CN109401449A - 一种壳聚糖可降解生物种子包衣剂及其制备方法 - Google Patents
一种壳聚糖可降解生物种子包衣剂及其制备方法 Download PDFInfo
- Publication number
- CN109401449A CN109401449A CN201811262402.3A CN201811262402A CN109401449A CN 109401449 A CN109401449 A CN 109401449A CN 201811262402 A CN201811262402 A CN 201811262402A CN 109401449 A CN109401449 A CN 109401449A
- Authority
- CN
- China
- Prior art keywords
- reactor tank
- coating agent
- seed
- parts
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种壳聚糖可降解生物种子包衣剂及其制备方法，该方法包括向反应罐中加入90～120重量份的纯化水以及2～4重量份的冰醋酸溶液，所述反应罐为具有加热装置以及搅拌装置的反应罐；启动所述加热装置以及搅拌装置将所述反应罐升温到40～60℃后，向所述应罐中投放2～5重量份的壳聚糖。该包衣剂采用天然无污染的壳聚糖作为成膜主体，配合聚乙烯吡咯烷酮等物质，使得其具有良好的成膜性，形成的保护膜可以作为营养元素、杀菌物质以及杀虫物质的载体使用，可以均匀包裹于种子外部形成种子包衣，有效提高作物的抗病性能，促进种子发芽生长。该包衣剂随着种子发芽生长会自然降解，同时降解后还可以作为肥料被植物吸收。
Description
技术领域
本发明涉及种子包衣剂技术领域，特别是涉及一种壳聚糖可降解生物种子包衣剂及其制备方法。
背景技术
种子包衣是20世纪80年代中期研究开发的一项促进农业增产丰收的高新技术，用种衣剂包过的种子播种后，能迅速吸水膨胀。随着种子内胚胎的逐渐发育以及幼苗的不断生长，种衣剂将含有的各种有效成分缓慢地释放，被种子幼苗逐步吸收到体内，从而达到防治苗期病虫害、促进生长发育、提高作物产量的目的。
现在技术中用于种子包衣的包衣剂大多是采用化学原料制作而成，可能会对土壤等造成污染。另外由于现有技术中的包衣剂大多是粉剂，进行包衣处理后包衣剂容易脱落，同时由于包衣剂大多具有毒性，脱落的包衣剂会对生物产生一定的危害。
发明内容
本发明提供了一种壳聚糖可降解生物种子包衣剂及其制备方法。
本发明提供了如下方案：
一种壳聚糖可降解生物种子包衣剂的制备方法，包括：
向反应罐中加入90～120重量份的纯化水以及2～4重量份的冰醋酸溶液，所述反应罐为具有加热装置以及搅拌装置的反应罐；
启动所述加热装置以及搅拌装置将所述反应罐升温到40～60℃后，向所述应罐中投放2～5重量份的壳聚糖；
在恒温40～60℃下搅拌1～2小时后，向所述反应罐内注入2～5重量份的乙醇继续搅拌；
在恒温40～60℃下搅拌3～20分钟后，向所述反应罐内注入2～7重量份的聚乙烯吡咯烷酮继续搅拌，搅拌1～2分钟后关闭所述反应罐的加热装置以及搅拌装置并静置；
静置0.5～10小时后将所述反应罐内的物质移入过滤装置内，经过滤即得所述可降解生物种子包衣剂。
优选的：以1.5～3℃每秒的升温速度将所述反应罐升温到40～60℃。
优选的：启动所述反应罐的搅拌装置以1400转/分钟转速搅拌15分钟后，向所述反应罐内注入2～7重量份的聚乙烯吡咯烷酮继续搅拌；搅拌1～2分钟后关闭所述反应罐的加热装置及搅拌装置并静置。
优选的：启动所述反应罐的搅拌装置以1400转/分钟转速搅拌15分钟后，向所述反应罐内注入2～5重量份的聚乙烯吡咯烷酮、3～6重量份的助剂继续搅拌；搅拌1～2分钟后关闭所述反应罐的加热装置及搅拌装置并静置。
优选的：所述助剂包括活性成分为3～3.5份，分散剂为2～4份，消泡剂为0.5～1份，润湿剂为2～3份，微量元素为0.02～0.42份，染料为0.5～2份，增稠剂为0.25～1份，抗冻剂为0.5～1份，填料为1～2份、杀虫活性组分。
优选的：所述壳聚糖的分子式为(C6H11NO4)N，分子量为161.2，有效物质含量不小于99％。
一种采用所述的壳聚糖可降解生物种子包衣剂的制备方法制备而成的壳聚糖可降解生物种子包衣剂。
根据本发明提供的具体实施例，本发明公开了以下技术效果：
通过本发明，可以实现一种壳聚糖可降解生物种子包衣剂及其制备方法，在一种实现方式下，该方法可以包括向反应罐中加入90～120重量份的纯化水以及2～4重量份的冰醋酸溶液，所述反应罐为具有加热装置以及搅拌装置的反应罐；启动所述加热装置以及搅拌装置将所述反应罐升温到40～60℃后，向所述应罐中投放2～5重量份的壳聚糖；在恒温40～60℃下搅拌1～2小时后，向所述反应罐内注入2～5重量份的乙醇继续搅拌；在恒温40～60℃下搅拌3～20分钟后，向所述反应罐内注入2～7重量份的聚乙烯吡咯烷酮继续搅拌，搅拌1～2分钟后关闭所述反应罐的加热装置以及搅拌装置并静置；静置0.5～10小时后将所述反应罐内的物质移入过滤装置内，经过滤即得所述可降解生物种子包衣剂。该包衣剂在使用时，将适量的包衣剂喷洒于待包衣种子上，自然风干即可。该包衣剂采用天然无污染的壳聚糖作为成膜主体，配合聚乙烯吡咯烷酮等物质，使得其具有良好的成膜性，形成的保护膜可以作为营养元素、杀菌物质以及杀虫物质的载体使用，可以均匀包裹于种子外部形成种子包衣，有效提高作物的抗病性能，促进种子发芽生长。该包衣剂随着种子发芽生长会自然降解，同时降解后还可以作为肥料被植物吸收。
当然，实施本发明的任一产品并不一定需要同时达到以上所述的所有优点。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员所获得的所有其他实施例，都属于本发明保护的范围。
实施例
本发明实施例提供了一种壳聚糖可降解生物种子包衣剂的制备方法，该方法包括向反应罐中加入90～120重量份的纯化水以及2～4重量份的冰醋酸溶液，所述反应罐为具有加热装置以及搅拌装置的反应罐；本申请提供的纯化水为H2O 18.02，为饮用水经蒸馏法、离子交换法、反渗透法或其他适宜的方法制得的供药用的水，不含任何添加剂。
启动所述加热装置以及搅拌装置将所述反应罐升温到40～60℃后，向所述应罐中投放2～5重量份的壳聚糖；具体的，以1.5～3℃每秒的升温速度将所述反应罐升温到40～60℃。
在恒温40～60℃下搅拌1～2小时后，向所述反应罐内注入2～5重量份的乙醇继续搅拌；
在恒温40～60℃下搅拌3～20分钟后，向所述反应罐内注入2～7重量份的聚乙烯吡咯烷酮继续搅拌，搅拌1～2分钟后关闭所述反应罐的加热装置以及搅拌装置并静置；具体的，启动所述反应罐的搅拌装置以1400转/分钟转速搅拌15分钟后，向所述反应罐内注入2～7重量份的聚乙烯吡咯烷酮继续搅拌；搅拌1～2分钟后关闭所述反应罐的加热装置及搅拌装置并静置。本申请提供的聚乙烯吡咯烷酮，是一种非离子型高分子化合物，是N-乙烯基酰胺类聚合物中最具特色，且被研究得最深、广泛的精细化学品品种。已发展成为非离子、阳离子、阴离子3大类，工业级、医药级、食品级3种规格，相对分子质量从数千至一百万以上的均聚物、共聚物和交联聚合物系列产品，并以其优异独特的性能获得广泛应用。该聚乙烯吡咯烷酮与壳聚糖配合使用时，可以保证制作而成的种子包衣剂的成膜性更好。
该种子包衣剂本身无需添加任何元素既可以为种子提高一定的应用成分，当然可以想到是，为了满足某些植物对营养元素特殊的要求，在实际生产中，还可以根据需要在制备过程中加入相应的助剂原料。进一步的，启动所述反应罐的搅拌装置以1400转/分钟转速搅拌15分钟后，向所述反应罐内注入2～5重量份的聚乙烯吡咯烷酮、3～6重量份的助剂继续搅拌；搅拌1～2分钟后关闭所述反应罐的加热装置及搅拌装置并静置。所述助剂包括活性成分为3～3.5份，分散剂为2～4份，消泡剂为0.5～1份，润湿剂为2～3份，微量元素为0.02～0.42份，染料为0.5～2份，增稠剂为0.25～1份，抗冻剂为0.5～1份，填料为1～2份、杀虫活性组分。
静置0.5～10小时后将所述反应罐内的物质移入过滤装置内，经过滤即得所述可降解生物种子包衣剂。
所述壳聚糖的分子式为(C6H11NO4)N，分子量为161.2，有效物质含量不小于99％。本申请提供的壳聚糖采用海洋生物虾蟹壳提取物，属纯生物源--甲壳素原料。本产品是以虾、蟹壳为主要原料。经生物化工技术提取的高分子多糖液态地膜。采用生物工艺，是一款生物产品。壳聚糖具有良好的成膜性、透气性、生物兼容性。它在皮肤表面形成薄膜，由于该膜是立体网状结构，各种保湿因子、生理功能物质均能包埋其中，并有持续缓释作用。壳聚糖的成膜原理通过壳聚糖羟基，壳聚糖溶液具有粘稠性，易于成膜的特性。利用壳聚糖易于成膜的特性，可制作成能被生物或酶降解的液态地膜具有培植植物或微生物的保水剂。壳聚糖对植物适应性广，亲和性好，无毒无副作用，对人畜无害，能够生物降解，在土壤中不板结土壤，可缓慢降解为小分子碳水化合物，对环境无公害，是一种优良的纯天然生态制剂。它能促使植物种子提前发芽。根系发达，根毛、须根、次生根数量大大增加。根乃植物之本，根际发达，会增强植物的吸肥吸水能力，增强抗旱、抗倒伏能力，增强免疫力，达到粗壮多结果之目的。壳聚糖能充分活化根际状态，溶解养分分子，迅速形成土壤溶液，使氮、磷、钾等养分能得到植物充分有效地吸收。使用壳聚糖作添加剂，可使土壤有益菌如放线菌增加1000倍、有害菌如镰刀菌及线虫类等显著减少，增强土壤供肥能力，从根本上改良土壤，根治板结，提高土壤有机质含量，便于连作。壳聚糖能提高作物产量，改善作物品质，并使其恢复自然风味，耐贮、耐运，同时减少农药残留量(国际标准以下)，可以通过绿色通道出口。壳聚糖替代种衣剂，可保护种子正常发育。用于种子贮存，可减少种子处理程序，经济实惠。研究表明，壳聚糖及其降解产物对土壤、种子有极强的杀菌作用，能强烈抑制有害真菌菌丝如霜霉菌、胞囊菌等。壳聚糖具有溶液粘稠、易于成膜的特性。其极强的成膜功能，能延缓肥料元素的释放，减少养分的损失而大大提高肥效，这样能从根本上解决肥料的浪费，节约资金，保护环境，有益于人类健康，壳聚糖与纤维素共混制成膜，可大大增加膜的机械强度，利用壳聚糖易于成膜的特性，可用其作种子包衣材料。壳聚糖在韩国、日本被誉为“植物疫苗”，可见其对作物所起的作用。壳聚糖制剂能使植物抗菌抗病毒能力增强，改变植物生长机理，增强调节系统的免疫功能，从而保证植物的正常生长发育。用壳聚糖拌种，可降低大豆根腐病的发病率和病情指数，防效达42.6％～46.9％，同时可促进大豆根系生长，单株果数、粒数、粒重增加，增产11.7％以上。
本申请实施例还可以提供一种采用所述的壳聚糖可降解生物种子包衣剂的制备方法制备而成的壳聚糖可降解生物种子包衣剂。
该包衣剂在使用时，将适量的包衣剂喷洒于待包衣种子上，自然风干即可。该包衣剂采用天然无污染的壳聚糖作为成膜主体，配合聚乙烯吡咯烷酮等物质，使得其具有良好的成膜性，形成的保护膜可以作为营养元素、杀菌物质以及杀虫物质的载体使用，可以均匀包裹于种子外部形成种子包衣，有效提高作物的抗病性能，促进种子发芽生长。该包衣剂随着种子发芽生长会自然降解，同时降解后还可以作为肥料被植物吸收。
需要说明的是，在本文中，诸如第一和第二等之类的关系术语仅仅用来将一个实体或者操作与另一个实体或操作区分开来，而不一定要求或者暗示这些实体或操作之间存在任何这种实际的关系或者顺序。而且，术语“包括”、“包含”或者其任何其他变体意在涵盖非排他性的包含，从而使得包括一系列要素的过程、方法、物品或者设备不仅包括那些要素，而且还包括没有明确列出的其他要素，或者是还包括为这种过程、方法、物品或者设备所固有的要素。在没有更多限制的情况下，由语句“包括一个……”限定的要素，并不排除在包括所述要素的过程、方法、物品或者设备中还存在另外的相同要素。
以上所述仅为本发明的较佳实施例而已，并非用于限定本发明的保护范围。凡在本发明的精神和原则之内所作的任何修改、等同替换、改进等，均包含在本发明的保护范围内。
Claims (7)
1.一种壳聚糖可降解生物种子包衣剂的制备方法，其特征在于，所述方法包括：
向反应罐中加入90～120重量份的纯化水以及2～4重量份的冰醋酸溶液，所述反应罐为具有加热装置以及搅拌装置的反应罐；
启动所述加热装置以及搅拌装置将所述反应罐升温到40～60℃后，向所述应罐中投放2～5重量份的壳聚糖；
在恒温40～60℃下搅拌1～2小时后，向所述反应罐内注入2～5重量份的乙醇继续搅拌；
在恒温40～60℃下搅拌3～20分钟后，向所述反应罐内注入2～7重量份的聚乙烯吡咯烷酮继续搅拌，搅拌1～2分钟后关闭所述反应罐的加热装置以及搅拌装置并静置；
静置0.5～10小时后将所述反应罐内的物质移入过滤装置内，经过滤即得所述可降解生物种子包衣剂。
2.根据权利要求1所述的壳聚糖可降解生物种子包衣剂的制备方法，其特征在于，以1.5～3℃每秒的升温速度将所述反应罐升温到40～60℃。
3.根据权利要求1所述的壳聚糖可降解生物种子包衣剂的制备方法，其特征在于，启动所述反应罐的搅拌装置以1400转/分钟转速搅拌15分钟后，向所述反应罐内注入2～7重量份的聚乙烯吡咯烷酮继续搅拌；搅拌1～2分钟后关闭所述反应罐的加热装置及搅拌装置并静置。
4.根据权利要求3所述的壳聚糖可降解生物种子包衣剂的制备方法，其特征在于，启动所述反应罐的搅拌装置以1400转/分钟转速搅拌15分钟后，向所述反应罐内注入2～5重量份的聚乙烯吡咯烷酮、3～6重量份的助剂继续搅拌；搅拌1～2分钟后关闭所述反应罐的加热装置及搅拌装置并静置。
5.根据权利要求4所述的壳聚糖可降解生物种子包衣剂的制备方法，其特征在于，所述助剂包括活性成分为3～3.5份，分散剂为2～4份，消泡剂为0.5～1份，润湿剂为2～3份，微量元素为0.02～0.42份，染料为0.5～2份，增稠剂为0.25～1份，抗冻剂为0.5～1份，填料为1～2份、杀虫活性组分。
6.根据权利要求1所述的壳聚糖可降解生物种子包衣剂的制备方法，其特征在于，所述壳聚糖的分子式为(C6H11NO4)N，分子量为161.2，有效物质含量不小于99％。
7.一种采用权利要求1至6任意一项所述的壳聚糖可降解生物种子包衣剂的制备方法制备而成的壳聚糖可降解生物种子包衣剂。