CN108078032A - A kind of processing method of mackintosh - Google Patents
A kind of processing method of mackintosh Download PDFInfo
- Publication number
- CN108078032A CN108078032A CN201611048114.9A CN201611048114A CN108078032A CN 108078032 A CN108078032 A CN 108078032A CN 201611048114 A CN201611048114 A CN 201611048114A CN 108078032 A CN108078032 A CN 108078032A
- Authority
- CN
- China
- Prior art keywords
- fabric
- mackintosh
- web process
- processing method
- processing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of processing method of mackintosh, and including web process, inner lining process, operating procedure is as follows：The web process concrete operations are as follows：1) dye：A) pre-treatment first is carried out to fabric：When cold dome 10 is small；B) by step 1), treated that fabric first cleans in overflow machine；Then operated into dyestuff, control temperature gradually heats colouring, then carries out to color, reduction cleaning；2) polytetrafluoroethylene (PTFE) is handled：By step 1), treated that fabric goes out cylinder is carried out dehydrating, first with clear water drying and shaping, in sink addition polymerization tetrafluoroethene auxiliary agent water-proofing treatment, and high-temperature shaping again；3) TPU pad pastings：A) calendering operation is carried out to fabric face with calender；B) glue and thermoplastic polyurethane film make fabric face and film compound on compounding machine；After inner lining process is web process processing, grid cloth is set in the inside of fabric.The waterproof effect of mackintosh is greatly improved, can be further generalized in practical applications.
Description
Technical field
The present invention relates to raincoat manufacture fields, and in particular to a kind of processing method of mackintosh.
Background technology
It is industrialized with present, information-based development, while living standard is promoted, the pursuit for quality of the life
It is higher and higher.
Raincoat is the clothes that keeps off the rain made of waterproof cloth.The waterproof cloth that raincoat is applicable in has adhesive plaster, oilcloth and the plastics thin
Film etc..Modern raincoat waterproof cloth focuses on gas permeability, common such as special nylon and Gore-Tex.Vapor-permeable type raincoat is beneficial to
People's aqueous vapor damp and hot when wearing rain-proof sheds out of raincoat, increases comfort level.
It needs for a long time in the personnel to work in the rain such as courier, sanitation worker, in the rain repairing person, harbour, harbour, container
The Field Force such as company, shipyard, sea-freight also usually need to wear raincoat to keep out wind and rain, common at present：One kind is to use
PVC (chemical names：Polyvinyl chloride, non-degradable are harmful to environment) plastic cement sewing rain cape or raincoat, covering be not easy for sternly it is wet
Body, covers too tight just very sultry, airtight, not environmentally, seeps water after even more easily being pullled at thread；Another kind is terylene face
Material+PVC coatings, similary to cover too tight just very sultry, airtight, not environmentally, thread is also to seep water after easily pullling.
In especially, in the environment of big, heavy rain, cause after raincoat infiltration：It is completely wet, very uncomfortable, it is big under outside
It is generally existing to spot inside rain, raincoat；Comfort is poor, and body is heavy during operation, work efficiency drop, exist safety and
Healthy hidden danger.
The content of the invention
In view of the deficiencies of the prior art, the present invention provides a kind of processing methods of mackintosh so that mackintosh
Waterproof effect and comfort level are further promoted.
In order to achieve the above object, the present invention is achieved by the following technical programs：
A kind of processing method of mackintosh, including web process, inner lining process, operating procedure is as follows：
The web process concrete operations are as follows：
1) dye：A) pre-treatment first is carried out to fabric：When cold dome (liquid caustic soda processing) 10 is small so that fabric processing rear face is soft
It is soft, gloss is full, cylinder difference is small during dyeing；
B) by step 1) treated fabric first cleans in overflow machine 1 it is small when；Then into dyestuff operate, control temperature from
100 DEG C -130 DEG C when gradually heating colouring 4-5 is small, then carry out to color, when reduction cleaning 1 is small, this dyeing can be to greatest extent
Partially middle difference is avoided, left and right difference is poor end to end to wait the problem of being susceptible in dyeing；
2) polytetrafluoroethylene (PTFE) is handled：By step 1), treated that fabric goes out cylinder is carried out dehydrating, first with 160 DEG C of clear water-
180 DEG C of drying and shapings once, in sink addition polymerization tetrafluoroethene auxiliary agent water-proofing treatment, 190 DEG C of sizings of high temperature again；
3) (before processing examines painting cloth to TPU pad pastings, examines to ensure quality and the reduction of finished product again before doing down one of technique
Waste)：A) calendering operation is carried out to fabric face with calender, the binding face that cloth is allowed on the premise of cloth color is not influenced is more flat
It is whole, glue can preferably be played a role, it is ensured that the stabilization of hydraulic pressure and the stabilization of washing after fitting；
B) glue and thermoplasticity polyurethane film make fabric face and film compound on compounding machine, post and are placed on A cabinet frames
On, wait factory's self-test in second day；
After the inner lining process is web process processing, grid cloth is set in the inside of fabric, it is personal, it breathes freely, increases
Wearing comfort.
Preferably, fabric carries out hydraulic pressure, moisture-inhibiting, washing fastness detection after web process processing.
Preferably, the micropore that fabric occurs after web process processing, using TPU adhesive tape, passes through high frequency equipment
It is pressed, it is ensured that complete leakproof.Guarantee in the rain for a long time without the comfortable work of infiltration.
Preferably, the temperature for calender being controlled in the step 3) of the web process is 130 DEG C, 50 tons of pressure, speed per hour
30 yards.
Preferably, treated that fabric outer surface carries out stickup reflecting strips for the web process, adds security warning,
Improve the security in the course of work.
Preferably, the fabric selected as terylene or Oxford cloth.
The present invention provides a kind of processing methods of mackintosh, first carry out web process processing, and cloth cover is soft, bright and clean,
Full, cylinder difference is small during dyeing, then into dyestuff from when 100 ° -130 ° gradually heating colouring 4-5 is small, then carries out to color, reduction is clear
Wash 1 it is small when, strengthen color fastness, go out cylinder and be carried out dehydrating, first with 160 ° of -180 ° of drying and shapings of clear water once.In sink plus spy
Fluorine dragon auxiliary agent water-proofing treatment, again 190 ° of high temperature sizing improve the waterproof effect of cloth cover.
The present invention can produce the best raincoat of water resistance highest, gas permeability, be improved well in work in the rain
Environment improves comfort level and work efficiency, reduces security risk.
Specific embodiment
To make the purpose, technical scheme and advantage of the embodiment of the present invention clearer, below in conjunction with the implementation of the present invention
Example, is clearly and completely described the technical solution in the embodiment of the present invention, it is clear that described embodiment is the present invention
Part of the embodiment, instead of all the embodiments.Based on the embodiments of the present invention, those of ordinary skill in the art are not having
All other embodiments obtained under the premise of creative work are made, belong to the scope of protection of the invention.
Embodiment 1：
The present embodiment provides a kind of processing methods of mackintosh, and including web process, inner lining process, operating procedure is as follows
It is shown：
Web process concrete operations are as follows：
1) dye：A) pre-treatment first is carried out to fabric：When cold dome (liquid caustic soda processing) 10 is small so that fabric processing rear face is soft
It is soft, gloss is full, cylinder difference is small during dyeing；
B) by step 1) treated fabric first cleans in overflow machine 1 it is small when；Then into dyestuff operate, control temperature from
100 DEG C -130 DEG C when gradually heating colouring 4-5 is small, then carry out to color, when reduction cleaning 1 is small, this dyeing can be to greatest extent
Partially middle difference is avoided, left and right difference is poor end to end to wait the problem of being susceptible in dyeing；
2) polytetrafluoroethylene (PTFE) is handled：By step 1), treated that fabric goes out cylinder is carried out dehydrating, first with 160 DEG C of clear water-
180 DEG C of drying and shapings once, in sink addition polymerization tetrafluoroethene auxiliary agent water-proofing treatment, 190 DEG C of sizings of high temperature again；
3) (before processing examines painting cloth to TPU pad pastings, examines to ensure quality and the reduction of finished product again before doing down one of technique
Waste)：A) calendering operation is carried out to fabric face with calender, the binding face that cloth is allowed on the premise of cloth color is not influenced is more flat
It is whole, glue can preferably be played a role, it is ensured that the stabilization of hydraulic pressure and the stabilization of washing after fitting；
B) glue and thermoplasticity polyurethane film make fabric face and film compound on compounding machine, post and are placed on A cabinet frames
On, wait factory's self-test in second day；
After inner lining process is web process processing, grid cloth is set in the inside of fabric, it is personal, it breathes freely, increases dress and relax
Appropriateness.
Fabric carries out hydraulic pressure, moisture-inhibiting, washing fastness detection after web process processing.
The micropore that fabric occurs after web process processing, using TPU adhesive tape, is pressed by high frequency equipment, it is ensured that
Complete leakproof.Guarantee in the rain for a long time without the comfortable work of infiltration.
The temperature that calender is controlled in the step 3) of web process is 130 DEG C, 50 tons of pressure, 30 yards of speed per hour.
Treated that fabric outer surface carries out stickup reflecting strips for web process.
Fabric selected as terylene or Oxford cloth.
Embodiment 2：
The present embodiment provides a kind of processing methods of mackintosh, and including web process, inner lining process, operating procedure is as follows
It is shown：
Web process concrete operations are as follows：
1) dye：A) pre-treatment first is carried out to fabric：When cold dome (liquid caustic soda processing) 10 is small so that fabric processing rear face is soft
It is soft, gloss is full, cylinder difference is small during dyeing；
B) by step 1) treated fabric first cleans in overflow machine 1 it is small when；Then into dyestuff operate, control temperature from
100 DEG C -130 DEG C when gradually heating colouring 4-5 is small, then carry out to color, when reduction cleaning 1 is small, this dyeing can be to greatest extent
Partially middle difference is avoided, left and right difference is poor end to end to wait the problem of being susceptible in dyeing；
2) polytetrafluoroethylene (PTFE) is handled：By step 1), treated that fabric goes out cylinder is carried out dehydrating, first with 160 DEG C of clear water-
180 DEG C of drying and shapings once, in sink addition polymerization tetrafluoroethene auxiliary agent water-proofing treatment, 190 DEG C of sizings of high temperature again；
3) (before processing examines painting cloth to TPU pad pastings, examines to ensure quality and the reduction of finished product again before doing down one of technique
Waste)：A) calendering operation is carried out to fabric face with calender, the binding face that cloth is allowed on the premise of cloth color is not influenced is more flat
It is whole, glue can preferably be played a role, it is ensured that the stabilization of hydraulic pressure and the stabilization of washing after fitting；
B) glue and thermoplasticity polyurethane film make fabric face and film compound on compounding machine, post and are placed on A cabinet frames
On, wait factory's self-test in second day；
After inner lining process is web process processing, grid cloth is set in the inside of fabric, it is personal, it breathes freely, increases dress and relax
Appropriateness.
Fabric carries out hydraulic pressure, moisture-inhibiting, washing fastness detection after web process processing.
The micropore that fabric occurs after web process processing, using TPU adhesive tape, is pressed by high frequency equipment, it is ensured that
Complete leakproof.Guarantee in the rain for a long time without the comfortable work of infiltration.
Treated that fabric outer surface carries out stickup reflecting strips for web process.
Embodiment 3：
The present embodiment provides a kind of processing methods of mackintosh, and including web process, inner lining process, operating procedure is as follows
It is shown：
Web process concrete operations are as follows：
1) dye：A) pre-treatment first is carried out to fabric：When cold dome (liquid caustic soda processing) 10 is small so that fabric processing rear face is soft
It is soft, gloss is full, cylinder difference is small during dyeing；
B) by step 1) treated fabric first cleans in overflow machine 1 it is small when；Then into dyestuff operate, control temperature from
100 DEG C -130 DEG C when gradually heating colouring 4-5 is small, then carry out to color, when reduction cleaning 1 is small, this dyeing can be to greatest extent
Partially middle difference is avoided, left and right difference is poor end to end to wait the problem of being susceptible in dyeing；
2) polytetrafluoroethylene (PTFE) is handled：By step 1), treated that fabric goes out cylinder is carried out dehydrating, first with 160 DEG C of clear water-
180 DEG C of drying and shapings once, in sink addition polymerization tetrafluoroethene auxiliary agent water-proofing treatment, 190 DEG C of sizings of high temperature again；
3) (before processing examines painting cloth to TPU pad pastings, examines to ensure quality and the reduction of finished product again before doing down one of technique
Waste)：A) calendering operation is carried out to fabric face with calender, the binding face that cloth is allowed on the premise of cloth color is not influenced is more flat
It is whole, glue can preferably be played a role, it is ensured that the stabilization of hydraulic pressure and the stabilization of washing after fitting；
B) glue and thermoplasticity polyurethane film make fabric face and film compound on compounding machine, post and are placed on A cabinet frames
On, wait factory's self-test in second day；
After inner lining process is web process processing, grid cloth is set in the inside of fabric, it is personal, it breathes freely, increases dress and relax
Appropriateness.
The above embodiments are merely illustrative of the technical solutions of the present invention, rather than its limitations；Although with reference to the foregoing embodiments
The present invention is described in detail, it will be understood by those of ordinary skill in the art that：It still can be to foregoing each implementation
Technical solution recorded in example modifies or carries out equivalent substitution to which part technical characteristic；And these modification or
It replaces, the essence of appropriate technical solution is not made to depart from the spirit and scope of various embodiments of the present invention technical solution.
Claims (6)
- A kind of 1. processing method of mackintosh, including web process, inner lining process, which is characterized in that the following institute of operating procedure Show：The web process concrete operations are as follows：1) dye：A) pre-treatment first is carried out to fabric：When cold dome (liquid caustic soda processing) 10 is small；B) by step 1) treated fabric first cleans in overflow machine 1 it is small when；Then operated into dyestuff, control temperature from 100 DEG C -130 DEG C when gradually heating colouring 4-5 is small, then carry out to color, when reduction cleaning 1 is small；2) polytetrafluoroethylene (PTFE) is handled：By step 1), treated that fabric goes out cylinder is carried out dehydrating, first with 160 DEG C -180 DEG C of clear water Drying and shaping once, in sink addition polymerization tetrafluoroethene auxiliary agent water-proofing treatment, 190 DEG C of sizings of high temperature again；3) TPU pad pastings：A) calendering operation is carried out to fabric face with calender；B) glue and thermoplasticity polyurethane film make fabric face and film compound on compounding machine；After the inner lining process is web process processing, grid cloth is set in the inside of fabric.
- 2. the processing method of mackintosh as described in claim 1, which is characterized in that fabric after the web process processing Carry out hydraulic pressure, moisture-inhibiting, washing fastness detection.
- 3. the processing method of mackintosh as claimed in claim 2, which is characterized in that fabric after the web process processing The micropore of appearance using TPU adhesive tape, is pressed by high frequency equipment.
- 4. the processing method of mackintosh as described in claim 1, which is characterized in that in the step 3) of the web process The temperature for controlling calender is 130 DEG C, 50 tons of pressure, 30 yards of speed per hour.
- 5. the processing method of mackintosh as described in claim 1, which is characterized in that the web process treated base Cloth outer surface carries out stickup reflecting strips.
- 6. the processing method of mackintosh as described in claim 1, which is characterized in that the fabric selected as terylene or ox Tianjin cloth.