CN108842160A - 一种电解水制氢能源用钌掺杂铁镍合金催化剂及制备方法 - Google Patents
一种电解水制氢能源用钌掺杂铁镍合金催化剂及制备方法 Download PDFInfo
- Publication number
- CN108842160A CN108842160A CN201810673736.3A CN201810673736A CN108842160A CN 108842160 A CN108842160 A CN 108842160A CN 201810673736 A CN201810673736 A CN 201810673736A CN 108842160 A CN108842160 A CN 108842160A
- Authority
- CN
- China
- Prior art keywords
- ruthenium
- source
- nickel
- hydrogen production
- iron
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明涉及电解水制氢的领域，公开了一种电解水制氢能源用钌掺杂铁镍合金催化剂及制备方法。包括如下制备过程：（1）将镍源、铁源、钌源和助剂加入去离子水中配制为溶胶；（2）将聚苯胺包覆的泡沫镍粉末浸渍于溶胶中，静置陈化；（3）过滤烘干后高温煅烧，制得核壳结构的钌掺杂铁镍合金催化剂。本发明制得的催化剂与普通制氢催化剂相比，将铁镍钌合金包覆于泡沫镍表层，增加了催化剂的反应活性位点，有效降低了水的自发电解势垒，提高了催化剂的析氢能力，具有优异的氢催化性能，催化活性好，用于电解水制氢时效率高。
Description
技术领域
本发明涉及电解水制氢的领域，公开了一种电解水制氢能源用钌掺杂铁镍合金催化剂及制备方法。
背景技术
随着环境保护的加强，越来越多的研究关注于绿色无污染能源。其中氢能清洁无污染、高效、可再生，是未来最有潜力的能源载体。氢能源作为高效、洁净和理想的二次能源已经受到了全世界的广泛重视。大规模、廉价地生产氢是开发和利用氢能的重要环节之一。在目前制氢技术中，利用电解水技术制氢是目前最有潜力的技术，也是一种经济有效的技术。
水电解制氢是一种较为方便的制取氢气的方法。在充满电解液的电解槽中通入直流电，水分子在电极上发生电化学反应，分解成氢气和氧气。电解水制氢是一种高效、清洁的制氢技术，其制氢工艺简单，产品纯度高，氢气、氧气纯度一般可达99.9％，是最有潜力的大规模制氢技术。特别是随着目前可再生能源发电的日益增长，氢气将成为电能存储的理想载体。
在电解水制氢方法中，优良的催化剂是提高制氢效率有着举足轻重的作用，成功的设计出低温高效催化剂是制氢研究的关键技术之一。用作电解水制氢的催化剂主要由半导体材料、贵金属及其化合物等。近年来研究发现，NiFe双金属氢氧化物（NiFe-LDH）在碱性溶液中表现出优异的电催化分解水析氧（OER）性能，在制氢技术中，提高催化剂对于水的自发电离的性能，从而提高催化活性具有十分重要的实际意义。
中国发明专利申请号201610141649.4公开了一种具有多形貌的金属掺杂W18O49电催化剂及其在电解水制氢中的应用，具体是利用W18O49在特定晶向的择优生长特性并以溶剂热法制备W18O49催化剂，通过改变前驱体溶液的浓度，可获得纳米纤维、纳米纤维束和由纳米纤维构成的微球三种形貌，并且可通过掺入钯、钼等元素提高其电催化性能。该发明充分利用W18O49的一维纳米纤维结构促进电子传输，并且催化剂中大量的氧空位为H+还原生成H2提供了充足的活性位点；此外，固态W18O49纳米纤维能够与液相电解质完全接触，有利于H+在纳米纤维构成的三维网络中扩散，从而提高其催化性能。该发明所述多形貌电催化剂电催化活性高、稳定性好、制备方法简便易行、成本低廉。
中国发明专利申请号201611167015.2公开了一种电解水制氢的催化剂，催化剂是碳担载纳米铜铂合金。该发明的催化剂具有更多的活性位点，提高电化学催化效率；同时铜的加入减少了铂的载量，进一步降低了成本；由于金属间的协同作用，铂铜合金可以有效的降低电化学反应的过电位，降低了电解池电压，减少了能耗成本。
根据上述，现有方案中用于电解水制氢的金属氢氧化物催化剂，存在析氢性能非常差，分解水需要很大的电压输入，并且析氢动力学主要受限于水电离出氢离子过程较慢，进而影响电价水制氢的效率，本发明提出了一种电解水制氢能源用钌掺杂铁镍合金催化剂及制备方法，可有效解决上述技术问题。
发明内容
目前应用较广的电解水制氢的金属氢氧化物催化剂存在析氢性能非常差，电压输入要求高，水电离出氢离子过程较慢，制氢效率低等缺陷。
为解决上述问题，本发明采用以下技术方案：
一种电解水制氢能源用钌掺杂铁镍合金催化剂的制备方法，制备的具体过程为：
（1）将镍源、铁源、钌源和助剂加入去离子水中，配制为溶胶；
（2）先将聚苯胺包覆的泡沫镍粉末浸渍于步骤（1）制得的溶胶中，然后静置陈化至体系达到平衡；
（3）先过滤、烘干，然后在还原气氛下进行高温煅烧，除去聚苯胺，制得核壳结构的钌掺杂铁镍合金催化剂。
优选的，步骤（1）所述镍源为氯化镍、硫酸镍、硝酸镍中的至少一种。
优选的，步骤（1）所述铁源为氯化铁、硫酸铁、硝酸铁、溴化铁中的至少一种。
优选的，步骤（1）所述钌源为三氯化钌、硝酸钌中的至少一种。
优选的，步骤（1）所述助剂微胶体稳定剂，如壳聚糖、明胶中的一种。
优选的，步骤（1）所述溶胶中，镍源10~12重量份、铁源20~25重量份、钌源4~6重量份、助剂2~5重量份、去离子水52~64重量份。
优选的，步骤（2）所述包覆聚苯胺厚度为1-10μm。
优选的，步骤（2）所述静置陈化的时间为4~6h。
优选的，步骤（3）所述高温煅烧的温度为500~700℃，时间为2~3h。
由上述方法制备得到的一种电解水制氢能源用钌掺杂铁镍合金催化剂，通过铁、镍、钌的无机盐配置为溶胶，自发附着于聚苯胺膜表面，通过高温烧结去除聚苯胺后，铁镍钌合金均匀包覆在泡沫镍表层。
测试本发明制备的钌掺杂铁镍合金催化剂的电解最低槽压、制氢电耗及产氢速率，并与NiFe双金属氢氧化物催化剂，本发明的方法具有明显优势，如表1所示。
表1：
本发明提供了一种电解水制氢能源用钌掺杂铁镍合金催化剂及制备方法，与现有技术相比，其突出的特点和优异的效果在于：
1、提出了将铁镍钌合金包覆于泡沫镍表层制备电解水制氢能源用钌掺杂铁镍合金催化剂的方法。
2、通过引入金属钌，增加了催化剂的反应活性位点，有效降低了水的自发电解势垒，提高了催化剂的析氢能力，可提供更多的活性氢。
3、本发明制得的的催化剂具有优异的氢催化性能，催化活性好，用于电解水制氢时效率高。
具体实施方式
以下通过具体实施方式对本发明作进一步的详细说明，但不应将此理解为本发明的范围仅限于以下的实例。在不脱离本发明上述方法思想的情况下,根据本领域普通技术知识和惯用手段做出的各种替换或变更,均应包含在本发明的范围内。
实施例1
（1）将镍源、铁源、钌源和壳聚糖加入去离子水中，配制为溶胶；镍源为氯化镍。铁源为氯化铁。钌源为硝酸钌。溶胶中，镍源10重量份、铁源20重量份、钌源6重量份、助剂4重量份、去离子水60重量份。
（2）先将聚苯胺包覆的泡沫镍粉末浸渍于步骤（1）制得的溶胶中，然后静置陈化至体系达到平衡；静置陈化的时间为5h。
（3）先过滤、烘干，然后在还原气氛下进行高温煅烧，除去聚苯胺，制得核壳结构的钌掺杂铁镍合金催化剂。高温煅烧的温度为700℃，时间为2h。
实施例1制得的合金催化剂，其电解最低槽压、制氢电耗、产氢速率如表2所示。
实施例2
（1）将镍源、铁源、钌源和明胶加入去离子水中，配制为溶胶；镍源为硫酸镍。铁源为硫酸铁。钌源为三氯化钌。溶胶中，镍源12重量份、铁源25重量份、钌源6重量份、助剂2重量份、去离子水55重量份。
（2）先将聚苯胺包覆的泡沫镍粉末浸渍于步骤（1）制得的溶胶中，然后静置陈化至体系达到平衡；静置陈化的时间为6h。
（3）先过滤、烘干，然后在还原气氛下进行高温煅烧，除去聚苯胺，制得核壳结构的钌掺杂铁镍合金催化剂。高温煅烧的温度为500℃，时间为3h。
实施例2制得的合金催化剂，其电解最低槽压、制氢电耗、产氢速率如表2所示。
实施例3
（1）将镍源、铁源、钌源和壳聚糖加入去离子水中，配制为溶胶；镍源为硝酸镍。铁源为硝酸铁。钌源为硝酸钌。溶胶中，镍源10重量份、铁源22重量份、钌源6重量份、助剂2重量份、去离子水60重量份。
（2）先将聚苯胺包覆的泡沫镍粉末浸渍于步骤（1）制得的溶胶中，然后静置陈化至体系达到平衡；静置陈化的时间为4h。
（3）先过滤、烘干，然后在还原气氛下进行高温煅烧，除去聚苯胺，制得核壳结构的钌掺杂铁镍合金催化剂。高温煅烧的温度为650℃，时间为2h。
实施例3制得的合金催化剂，其电解最低槽压、制氢电耗、产氢速率如表2所示。
实施例4
（1）将镍源、铁源、钌源和明胶加入去离子水中，配制为溶胶；镍源为硝酸镍。铁源为溴化铁。钌源为三氯化钌。溶胶中，镍源12重量份、铁源25重量份、钌源6重量份、助剂5重量份、去离子水52重量份。
（2）先将聚苯胺包覆的泡沫镍粉末浸渍于步骤（1）制得的溶胶中，然后静置陈化至体系达到平衡；静置陈化的时间为6h。
（3）先过滤、烘干，然后在还原气氛下进行高温煅烧，除去聚苯胺，制得核壳结构的钌掺杂铁镍合金催化剂。高温煅烧的温度为550℃，时间为2h。
实施例4制得的合金催化剂，其电解最低槽压、制氢电耗、产氢速率如表2所示。
实施例5
（1）将镍源、铁源、钌源和壳聚糖加入去离子水中，配制为溶胶；镍源为氯化镍。铁源为硫酸铁。钌源为硝酸钌。溶胶中，镍源10重量份、铁源22重量份、钌源5重量份、助剂5重量份、去离子水58重量份。
（2）先将聚苯胺包覆的泡沫镍粉末浸渍于步骤（1）制得的溶胶中，然后静置陈化至体系达到平衡；静置陈化的时间为5h。
（3）先过滤、烘干，然后在还原气氛下进行高温煅烧，除去聚苯胺，制得核壳结构的钌掺杂铁镍合金催化剂。高温煅烧的温度为700℃，时间为2h。
实施例5制得的合金催化剂，其电解最低槽压、制氢电耗、产氢速率如表2所示。
实施例6
（1）将镍源、铁源、钌源和壳聚糖加入去离子水中，配制为溶胶；镍源为硝酸镍。铁源为氯化铁。钌源为三氯化钌。溶胶中，镍源10重量份、铁源25重量份、钌源5重量份、助剂3重量份、去离子水57重量份。
（2）先将聚苯胺包覆的泡沫镍粉末浸渍于步骤（1）制得的溶胶中，然后静置陈化至体系达到平衡；静置陈化的时间为5h。
（3）先过滤、烘干，然后在还原气氛下进行高温煅烧，除去聚苯胺，制得核壳结构的钌掺杂铁镍合金催化剂。高温煅烧的温度为600℃，时间为2h。
实施例6制得的合金催化剂，其电解最低槽压、制氢电耗、产氢速率如表2所示。
对比例1
对比例1没有添加钌源，制得的合金催化剂，其电解最低槽压、制氢电耗、产氢速率如表2所示。
上述性能指标的测试方法为：
采用HD-D300水电解水制氢装置进行试验，水的体积为10L，加1g入本发明制得催化剂，为了便于定性比较，水解装置其余条件均为常规条件，在同等条件下实验，水的试验温度为50℃，测定电解最低槽压，以及制氢电耗，根据制得的氢气的量，测定并计算产氢效率。
表2：
Claims (10)
1.一种电解水制氢能源用钌掺杂铁镍合金催化剂的制备方法，其特征在于，制备的具体过程为：
（1）将镍源、铁源、钌源和助剂加入去离子水中，配制为溶胶；
（2）先将聚苯胺包覆的泡沫镍粉末浸渍于步骤（1）制得的溶胶中，然后静置陈化至体系达到平衡；
（3）先过滤、烘干，然后在还原气氛下进行高温煅烧，除去聚苯胺，制得核壳结构的钌掺杂铁镍合金催化剂。
2.根据权利要求1所述一种电解水制氢能源用钌掺杂铁镍合金催化剂的制备方法，其特征在于：步骤（1）所述镍源为氯化镍、硫酸镍、硝酸镍中的至少一种。
3.根据权利要求1所述一种电解水制氢能源用钌掺杂铁镍合金催化剂的制备方法，其特征在于：步骤（1）所述铁源为氯化铁、硫酸铁、硝酸铁、溴化铁中的至少一种。
4.根据权利要求1所述一种电解水制氢能源用钌掺杂铁镍合金催化剂的制备方法，其特征在于：步骤（1）所述钌源为三氯化钌、硝酸钌中的至少一种。
5.根据权利要求1所述一种电解水制氢能源用钌掺杂铁镍合金催化剂的制备方法，其特征在于：步骤（1）所述助剂为胶体稳定剂。
6.根据权利要求1所述一种电解水制氢能源用钌掺杂铁镍合金催化剂的制备方法，其特征在于：步骤（1）所述溶胶中，镍源10~12重量份、铁源20~25重量份、钌源4~6重量份、助剂2~5重量份、去离子水52~64重量份。
7.根据权利要求1所述一种电解水制氢能源用钌掺杂铁镍合金催化剂的制备方法，其特征在于：步骤（2）所述包覆聚苯胺的厚度为1-10μm。
8.根据权利要求1所述一种电解水制氢能源用钌掺杂铁镍合金催化剂的制备方法，其特征在于：步骤（2）所述静置陈化的时间为4~6h。
9.根据权利要求1所述一种电解水制氢能源用钌掺杂铁镍合金催化剂的制备方法，其特征在于：步骤（3）所述高温煅烧的温度为500~700℃，时间为2~3h。
10.权利要求1~9任一项所述方法制备得到的一种电解水制氢能源用钌掺杂铁镍合金催化剂。