CN108864934A - 一种rtv防污闪涂料 - Google Patents
一种rtv防污闪涂料 Download PDFInfo
- Publication number
- CN108864934A CN108864934A CN201810757797.8A CN201810757797A CN108864934A CN 108864934 A CN108864934 A CN 108864934A CN 201810757797 A CN201810757797 A CN 201810757797A CN 108864934 A CN108864934 A CN 108864934A
- Authority
- CN
- China
- Prior art keywords
- parts
- pollution flashover
- flashover coating
- rtv anti
- rtv
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种RTV防污闪涂料，包括如下质量份数的各组分：基胶35～50份；硅油1.5～2份；氢氧化铝7～11份；白炭黑3.5～8.5份；铁红1.5～2.5份；十溴联苯醚1～5份；稀释剂30～35份；催化剂0.2～1份；交联剂1～2.5份；偶联剂1.5～3.5份。本发明具备良好的电气性能和机械性能，使用寿命长，可以为电力输变电外绝缘设备提供优良的防污闪保障。
Description
技术领域
本发明涉及化工技术领域，特别是涉及一种RTV防污闪涂料。
背景技术
绝缘子是高压输电线路和变电站的重要外绝缘设备。污闪是指电气设备绝缘表面附着的污秽物在潮湿条件下，其可溶物质逐渐溶于水，在绝缘表面形成一层导电膜，使绝缘子的绝缘水平大大降低，在电力场的作用下出现强烈放电的现象。现有的室温硫化硅橡胶(Room temperature vulcanized silicone rubber，RTV)防污闪涂料在如广东等海滨地区的高温、高湿、盐雾的气候环境下运行时，容易出现起皮、粉化、脱落的附着力下降和憎水性下降等老化现象。
发明内容
为了弥补上述现有技术的不足，本发明提出一种RTV防污闪涂料，可在绝缘子上保持良好的附着力和憎水性，提供良好的防污闪保障。
本发明的技术问题通过以下的技术方案予以解决：
一种RTV防污闪涂料，包括如下质量份数的各组分：基胶35～50份；硅油
1.5～2份；氢氧化铝7～11份；白炭黑3.5～8.5份；铁红1.5～2.5份；十溴联苯醚1～5份；稀释剂30～35份；催化剂0.2～1份；交联剂1～2.5份；偶联剂1.5～3.5份。
优选地，所述基胶为端羟基聚二甲基硅氧烷，粘度为10000～35000cs。
优选地，所述硅油的粘度为300-600cs。
优选地，所述氢氧化铝为疏水型，其粒径为3～10微米，氢氧化铝的质量分数大于99.5％。
优选地，所述白炭黑为气相法白炭黑，粒径为10～20纳米。
优选地，所述铁红为疏水型，其中，氧化铁的质量含量大于94％，相对着色力为95％～105％。
优选地，所述稀释剂为120号溶剂油。
优选地，所述催化剂为二月桂酸二丁基锡。
优选地，所述交联剂为：甲基三甲氧基硅烷、甲基三丁酮肟基硅烷和乙烯基三丁酮肟基硅烷三者按质量比1:0.3～0.5:1～1.5的混合物。
优选地，所述偶联剂为γ-氨丙基三乙氧基硅烷、γ-甲基丙烯酰氧基丙基三甲氧基硅烷和γ-(2,3-环氧丙氧基)丙基三甲氧基硅烷三者按质量比1:0.5～0.8:2～3的混合物。
本发明与现有技术对比的有益效果包括：
本发明的RTV防污闪涂料尤其适用于高温、高湿、盐雾的气候环境，可以耐受这类气候环境而保持良好的憎水性和附着力，具备良好的电气性能和机械性能，使用寿命长，可以为电力输变电外绝缘设备提供优良的防污闪保障。
具体实施方式
下面结合优选的实施方式对本发明作进一步说明。
一种RTV防污闪涂料，包括如下质量份数的各组分：基胶35～50份；硅油
1.5～2份；氢氧化铝7～11份；白炭黑3.5～8.5份；铁红1.5～2.5份；十溴联苯醚1～5份；稀释剂30～35份；催化剂0.2～1份；交联剂1～2.5份；偶联剂1.5～3.5份。
在优选的实施方式中，所述基胶为端羟基聚二甲基硅氧烷，粘度为10000～35000cs。
在优选的实施方式中，所述硅油的粘度为300-600cs。
在优选的实施方式中，所述氢氧化铝为疏水型，其粒径为3～10微米，氢氧化铝的质量分数大于99.5％。
在优选的实施方式中，所述白炭黑为气相法白炭黑，粒径为10～20纳米。所用的纳米粒径的气相法白炭黑作为纳米填料可以提高涂料的阻燃性和对紫外光的耐候性。
在优选的实施方式中，所述铁红为疏水型，其中，氧化铁的质量含量大于94％，相对着色力为95％～105％，可以进一步提高涂料对湿热气候抗性。
在优选的实施方式中，所述稀释剂为120号溶剂油。
在优选的实施方式中，所述催化剂为二月桂酸二丁基锡。
在优选的实施方式中，所述交联剂为：甲基三甲氧基硅烷、甲基三丁酮肟基硅烷和乙烯基三丁酮肟基硅烷三者按质量比1:0.3～0.5:1～1.5的混合物。复配的交联剂使得长度较短的基胶的分子链以交联剂中一部分官能团为媒介连接成为长分子链。
在优选的实施方式中，所述偶联剂为γ-氨丙基三乙氧基硅烷、γ-甲基丙烯酰氧基丙基三甲氧基硅烷和γ-(2,3-环氧丙氧基)丙基三甲氧基硅烷三者按质量比1:0.5～0.8:2～3的混合物。复配的偶联剂主要和基胶发生反应，使出料后的RTV防污闪涂料与玻璃、瓷等表面可以发生反应，可以提高涂料对底材的粘接性。
以下通过更具体的实施例对本发明作进一步阐述。
实施例1
将粘度35000cs的端羟基聚二甲基硅氧烷35份，粘度500cs的硅油1.5份，疏水型氢氧化铝7份(粒径3～10微米，氢氧化铝的质量分数大于99.5％，余量为不可避免的杂质，如氧化钠、二氧化硅和氧化铁等)，气相法白炭黑3.5份(粒径为10～20纳米)，疏水型铁红1.5份(氧化铁的质量含量大于94％，余量为不可避免的杂质)，铁红的相对着色力为95％～105％(按照标准DIN 6174No.038,2009-08-01测得)，十溴联苯醚1份，120号溶剂油35份充分混合、分散、研磨，倒入反应釜内，并抽真空-0.1MPa，加入催化剂二月桂酸二丁基锡0.2份，交联剂(复配质量比：甲基三甲氧基硅烷：甲基三丁酮肟基硅烷：乙烯基三丁酮肟基硅烷＝1:0.3:1)1份，偶联剂(复配质量比：γ-氨丙基三乙氧基硅烷：γ-甲基丙烯酰氧基丙基三甲氧基硅烷：γ-(2,3-环氧丙氧基)丙基三甲氧基硅烷＝1:0.5:2)1.5份，搅拌并恒温电加热至70～80摄氏度，10h后取料。将制得的RTV防污闪涂料涂覆在洁净玻璃试片表面，涂层厚度为0.4mm，通过1000h盐雾和1000h紫外光照试验(实验温度为50～60℃，在冷凝过程中环境中的水蒸气会凝结在涂层表面)后，测试得到其附着力为划格法0级，憎水性保持HC1级，通过测试撕裂强度，得到其撕裂强度为4.5～5.8kN/m，且测得工频击穿场强在20～28kV/mm；而现有的RTV防污闪涂料制备的涂层经上述老化后划格法附着力为3级及以上，憎水性下降为HC3级，撕裂强度为3.5kN/m，工频击穿场强在18kV/mm以下。
实施例2
将粘度25000cs的端羟基聚二甲基硅氧烷50份，粘度400cs的硅油2份，疏水型氢氧化铝11份(粒径3～10微米，氢氧化铝的质量分数大于99.5％，余量为不可避免的杂质，如氧化钠、二氧化硅和氧化铁等)，气相法白炭黑8.5份(粒径为10～20纳米)，疏水型铁红2.5份(氧化铁的质量含量大于94％，余量为不可避免的杂质)，铁红的相对着色力为95％～105％(按照标准DIN 6174No.038,2009-08-01测得)，十溴联苯醚1份，120号溶剂油30份充分混合、分散、研磨，倒入反应釜内，并抽真空-0.1MPa，加入催化剂二月桂酸二丁基锡1份，交联剂(复配质量比：甲基三甲氧基硅烷：甲基三丁酮肟基硅烷：乙烯基三丁酮肟基硅烷＝1:0.5:1.5)2.5份，偶联剂(复配质量比：γ-氨丙基三乙氧基硅烷：γ-甲基丙烯酰氧基丙基三甲氧基硅烷：γ-(2,3-环氧丙氧基)丙基三甲氧基硅烷＝1:0.8:3)3.5份，搅拌并恒温电加热至70～80摄氏度，18h后取料。将制得的RTV防污闪涂料涂覆在洁净玻璃试片表面，涂层厚度为0.4mm，通过1000h盐雾和1000h紫外光照试验(实验温度为50～60℃，在冷凝过程中环境中的水蒸气会凝结在涂层表面)后，测试得到其附着力为划格法0级，憎水性保持HC1级，通过测试撕裂强度，得到其撕裂强度为4.5～6.5kN/m，且测得工频击穿场强在20～25kV/mm；而现有的RTV防污闪涂料制备的涂层经上述老化后划格法附着力为3级及以上，憎水性下降为HC3级，撕裂强度为3.5kN/m，工频击穿场强在18kV/mm以下。
以上内容是结合具体的优选实施方式对本发明所作的进一步详细说明，不能认定本发明的具体实施只局限于这些说明。对于本发明所属技术领域的技术人员来说，在不脱离本发明构思的前提下，还可以做出若干等同替代或明显变型，而且性能或用途相同，都应当视为属于本发明的保护范围。
Claims (10)
1.一种RTV防污闪涂料，其特征在于，包括如下质量份数的各组分：基胶35～50份；硅油1.5～2份；氢氧化铝7～11份；白炭黑3.5～8.5份；铁红1.5～2.5份；十溴联苯醚1～5份；稀释剂30～35份；催化剂0.2～1份；交联剂1～2.5份；偶联剂1.5～3.5份。
2.如权利要求1所述的RTV防污闪涂料，其特征在于，所述基胶为端羟基聚二甲基硅氧烷，粘度为10000～35000cs。
3.如权利要求1所述的RTV防污闪涂料，其特征在于，所述硅油的粘度为300-600cs。
4.如权利要求1所述的RTV防污闪涂料，其特征在于，所述氢氧化铝为疏水型，其粒径为3～10微米，氢氧化铝的质量分数大于99.5％。
5.如权利要求1所述的RTV防污闪涂料，其特征在于，所述白炭黑为气相法白炭黑，粒径为10～20纳米。
6.如权利要求1所述的RTV防污闪涂料，其特征在于，所述铁红为疏水型，其中，氧化铁的质量含量大于94％，相对着色力为95％～105％。
7.如权利要求1所述的RTV防污闪涂料，其特征在于，所述稀释剂为120号溶剂油。
8.如权利要求1所述的RTV防污闪涂料，其特征在于，所述催化剂为二月桂酸二丁基锡。
9.如权利要求1所述的RTV防污闪涂料，其特征在于，所述交联剂为：甲基三甲氧基硅烷、甲基三丁酮肟基硅烷和乙烯基三丁酮肟基硅烷三者按质量比1:0.3～0.5:1～1.5的混合物。
10.如权利要求1所述的RTV防污闪涂料，其特征在于，所述偶联剂为γ-氨丙基三乙氧基硅烷、γ-甲基丙烯酰氧基丙基三甲氧基硅烷和γ-(2,3-环氧丙氧基)丙基三甲氧基硅烷三者按质量比1:0.5～0.8:2～3的混合物。