CN108145336A - 一种镀镍钢带焊锡性能的检测方法 - Google Patents
一种镀镍钢带焊锡性能的检测方法 Download PDFInfo
- Publication number
- CN108145336A CN108145336A CN201611111207.1A CN201611111207A CN108145336A CN 108145336 A CN108145336 A CN 108145336A CN 201611111207 A CN201611111207 A CN 201611111207A CN 108145336 A CN108145336 A CN 108145336A
- Authority
- CN
- China
- Prior art keywords
- plated steel
- nickel
- steel strip
- scolding tin
- nickel plated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公布了一种镀镍钢带焊锡性能的检测方法，包括如下步骤：将镀镍钢带裁剪成两片长条型的镍片，然后将两条所述镍片上端固定在夹具上的部分重合，下端分开30度角浸入焊料中，经过3‑5秒后拿出来，最后再通过拉力机检测两片镍片的结合力。本发明的方法可以定量的来检测镀镍钢带焊锡性能，同时也可以考察镍层表面润湿面积，可以检测出一些润湿面积良好，结合力却较差的镀镍钢带，避免使用后带来脱离的风险。
Description
技术领域
本发明涉一种镀镍钢带焊锡性能的检测方法。
背景技术
连续电镀作为电镀行业的一支，以其高的线速度、高产能、低成本逐渐占据了重要的地位，特别是高速电镀装备得到了长足的发展，以日本、美国、德国的先进设备大量被引进。实际应用中镀镍钢带作为连接片使用时，需要进行锡焊，由于镍具有自钝化性能，一旦发生钝化后，镍层表面形成一层氧化膜，会影响到镍层的焊锡性能，目前国家标准中采用浸入法通过表面的润湿面积大小来确定焊锡性能的好坏，经过大量的实验证明并非润湿性好的镀镍钢带其焊锡的结合力就一定好，本发明所述发方法可以定量的来检测镀镍钢带焊锡性能，同时也可以考察镍层表面润湿面积。
发明内容
本发明目的是针对现有技术存在的缺陷提供一种镀镍钢带焊锡性能的检测方法。
本发明为实现上述目的，采用如下技术方案：一种镀镍钢带焊锡性能的检测方法，包括如下步骤：
将镀镍钢带裁剪成两片长条型的镍片，然后将两条所述镍片上端固定在夹具上的部分重合，下端分开30度角浸入焊料中，经过3-5秒后拿出来，最后再通过拉力机检测两片镍片的结合力。
进一步的方案，所述镍片的长度为30-40mm，宽度为2-3mm，厚度为0.1-1.0mm。
进一步的方案，所述焊料的锡含量为63％(质量百分比)，铅含量为37％(质量百分比)。
进一步的方案，所述镍片在浸入焊料前先浸入助焊剂中，然后再用干净的纸吸干多余的助焊剂。
进一步的方案，所述助焊剂为20％(质量白比分)的松香异丙醇溶液。
进一步的方案，所述拉力机具有上下两个夹具，分别固定两片镍片，用于检测焊接再一起的镍片最大承受拉力值。
本发明的有益效果：本发明的方法可以定量的来检测镀镍钢带焊锡性能，同时也可以考察镍层表面润湿面积，可以检测出一些润湿面积良好，结合力却较差的镀镍钢带，避免使用后带来脱离的风险。
附图说明
图1为两片镍片浸入助焊剂和焊料前的结构示意图。
具体实施方式
图1为两片镍片浸入助焊剂和焊料前的结构示意图。
本发明公开了一种镀镍钢带焊锡性能的检测方法，包括如下步骤：
将镀镍钢带裁剪成两片长条型的镍片(由第一镍片1和第二镍片2构成，如图1所示)，然后将两条所述镍片上端固定在夹具上的部分重合，下端分开30度角浸入焊料中，经过3-5秒后拿出来，最后再通过拉力机检测两片镍片的结合力。
进一步的方案是，所述镍片的长度为30-40mm，宽度为2-3mm，厚度为0.1-1.0mm。
进一步的方案是，所述焊料的锡含量为63％(质量百分比)，铅含量为37％(质量百分比)。
进一步的方案是，所述镍片在浸入焊料前先浸入助焊剂中，然后再用干净的纸吸干多余的助焊剂。
进一步的方案是，所述助焊剂为20％(质量白比分)的松香异丙醇溶液。
进一步的方案是，所述拉力机具有上下两个夹具，分别固定两片镍片，用于检测焊接再一起的镍片最大承受拉力值。
考虑浸入和提出过程中人为因素的影响，我们采用电工推杆来自动控制浸入和提出，并通过时间程序控制浸入速度，浸入后的停留时间，提出速度，提出后停留时间，镍片通过夹具固定在电动推杆上。使用拉力机检测焊锡后两镍片的结合力，检测断裂最大拉力值为镍片的焊锡结合力，通过对比结合力的大小来判断锡焊性能好坏。
以上所述仅为本发明的较佳实施例，并不用以限制本发明，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (6)
1.一种镀镍钢带焊锡性能的检测方法，其特征在于，包括如下步骤：
将镀镍钢带裁剪成两片长条型的镍片，然后将两条所述镍片上端固定在夹具上的部分重合，下端分开30度角浸入焊料中，经过3-5秒后拿出来，最后再通过拉力机检测两片镍片的结合力。
2.根据权利要求1所述的镀镍钢带焊锡性能的检测方法，其特征在于，所述镍片的长度为30-40mm，宽度为2-3mm，厚度为0.1-1.0mm。
3.根据权利要求1所述镀镍钢带焊锡性能的检测方法，其特征在于，所述焊料的锡含量为63％(质量百分比)，铅含量为37％(质量百分比)。
4.根据权利要求1所述的镀镍钢带焊锡性能的检测方法，其特征在于，所述镍片在浸入焊料前先浸入助焊剂中，然后再用干净的纸吸干多余的助焊剂。
5.根据权利要求1所述的镀镍钢带焊锡性能的检测方法，其特征在于，所述助焊剂为20％(质量白比分)的松香异丙醇溶液。
6.根据权利要求1所述的镀镍钢带焊锡性能的检测方法，其特征在于，所述拉力机具有上下两个夹具，分别固定两片镍片，用于检测焊接再一起的镍片最大承受拉力值。