CN108819298A - 一种具有防静电功能玻璃钢制品及制备方法 - Google Patents
一种具有防静电功能玻璃钢制品及制备方法 Download PDFInfo
- Publication number
- CN108819298A CN108819298A CN201810310049.5A CN201810310049A CN108819298A CN 108819298 A CN108819298 A CN 108819298A CN 201810310049 A CN201810310049 A CN 201810310049A CN 108819298 A CN108819298 A CN 108819298A
- Authority
- CN
- China
- Prior art keywords
- fiber reinforced
- mold
- glass
- reinforced plastics
- glass fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种具有防静电功能玻璃钢制品及制备方法,包括玻璃钢制品，防静电功能玻璃钢制品中玻璃纤维具有增强玻璃本身强度，合成树脂胶黏剂具有粘合作用，通过合成树脂胶黏剂将散着的玻璃纤维粘结为一个整体，使之成为具有预定物理性质、化学性质的玻璃钢，将玻璃钢模具中涂抹一层脱模剂，将玻璃纤维铺在钢化玻璃模具中，向玻璃钢模具中注入合成树脂胶黏剂，合成树脂胶黏剂与玻璃纤维融合在一起，然后经过迅速降温冷却，可以形成一个连通的网络结构，对其表面进行金属化处理后,将有效提高玻璃钢的导电性能，在玻璃纤维表面形成薄的金属导电层，该方法的生产成本很低，同时对于玻璃钢本身的性能不会产生影响。
Description
技术领域
本发明涉及玻璃钢制品技术领域，具体为一种具有防静电功能玻璃钢制品及制备方法。
背景技术
目前，制备具有防静电功能玻璃钢制品的研究主要集中在两个方面 ：一是采用碳纤维取代玻璃纤维制备玻璃钢，由于碳纤维具有导电性，因此获得了表面电阻较低的玻璃钢；二是采用导电性胶体代替玻璃钢使用的树脂，玻璃纤维与导电胶体构成玻璃钢，其导电性由导电胶体来获得。存在的问题有：一个是碳纤维与玻璃纤维相比较，价格太贵，因此只适用于高端制品的制造；第二所使用的导电胶体，大部分是将碳粉或其他金属微粉加入树脂中得到 , 为获得所要求的导电性，所加入的导电性粉体数量较大，而这很容易产生胶体性能的下降。
发明内容
本发明的目的在于提供一种该方法的生产成本很低，同时对于玻璃钢本身的性能不会产生影响的一种具有防静电功能玻璃钢制品及制备方法，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：一种具有防静电功能玻璃钢制品,包括玻璃钢制品，所述玻璃钢制品上包括模具，所述模具的内部底层设有脱模剂，模具的内部设有玻璃纤维、合成树脂胶黏剂、无机填料、色浆、固化剂、促进剂。
优选的，所述脱模剂5-6份，玻璃纤维20-30份，合成树脂胶黏剂50-60份，无机填料10-20份，色浆5-8份，固化剂10份，促进剂5-8份。
优选的，所述玻璃钢制品的模具采用铝合金材料，模具的内表面采用镀锌处理。
优选的，所述无机填料采用碳化硅微粉、轻质碳酸钙。
优选的，所述脱模剂为聚氯乙烯。
优选的，所述固化剂采用缩二脲（N75）。
优选的，所述玻璃钢制品在制备时温度为700℃，降温时间控制在15min-20min。
优选的，一种具有防静电功能玻璃钢制品，其制备法包括以下步骤：
A、首先将玻璃钢模具中涂抹一层脱模剂，等待脱模剂干燥；将玻璃纤维铺在钢化玻璃模具中；
B、待脱模剂干燥后,将50-60份的合成树脂胶黏剂、10-20份的无机填料 5 － 8促进剂按照比例混合后进行加热，温度升高到700℃后保持这一温度10min-15min；
C、将融化后的玻璃钢制品原料倒入准备好的模具中，将模具密封后抽去模具中的空气，同时向模具中注入冷气进行迅速降温，持续降温20min-25min；
D、待降温成功后，打开模具，将成型的玻璃钢取出，然后再向模具中涂刷一层脱模剂，再向涂油脱模剂的模具中注入合成树脂胶黏剂与无机填料；
E、将初步成型的玻璃钢再次放入涂刷过脱模剂的模具中，加热升温使温度维持在700℃10min后迅速降温，持续降温20min后取出玻璃钢制品。
与现有技术相比，本发明的有益效果是：
玻璃钢制品对其表面进行金属化处理后,将有效提高玻璃钢的导电性能，在玻璃纤维表面形成薄的金属导电层，该方法的生产成本很低，同时对于玻璃钢本身的性能不会产生影响。
具体实施方式
下面对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
本发明提供如下技术方案：一种具有防静电功能玻璃钢制品,包括玻璃钢制品，玻璃钢制品上包括模具，玻璃钢制品的模具采用铝合金材料，模具的内表面采用镀锌处理，经过镀锌处理过的铝合金模具不仅在取出玻璃钢制品时候比较方便，同时还能保证玻璃钢制品表面的光滑，在模具的内部底层设有脱模剂，模具的内部设有玻璃纤维、合成树脂胶黏剂、无机填料、色浆、固化剂、促进剂，在玻璃钢制品中的材料脱模剂5-6份，玻璃纤维20-30份，合成树脂胶黏剂50-60份，无机填料10-20份，无机填料采用碳化硅微粉、轻质碳酸钙，色浆5-8份，固化剂10份，固化剂采用缩二脲（N75），促进剂5-8份，玻璃钢制品在制备时温度为700℃，降温时间控制在15min-20min。
首先将玻璃钢模具中涂抹一层脱模剂，等待脱模剂干燥；将玻璃纤维铺在钢化玻璃模具中，待脱模剂干燥后,将50-60份的合成树脂胶黏剂、10-20份的无机填料 5 － 8促进剂按照比例混合后进行加热，温度升高到700℃后保持这一温度10min-15min，然后将融化后的玻璃钢制品原料倒入准备好的模具中，将模具密封后抽去模具中的空气，同时向模具中注入冷气进行迅速降温，持续降温20min-25min，待降温成功后，打开模具，将成型的玻璃钢取出，然后再向模具中涂刷一层脱模剂，再向涂油脱模剂的模具中注入合成树脂胶黏剂与无机填料，将初步成型的玻璃钢再次放入涂刷过脱模剂的模具中，加热升温使温度维持在700℃10min后迅速降温，持续降温20min后取出玻璃钢制品。
玻璃钢制品对其表面进行金属化处理后,将有效提高玻璃钢的导电性能，在玻璃纤维表面形成薄的金属导电层，该方法的生产成本很低，同时对于玻璃钢本身的性能不会产生影响。
一种具有防静电功能玻璃钢制品，其制备法包括以下步骤：
A、首先将玻璃钢模具中涂抹一层脱模剂，等待脱模剂干燥；将玻璃纤维铺在钢化玻璃模具中；
B、待脱模剂干燥后,将50-60份的合成树脂胶黏剂、10-20份的无机填料 5 － 8促进剂按照比例混合后进行加热，温度升高到700℃后保持这一温度10min-15min；
C、将融化后的玻璃钢制品原料倒入准备好的模具中，将模具密封后抽去模具中的空气，同时向模具中注入冷气进行迅速降温，持续降温20min-25min；
D、待降温成功后，打开模具，将成型的玻璃钢取出，然后再向模具中涂刷一层脱模剂，再向涂油脱模剂的模具中注入合成树脂胶黏剂与无机填料；
E、将初步成型的玻璃钢再次放入涂刷过脱模剂的模具中，加热升温使温度维持在700℃10min后迅速降温，持续降温20min后取出玻璃钢制品。
本发明的有益效果是：
玻璃钢制品对其表面进行金属化处理后,将有效提高玻璃钢的导电性能，在玻璃纤维表面形成薄的金属导电层，该方法的生产成本很低，同时对于玻璃钢本身的性能不会产生影响。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (8)
1.一种具有防静电功能玻璃钢制品,包括玻璃钢制品，其特征在于：所述玻璃钢制品上包括模具，所述模具的内部底层设有脱模剂，模具的内部设有玻璃纤维、合成树脂胶黏剂、无机填料、色浆、固化剂、促进剂。
2.根据权利要求1所述的一种具有防静电功能玻璃钢制品，其特征在于：所述脱模剂5-6份，玻璃纤维20-30份，合成树脂胶黏剂50-60份，无机填料10-20份，色浆5-8份，固化剂10份，促进剂5-8份。
3.根据权利要求1所述的一种具有防静电功能玻璃钢制品，其特征在于：所述玻璃钢制品的模具采用铝合金材料，模具的内表面采用镀锌处理。
4.根据权利要求1所述的一种具有防静电功能玻璃钢制品，其特征在于：所述无机填料采用碳化硅微粉、轻质碳酸钙。
5.根据权利要求1所述的一种具有防静电功能玻璃钢制品，其特征在于：所述脱模剂为聚氯乙烯。
6.根据权利要求1所述的一种具有防静电功能玻璃钢制品，其特征在于：所述固化剂采用缩二脲（N75）。
7.根据权利要求1所述的一种具有防静电功能玻璃钢制品，其特征在于：所述玻璃钢制品在制备时温度为700℃，降温时间控制在15min-20min。
8.实现权利要求1所述的一种具有防静电功能玻璃钢制品，其制备法包括以下步骤：
A、首先将玻璃钢模具中涂抹一层脱模剂，等待脱模剂干燥；将玻璃纤维铺在钢化玻璃模具中；
B、待脱模剂干燥后,将50-60份的合成树脂胶黏剂、10-20份的无机填料 5 － 8促进剂按照比例混合后进行加热，温度升高到700℃后保持这一温度10min-15min；
C、将融化后的玻璃钢制品原料倒入准备好的模具中，将模具密封后抽去模具中的空气，同时向模具中注入冷气进行迅速降温，持续降温20min-25min；
D、待降温成功后，打开模具，将成型的玻璃钢取出，然后再向模具中涂刷一层脱模剂，再向涂油脱模剂的模具中注入合成树脂胶黏剂与无机填料；
E、将初步成型的玻璃钢再次放入涂刷过脱模剂的模具中，加热升温使温度维持在700℃10min后迅速降温，持续降温20min后取出玻璃钢制品。