CN109627859A - 一种绿色环保型水性木油 - Google Patents
一种绿色环保型水性木油 Download PDFInfo
- Publication number
- CN109627859A CN109627859A CN201811538793.7A CN201811538793A CN109627859A CN 109627859 A CN109627859 A CN 109627859A CN 201811538793 A CN201811538793 A CN 201811538793A CN 109627859 A CN109627859 A CN 109627859A
- Authority
- CN
- China
- Prior art keywords
- water
- agent
- wood oil
- environment
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种绿色环保型水性木油，由水性苯丙乳液和水性丙烯酸乳液混拼为成膜物质，配合成膜助剂、PH值调节剂、消泡剂、润湿剂、流平剂、分散剂、防水剂、增稠剂及水性蜡浆制备而成。各组分按重量计：水性苯丙乳液55～63%，水性丙烯酸类乳液10～15%，成膜助剂1.5～7%，PH值调节剂0.1～0.5%，消泡剂0.1～0.4%，润湿剂0.1～0.3%，流平剂0.05～0.3%，分散剂0.2～0.5%，防水剂0.1～0.25%，增稠剂0.5～1.8%，高滑蜡乳液0.5～2.5%，水性消光蜡浆1.5～5.5，去离子水11.75～20.9%。本发明制备的水性木油净味、低VOC、对人体无刺激，绿色健康环保；渗透性好，对大多数木材具有极佳的附着力，适用范围广；漆膜硬度高、表面性能好、耐水性能好，极佳的保护能力；手感极佳，提高木器制品的附加值。
Description
技术领域
本发明涉及一种绿色环保型水性木油，属环保类水性木油技术领域。
背景技术
木油源自我国的油桐林木果实油，以原产我国的三年桐和千年桐最为普遍。油桐种子榨出的油叫桐油；木油桐种子榨出的油叫木油，质量稍逊。木油为天然植物油，属干性油。
公告号CN102604518公开了一种环保型天然木油，该木油由IPDI改性豆油漆醇酸树脂、防结皮剂、高效复合催干剂、复合环保溶剂制备而成，属溶剂性油性木油。溶剂性木油生产时会产生大量的挥发性有机化合物VOC，对环境造成污染。
水性丙烯酸涂料是一类环境友好型涂料，不含三苯、重金属、甲醛、不含烷基酚聚氧乙烯醚及其他有毒有害物质，对人体无刺激，该类涂料具有色浅、保色、保光、耐候、耐腐蚀和耐污染等优点，综合性能优良，应用广泛。自2009年中国木器涂料产量已跃居全球第一，但其中大多数是溶剂型涂料，带来大量的VOC，为此，水性木器涂料成为了人们关注的重点之一，水性丙烯酸木器涂料，低VOC，装饰性好，综合性能良好，适用性好，是木器涂料增长最快的品种之一。
木制品在使用、存储过程中，极易受到水的侵害，出现水分浸润干燥过程导致木制品变形、在潮湿环境发霉生菌等情况，这将极大的降低木制品的使用寿命。对木制品进行合理的涂装，不但能为木制品提供保护，还可以改善其表观，提升其价值。
发明内容
本发明的目的是，为了解决木制品涂料的环保问题，本发明公开一种绿色环保型水性木油。
本发明实现的技术方案如下：一种绿色环保型水性木油，所述木油由水性苯丙乳液和水性丙烯酸乳液混拼为成膜物质，配合成膜助剂、PH值调节剂、消泡剂、润湿剂、流平剂、分散剂、防水剂、增稠剂及水性蜡浆制备而成。
各组分按重量计：水性苯丙乳液55～63％，水性丙烯酸类乳液10～15％，成膜助剂1.5～7％，PH值调节剂0.1～0.5％，消泡剂0.1～0.4％，润湿剂0.1～0.3％，流平剂0.05～0.3％，分散剂0.2～0.5％，防水剂0.1～0.25％，增稠剂0.5～1.8％，高滑蜡乳液0.5～2.5％，水性消光蜡浆1.5～5.5,去离子水11.75～20.9％。
所述成膜助剂为丙二醇甲醚、二丙二醇甲醚、丙二醇苯醚、丙二醇丁醚、二丙二醇丁醚、Texanol(酯醇十二)中的两种或多种。
所述PH值调节剂为N,N二甲基乙醇胺、AMP-95中的一种或两种。
所述消泡剂为有机硅水性消泡剂，成分是聚硅氧烷和疏水性固体聚乙二醇的混合物。
所述润湿剂为有机硅表面活性剂，成分是聚醚硅氧烷共聚物。
所述流平剂为有机硅类的表面助剂，成分是聚醚改性聚二甲基硅氧烷溶液、聚醚硅氧烷共聚物的一种或两种。
所述分散剂为带有颜料亲和基团的高分子量嵌段共聚物类润湿分散剂。
所述防水剂为有机硅防水剂。
所述增稠剂为聚氨酯缔合型增稠剂。
本发明的有益效果是，本发明制备的水性木油净味、低VOC、对人体无刺激，绿色健康环保；渗透性好，对大多数木材具有极佳的附着力，适用范围广；漆膜硬度高、表面性能好、耐水性能好，极佳的保护能力；手感极佳，提高木器制品的附加值。
本发明采用的水性苯丙乳液是快干型苯丙乳液，耐水性好，具有较高的玻璃化转变温度；采用水性碱溶性丙烯酸类乳液，玻璃化转变温度较低，柔韧性好，耐水性好，对基材的渗透性、附着力极佳；两种树脂搭配涂膜质量更好,性能佳。
本发明采用采用高密度聚乙烯蜡，抗刮显著，高滑油腻手感，耐擦洗性能，抗回粘和疏水荷叶效果显著；采用水性消光蜡浆，易分散，透明度高，消光强，手感滑爽不含乳化剂，有助消泡；两种蜡浆复配效果更好。
本发明采用了先进的消泡剂、流平剂、润湿剂、分散剂、防水剂、增稠剂助剂，满足了目前木油的生产及施工要求。
本发明采用的复合成膜助剂毒性低、气味小、无毒性，可降解，绝对无苯且VOC含量低，符合绿色环保健康的要求。
具体实施方式
实施例1：
本实施例一种绿色环保型水性木油，按一般制漆工艺的制作而成，其配方具体成分及按质量配比如下：
水性快干苯丙类乳液55％，水性碱溶性丙烯酸类乳液15％，第一成膜助剂5％，第二成膜助剂2％，PH值调节剂0.2％，消泡剂0.4％，润湿剂0.3％，流平剂0.1％，分散剂0.3％，防水剂0.2％，增稠剂1.6％，高滑蜡乳液2％，水性消光蜡浆5％,去离子水12.9％。
本实施例中，成膜助剂包括两种：第一成膜助剂为二丙二醇甲醚，第二成膜助剂为二丙二醇丁醚。
PH值调节剂是多功能助剂AMP-95，主要成分是2-氨基-2-甲基-1-丙醇。
消泡剂是有机硅水性消泡剂，主要成分是聚硅氧烷和疏水性固体聚乙二醇的混合物。
润湿剂是有机硅表面活性剂，主要成分是聚醚硅氧烷共聚物。
流平剂是聚醚改性聚二甲基硅氧烷溶液、聚醚硅氧烷共聚物的一种或两种。
分散剂是带有颜料亲和基团的高分子量嵌段共聚物类溶液。
防水剂是有机硅交联剂。
增稠剂是聚氨酯缔合型增稠剂。
本实施例中的水性蜡浆是高密度聚乙烯蜡，为两种聚乙烯蜡产品配合使用，一种为水性高滑透明蜡乳液，另一种为水性蜡浆。
实施例2：
本实施例一种绿色环保型水性木油，按一般制漆工艺的制作而成，其配方具体成分及按质量配比如下：
水性快干苯丙类乳液55％，水性碱溶性丙烯酸类乳液15％，第一成膜助剂3％，第二成膜助剂1.5％，PH值调节剂0.2％，消泡剂0.4％，润湿剂0.2％，流平剂0.5％，分散剂0.1％，防水剂0.2％，增稠剂1.8％，高滑蜡乳液1％，水性消光蜡浆2％,去离子水19.1％。
本实施例中的成膜助剂有两种：第一成膜助剂为二丙二醇甲醚，第二成膜助剂为二丙二醇丁醚。
PH值调节剂是多功能助剂AMP-95，主要成分是2-氨基-2-甲基-1-丙醇。
消泡剂是有机硅水性消泡剂，主要成分是聚硅氧烷和疏水性固体聚乙二醇的混合物。
润湿剂是有机硅表面活性剂，主要成分是聚醚硅氧烷共聚物。
流平剂是聚醚改性聚二甲基硅氧烷溶液、聚醚硅氧烷共聚物的一种或两种。
分散剂是带有颜料亲和基团的高分子量嵌段共聚物类溶液。
防水剂是有机硅交联剂。
增稠剂是聚氨酯缔合型增稠剂。
本实施例中的水性蜡浆是高密度聚乙烯蜡，为两种聚乙烯蜡产品配合使用，一种为水性高滑透明蜡乳液，另一种为水性蜡浆。
实施例3：
本实施例一种绿色环保型水性木油，按一般制漆工艺的制作而成，其配方具体成分及按质量配比如下：
水性快干苯丙类乳液63％，水性碱溶性丙烯酸类乳液10％，第三成膜助剂5％，第四成膜助剂2％，PH值调节剂0.15％，消泡剂0.3％，润湿剂0.3％，流平剂0.1％，分散剂0.3％，防水剂0.2％，增稠剂1.8％，高滑蜡乳液2％，水性消光蜡浆5％,去离子水9.85％。
本实施例中的成膜助剂有两种：第三成膜助剂为丙二醇甲醚，第四成膜助剂为丙二醇苯醚。
PH值调节剂是多功能助剂AMP-95，主要成分是2-氨基-2-甲基-1-丙醇。
消泡剂是有机硅水性消泡剂，主要成分是聚硅氧烷和疏水性固体聚乙二醇的混合物。
润湿剂是有机硅表面活性剂，主要成分是聚醚硅氧烷共聚物。
流平剂是聚醚改性聚二甲基硅氧烷溶液、聚醚硅氧烷共聚物的一种或两种。
分散剂是带有颜料亲和基团的高分子量嵌段共聚物类溶液。
防水剂是有机硅交联剂。
增稠剂是聚氨酯缔合型增稠剂。
本实施例中的水性蜡浆是高密度聚乙烯蜡，为两种聚乙烯蜡产品配合使用，一种为水性高滑透明蜡乳液，另一种为水性蜡浆。
实施例4：
本实施例一种绿色环保型水性木油，按一般制漆工艺的制作而成，其配方具体成分及按质量配比如下：
水性快干苯丙类乳液55％，水性碱溶性丙烯酸类乳液15％，第五成膜助剂5％，第六成膜助剂2％，PH值调节剂0.2％，消泡剂0.3％，润湿剂0.3％，流平剂0.3％，分散剂0.3％，防水剂0.2％，增稠剂0.6％，高滑蜡乳液2％，水性消光蜡浆5％,去离子水13.8％。
本实施例中的成膜助剂有两种：第五成膜助剂为二丙二醇甲醚，第六成膜助剂为Texanol(酯醇十二)。
PH值调节剂是N,N二甲基乙醇胺。
消泡剂是有机硅水性消泡剂，主要成分是聚硅氧烷和疏水性固体聚乙二醇的混合物。
润湿剂是有机硅表面活性剂，主要成分是聚醚硅氧烷共聚物。
流平剂是聚醚改性聚二甲基硅氧烷溶液、聚醚硅氧烷共聚物的一种或两种。
分散剂是带有颜料亲和基团的高分子量嵌段共聚物类溶液。
防水剂是有机硅交联剂。
增稠剂是聚氨酯缔合型增稠剂。
本实施了例中的水性蜡浆是高密度聚乙烯蜡，为两种聚乙烯蜡产品配合使用，一种为水性高滑透明蜡乳液，另一种为水性蜡浆。
实施例5：
本实施例一种绿色环保型水性木油，按一般制漆工艺的制作而成，其配方具体成分及按质量配比如下：
水性快干苯丙类乳液59％，水性碱溶性丙烯酸类乳液12％，第五成膜助剂2％，第六成膜助剂1％，PH值调节剂0.17％，消泡剂0.3％，润湿剂0.2％，流平剂0.2％，分散剂0.2％，防水剂0.2％，增稠剂1.9％，高滑蜡乳液2％，水性消光蜡浆3％,去离子水17.83％。
本实施例中的成膜助剂有两种：第五成膜助剂为二丙二醇甲醚，第六成膜助剂为Texanol(酯醇十二)。
PH值调节剂是多功能助剂AMP-95，主要成分是2-氨基-2-甲基-1-丙醇。
消泡剂是有机硅水性消泡剂，主要成分是聚硅氧烷和疏水性固体聚乙二醇的混合物。
润湿剂是有机硅表面活性剂，主要成分是聚醚硅氧烷共聚物。
流平剂是聚醚改性聚二甲基硅氧烷溶液、聚醚硅氧烷共聚物的一种或两种。
分散剂是带有颜料亲和基团的高分子量嵌段共聚物类溶液。
防水剂是有机硅交联剂。
增稠剂是聚氨酯缔合型增稠剂。
本实施例中的水性蜡浆是高密度聚乙烯蜡，为两种聚乙烯蜡产品配合使用，一种为水性高滑透明蜡乳液，另一种为水性蜡浆。
所述绿色环保型水性木油各项性能指标和环保指标如下：
表1快干苯丙乳液性能指标
| 固体含量 | 40％ |
| PH值 | 8.0-8.5 |
| 粘度(mpa.s/25℃) | 100 |
| MFFT最低成膜温度(℃) | 44 |
| 特性 | 不含烷基酚聚氧乙烯醚 |
表2水性碱溶性丙烯酸类乳液性能指标
| 固体含量 | 45％ |
| PH值 | 5.3 |
| 粘度(mpa.s/25℃) | 25 |
| MFFT最低成膜温度(℃) | 10 |
| 特性 | 不含烷基酚聚氧乙烯醚 |
表3绿色环保型水性木油性能及有害物限量指标
尽管上述实施例为本发明较佳的实施方式，但本发明的实施方式并不受上述实施例的约束，其他的任何未背离本发明的精神实质与原理下所作的改变、修饰、替代、组合、简化，均应为等效的置换方式，都包含在本发明的保护范围之内。
Claims (9)
1.一种绿色环保型水性木油，其特征在于，所述木油由水性苯丙乳液和水性丙烯酸乳液混拼为成膜物质，配合成膜助剂、PH值调节剂、消泡剂、润湿剂、流平剂、分散剂、防水剂、增稠剂及水性蜡浆制备而成；
各组分按重量计：水性苯丙乳液55～63%，水性丙烯酸类乳液10～15%，成膜助剂1.5～7%，PH值调节剂0.1～0.5%，消泡剂0.1～0.4%，润湿剂0.1～0.3%，流平剂0.05～0.3%，分散剂0.2～0.5%，防水剂0.1～0.25%，增稠剂0.5～1.8%，高滑蜡乳液0.5～2.5%，水性消光蜡浆1.5～5.5，去离子水11.75～20.9%。
2.根据权利要求1所述一种绿色环保型水性木油，其特征在于，所述成膜助剂为丙二醇甲醚、二丙二醇甲醚、丙二醇苯醚、丙二醇丁醚、二丙二醇丁醚、酯醇十二中的两种或多种。
3.根据权利要求1所述一种绿色环保型水性木油，其特征在于，所述PH值调节剂为N,N二甲基乙醇胺、AMP-95中的一种或两种。
4.根据权利要求1所述一种绿色环保型水性木油，其特征在于，所述消泡剂为有机硅水性消泡剂，成分是聚硅氧烷和疏水性固体聚乙二醇的混合物。
5.根据权利要求1所述一种绿色环保型水性木油，其特征在于，所述润湿剂为有机硅表面活性剂，成分是聚醚硅氧烷共聚物。
6.根据权利要求1所述一种绿色环保型水性木油，其特征在于，所述流平剂为有机硅类的表面助剂，成分是聚醚改性聚二甲基硅氧烷溶液、聚醚硅氧烷共聚物的一种或两种。
7.根据权利要求1所述一种绿色环保型水性木油，其特征在于，所述分散剂为带有颜料亲和基团的高分子量嵌段共聚物类润湿分散剂。
8.根据权利要求1所述的一种绿色环保型水性木油，其特征在于，所述防水剂为有机硅防水剂。
9.根据权利要求1所述的一种绿色环保型水性木油，其特征在于，所述增稠剂为聚氨酯缔合型增稠剂。