CN109020192A - 一种具有高应变点、可快速离子交换和耐弱酸性的锌磷铝硅酸盐玻璃 - Google Patents
一种具有高应变点、可快速离子交换和耐弱酸性的锌磷铝硅酸盐玻璃 Download PDFInfo
- Publication number
- CN109020192A CN109020192A CN201811211310.2A CN201811211310A CN109020192A CN 109020192 A CN109020192 A CN 109020192A CN 201811211310 A CN201811211310 A CN 201811211310A CN 109020192 A CN109020192 A CN 109020192A
- Authority
- CN
- China
- Prior art keywords
- glass
- ion exchange
- weak acid
- point
- acid resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种具有高应变点、可快速离子交换和耐弱酸性的锌磷铝硅酸盐玻璃，以质量分数计，所述玻璃包含的组分为：SiO2 56～65%，Al2O3 17～22%，Na2O 10～16%，K2O 0～1%，Li2O 0～1%，P2O5 0～5%，B2O3 0～2%，MgO 0～0.5%，ZnO 1~8%，TiO2 0～1%，SrO 0～0.5%，SnO2 0～0.5%，CeO2 0～0.5%，各组分之和为100%；所述玻璃的应变点温度≥580℃,压缩应力值≥900MPa，压缩应力层≥35μm。本发明通过优化玻璃组成，获得具有高压缩应力值和高压缩应力层，并且可耐弱酸性的玻璃。
Description
技术领域
本发明涉及玻璃材料技术领域，具体涉及一种具有高应变点、可快速离子交换和耐弱酸性的锌磷铝硅酸盐玻璃。
背景技术
随着触摸屏和显示器市场的发展和需求，带动了触摸屏和显示器盖板玻璃迅速发展和需求。伴随人们对智能手机等移动终端装置外观以及性能的追求，盖板玻璃从传统的2D外形，逐步向2.5D、3D外形过渡。这也对作为保护屏幕用的盖板玻璃性能提出了更为苛刻的要求。但是，普通的硅酸盐玻璃强度还是不能满足日常使用需求，如手机的多次跌落以及与尖锐物体的碰撞等，都会造成屏幕的破损。要求盖板玻璃需要具有高的抗断裂、抗弯曲以及抗摔落性能，对于厚度小于1mm的盖板玻璃，一般需要通过化学钢化处理使玻璃具有表面压应力（Compressive Stress,简称CS）和一定深度的离子交换层（Depth of Layer,简称DOL），同时具有较高的CS和DOL玻璃可以有效的抑制玻璃表面缺陷扩展，从而提高玻璃表面硬度、抗刮伤性以及抗摔落性能。
当玻璃进行离子交换时，玻璃的离子交换效果取决于离子交换的温度和时间，温度越高，离子交换的速度越快，压应力层越深，但表面压缩应力值越小，主要是离子交换过程中，玻璃存在应力松弛现象。一般可通过降低离子交换的温度减轻玻璃的应力松弛，从而维持较高的表面压缩应力值，但同时离子交换的效率降低，导致压缩应力层过低，因此，很难同时达到高表面压缩应力值和高压缩应力层。
此外，随着2.5D、3D等曲面造型的触控显示屏渐成为主流产品，玻璃被要求加工成具有2.5D 、3D曲面造型的产品。当玻璃从2D被加工成2.5D和3D时，需要对玻璃表面进行造型加工，例如采用CNC制程加工2.5D玻璃以及采用热弯成型制程加工3D玻璃，玻璃表面不可避免的在加工制程中受到损伤，且玻璃表面残留许多脏污，例如氧化铈等抛光粉。为除去玻璃表面的脏污，一般采用弱酸性清洗剂对玻璃进行清洗，例如采用PH≈2的草酸溶液，因此，要求玻璃表面具有一定耐弱酸性能，避免玻璃表面不被弱酸破坏而产生可见划伤，从而降低玻璃的透过率影响良率。尤其当玻璃中引入一定量的P2O5组分后，玻璃的化学稳定性降低，从而使玻璃的耐弱酸性能降低；目前未见过能解决上述问题的报道。
发明内容
本发明的目的在于提供一种具有高应变点、可快速离子交换和耐弱酸性的锌磷铝硅酸盐玻璃，该玻璃同时具有高表面压缩应力、高压缩应力层和耐弱酸性。
为实现上述目的，本发明采用如下技术方案：
一种具有高应变点、可快速离子交换和耐弱酸性的锌磷铝硅酸盐玻璃，以质量分数计，所述玻璃包含的组分为SiO2 56～65 %，Al2O3 17～22%，Na2O 10～16 %，K2O 0～1%， Li2O 0～1%， P2O5 0～5%， B2O3 0～2%，MgO 0～0.5%，ZnO 1~8%，TiO2 0～1%，SrO 0～0.5%，SnO2 0～0.5%，CeO2 0～0.5%，各组分之和为100%。
所述玻璃的组分中，SiO2+Al2O3+P2O3≥78%，(MgO+ZnO+SrO+Al2O3)/( Li2O+Na2O+
K2O+B2O3) ≥1.3，玻璃的应变点温度≥580℃，压缩应力值≥900MPa，压缩应力层≥35μm。
优选地，所述玻璃的组分中，SiO2+Al2O3+P2O3≥80%，(Al2O3+P2O5)/ZnO＞3，(MgO+ZnO+SrO+Al2O3)/( Li2O+Na2O+K2O+B2O3) ≥1.5，玻璃的应变点温度≥600℃，压缩应力层≥40μm。
所述玻璃的组分中，（Li2O+Na2O+K2O + Al2O3）/SiO2＜0.60，玻璃具有耐弱酸性，且在60℃草酸溶液中浸泡6hrs后单位面积重量损失率≤0.15mg/cm3。
以下对各成分的含量进行数值限定的理由加以说明：
SiO2：SiO2为主要玻璃成形体，属必需成分之一，主要构成了玻璃网状主结构，其赋予玻璃较佳的化学稳定性、机械性能和成型性能。玻璃中SiO2成分属于酸性物质侵蚀的主要组分，且其能提高玻璃的应变点温度，因此SiO2含量至少为56 %，优选地，至少为59 %，更优选地，至少为60 %；但高SiO2含量会使玻璃熔化温度提高，从而导致玻璃出现大量小气泡的缺陷，同时也会降低玻璃离子交换后的表面压缩应力和压缩应力层，因此SiO2含量至多为65%，优选地，至多为64 %，更优选地，至多为63 %。
Al2O3：Al2O3为玻璃的必需成分之一，属于网络中间体组成。在高碱浓度玻璃成分中，碱性离子对Al3+离子进行电荷平衡，使多数氧化铝倾向于成为玻璃铝氧四面体，构成了玻璃网状主结构，从而提高玻璃稳定性和机械性能。Al2O3在玻璃中形成的铝氧四面体在玻璃中体积比硅氧四面体体积要大，玻璃体积发生膨胀，从而降低玻璃的密度，为玻璃在离子交换过程提供交换通道，提高玻璃压缩应力层深，同时高Al2O3浓度玻璃具有高应变点温度，从而使得玻璃离子交换后玻璃维持较高的压缩成应力，玻璃中Al2O3含量至少为17 %，优选地，至少为18 %；但Al2O3属于极难熔氧化物，其能快速提高玻璃高温粘度，致使玻璃澄清均化难度加大，玻璃中的气泡缺陷浓度大量增加，因此在玻璃中Al2O3含量至多为22 %，优选地，至多为21 %。
Na2O：Na2O为玻璃的必需成分之一，玻璃中高浓度的Na2O，使得玻璃中含有足够多的Na+，与硝酸钾熔盐中K+离子进行交换，从而在玻璃表面产生高压缩应力。此外，Na2O可提供大量游离氧来源，对玻璃硅氧网络结构体起破坏作用，大大降低玻璃的粘度，有助于玻璃熔化与澄清，因此，本发明中Na2O含量不低于10 %，优选地，不低于11%，更优选地，不低于12%。但Na2O浓度过高，将使得玻璃机械性能和化学稳定性能劣化，尤其在高氧化铝浓度和含磷成分的硅酸玻璃中，Na2O更容易倾向与水中的氢离子交换而溶入水中，加速玻璃表面化学性能变化，因此玻璃中Na2O含量至多为16 %，优选地，至多为16 %。
Li2O：玻璃组分至多包含1 %Li2O，其属于非必要成分。玻璃中一定Li2O浓度有助于降低玻璃的熔化粘度，从而改善熔化效果，但高Li2O倾向于阻碍Na+和K+交换，优选地，玻璃中不含Li2O。
K2O：玻璃中K2O属于非必要成分，K2O可以改善玻璃熔化与澄清效果；当玻璃中维持较高K2O浓度有助于获得高压缩应力层，但这种压缩应力层未必是熔盐中钾离子与钠离子发生离子交换而形成；同时高K2O浓度对玻璃离子交换产生的表面压应力降低更为明显；此外，玻璃中高K2O浓度化学稳定性劣化，使玻璃抗酸性变差。因此，本发明的玻璃中K2O含量至多为1%，优选为0，其主要通过原料杂质引入。
B2O3：玻璃中B2O3成分属于网络形成体氧化物，可明显降低高温玻璃粘度；高浓度B2O3在高温熔制过程中存在氧化物挥发现象，不利于玻璃成分稳定，且B2O3能降低玻璃应变点温度，且其倾向于在玻璃表面上，玻璃表面抗耐性能劣化。离子交换的实验表明，高 B2O3浓度不利于玻璃获得高压缩应力和高应力层深度，因此B2O3含量小于2 %，优选为0。
P2O5：玻璃中P2O5属于玻璃形成体成分，其以[PO4]四面体相互连成网络，但P2O5形成的网络结构属于层状，且层间由范德华力相互连接，使玻璃网络结构呈疏松状态，网络空隙变大，有利于玻璃中Na离子和熔盐中K离子进行相互扩散，玻璃强化工艺过程中离子交换起促进作用，对快速获得较高压缩应力层起重要作用。但玻璃中P2O5具有粘度小，化学稳定性差和热膨胀系数大作用，因此低浓度P2O5能提供玻璃具有较好化学稳定性，高浓度的P2O5使玻璃表面的抗酸性劣化。因此P2O5含量至多为5%，优选1～4 %。
ZnO：玻璃中ZnO属于二价金属氧化物，其为玻璃网络外体成分，对玻璃网络结构起破坏作用，降低玻璃熔化温度，是良好的助熔剂，有利于澄清。在高碱金属氧化物硅酸盐玻璃中，Zn2+存在六配位[ZnO6]和四配位[ZnO4]状态，其中六配位[ZnO6]结构较为致密，而四配位[ZnO4]结构较为疏松，四配位数量随碱金属氧化物增加而增加。当四配位[ZnO4]含量较多时，玻璃网络更为疏松，有利于玻璃中离子（Na+）迁移，从而提高玻璃离子交换层深度，相比同族的CaO、MgO和SrO对离子交换的阻碍作用，ZnO含量对提高玻璃离子交换效率、交换深度和提高玻璃表面强度具有积极作用，但过高浓度的ZnO倾向于形成锌尖晶石（ZnAl2O4）或硅酸锌（Zn2SiO4），从而提高玻璃的失透温度。因此ZnO含量控制在1～8 %。优先为2～6 %。
MgO：玻璃中MgO属于二价金属氧化物，其为玻璃网络外体成分，对玻璃网络结构起破坏作用，降低玻璃熔化温度，有利于澄清。但高MgO浓度对玻璃强度提高作用有限；并且在玻璃的抗酸性能方面，MgO效果比ZnO效果差，因此，MgO含量至多为1%。
SrO：玻璃中SrO属于二价金属氧化物，其为玻璃网络外体成分，对玻璃网络结构起破坏作用，降低玻璃熔化温度，有利于澄清。但高SrO浓度提高玻璃密度，且原料成本昂贵。因此SrO含量至多为0.5 %。
除上述的氧化物之外，本发明的玻璃中含有化学澄清剂。其中SnO2为主要高温澄清剂，且环保无毒，但高浓度的SnO2易于产生过量氧，造成过多气泡残留在玻璃中，其含量至多为0.5 %。其中CeO2为氧化澄清剂，也可为脱色剂，提高玻璃透过率，但浓度过高，易导致玻璃着色，从而降低透过率，因此，其含量至多为0.5 %。
本发明的锌磷铝硅酸盐玻璃玻璃具有高表面压缩应力，是通过提高玻璃的应变点温度，降低离子交换过程中的应力松弛现象获得的。玻璃中凡是对玻璃网络结果起破坏作用的氧化物，例如Na2O、K2O和Li2O，其对降低玻璃应变点温度的作用最明显；而玻璃中有利于形成网络结构的组分，例如Al2O3、SiO2和P2O5对提高应变温度起作用最明显，因此本发明中玻璃具有高浓度的SiO2、Al2O3和P2O5含量，SiO2+Al2O3+P2O5≥76wt%并限制(MgO+ZnO+SrO+Al2O3)/( Li2O+Na2O
+K2O+B2O3)≥1.3。优选地，SiO2+Al2O3+P2O5≥80wt%；优选地，(MgO+ZnO+SrO
+Al2O3)/( Li2O+Na2O+K2O+B2O3)≥1.5；从而改善玻璃的离子交换效率，缩短玻璃强化时间，改善玻璃的表面压缩应力值和压缩应力层。
本发明中的玻璃具有良好的耐弱酸的能力，本发明通过三方面改善玻璃的耐弱酸性能，一方面提高玻璃中SiO2组成含量，该组成对改善玻璃耐弱酸效果尤为明显，要求玻璃中SiO2浓度不低于56wt%；一方面对玻璃中Li2O、Na2O、K2O和Al2O3导致玻璃表面的耐弱酸能力降低成分进行限制，限制条件为（Li2O+Na2O+K2O + Al2O3）/SiO2＜0.60；另一方面，引入高ZnO浓度，降低MgO浓度来改善玻璃耐弱酸的能力。
本发明的显著优点在于：本发明一方面通过合理的成分配比提高玻璃的应变点温度和改善玻璃的离子交换效率，获得具有高表面压缩应力值和压缩应力层强化玻璃；另一方面，本发明提高玻璃中SiO2组成含量，并对玻璃中Li2O、Na2O、K2O和Al2O3导致玻璃表面的耐弱酸能力降低成分进行限制和在高铝玻璃成分中引入ZnO浓度，降低MgO浓度，从而改善改善玻璃耐弱酸的能力。
具体实施方式
以下结合具体实施例对本发明做进一步说明，但本发明不仅仅限于这些实施例。
实施例1-12和对比例1-2：
1、测试样品制备
实施案1-12及对比例1-2的样品制备：依据石英砂、氧化铝、碳酸钠等原料纯度与水分含量进行称量，进行均匀混合获得均匀的配料；然后将配合料从塑料瓶中转移至约800ml铂坩埚中，将铂坩埚置入硅钼棒高温炉炉内，逐渐升温至1650℃，持温4～8小时，通过搅拌加速玻璃气泡排出和使玻璃均化消除。在熔融后，将熔融液倒入至耐热不锈钢模具进行成型，然后取出玻璃块并移入箱式退火炉内进行630℃约2小时的热处理，随后以小于1℃/分的速率降至570℃，之后自然冷却至室温。将玻璃块进行切割研磨制备成符合相关测试样品。为取得更加稳定的测量结果，应选择化学级的配合原料。
实施案1-12及对比例1-2的样品包含的成分如表一所示：
注释：表中RO为MgO、ZnO和SrO质量分数之和，R2O为Li2O、Na2O和K2O质量份数之和。
2、物理性质符号及测量方法定义
实施例1-12及对比例1-2玻璃的物理性质如表二所示，其定义及解释如下所示：
（1）Tsoftening：玻璃粘度为107.6泊时的软化点温度，根据ASTM C-338《Standard TestMethod for Softening Point of Glass》标准方法测量；
（2）Tanneal: 玻璃粘度为1013泊时的退火点温度，根据ASTM C-336《Standard TestMethod for Annealing Point and Strain Point of Glass by Fiber Elongation》标准方法测量；
（3）Tstain: 玻璃粘度为1014.5泊时的应力点温度，根据ASTM C-336《Standard TestMethod for Annealing Point and Strain Point of Glass by Fiber Elongation》标准方法测量；
（4）CS：表面压缩应力Compressive Stress简称，即采用日本折原工业有限公司FSM-6000LE表面应力计进行测试。
（5）DOL：表面压缩应力层 Depth of Layer简称，采用日本折原工业有限公司FSM-6000LE表面应力计进行测试。
（6）单位面积重量损失率：将玻璃切割成规则形状的玻璃片，镶样进行粗磨，最后采用2000目砂纸对玻璃样品上下表面进行精磨。干燥后将样品浸没在PH≈2的草酸溶液中，温度设定为60℃，时间为6小时；采用万分之一精密天平测量浸泡前后玻璃质量变化，通过测量玻璃表面积计算获得玻璃在弱酸性溶液中的重量损失比。
（7）d:密度（克/毫升），根据《GB/T 7962.20-2010 无色光学玻璃测试方方法-密度测试方法》标准进行测量，环境温度为22±0.5℃；
（8）CTE：平均线热膨胀系数 Coefficient of Linear Thermal Expansion简称，采用ASTM E228 《Standard Test Method for Linear Thermal Expansion of SolidMaterials With a Push-Rod Dilatometer》 标准方法进行测量，温度范围为30℃～300℃。
从表1和表2可知，（1）虽然对比例1玻璃的应变点高于580℃，离子交换后玻璃表面获得高压缩应力值，但玻璃中ZnO＞9%，且(Al2O3+P2O5)/ZnO＜3%，故压缩应力层较差，低于35μm，由此可知离子交换效率明显比实施例1-12玻璃低；且由于对比例1玻璃中SiO2含量低于56%，（Li2O+Na2O+K2O + Al2O3）/SiO2＜0.60，对比例1玻璃在PH=2和60℃的草酸溶液中，浸泡6小时后，单位面积重量损失率为2.23 mg/cm3，玻璃耐弱酸性能差，在玻璃后端草酸浸泡清洗中，玻璃表面将被弱酸侵蚀从而造成强度下降或表面出现雾化。（2）对比例2玻璃的应变点温度较低，离子交换后玻璃表面获得压缩应力值低，同时其压缩应力层较差，低于35μm；即使SiO2含量高于56wt%,但（Li2O+Na2O+K2O + Al2O3）/SiO2＜0.60，对比例1玻璃在PH=2和60℃的草酸溶液中，浸泡6小时后，单位面积重量损失率为0.18mg/cm3，在玻璃后端草酸浸泡清洗中，玻璃表面将被弱酸侵蚀从而造成强度下降或表面出现雾化。
以上所述仅为本发明的较佳实施例，凡依本发明申请专利范围所做的均等变化与修饰，皆应属本发明的涵盖范围。
Claims (6)
1.一种具有高应变点、可快速离子交换和耐弱酸性的锌磷铝硅酸盐玻璃，其特征在于：以质量分数计，所述玻璃包含的组分为：SiO2 56～65 %，Al2O3 17～22%，Na2O 10～16 %，K2O0～1%，Li2O 0～1%，P2O5 0～5%，B2O3 0～2%，MgO 0～0.5%，ZnO 1~8%，TiO2 0～1%，SrO 0～0.5%，SnO2 0～0.5%，CeO2 0～0.5%，各组分之和为100%；所述玻璃的组分以质量分数计：SiO2+Al2O3+P2O3≥78%，(MgO+ZnO+SrO+Al2O3)/( Li2O+Na2O+K2O+B2O3) ≥1.3，(Al2O3+P2O5)/ZnO＞3；所述玻璃的应变点温度≥580℃；所述玻璃是能进行快速离子交换的。
2.根据权利要求1所述的一种具有高应变点、可快速离子交换和耐弱酸性的锌磷铝硅酸盐玻璃，其特征在于：所述玻璃的组分以质量分数计：SiO2+Al2O3+P2O3≥80%。
3.根据权利要求1所述的一种具有高应变点、可快速离子交换和耐弱酸性的锌磷铝硅酸盐玻璃，其特征在于：所述玻璃的压缩应力层≥35μm。
4.根据权利要求1所述的一种具有高应变点、可快速离子交换和耐弱酸性的锌磷铝硅酸盐玻璃，其特征在于：所述玻璃的压缩应力值≥900MPa。
5.根据权利要求1所述的一种具有高应变点、可快速离子交换和耐弱酸性的锌磷铝硅酸盐玻璃，其特征在于：所述玻璃在60℃草酸溶液中浸泡6hrs后单位面积重量损失率≤0.15mg/cm3。
6.根据权利要求1所述的一种具有高应变点、可快速离子交换和耐弱酸性的锌磷铝硅酸盐玻璃，其特征在于：所述玻璃的组分以质量分数计：（Li2O+Na2O+K2O+Al2O3）/SiO2＜0.60。