CN1097105C - 抗切割的纱线和织物及服装 - Google Patents

抗切割的纱线和织物及服装 Download PDF

Info

Publication number
CN1097105C
CN1097105C CN96199548A CN96199548A CN1097105C CN 1097105 C CN1097105 C CN 1097105C CN 96199548 A CN96199548 A CN 96199548A CN 96199548 A CN96199548 A CN 96199548A CN 1097105 C CN1097105 C CN 1097105C
Authority
CN
China
Prior art keywords
cut
yarn
yarns
resistant
twist
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN96199548A
Other languages
English (en)
Other versions
CN1207145A (zh
Inventor
L·J·普里克特
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
EIDP Inc
Original Assignee
EI Du Pont de Nemours and Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by EI Du Pont de Nemours and Co filed Critical EI Du Pont de Nemours and Co
Publication of CN1207145A publication Critical patent/CN1207145A/zh
Application granted granted Critical
Publication of CN1097105C publication Critical patent/CN1097105C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明公开了一种用对位型芳族聚酰胺纱线制成的织物，抗切割性增高且保持舒适性，其中纱线为低捻度而纱线中的短纤维具有高的线密度。

Description

抗切割的纱线和织物及服装
发明背景
用于抗切割服装的织物由于可以理解的要求要用高模量的高强度纱线，一般是刚性大和笨重些。过去抗切割服装诸如手套，围裙和防护袖套是由刚性纱线加工而成，这种纱线制成的织物硬且不舒适而且手感粗糙，而对纱线作改进使得到的织物抗切割性提高，结果使得到的织物更硬和更不舒服。本发明涉及到抗切割的机织物和针织物，它们在保持相当或较软的手感下显示出抗切割性得到改进提高。
发明概要
本发明涉及抗切割性得到提高的服装，它是由线密度为150至5900dtex(133至5315旦)和捻系数为小于26的纱线所制成，其中纱线包含有线密度为3至6dtex(3.7至5.4旦长度为2.5至15.2厘米(1至6英寸)的对位型芳族聚酰胺短纤维。
本发明还涉及到纱线和由此纱线制成的具有重量为每平方米135至1017克(4至30盎司/码2)的抗切割织物。详细说明
长期以来在防护服领域内在舒适性和有效性之间有矛盾；而且作了很大的努力在保持舒适的同时提高它的有效性。本发明就是代表了在抗切割服装和织物领域中这样的改进。采用本发明就能够在保持织物和防护服如抗切割手套的舒适下提高抗切割的有效性。
已经发现，由对位型芳族聚酰胺纤维纺成的纱线所制成的防护服，如果纱线的捻度比较小就会比较柔软。此外，已发现这样服装的织物的抗切割性是与织物中纱线的捻度大小无关，而是，织物的抗切割性是随纱线所用的单纤维线密度的提高而得到改善。
对位型芳族聚酰胺纤维表示这种纤维是由对位型芳族聚酰胺聚合物所制成；而且聚对苯二甲酰对苯二胺(PPD-T)是最好的对位型芳族聚酰胺聚合物。PPD-T表示是由对苯二胺与对苯二酰氯克分子对克分子聚合而得到的均聚物，或，由结合有少量其它二胺的对苯二胺与结合有少量其它二酰氯的对苯二酰氯而得到的共聚物。通常，多至对苯二胺或对苯二酰氯的约10％克分子量或者是略高些的其它二胺和其它二酰氯也是能用的，只要其它二胺和其它二酰氯没有反应基团与聚合反应相干扰。PPD-T也表示结合有其它芳族二胺和其它芳族二酰氯，例如2，6-萘酰氯或是氯或二氯对苯二酰氯的共聚物，只要其它芳族二胺和芳族二酰氯在数量上对于对位型芳族聚酰胺的性能不起反作用。
对位型芳族聚酰胺纤维中也可用添加剂，并且已知道多至10％(重量)的其它聚合物材料可以和芳族聚酰胺相混合，或者可以用由多至10％其它二胺取代芳族聚酰胺中的二胺或是多至10％其它二酰氯取代芳族聚酰胺中的二酰氯的共聚物。
纺纱线用的短纤维一般是有一个特定长度和特定的线密度。本发明所用的纤维可以为任意长度，只要适合于纺纱线加工。短纤维的长度可以用2.5至15.2厘米(1至6英寸)而长度以3.8至11.4厘米(1.5至4.5英寸)为好。短纤维长度小于2.5厘米所制成的纱线已经知道需要有很高的捻度来保持加工强度；而由短纤维长度大于15.2厘米所制造的纱线就更难于制造，因为短纤维长度长了以后会造成相互缠结和断裂而得到很短的纤维。本发明所用的短纤维一般是由连续的长丝切割成一定的预定长度而得；但是短纤维也可以由其它方法制得诸如牵切法；而纱线也可由这样的纤维以及多种或不同分布的短纤维长度所制成。
纺制的纱线是由纺纱线时加捻而使之结合在一起。卷曲的短纤维是在纺纱线机上纺纱线而形成带一定捻度的纱线，加捻使纤维相互缠结在一起形成纱线。过去，防护服用的抗切割织物在实际应用中使用高捻度的纱线。一般认为高强度的纱线是需要用高捻度；而好的抗切割性是需要有高强度。高捻度使纤维在形成的纱线中抱合得很紧从而产生出相当硬的纱线。
现在已发现有效的防护不需要用高捻度的纱线；并且事实上已经知道抗切割性与制作防护织物所用的纱线的捻度无关。但是，捻度对这样的织物的柔软性或舒适性是一个很重要的因素。已经发现用低捻度纱线做成的织物要比高捻度纱线做成的织物柔软得多而且“手感”好得多。此外，已知道降低捻度可以提高织物的柔软性，而与它所用的纱线种类或制造的材料无关。
纱线捻度一般由称为“捻系数”的系数来表示，它也可以称为捻度因子。较高的捻系数表示捻度量较大。直到现在，防护服中抗切割织物最好是由捻系数为大于28(tex)1/2(捻/厘米)的纱线所制成并用线密度小于或等于2.5dtex的短纤维。纱线的捻系数(TF)是表明纱线中纤维的加捻度，考虑到纱线的线密度，能用几种量纲制的任一种进行确定：
号数制
TF＝(捻/厘米)(号数)1/2
英制支数制
TF＝(捻/英寸)/(英制棉纱线支数)1/2
公制支数制
TF＝(捻/米)/(纱线的公支数)1/2
纱线的“英制棉纱线支数”是454克(1磅)重、长768米(840码)纱线的绞纱线数。
纱线的“公支数”是1千克重量纱线的千米数。
对本文来说，号数制捻系数用的是号数1/2捻/厘米的SI单位。
在本发明的织物中已经知道捻系数小于约26的纱线能得到柔软的织物，它能制成舒适又抗切割的手套。在纱线中需要有一些捻度，目的是为了使纱线能保持在一起，从测试表明，抗切割性并不受纱线捻度变化的影响。即，以增加捻度使纱线有附加的强度并不能转而提高抗切割性。已得出结论，实际表明，本发明的纱线应有的捻系数至少约为10。对单根的10英支(等于590dtex)的纱线，捻系数为约10换算成捻度为约每厘米1.3捻。本发明的纱线最好有一个捻系数为15至22。
纱线是由短纤维制成的。已经知道在本发明实际应用中的纱线应该有一个纱线线密度为150至5900dtex，而最好为550至4700dtex。纱线可以由单根或几根合股而成并可以是或不是加捻在一起。
对于单根纤维的线密度，已发现增加短纤维的线密度可以提高纱线的抗切割性。过去，抗切割性防护服的纱线用的单根短纤维为约2.5dtex或小些。虽然那样的纱线适合于许多用途，已知织物的抗切割性能随纱线中所用短纤维线密度的增加而得到提高。此外，已知这样织物的舒适性会随着它用的纱线的捻度的减小而得到保持。由此，应用本发明能制成与已知产品相当的具有抗切割性和舒适性得到提高的织物。例如，抗切割性得到提高的织物能用捻系数小于26、含有线密度为3至6dtex的对位型芳族聚酰胺短纤维的纱线制成。这样的织物会由纤维线密度的增加而得到抗切割性提高并能由纱线捻度的减少而保持舒适性。
从舒适方面看，已发现本发明的低捻度纱线，应是由线密度为3至6dtex并最好是4至5dtex的短纤维所制成。小于约3dtex的纤维也许不会得到本发明的提高的抗切割性。大于约6dtex的纤维呈现出很好的抗切割性，但是不美观而且得不到有合适舒适性的织物。
本发明的纱线可以由任何合适的纺纱线方法加工而成，例如，棉/精毛纺/粗毛纺的环锭纺纱线及自由端纺纱线。
本发明纺制的纱线具有低捻度和高的线密度，它能制成高抗切割性的针织或机织或是甚至单向铺设的织物。而且，纺制的纱线也可以直接由纺织机制成手套及其它服装。抗切割性是纱线中长丝线密度的一个函数而不是纱线在织物中所呈现的方式的函数。测定方法 抗切割性，采用的方法是“用于测量防护服用织物的抗切割性的标准测定方法”，推荐为ASTM标准(ASTM分组委员会F23.20)。在实行测定时，一个刀刃在特定的力下横拉过贴在心轴上的样品一次。以几种不同的力，记录从开始接触到割穿的拉过距离并构造一个力与割穿距离关系的图。从图上确定在割穿距离为25毫米处的力并被取准以作为供给的刀一致性的根据。记录所取准的力，作为抗切割力。
刀刃为不锈钢的刀片，锋利的刀口长70毫米。在测定开始和结束时，供给的刀片用400克的负荷在聚氯丁橡胶校准材料上进行校准。每次切割测定要用一片新的刀刃。
样品是一块50×100毫米的长方形织物切片，以经纱线与纬纱线方向成45°切下。
心轴是一根圆的导电的棒，其半径为38毫米，将样品用双面胶带贴在它的上面。刀刃与心轴纵向轴线成直角横拉过心轴上的织物。当刀刃与心轴产生通电接触时割穿被记录下来。
例子 要测定的针织手套和织物
四种不同线密度的对位型芳族聚酰胺长丝纱线被卷曲后切割成短纤维用于纺纱线成为供这些例子用的测试纱线。长丝纱线是聚对苯二甲酰对苯二胺纱线，是由杜邦公司(E.I.du Pont de Nemours andCompany)以商标Kevlar29出售，它是由线密度为1.67，2.50，4.67和6.67dtex长丝制成。短纤维的长度是11.4厘米。
每种短纤维的一部分由精毛纺设备纺制成不同捻度的纱线。双股纱线是纺成线密度590dtex(英支20/2)，捻系数如表1及表2所示。
样品手套和样品织物是在Shima Seiki手套编织机上用这些纱线编织而成，起针为4和6根。4根起针得到的编织织物和粗支纱线编织手套平均重量为478克/米2(14.1盎司/码2)；而6根起针得到的编织织物和手套平均重量为783克/米2(23.1盎司/码2)。例1
上述制备的手套被用于作抗切割性测定以得到抗切割性与织物参数的短纤维线密度和纱线捻系数之间的关系资料。那些测定的结果列出在下面的表1和表2中，分别对应6根和4根的织物。
                 表1(6根的织物)线密度     1.67dtex    2.50dtex  4.67dtex   6.67dtex捻度                   抗切割性(公斤-力)14          1.4        1.6        1.8          -17          1.3        1.6        1.7         1.819          1.4        1.5        1.6         1.822          1.3        1.4        1.6         1.724          1.3        1.5        1.9         2.326          1.3        1.4        1.8         1.829          1.4        1.5        1.9         2.031          1.3       1.4       1.7        1.8平均         1.3        1.5        1.8         1.9
                 表2(4根的织物)线密度      1.67dtex    2.5dtex   4.67dtex   6.67dtex捻度                   抗切割性(公斤-力)14          1.0         1.1        1.2          -17          1.0         1.1        1.5         1.6
 19         1.1         1.2         1.4         1.5
 22         1.1         1.2         1.4         1.5
 24         0.9         1.2         1.4         1.6
 26         1.0         1.0         1.6         1.5
 29         1.0         1.2         1.5         1.6
 31         1.2        1.1        1.4        1.5
平均        1.0         1.1         1.4         1.5
由这个例子得到的抗切割性数据看出抗切割性是短纤维线密度的一个确定函数而与捻度相对无关。抗切割性随短纤维线密度的增加而显著地改善，而且在短纤维线密度大于2.5dtex处提高最为显著。例2
上述制备的6根织物被用于作舒适性测定，其中31个织物样品用感触来确定每个样品的“手感”。由10个人对每个样品作感触并以1-5的尺度(1为最硬而5为最软)对柔软性进行评定。10个人的全部评定被平均并记录在下面的表3中。
                      表3线密度     1.67dtex    2.50dtex    4.67dtex  6.67dtex捻度                 舒适性评定(10人平均)
14      4.4         4.4          3.2         -
17      4.2         4.4          3.1        2.9
19      4.2         4.0          3.0        2.5
22      3.6         3.5          2.5        2.1
24      3.5         3.5          2.2        2.5
26      3.3         3.2          2.0        1.3
29      3.0         2.4          2.0        1.8
31      2.8         2.0          1.4        1.4
从这个例子的舒适性数据可知舒适性是纱线捻度的一个直接函数。当捻度减小时舒适性显著的改善。如前面所说明的，商业上提供的手套一般所用的织物是线密度小于约2.5dtex的短纤维和最好捻系数为大于28的纱线所制的。从表3可以明白这样的织物所评定的舒适性在这些测定中为2至3；而本发明由线密度为4.67dtex和捻系数为小于26的纱线所制成的那种织物是至少被评定为好。随着短纤维线密度的降低和捻度的减少舒适性明显增加。
例1和2表明由短纤维线密度大于2.5dtex的纱线制成的织物显示出抗切割性提高而由小于6.67dtex和捻系数小于26的纱线所制成的织物显示出舒适性提高。那些结果的组合表明短纤维线密度3至6dtex和捻系数小于26的纱线将使织物同时具有抗切割性并保持舒适。

Claims (17)

1.一种抗切割纱线，具有线密度150至5900dtex且捻系数小于26，其特征在于纱线包括线密度为3至6dtex和长度为2.5至15.2厘米的对位型芳族聚酰胺短纤维。
2.根据权利要求1的纱线，其特征在于短纤维有4至5dtex的线密度。
3.根据权利要求1的纱线，其特征在于纱线有一个15至22的捻系数。
4.根据权利要求2的纱线，其特征在于纱线有一个15至22的捻系数。
5.一种由抗切割纱线制成的抗切割织物，所述纱线具有线密度150至5900dtex且捻系数小于26，其特征在于纱线包括线密度为3至6dtex和长度为2.5至15.2厘米的对位型芳族聚酰胺短纤维，并且织物的重量为每平方米135至1017克。
6.根据权利要求5的抗切割织物，其特征在于短纤维有4至5dtex的线密度。
7.根据权利要求5的抗切割织物，其特征在于纱线有一个15至22的捻系数。
8.根据权利要求6的抗切割织物，其特征在于纱线有一个15至22的捻系数。
9.根据权利要求5-8任一的抗切割织物，其特征在于所述织物是由所述纱线通过机织而形成的。
10.根据权利要求5-8任一的抗切割织物，其特征在于所述织物是由所述纱线通过针织而形成的。
11.一种抗切割服装，其特征在于由根据权利要求5-8任一的抗切割织物制成。
12.一种抗切割服装，其特征在于由根据权利要求9的抗切割织物制成。
13.一种抗切割服装，其特征在于由根据权利要求10的抗切割织物制成。
14.根据权利要求11的抗切割服装，其形式为手套。
15.根据权利要求12的抗切割服装，其形式为手套。
16.根据权利要求13的抗切割服装，其形式为手套。
17.一种抗切割服装，其特征在于由根据权利要求1的抗切割纱线制成。。
CN96199548A 1996-01-05 1996-12-31 抗切割的纱线和织物及服装 Expired - Fee Related CN1097105C (zh)