CN108818800A - It is a kind of using be unfolded after bamboo wood as the method for processing sheet material of raw material - Google Patents
It is a kind of using be unfolded after bamboo wood as the method for processing sheet material of raw material Download PDFInfo
- Publication number
- CN108818800A CN108818800A CN201810742509.1A CN201810742509A CN108818800A CN 108818800 A CN108818800 A CN 108818800A CN 201810742509 A CN201810742509 A CN 201810742509A CN 108818800 A CN108818800 A CN 108818800A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- splice plate
- plate
- stiffener
- unfolded
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention provides a kind of bamboo woods using after being unfolded as the method for processing sheet material of raw material, belongs to bamboo processing technical field.This method is to retain the thick bamboo tube of bamboo knot as substrate, after expansion, bamboo knot point removal is spare, positioning protrusion and locating slot are opened up in the tabasheer side of the plate of removal bamboo knot, by way of overlapping splicing, forms the plate of double-layer structure, wherein, stiffener is formed after bamboo knot is the partially unfolded, for being embedded in both side plate structure, to enhance the horizontal and vertical intensity of plate.The present invention has many advantages, such as to can be improved bamboo board flatness, improves utilization rate of bamboo, enhancing timber intensity, extends plate service life, optimization plate appearance.
Description
Technical field
The invention belongs to bamboo processing technical field, it is related to a kind of bamboo wood using after being unfolded as the sheet fabrication side of raw material
Method.
Background technique
Thick bamboo tube is truncated, machining removes interior acromere and bamboo blueness, tabasheer, cracks, and expansion mould is sent into after hot mastication
The perimeter of the whole bamboo spreading bamboo veneer obtained after middle flattening, breadth and thick bamboo tube is of substantially equal, and unfolded surface is visible by naked eyes
Crackle.Compared with the bamboo clappers of traditional bamboo cane splicing, the bamboo clappers quality after expansion is significantly improved.Finished product, which can directly provide user, to be made
With, also can be used as new material carry out deep processing after other kinds wood-based panel product is made.
But bamboo expansion plate equally exists many technical problems, and bamboo board is made to react relatively cold in the market,
Including the bamboo knot position of deploying type bamboo wood, because fibre density is larger, fiber distribution is irregular and intensive, plate is caused to exist
Bamboo knot position is easily deformed, and specifically bamboo knot two sides expand and the position deformation of bamboo knot is small, other positions in addition to bamboo knot
Because fibre density is relatively low, and fibre density is relatively uniform, and deformation is also relatively uniform, keeps the position deformation of bamboo knot prominent, from
And influence the overall aesthetic degree, stability and using effect of bamboo board.
The fibre density of the bamboo blueness side of bamboo is bigger than the fibre density of tabasheer side, and from tabasheer side to bamboo blueness side
Fibre density is gradually increased, and then shows that density is big in bamboo knot position, and bamboo fibre distinguishes the state of the V-shaped protrusion in outside two sides,
Bamboo processing is set to be easy to cause out-of-flatness in bamboo knot position in the process, the fiber for making bamboo clappers Huang side need integrally to eliminate is more,
Influence the utilization rate of bamboo wood.
Using the bamboo wood after being unfolded, as the bamboo board of raw material, there is also the defects in intensity, because bamboo fibre genesis analysis, leads
The buckling strength for causing it lateral is lower, even spliced plate, equally exists such problems, influence plate applies model
It encloses and application.
Summary of the invention
It is original in view of the above problems existing in the prior art, the purpose of the present invention is to provide a kind of bamboo wood with after being unfolded
The method for processing sheet material of material improves the flat of plate the technical problem to be solved by the present invention is to how improve the utilization rate of bamboo wood
Whole degree, aesthetics and durability degree.
Object of the invention can be realized by the following technical scheme：It is a kind of using be unfolded after bamboo wood add as the plate of raw material
Work method, which is characterized in that this method includes the following steps：
A, the thick bamboo tube for cutting two bamboo knots of reservation is base-material, and each substrate of the diameter difference within 5mm is classified, and will be divided
The good each group substrate of class carries out following manufacturing procedure respectively；
B, the notch of strip is longitudinally opened up on substrate, will open up each substrate jaggy be placed in softening kettle in boiling it is soft
Change；
C, the substrate after softening is unfolded in press-stretched machine, while expansion, to being opened up on the bamboo surface of tabasheer side
The escape groove parallel with bamboo fibre, each escape groove are equidistantly uniformly distributed；
D, by bamboo knot position transverse direction cutting, bamboo knot position forms the stiffener of strip, and the substrate between adjacent bamboo knot is formed
The splice plate of rectangle；
E, each splice plate is cut, make each splice plate be processed into equal thickness, etc. side lengths rectangular slab；To escape groove into
Row processing, makes the structure that tabasheer side processes saw-toothed positioning protrusion and the locating slot that is adapted to positioning protrusion is alternate；
F, two implantation slots are opened up on splice plate, the implantation slot is vertical with positioning protrusion；
G, each piece of splice plate is compacted by roll squeezer；
H, by the splicing of each splice plate in doubling plate, the tabasheer side face of splice plate, and make the positioning of the splice plate on upper layer
Protrusion is corresponding with the locating slot of the splice plate of lower layer, and institute is buried between the implantation slot of the splice plate of the splice plate and lower layer on upper layer
State stiffener, when splicing smears adhesive glue, forms semifinished sheet；
I, it is needed according to size by the splice plate and stiffener of the splice plate on the extra upper layer in semifinished sheet edge, lower layer
It removes, the processing of this bamboo board is completed after progress surface post-processing.
In a kind of method for processing sheet material of the above-mentioned bamboo wood using after being unfolded as raw material, the two sides up and down of the stiffener
A recess, the bottom surface of the recess face splice plate are respectively provided on face.
In a kind of method for processing sheet material of the above-mentioned bamboo wood using after being unfolded as raw material, the length and spelling of the stiffener
Fishplate bar it is of same size, the stiffener is embedded in the implantation slot of contiguous concatenation plate simultaneously.
In a kind of method for processing sheet material of the above-mentioned bamboo wood using after being unfolded as raw material, the splice plate on upper layer and lower layer are spelled
It is dislocatedly distributed between fishplate bar.
Compared with prior art, the present invention has the following advantages that：
1, by opening up positioning protrusion and locating slot in tabasheer side, by the positioning protrusion and locating slot of teeth shape, make
Intensity between the splice plate on upper layer and the splice plate of lower layer is higher；It is originally used for during reducing stress, bamboo wood being prevented to be unfolded
The escape groove of cracking, is processed to locating slot and positioning protrusion, spliced plate compactness can not only be made to improve, intensity increases
Add, improve the utilization rate of bamboo wood, but also can effectively prevent from misplacing between the splice plate on upper layer and the splice plate of lower layer, makes
Splicing is simpler, and the difficulty in splicing reduces, and precision improves, and the integraty of plate is more preferable.
2, as the surface of plate and bottom surface, bamboo knot position is eliminated, makes the flatness, aesthetics, durability degree of plate
It gets a promotion, during handling plate, because eliminating bamboo knot, difficulty of processing is also reduced, for example the surface treatment such as scabbles
When, be more easier, flatness it is higher, excision relatively small thickness can keep higher straightness, flatness and finish, improve
The utilization rate of plate.
3, bamboo knot has the characteristics that intensity is high, meanwhile, because of its fibre density height, there is also what is easily rebounded to lack after deployment
Point, by opening up implantation slot on splice plate, stiffener made of bamboo knot is made is implanted into the splice plate on upper layer and the spelling of lower layer
In implantation slot between fishplate bar, meanwhile, the direction of stiffener is vertical with the direction of the positioning protrusion on splice plate, i.e., with bamboo wood
Machine direction is vertical, and the integral strength of plate not only can be improved, and makes bend resistance intensity and stretch-proof that plate is horizontal and vertical
Intensity is greatly improved, but also can use the characteristic of stiffener rebound, and stiffener is made to have the function of " reed ",
Make higher against intensity between the positioning protrusion between the splice plate on upper layer and the splice plate of lower layer, compactness is more preferable, to bamboo
Knot is utilized, and is kept the utilization rate of bamboo wood higher, is avoided wasting.
4, the bending rebound of splice plate, by way of the stacked relative between the splice plate on upper layer and the splice plate of lower layer
It avoids, the implantation direction of stiffener carries out the rebound of stiffener in the plane of plate, and utilizes the rebound of stiffener, mentions
The whole splicing intensity of high plate has technical contribution outstanding, and in the flatness of plate, aesthetics for this field
It is upper that there is qualitative leap, while greatly being promoted to having in the utilization rate of bamboo wood.
5, recess is arranged in the two sides up and down of stiffener, on the one hand " can amplify " rebound effect of stiffener, hold that it more
Easily rebound, and can be improved the integral strength of stiffener, keep the buckling strength of stiffener higher.
6, the splice plate of the splice plate on dislocation splicing upper layer and lower layer, dislocation implantation stiffener, makes the integraty of plate more
By force, the intensity of plate and the integrality of plate are more preferable.
Detailed description of the invention
Fig. 1 is the structural schematic diagram of materials thick bamboo tube in this method.
Fig. 2 is the connecting method schematic diagram of each splice plate in this method.
Fig. 3 is the sectional view of splice plate in this method.
Fig. 4 be in this method after board material splice along the sectional view in vertical bamboo fibre direction.
Fig. 5 be in this method in board material splice along the sectional view of parallel bamboo machine direction.
Fig. 6 is the enlarged drawing of part A in Fig. 5.
In figure, 1, base-material；11, notch；2, stiffener；3, splice plate；31, positioning protrusion；32, locating slot；33, it is implanted into
Slot.
Specific embodiment
Following is a specific embodiment of the present invention in conjunction with the accompanying drawings, technical scheme of the present invention will be further described,
However, the present invention is not limited to these examples.
By taking the bamboo of Xianning as an example, take bamboo middle section, using diameter 80 ± 5mm substrate as objective for implementation, carry out as follows
Step：
1, as shown in Figure 1, longitudinally opening up the notch 11 of strip on substrate, each substrate for opening up jagged 11 is placed in soft
Change boiling softening in kettle；
2, the substrate after softening is unfolded in press-stretched machine, while expansion, to being opened up on the bamboo surface of tabasheer side
The escape groove parallel with bamboo fibre, each escape groove are equidistantly uniformly distributed, and layout pitch is in 6mm or so；
3, by bamboo knot position transverse direction cutting, bamboo knot position forms the stiffener 2 of strip, and the substrate between adjacent bamboo knot is formed
The splice plate 3 of rectangle；
4, as shown in Fig. 3, Fig. 4, Fig. 5 and Fig. 6, each splice plate 3 is cut, make each splice plate 3 be processed into equal thickness,
Etc. side lengths rectangular slab；Escape groove is processed, tabasheer side is made to process saw-toothed positioning protrusion 31 and and convex
The alternate structure of the locating slot 32 of 31 adaptations is played, positioning protrusion 31 and locating slot 32 are processed by escape groove, adopted
It is carried out with cutting element；
5, two implantation slots 33, the implantation slot 33 and positioning protrusion 31 as shown in Figure 2 and Figure 6, are opened up on splice plate 3
Vertically, the depth for being implanted into slot 33 is 1~3mm, and width is folded in 15~30mm due to the presence of positioning protrusion 31 and locating slot 32
The depth of corresponding two implantation slot 33 is implanted into the size of slot 33 due to needing gluing in 6~10mm with 2 energy of stiffener after conjunction
Enough being easily inserted is advisable；
6, each piece of splice plate 3 is compacted by roll squeezer；
7, as shown in Fig. 2, by the splicing of each splice plate 3 in doubling plate, the tabasheer side face of splice plate 3, and make upper layer
The locating slot 32 of the splice plate 3 of the positioning protrusion 31 and lower layer of splice plate 3 is corresponding, in the splice plate 3 on upper layer and the splicing of lower layer
Bury the stiffener 2 between the implantation slot 33 of plate, when splicing smears adhesive glue, forms semifinished sheet；It is implanted into the position of slot 33
It sets in 3 quarterline position of splice plate, is not provided at the quarterline of 3 middle of splice plate, other two quarterlines
Place opens up an implantation slot 33 respectively；
8, it is needed according to size by the splice plate 3 on the extra upper layer in semifinished sheet edge, the splice plate 3 of lower layer and reinforcement
Item 2 removes, and the processing of this bamboo board is completed after progress surface post-processing.
Wherein, a recess, the bottom surface of the recess face splice plate 3 are respectively provided on the two sides up and down of stiffener 2.
The length of stiffener 2 is of same size with splice plate 3, and the stiffener 2 is embedded in the plant of contiguous concatenation plate 3 simultaneously
Enter in slot 33.
It is dislocatedly distributed between the splice plate 3 and lower layer's splice plate 3 on upper layer.
The bamboo board according to made from the above method has extraordinary effect, as follows：
By opening up positioning protrusion 31 and locating slot 32 in tabasheer side, pass through the positioning protrusion 31 and locating slot of teeth shape
32, keep the intensity between the splice plate 3 on upper layer and the splice plate 3 of lower layer higher；It is originally used for reducing stress, bamboo wood is prevented to be unfolded
The escape groove to crack in the process is processed to locating slot 32 and positioning protrusion 31, can not only make spliced plate compactness
It improves, intensity increase, improves the utilization rate of bamboo wood, but also can effectively prevent the splice plate 3 on upper layer and the splicing of lower layer
It misplaces between plate 3, keeps splicing simpler, the difficulty in splicing reduces, and precision improves, and the integraty of plate is more
It is good.
As the surface and bottom surface of plate, bamboo knot position is eliminated, obtains the flatness, aesthetics, durability degree of plate
To promotion, during handling plate, because eliminating bamboo knot, difficulty of processing is also reduced, such as when the surface treatment such as scabbling,
Be more easier, flatness it is higher, excision relatively small thickness can keep higher straightness, flatness and finish, improve plate
The utilization rate of material.
Bamboo knot has the characteristics that intensity is high, meanwhile, because of its fibre density height, the shortcomings that there is also easy rebounds after deployment,
By opening up implantation slot 33 on splice plate 3, stiffener 2 made of bamboo knot is made is implanted into splice plate 3 and the lower layer on upper layer
In implantation slot 33 between splice plate 3, meanwhile, the direction of stiffener 2 is vertical with the direction of positioning protrusion 31 on splice plate 3,
It is i.e. vertical with the machine direction of bamboo wood, the integral strength of plate not only can be improved, the bend resistance for keeping plate horizontal and vertical is strong
Degree and tensile strength are greatly improved, but also can use the characteristic of the rebound of stiffener 2, have stiffener 2
The effect of " reed ", make between the positioning protrusion 31 between the splice plate 3 on upper layer and the splice plate 3 of lower layer against intensity more
Height, compactness is more preferable, utilizes to bamboo knot, keeps the utilization rate of bamboo wood higher, avoids wasting.
The bending of splice plate 3 rebounds, and passes through the side of the stacked relative between the splice plate 3 on upper layer and the splice plate 3 of lower layer
Formula avoids, and the implantation direction of stiffener 2 carries out the rebound of stiffener 2 in the plane of plate, and utilizes the anti-of stiffener 2
Bullet, the whole splicing intensity for improving plate have technical contribution outstanding, and in the flatness of plate, beauty for this field
There is qualitative leap on sight degree, while greatly being promoted to having in the utilization rate of bamboo wood.
Recess is arranged in the two sides up and down of stiffener 2, on the one hand " can amplify " rebound effect of stiffener 2, hold that it more
Easily rebound, and can be improved the integral strength of stiffener 2, keep the buckling strength of stiffener 2 higher.
The splice plate 3 on dislocation splicing upper layer and the splice plate 3 of lower layer, dislocation implantation stiffener 2 make the integraty of plate more
By force, the intensity of plate and the integrality of plate are more preferable.
Specific embodiment described herein is only an example for the spirit of the invention.The neck of technology belonging to the present invention
The technical staff in domain can make various modifications or additions to the described embodiments or replace by a similar method
In generation, however, it does not deviate from the spirit of the invention or beyond the scope of the appended claims.
Claims (4)
1. a kind of bamboo wood using after being unfolded is the method for processing sheet material of raw material, which is characterized in that this method includes the following steps：
A, the thick bamboo tube for cutting two bamboo knots of reservation is base-material (1), and each substrate of the diameter difference within 5mm is classified, and will be divided
The good each group substrate of class carries out following manufacturing procedure respectively；
B, each substrate for opening up jagged (11) is placed in boiling in softening kettle by the notch (11) that strip is longitudinally opened up on substrate
Softening；
C, the substrate after softening is unfolded in press-stretched machine, while expansion, to being opened up on the bamboo surface of tabasheer side and bamboo
The escape groove of fibers parallel, each escape groove are equidistantly uniformly distributed；
D, by bamboo knot position transverse direction cutting, bamboo knot position forms the stiffener (2) of strip, and the substrate between adjacent bamboo knot forms square
The splice plate (3) of shape；
E, each splice plate (3) is cut, make each splice plate (3) be processed into equal thickness, etc. side lengths rectangular slab；To escape groove
It is processed, the locating slot (32) for making tabasheer side process saw-toothed positioning protrusion (31) and be adapted to positioning protrusion (31)
Alternate structure；
F, two implantation slots (33) are opened up on splice plate (3), the implantation slot (33) is vertical with positioning protrusion (31)；
G, each piece of splice plate (3) is compacted by roll squeezer；
H, by each splice plate (3) splicing in doubling plate, the tabasheer side face of splice plate (3), and make the splice plate (3) on upper layer
The locating slot (32) of positioning protrusion (31) and the splice plate (3) of lower layer is corresponding, the splice plate in splice plate (3) and lower layer on upper layer
Implantation slot (33) between bury the stiffener (2), when splicing, smears adhesive glue, forms semifinished sheet；
I, it is needed according to size by the splice plate (3) on the extra upper layer in semifinished sheet edge, the splice plate (3) of lower layer and reinforcement
Item (2) removes, and the processing of this bamboo board is completed after progress surface post-processing.
2. a kind of bamboo wood using after being unfolded is the method for processing sheet material of raw material according to claim 1, which is characterized in that described
A recess, the bottom surface of the recess face splice plate (3) are respectively provided on the two sides up and down of stiffener (2).
3. a kind of bamboo wood using after being unfolded according to claim 1 or claim 2 is the method for processing sheet material of raw material, which is characterized in that
The length of the stiffener (2) is of same size with splice plate (3), and the stiffener (2) is embedded in contiguous concatenation plate (3) simultaneously
Implantation slot (33) in.
4. a kind of bamboo wood using after being unfolded according to claim 1 or claim 2 is the method for processing sheet material of raw material, which is characterized in that
It is dislocatedly distributed between the splice plate (3) and lower layer's splice plate (3) on upper layer.