CN109516816A - A kind of shell active carbon removes ceramic material of scale and preparation method thereof - Google Patents
A kind of shell active carbon removes ceramic material of scale and preparation method thereof Download PDFInfo
- Publication number
- CN109516816A CN109516816A CN201811566195.0A CN201811566195A CN109516816A CN 109516816 A CN109516816 A CN 109516816A CN 201811566195 A CN201811566195 A CN 201811566195A CN 109516816 A CN109516816 A CN 109516816A
- Authority
- CN
- China
- Prior art keywords
- parts
- active carbon
- conch meal
- shell
- ceramic material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the ceramic materials that a kind of shell active carbon removes scale, its raw material poidometer by weight is as follows: 10-15 parts of conch meal, 7-12 parts of rock phosphate in powder, 10-15 parts of zeolite, 20-25 parts of clay, 8-12 parts of silicon ore, 6-15 parts of stone needle, 10-15 parts of active carbon, 9-12 parts of selenium mine soil, 8-15 parts of diatomite.Conch meal and active carbon is added in the present invention, ceramic liner is added as raw material using the conch meal and active carbon of crushing, so that the conch meal in conch meal be enable to play the role of absorption; and there is no saturability; service life using for a long time, can adsorb hazardous substance for a long time, protect family health；The rock phosphate in powder and silicon ore of addition, it can stablize various carbonate in water, and calcium carbonate not soluble in water can be made to be converted into the calcium monohydrogen phosphate for being dissolved in water, it is made to keep stablizing in a heated state, therefore achieve the purpose that control fouling.The liner of such ceramic material has health care, sterilizes, and absorption purifies water, the effect of scale-deposit-preventing.
Description
Technical field
The present invention relates to technical field of ceramic material more particularly to a kind of shell active carbon go scale ceramic material and its
Preparation method.
Background technique
Common ceramic material has clay, aluminium oxide, kaolin etc..The general hardness of ceramic material is higher, but plasticity compared with
Difference.Ceramic material is used in feeder, on decoration more.
It is poor to the adsorptivity of impurity in water using liner made of existing ceramic material, it cannot be adsorbed with for a long time
Evil substance, and liner is easy to fouling in a heated state, long-time service is not conducive to good health.
Summary of the invention
The purpose of the present invention is to solve disadvantages existing in the prior art, and a kind of shell active carbon proposed removes water
The ceramic material and preparation method thereof of dirt.
To achieve the goals above, present invention employs following technical solutions:
A kind of shell active carbon removes the ceramic material of scale, and raw material poidometer by weight is as follows: 10-15 parts of conch meal, phosphorus
7-12 parts of ore, 10-15 parts of zeolite, 20-25 parts of clay, 8-12 parts of silicon ore, 6-15 parts of stone needle, 10-15 parts of active carbon, selenium mine
It is 9-12 parts native, 8-15 parts of diatomite.
Preferably, the conch meal impregnates in the hydrochloric acid solution of 0.1-0.3% the preparation method is as follows: cleaning shell
30-40min is calcined 1-2 hours at 900-1000 DEG C after taking-up drains, is washed with deionized water, dries, using planetary ball
Grinding machine is ground, and be finally sieved to obtain conch meal.
Preferably, the conch meal is any one in pearl shell, abalone shells or oyster shell, the conch meal.
Preferably, the sieve mesh number used is sieved as 120-200.
A kind of shell active carbon goes the preparation method of the ceramic material of scale, includes the following steps:
S1: respectively by rock phosphate in powder, zeolite, silicon ore, stone needle crushed, is sieved, is then placed in ball mill, is milled to partial size
It is 50-100 μm, obtains mixture A；
S2: to clay, selenium mine soil and diatomite are dried, and are crushed, and obtain mixture B after being then sieved；
It after S3: mixture A and mixture B mixing, then puts into conch meal and active carbon after mixing, is baked, bake temperature
Degree is 450-520 DEG C, and baking time is 4-5 hours, finally screens, obtains ceramic material.
Compared with prior art, the beneficial effects of the present invention are: a kind of shell active carbon provided by the invention removes scale
Ceramic material and preparation method thereof is added conch meal and active carbon, adds using the conch meal and active carbon of crushing as raw material
Enter ceramic liner, so that the conch meal in conch meal be enable to play the role of absorption, and there is no saturability, it is permanent that the service life uses, can
Absorption hazardous substance for a long time protects family health；
The rock phosphate in powder and silicon ore of addition, it can stablize various carbonate in water, and calcium carbonate not soluble in water can be made to be converted into
It is dissolved in the calcium monohydrogen phosphate of water, it is made to keep stablizing in a heated state, therefore achievees the purpose that control fouling, using shell activity
The liner water that charcoal ceramic liner purifies has good health value；
Selenium mine soil is added, supplements the selenium element of needed by human body, may participate in human metabolism, improve the immunity of the human body；
Be added stone needle, supplement human body necessary to calcium, magnesium, zinc, chromium, strontium, etc. more than 20 kinds of anti-aging elements；
The liner of such ceramic material has health care, sterilizes, and absorption purifies water, the effect of scale-deposit-preventing, and service life
Long, persistently protection is healthy.
Specific embodiment
In order to make the objectives, technical solutions, and advantages of the present invention clearer, below in conjunction with specific embodiment, to this
Invention is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, not
For limiting the present invention.
Embodiment 1
A kind of shell active carbon removes the ceramic material of scale, and raw material poidometer by weight is as follows: 10 parts of conch meal, rock phosphate in powder
7 parts, 10 parts of zeolite, 20 parts of clay, 8 parts of silicon ore, 6 parts of stone needle, 10 parts of active carbon, 9 parts, 8 parts of diatomite of soil of selenium mine.
Specifically, the conch meal impregnates in 0.1% hydrochloric acid solution the preparation method is as follows: cleaning shell
40min is calcined 1 hour at 1000 DEG C after taking-up drains, is washed with deionized water, dries, ground using planetary ball mill
It is milled broken, be finally sieved to obtain conch meal.
Specifically, the conch meal is any one in pearl shell, abalone shells or oyster shell, the conch meal.
Specifically, the sieve mesh number that uses of sieving is 200.
A kind of shell active carbon goes the preparation method of the ceramic material of scale, includes the following steps:
S1: respectively by rock phosphate in powder, zeolite, silicon ore, stone needle crushed, is sieved, is then placed in ball mill, is milled to partial size
It is 50 μm, obtains mixture A；
S2: to clay, selenium mine soil and diatomite are dried, and are crushed, and obtain mixture B after being then sieved；
It after S3: mixture A and mixture B mixing, then puts into conch meal and active carbon after mixing, is baked, bake temperature
Degree is 450 DEG C, and baking time is 5 hours, finally screens, obtains ceramic material.
Embodiment 2
A kind of shell active carbon removes the ceramic material of scale, and raw material poidometer by weight is as follows: 15 parts of conch meal, rock phosphate in powder
12 parts, 15 parts of zeolite, 25 parts of clay, 12 parts of silicon ore, 15 parts of stone needle, 15 parts of active carbon, 12 parts, 15 parts of diatomite of soil of selenium mine.
Specifically, the conch meal impregnates in 0.3% hydrochloric acid solution the preparation method is as follows: cleaning shell
30min is calcined 2 hours at 1000 DEG C after taking-up drains, is washed with deionized water, dries, ground using planetary ball mill
It is milled broken, be finally sieved to obtain conch meal.
Specifically, the conch meal is any one in pearl shell, abalone shells or oyster shell, the conch meal.
Specifically, the sieve mesh number that uses of sieving is 180.
A kind of shell active carbon goes the preparation method of the ceramic material of scale, includes the following steps:
S1: respectively by rock phosphate in powder, zeolite, silicon ore, stone needle crushed, is sieved, is then placed in ball mill, is milled to partial size
It is 100 μm, obtains mixture A；
S2: to clay, selenium mine soil and diatomite are dried, and are crushed, and obtain mixture B after being then sieved；
It after S3: mixture A and mixture B mixing, then puts into conch meal and active carbon after mixing, is baked, bake temperature
Degree is 520 DEG C, and baking time is 4 hours, finally screens, obtains ceramic material.
A kind of shell active carbon provided by the invention removes ceramic material of scale and preparation method thereof, and conch meal and work is added
Property charcoal, using crushing conch meal and active carbon as raw material be added ceramic liner, to enable the conch meal in conch meal
There is absorption, and there is no saturability, the service life using for a long time, can adsorb hazardous substance for a long time, protect family health；
The rock phosphate in powder and silicon ore of addition, it can stablize various carbonate in water, and calcium carbonate not soluble in water can be made to be converted into
It is dissolved in the calcium monohydrogen phosphate of water, it is made to keep stablizing in a heated state, therefore achievees the purpose that control fouling, using shell activity
The liner water that charcoal ceramic liner purifies has good health value；
Selenium mine soil is added, supplements the selenium element of needed by human body, may participate in human metabolism, improve the immunity of the human body；
Be added stone needle, supplement human body necessary to calcium, magnesium, zinc, chromium, strontium, etc. more than 20 kinds of anti-aging elements；
The liner of such ceramic material has health care, sterilizes, and absorption purifies water, the effect of scale-deposit-preventing, and service life
Long, persistently protection is healthy.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (5)
1. the ceramic material that a kind of shell active carbon removes scale, it is characterised in that: its raw material poidometer by weight is as follows: shell
10-15 parts of powder, 7-12 parts of rock phosphate in powder, 10-15 parts of zeolite, 20-25 parts of clay, 8-12 parts of silicon ore, 6-15 parts of stone needle, active carbon
10-15 parts, 9-12 parts of selenium mine soil, 8-15 parts of diatomite.
2. the ceramic material that a kind of shell active carbon according to claim 1 removes scale, it is characterised in that: the conch meal
30-40min is impregnated in the hydrochloric acid solution of 0.1-0.3% the preparation method is as follows: cleaning shell, taking-up drain after, 900-
It is calcined 1-2 hours at 1000 DEG C, is washed with deionized water, dries, ground using planetary ball mill, is finally sieved
Obtain conch meal.
3. the ceramic material that a kind of shell active carbon according to claim 1 removes scale, it is characterised in that: the conch meal
For any one in pearl shell, abalone shells or oyster shell, the conch meal.
4. the ceramic material that a kind of shell active carbon according to claim 2 removes scale, it is characterised in that: use of being sieved
Sieve mesh number is 120-200.
5. the preparation method that a kind of shell active carbon described in claim 1 removes the ceramic material of scale, it is characterised in that: including
Following steps:
S1: respectively by rock phosphate in powder, zeolite, silicon ore, stone needle crushed, is sieved, is then placed in ball mill, is milled to partial size
It is 50-100 μm, obtains mixture A；
S2: to clay, selenium mine soil and diatomite are dried, and are crushed, and obtain mixture B after being then sieved；
It after S3: mixture A and mixture B mixing, then puts into conch meal and active carbon after mixing, is baked, bake temperature
Degree is 450-520 DEG C, and baking time is 4-5 hours, finally screens, obtains ceramic material.