CN108842206A - 一种长效型抑菌纤维的制备方法 - Google Patents
一种长效型抑菌纤维的制备方法 Download PDFInfo
- Publication number
- CN108842206A CN108842206A CN201810630132.0A CN201810630132A CN108842206A CN 108842206 A CN108842206 A CN 108842206A CN 201810630132 A CN201810630132 A CN 201810630132A CN 108842206 A CN108842206 A CN 108842206A
- Authority
- CN
- China
- Prior art keywords
- parts
- long
- preparation
- acting type
- prepare
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种长效型抑菌纤维的制备方法，其特征在于：包括以下步骤：（1）制备纺丝液；（2）制备抗菌剂；（3）制备抗菌纤维。与现有技术相比，本发明的有益效果为：本发明的方法将抗菌剂与纺丝液混合纺丝，制得的纤维具有优良的抗菌除臭性能；本发明的抗菌剂具有良好的吸水性和生物相容性，具有持久、高效的杀菌特点，利用抗菌剂制得的抗菌纤维还具有良好的透气性和吸水性。
Description
技术领域
本发明涉及纺织纤维整理领域，特别是一种长效型抑菌纤维的制备方法。
背景技术
再生纤维素纤维是天然纤维素经过一系列复杂的化学变化和物理变化制成的可再生纤维，主要组成物质为纤维素，具有优良的染色性能和光泽，同时还拥有极佳服用性能和广泛的适用性能，此外，其悬垂性远胜于棉、麻所制成的纺织品。其用途几乎遍及所有的工业、农业、生活衣着等各方面，是纺织工业的重要原料之一。
近年来，随着人们对生活品质的要求越来越高，各种功能性的产品也是层出不穷，抗菌、防螨、芳香整理等产品，也越来越多的手到消费者的青睐。而再生纤维素纤维的产品以其良好的各项性能，目前已经普及到人们生活的各个领域，包括服装、家纺等。近年来，各种有着特殊功能的的再生纤维素纤维制品，自然也是受到了很多消费者的推崇，尤其是防螨、抗菌、除臭等产品。
发明内容
本发明的目的是提供一种长效型抑菌纤维的制备方法，以解决现有技术中的不足，它能够赋予再生纤维素纤维以抗菌除臭的性能。
本发明提供了一种长效型抑菌纤维的制备方法，包括以下步骤：
（1）制备纺丝液：将含有纤维素纤维的原料的浆粕进行浸渍压榨、粉碎、老成、黄化、连续溶解、过滤以及脱泡处理后，得到纺丝液；
（2）制备抗菌剂：首25份抗菌防螨母粒、20份2-甲基-4-异噻唑啉-3-酮、0.6份丁香酚和/或异丁香酚、5份十亚甲基双胍二盐酸盐、20份聚羟丙基二甲基氯化铵、42份十二烷基羧甲基钠型咪唑啉醋酸盐、1.2份乙二胺二邻羟苯基大乙酸铁钠、3份氧化锌、4份分散剂、2份乳化剂、2份粘合剂以及0.6份表面处理剂混合后得复合抗菌剂；
（3）制备抗菌纤维：将复合抗菌剂与纺丝液混合后进行湿法纺丝。
优选地是，所述抗菌防螨母粒包括以下重量份数的组分：6-20份抗菌防螨粉体，1-3份铝酸酯偶联剂，1-3份硬酯酸，0.05-1份三[2 .4-二叔丁基苯基]亚磷酸酯以及0.05-1份四[β-(3，5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯。
优选地是，所述分散剂为三聚磷酸钠、六偏磷酸钠火焦磷酸钠中的一种或几种。
优选地是，所述乳化剂为司盘-60、司盘-80、丙二醇脂肪酸酯或单硬脂酸甘油酯中的一种或几种。
优选地是，所述表面处理剂选自硅烷偶联剂、铝酸酯偶联剂、钛酸酯偶联剂、铝钛偶联剂、硬脂酸、硬脂酸盐、二氧化钛、二氧化硅中的一种或几种。
与现有技术相比，本发明的有益效果为：本发明的方法将抗菌剂与纺丝液混合纺丝，制得的纤维具有优良的抗菌除臭性能；本发明的抗菌剂具有良好的吸水性和生物相容性，具有持久、高效的杀菌特点，利用抗菌剂制得的抗菌纤维还具有良好的透气性和吸水性。
具体实施方式
本发明的实施例：一种长效型抑菌纤维的制备方法，包括以下步骤：
（1）制备纺丝液：将含有纤维素纤维的原料的浆粕进行浸渍压榨、粉碎、老成、黄化、连续溶解、过滤以及脱泡处理后，得到纺丝液；
（2）制备抗菌剂：首25份抗菌防螨母粒、20份2-甲基-4-异噻唑啉-3-酮、0.6份丁香酚和/或异丁香酚、5份十亚甲基双胍二盐酸盐、20份聚羟丙基二甲基氯化铵、42份十二烷基羧甲基钠型咪唑啉醋酸盐、1.2份乙二胺二邻羟苯基大乙酸铁钠、3份氧化锌、4份分散剂、2份乳化剂、2份粘合剂以及0.6份表面处理剂混合后得复合抗菌剂；
（3）制备抗菌纤维：将复合抗菌剂与纺丝液混合后进行湿法纺丝。
优选地是，所述抗菌防螨母粒包括以下重量份数的组分：6-20份抗菌防螨粉体，1-3份铝酸酯偶联剂，1-3份硬酯酸，0.05-1份三[2 .4-二叔丁基苯基]亚磷酸酯以及0.05-1份四[β-(3，5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯。
优选地是，所述分散剂为三聚磷酸钠、六偏磷酸钠火焦磷酸钠中的一种或几种。
优选地是，所述乳化剂为司盘-60、司盘-80、丙二醇脂肪酸酯或单硬脂酸甘油酯中的一种或几种。
优选地是，所述表面处理剂选自硅烷偶联剂、铝酸酯偶联剂、钛酸酯偶联剂、铝钛偶联剂、硬脂酸、硬脂酸盐、二氧化钛、二氧化硅中的一种或几种。
Claims (5)
1.一种长效型抑菌纤维的制备方法，其特征在于：包括以下步骤：
（1）制备纺丝液：将含有纤维素纤维的原料的浆粕进行浸渍压榨、粉碎、老成、黄化、连续溶解、过滤以及脱泡处理后，得到纺丝液；
（2）制备抗菌剂：首25份抗菌防螨母粒、20份2-甲基-4-异噻唑啉-3-酮、0.6份丁香酚和/或异丁香酚、5份十亚甲基双胍二盐酸盐、20份聚羟丙基二甲基氯化铵、42份十二烷基羧甲基钠型咪唑啉醋酸盐、1.2份乙二胺二邻羟苯基大乙酸铁钠、3份氧化锌、4份分散剂、2份乳化剂、2份粘合剂以及0.6份表面处理剂混合后得复合抗菌剂；
（3）制备抗菌纤维：将复合抗菌剂与纺丝液混合后进行湿法纺丝。
2.根据权利要求1所述的长效型抑菌纤维的制备方法，其特征在于：所述抗菌防螨母粒包括以下重量份数的组分：6-20份抗菌防螨粉体，1-3份铝酸酯偶联剂，1-3份硬酯酸，0.05-1份三[2 .4-二叔丁基苯基]亚磷酸酯以及0.05-1份四[β-(3，5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯。
3.根据权利要求1所述的长效型抑菌纤维的制备方法，其特征在于：所述分散剂为三聚磷酸钠、六偏磷酸钠火焦磷酸钠中的一种或几种。
4.根据权利要求1所述的长效型抑菌纤维的制备方法，其特征在于：所述乳化剂为司盘-60、司盘-80、丙二醇脂肪酸酯或单硬脂酸甘油酯中的一种或几种。
5.根据权利要求1所述的长效型抑菌纤维的制备方法，其特征在于：所述表面处理剂选自硅烷偶联剂、铝酸酯偶联剂、钛酸酯偶联剂、铝钛偶联剂、硬脂酸、硬脂酸盐、二氧化钛、二氧化硅中的一种或几种。