzene form, and 1,2- dimethylnaphthalene and 2- fluorine trifluomethoxybenzene is refined to purity greater than 99.9% through water removal, deoxygenation；The auxiliary reagent is diethylene glycol list second Ether and polyoxyethylene block copolymer.

S131. each component is weighed according to the formula of above-mentioned inorganic nano material printing ink；

S132., 500mL single-necked flask is provided, in the case of stirring, the stable red CdSe/ZnS quantum of addition oleyl amine Point, 1,2- dimethylnaphthalene, 2- fluorine trifluomethoxybenzene, diethylene glycol monoethyl ether and polyoxyethylene block copolymer, are stirred 30min obtains quantum dot printing ink composition；

S133. the quantum dot printing ink composition is injected into printing ink-jet printer cartridge, is being carried by ink-jet printer Inkjet printing on body is printed as 20 × 30um, the red quantum dot layer of 200 × 200ppi of resolution ratio.170 are heated on hot plate ℃、1×10^-4Volatile dry 30min under Torr obtains monochromatic quantum dot luminescent layer.

Embodiment 14

A kind of inorganic nano material printing ink, including the quantum dot and organic solvent that oleyl amine is stable, wherein the oleyl amine The mass ratio of stable quantum dot and organic solvent is 10:90；The neighbour two that the organic solvent is 55% by weight percentage 3- fluoro- 4- (trifluoromethyl) bromine that the 1- methyl naphthalene and weight percentage that methoxybenzene, weight percentage are 40% are 5% Benzyl composition, and o-dimethoxybenzene, 1- methyl naphthalene, 3- fluoro- 4- (trifluoromethyl) bromobenzyl solvent through water removal, deoxygenation be refined to it is pure Degree is greater than 99.9%.

S141. each component is weighed according to the formula of above-mentioned inorganic nano material printing ink；

S142., 500mL high-density polyethylene bottle is provided, in the case of stirring, successively adds the stable green of oleyl amine CdZnSe/CdZnS, o-dimethoxybenzene, 1- methyl naphthalene, 3- fluoro- 4- (trifluoromethyl) bromobenzyl, are stirred 30min, the amount of obtaining Son point printing ink composition；

S143. by the quantum dot printing ink composition by ink-jet printer inkjet printing on carrier, it is printed as 20 × The green quantum dot layer of 30um, 200 × 200ppi of resolution ratio.110 DEG C, 1 × 10 are heated on hot plate^-6Volatile dry under Torr 30min obtains monochromatic quantum dot luminescent layer.

Embodiment 15

The stable quantum dot 10% of oleyl amine；

Organic solvent 90%；

Wherein, the stable quantum dot of the oleyl amine blue CdS/CdZnS stable for oleyl amine, (green CdZnSe/CdZnS, Red CdSe/ZnS quantum dot)；Dodecane that the organic solvent is 30% by weight percentage, weight percentage are Benzyl carbinol and weight percentage that 39.5% 1,2,3,4-tetralin, weight percentage are 20% are the 2 of 10.5%, 2,2- tri- fluoro- 4- *-methoxy acetophenone compositions, and dodecane, 1,2,3,4-tetrahydro-naphthalene, benzyl carbinol and 2,2,2- tri- fluoro- 4- first Oxygroup acetophenone is refined to purity greater than 99.9% through water removal, deoxygenation.

S151. each component is weighed according to the formula of above-mentioned inorganic nano material printing ink；

S152. provide 500mL high-density polyethylene bottle, in the case of stirring, successively add dodecane, 1,2,3,4- tetra- The stable blue CdS/CdZnS of hydrogenated naphthalene, oleyl amine, (green CdZnSe/CdZnS, red CdSe/ZnS quantum dot), benzyl carbinol and 2,2,2- tri- fluoro- 4- *-methoxy acetophenones, are stirred 30min, obtain quantum dot printing ink composition；

S153. by the quantum dot printing ink composition by ink-jet printer inkjet printing on carrier, it is printed as 20 × Blue, green, the red side-by-side quantum dot layer of 30um, 200 × 200ppi of resolution ratio.160 DEG C, 1 are heated on hot plate ×10^-5Volatile dry 30min under Torr obtains three primary colours quantum dot light emitting layer.

Embodiment 16

A kind of inorganic nano material prints ink, including the stable quantum dot of oleyl amine, organic solvent and auxiliary reagent, In, the mass ratio of the stable quantum dot of the oleyl amine and organic solvent is 3:97；The organic solvent is by weight percentage 1,1,1,2,2,3,4,5,5, the 5- Decafluoropentane that 75% 1- methoxynaphthalene and weight percentage is 25% forms, and 1- first Oxygroup naphthalene and 1,1,1,2,2,3,4,5,5,5- Decafluoropentane are refined to purity greater than 99.9% through water removal, deoxygenation；It is described auxiliary Helping reagent is polycarbazole, polythiophene, alkyl glycol ether, fluorine-containing surfactant.

S161. each component is weighed according to the formula of above-mentioned inorganic nano material printing ink；

S162., 500mL single-necked flask is provided, in the case of stirring, the stable red CdSe/ZnS quantum of addition oleyl amine Point, 1- methoxynaphthalene, 1,1,1,2,2,3,4,5,5,5- Decafluoropentane, polycarbazole, polythiophene, alkyl glycol ether, fluorine-containing table Face activating agent, is stirred 30min, obtains quantum dot printing ink composition；

S163. the quantum dot printing ink composition is injected into printing ink-jet printer cartridge, is being carried by ink-jet printer Inkjet printing on body is printed as 20 × 30um, the red quantum dot layer of 200 × 200ppi of resolution ratio.160 are heated on hot plate ℃、1×10^-4Volatile dry 30min under Torr obtains monochromatic quantum dot luminescent layer.

Embodiment 17

A kind of inorganic nano material printing ink, including the quantum dot and organic solvent that oleyl amine is stable, wherein the oleyl amine The mass ratio of stable quantum dot and organic solvent is 5:95；The adjacent diformazan that the organic solvent is 55% by weight percentage Ten trifluorohexane of the 1H- composition that the 1-ethylnaphthalene and weight percentage that oxygroup benzene, weight percentage are 40% are 5%, and O-dimethoxybenzene, 1-ethylnaphthalene, ten trifluorohexane solvent of 1H- are refined to purity greater than 99.9% through water removal, deoxygenation.

S171. each component is weighed according to the formula of above-mentioned inorganic nano material printing ink；

S172., 500mL high-density polyethylene bottle is provided, in the case of stirring, successively adds the stable green of oleyl amine CdZnSe/CdZnS, o-dimethoxybenzene, 1-ethylnaphthalene, ten trifluorohexane of 1H-, are stirred 30min, obtain quantum dot ink Composition；

S173. by the quantum dot printing ink composition by ink-jet printer inkjet printing on carrier, it is printed as 20 × The green quantum dot layer of 30um, 200 × 200ppi of resolution ratio.120 DEG C, 1 × 10 are heated on hot plate^-6Volatile dry under Torr 30min obtains monochromatic quantum dot luminescent layer.

Embodiment 18

The stable quantum dot 10% of oleyl amine；

Organic solvent 90%；

Wherein, the stable quantum dot of the oleyl amine blue CdS/CdZnS stable for oleyl amine, (green CdZnSe/CdZnS, Red CdSe/ZnS quantum dot)；Dodecane, weight percentage of the organic solvent by weight percentage for 29.95% For 50% decahydronaphthalenes, weight percentage be 20% acetophenone and weight percentage be 0.05% PF 5070 group At, and dodecane, decahydronaphthalenes, acetophenone and PF 5070 are refined to purity greater than 99.9% through water removal, deoxygenation.

S181. each component is weighed according to the formula of above-mentioned inorganic nano material printing ink；

S182. provide 500mL high-density polyethylene bottle, in the case of stirring, successively add dodecane, decahydronaphthalenes, The stable blue CdS/CdZnS of oleyl amine, (green CdZnSe/CdZnS, red CdSe/ZnS quantum dot), acetophenone and perfluor heptan Alkane is stirred 30min, obtains quantum dot printing ink composition；

S183. by the quantum dot printing ink composition by ink-jet printer inkjet printing on carrier, it is printed as 20 × Blue, green, the red side-by-side quantum dot layer of 30um, 200 × 200ppi of resolution ratio.150 DEG C, 1 are heated on hot plate ×10^-5Volatile dry 30min under Torr obtains three primary colours quantum dot light emitting layer.

Embodiment 19

A kind of inorganic nano material prints ink, including the stable quantum dot of oleyl amine, organic solvent and auxiliary reagent, In, the mass ratio of the stable quantum dot of the oleyl amine and organic solvent is 4:96；The organic solvent is by weight percentage Trans- -2- fluorine the cyclohexanol that 82% dodecane and weight percentage is 18% forms, and dodecane and trans- -2- fluorine hexamethylene Alcohol is refined to purity greater than 99.9% through water removal, deoxygenation；The auxiliary reagent is 1,2,4- trimethoxy-benzene, benzene hexane, gathers Aniline.

S191. each component is weighed according to the formula of above-mentioned inorganic nano material printing ink；

S192., 500mL single-necked flask is provided, in the case of stirring, the stable red CdSe/ZnS quantum of addition oleyl amine Point, dodecane, trans- -2- fluorine cyclohexanol, 1,2,4- trimethoxy-benzenes, benzene hexane, polyaniline, are stirred 30min, the amount of obtaining Son point printing ink composition；

S193. the quantum dot printing ink composition is injected into printing ink-jet printer cartridge, is being carried by ink-jet printer Inkjet printing on body is printed as 20 × 30um, the red quantum dot layer of 200 × 200ppi of resolution ratio.160 are heated on hot plate ℃、1×10^-4Volatile dry 30min under Torr obtains monochromatic quantum dot luminescent layer.

Embodiment 20

A kind of inorganic nano material printing ink, including the quantum dot and organic solvent that oleyl amine is stable, wherein the oleyl amine The mass ratio of stable quantum dot and organic solvent is 10:90；The neighbour two that the organic solvent is 55% by weight percentage 2, the 5- difluoro-benzyl alcohol composition that the cyclohexyl benzene and weight percentage that methoxybenzene, weight percentage are 40% are 5%, and O-dimethoxybenzene, cyclohexyl benzene, 2,5- difluoro-benzyl alcohol solvent are refined to purity greater than 99.9% through water removal, deoxygenation.

S201. each component is weighed according to the formula of above-mentioned inorganic nano material printing ink；

S202., 500mL high-density polyethylene bottle is provided, in the case of stirring, successively adds the stable green of oleyl amine CdZnSe/CdZnS, o-dimethoxybenzene, cyclohexyl benzene, 2,5- difluoro-benzyl alcohol, are stirred 30min, obtain quantum dot ink Composition；

S203. by the quantum dot printing ink composition by ink-jet printer inkjet printing on carrier, it is printed as 20 × The green quantum dot layer of 30um, 200 × 200ppi of resolution ratio.130 DEG C, 1 × 10 are heated on hot plate^-6Volatile dry under Torr 30min obtains monochromatic quantum dot luminescent layer.

Embodiment 21

The stable quantum dot 10% of oleyl amine；

Organic solvent 90%；

Wherein, the stable quantum dot of the oleyl amine blue CdS/CdZnS stable for oleyl amine, (green CdZnSe/CdZnS, Red CdSe/ZnS quantum dot)；The organic solvent by weight percentage be 40% 1,2,4- trimethoxy-benzene, weight hundred Benzene hexane and weight percentage that decahydronaphthalenes that point content is 35%, weight percentage are 24.5% are the 1 of 0.5%, 1,1- tri- fluoro- sec-n-octyl alcohol composition, and 1,2,4- trimethoxy-benzenes, decahydronaphthalenes, benzene hexane and 1,1,1- tri- fluoro- sec-n-octyl alcohol pass through Water removal, deoxygenation are refined to purity greater than 99.9%.

S211. each component is weighed according to the formula of above-mentioned inorganic nano material printing ink；

S212. provide 500mL high-density polyethylene bottle, in the case of stirring, successively add 1,2,4- trimethoxy-benzenes, The stable blue CdS/CdZnS of decahydronaphthalenes, oleyl amine, (green CdZnSe/CdZnS, red CdSe/ZnS quantum dot), benzene hexane With 1,1,1- tri- fluoro- sec-n-octyl alcohol is stirred 30min, obtains quantum dot printing ink composition；

S213. by the quantum dot printing ink composition by ink-jet printer inkjet printing on carrier, it is printed as 20 × Blue, green, the red side-by-side quantum dot layer of 30um, 200 × 200ppi of resolution ratio.160 DEG C, 1 are heated on hot plate ×10^-5Volatile dry 30min under Torr obtains three primary colours quantum dot light emitting layer.

The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all in essence of the invention Made any modifications, equivalent replacements, and improvements etc., should all be included in the protection scope of the present invention within mind and principle.

Claims

1. a kind of inorganic nano material prints ink, which is characterized in that the solvent in the inorganic nano material printing ink is Organic solvent, the inorganic nano material printing ink include at least one inorganic nano material and at least one fluorine silicon alkanes Organic solvent, the structure of the fluorine silicon alkanes organic solvent is as shown in general structure I:

(R^b’)_n’-(R_f ^b)_n-(R_f ^a)_m-(R^a’)_m’-SiR₁(R₂)(R₃) Formulas I

The R^b’Aliphatic, aromatic group, F, Cl, Br, I, sulfonate group, sulfonyl ester group independently selected from H, C1-30, Methoxyl group；

2. inorganic nano material as described in claim 1 prints ink, which is characterized in that described partially fluorinated or perfluorinated Alkyl, aryl include-CF₂-、-C_kF_2k+1、-CFC_kF_2k+1-、-CF₂C_kF_2k+1、-C₆F_jH_5-j, wherein j is the positive integer of 1-4, k For the positive integer of 1-10.

3. inorganic nano material as described in claim 1 prints ink, which is characterized in that the fluorine silicon alkanes organic solvent Selected from dimethoxy-methyl (3,3,3- trifluoro propyl) silicon, (3,3,3- trifluoro propyl) dichloro methyl silane, Chlorodimethyl -3,3, 3- fluoropropyl silane, the fluoro- N- octyl silane of triethoxy -1H, 1H, 2H, 2H- 13, trifluoro propyl methyl cyclotrisiloxane, three Methyl-monosilane base 2- (fluorosulfonyl) difluoro acetate, bis- (fluoroform sulfonylamino acid) di-t-butyl silicon substrate esters, tert-butyl diformazan silicon Base triflate, dimethoxy-methyl (3,3,3- trifluoro propyl) silicon, the fluoro- 4- of 1- (trimethyl silicon substrate) benzene, 1H, 1H, 2H, Bis- (3,3,3- the trifluoro propyl) -1,1,3,3- tetramethyl-disilazanes of 2H- perfluoro decyl trichlorosilane, 1,3-, the bis- (front threes of 1,4- Base silicon substrate) phenyl tetrafluoride, (trimethyl silicon substrate) methyl trifluoro methane sulfonate, (heptafluoropropyl) trimethyl silane, bis- (nine fluorine hexyls Dimethylsilyl bis) methyl-monosilane, 1H, 1H, 2H, one of 2H- perfluoro decyl triethoxysilane or a variety of.

4. inorganic nano material as described in any one of claims 1-3 prints ink, which is characterized in that by weight, institute The mass ratio for stating inorganic nano material and the organic solvent is 0.01-20.0:80-99.9, and the fluorine-containing esters are organic molten Agent accounts for the 1-90% of the organic solvent gross weight.

5. inorganic nano material as claimed in claim 4 prints ink, which is characterized in that by weight, described inorganic to receive The mass ratio of rice material and organic solvent is 4-15:85-96, and the fluorine-containing based organic solvent accounts for the organic solvent gross weight 1-50%.

6. inorganic nano material as claimed in claim 5 prints ink, which is characterized in that the inorganic nano material off-set oil Ink is made of the inorganic nano material and the organic solvent, by weight, the inorganic nano material with it is described organic The mass ratio of solvent is 4-15:85-96, and the fluorine-containing based organic solvent accounts for the 1-50% of the organic solvent gross weight.

7. inorganic nano material as claimed in claim 5 prints ink, which is characterized in that the inorganic nano material printing Ink further includes auxiliary reagent, and the auxiliary reagent is selected from one of charge transfer agent, viscosity modifier and dispersing agent or several Kind.

8. inorganic nano material as claimed in claim 7 prints ink, which is characterized in that the inorganic nano material off-set oil Ink is made of the inorganic nano material, the organic solvent and the auxiliary reagent.

9. inorganic nano material as described in any one of claims 1-3 prints ink, which is characterized in that the fluorine silicon alkanes The boiling point of organic solvent is 80 DEG C -350 DEG C.

10. inorganic nano material as described in any one of claims 1-3 prints ink, which is characterized in that the fluorine containing silane Range of viscosities of the class organic solvent at 25 DEG C is 0.5mPa.s-50mPa.s, and the surface tension at 25 DEG C is 20-50mN/m.

11. a kind of preparation method of the printing of the inorganic nano material as described in claim any one of 1-10 ink, including following step It is rapid:

Inorganic nano material and organic solvent are provided, at least contain a kind of fluorine silicon alkanes organic solvent in the organic solvent；

12. a kind of preparation method of inorganic nano material film, comprising the following steps:

Inorganic nano material printing ink is prepared according to claim 11 the method；

Ink is printed in deposited on supports inorganic nano using inkjet printing, by being dried, it is thin to obtain inorganic nano material Film.

13. the preparation method of inorganic nano material film as claimed in claim 12, which is characterized in that the drying process Mode includes heating drying, cooling and drying, at least one of is dried under reduced pressure.

14. the preparation method of inorganic nano material film as claimed in claim 13, which is characterized in that the heating drying Temperature is 30-180 DEG C, time 0-30min；

The temperature of the cooling and drying is 0-20 DEG C；

The vacuum degree of the drying process is 1 × 10^-6Torr is to normal pressure.