CN108017816A - 环保材料及使用该环保材料所制成的窗帘叶片 - Google Patents
环保材料及使用该环保材料所制成的窗帘叶片 Download PDFInfo
- Publication number
- CN108017816A CN108017816A CN201610954425.5A CN201610954425A CN108017816A CN 108017816 A CN108017816 A CN 108017816A CN 201610954425 A CN201610954425 A CN 201610954425A CN 108017816 A CN108017816 A CN 108017816A
- Authority
- CN
- China
- Prior art keywords
- density polyethylene
- environment
- polypropylene
- polyethylene
- polyolefin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种环保材料及使用该环保材料所制成的窗帘叶片，该环保材料包含60至80wt％的无机矿盐母粒、15至35wt％的聚合单体的主链碳数为二或三的聚烯烃及5至10wt％的助剂。无机矿盐母粒包含碳酸钙及聚乙烯或聚丙烯，其中碳酸钙与聚乙烯或聚丙烯的重量比为8比2。聚烯烃为线性低密度聚乙烯、低密度聚乙烯、中密度聚乙烯、高密度聚乙烯或聚丙烯。助剂为接枝弹性体POE‑MA或PE‑MA。借此，该环保材料所制作的窗帘叶片能具有窗帘所需要的机械性质，且同时兼具低成本及免聚氯乙烯等特点。
Description
技术领域
本发明是关于一种环保材料，特别是关于一种适于制作窗帘叶片的环保材料。
背景技术
窗帘一般使用于建筑物门窗内部，以框架或轨道架设或吊置于窗户旁，用于遮挡直接穿透的光线，提供避光以及保护隐私的使用功能。常见的窗帘除布幕、布帘式的窗帘外，也有直立式或横式的百叶窗或片帘的窗帘，可提供消费者不同的选择。
传统横式或直立式窗连叶片的制作有采用实木者，可以提供良好的遮光及隔热效果，然而，在现今林业资源渐趋匮乏的情形下，不仅木料来源逐渐减少，造成成本上升，亦常有破坏林地与生态环境的争议。
在传统实木窗帘叶片之外，也有业者提供采用塑料制作的窗帘叶片，作为窗帘叶片的另一选项。然而，塑料制的窗帘叶片(如直立式叶片)一般采用聚氯乙烯制作，经消费者使用后若未妥善回收，容易被弃置混合于一般垃圾中，而于燃烧时产生戴奥辛，同样有容易造成地球环境危害的问题。
中国台湾专利TW 379272揭示一种环保纸的制造方法，其是由无机矿粉、聚乙烯及助剂作为原料制得，其虽采用对环境较为友善的原料，但因韧度较低，并不适于作为窗帘叶片使用。
因此，在符合窗帘叶片使用情境所需材料韧性或耐冲击力的前提下，能兼具低环境公害及成本可接受的材料，仍为窗帘生产业界及消费者所致力追寻。
发明内容
有鉴于此，本发明的主要目的在于提供一种适于制作窗帘叶片的材料，提供窗帘生产业界及消费者作为在木材及聚氯乙烯之外的另一选择。
本发明的目的也在于，希望减低因窗帘材料所造成的环境影响。
本发明的目的也在于，希望制作窗帘的材料具有可控制的或较低的成本。
为了实现上述及其他目的，本发明提供一种环保材料，其中包含60至80wt％的无机矿盐母粒、15至35wt％的聚合单体的主链碳数为二或三的聚烯烃及5至10wt％的助剂；所述无机矿盐母粒包含碳酸钙及聚乙烯，其中碳酸钙与聚乙烯的重量比为8比2；所述聚烯烃为线性低密度聚乙烯、低密度聚乙烯、中密度聚乙烯、高密度聚乙烯或聚丙烯；所述助剂为接枝弹性体POE-MA或PE-MA。
为了实现上述及其他目的，本发明还提供一种环保材料，其中包含80wt％的无机矿盐母粒及20wt％之聚合单体的主链碳数为二或三的聚烯烃；所述无机矿盐母粒包含碳酸钙及聚乙烯，其中碳酸钙与聚乙烯的重量比为8比2；所述聚烯烃为线性低密度聚乙烯、低密度聚乙烯、中密度聚乙烯、高密度聚乙烯或聚丙烯。
为了实现上述及其他目的，本发明还提供一种环保材料，是由60至80wt％的无机矿盐母粒、15至35wt％的聚合单体的主链碳数为二或三的聚烯烃及5至10wt％的助剂所组成；所述无机矿盐母粒包含碳酸钙及聚乙烯，其中碳酸钙与聚乙烯的重量比为8比2；所述聚烯烃为线性低密度聚乙烯、低密度聚乙烯、中密度聚乙烯、高密度聚乙烯或聚丙烯；所述助剂为POE-MA或PE-MA。
为了实现上述及其他目的，本发明还提供一种窗帘叶片，是以上述的环保材料所制成。
借由上述设计，使用本发明的环保材料所制作的窗帘叶片可以排除聚氯乙烯的使用，可避免或减少戴奥辛所带来的环境问题，同时，环保材料中含有相当程度的碳酸钙，属低成本且容易取得的材料，有助于窗帘相关业者控制生产成本，并且兼具所需的机械性质。
附图说明
图1为本发明环保材料所制成的窗帘叶片的立体示意图。
【附图标记说明】
窗帘叶片 1
拉绳 2
轨道 3
具体实施方式
为使本发明的目的、技术方案和优点更加清楚明白，以下结合具体实施例，并参照附图，对本发明作进一步的详细说明。
本发明提供一种环保材料，可以制作为片状，而可供使用于制作窗帘叶片。环保材料所适于制作的窗帘叶片，可以是片帘所使用的窗帘叶片，或直立式或横式的百叶窗，例如图1所示的直立式百叶窗，利用拉绳2将窗帘叶片1连接于轨道3，供使用者利用拉绳控制窗帘叶片1的开启位置与角度。此外，依生产者的设计或依消费者的需求，窗帘叶片也可能适用于其他种类的窗帘。除此之外，环保材料也可以制作为块状或板状，而可以用于制作地砖、窗框、饰片、折叠帘或其他适当场合。
本发明的环保材料主要包括60至80wt％(重量百分比)的无机矿盐母粒、15至35wt％的聚烯烃以及可能添加的5至10wt％的助剂。
无机矿盐母粒为重量份8的碳酸钙及重量份2的聚乙烯(PE)的混合物，混合后在常温下呈固体颗粒状，无机矿盐母粒中碳酸钙与聚乙烯的重量比为8比2，在无其他添加物的情形下无机矿盐母粒为80wt％的碳酸钙及20wt％的聚乙烯，惟其中可能混有少量杂质。
主链为二或三个碳素的聚烯烃为线性低密度聚乙烯(LLDPE)、低密度聚乙烯(LDPE)、中密度聚乙烯(MDPE)、高密度聚乙烯(HDPE)或聚丙烯(PP)，其中以线性低密度聚乙烯、高密度聚乙烯与聚丙烯较常用，又以线性低密度聚乙烯为较佳。
助剂为马来酸酐接枝聚烯烃(maleic anhydride-grafted polyolefinelastomer，POE-MA)或马来酸酐接枝聚烯烃聚乙烯(maleic anhydride-graftedpolyethylene，PE-MA)，其中以POE-MA为较佳。
除上述成分外，本发明的环保材料也可依适用场合的需求，在不显著影响材料物理性质与化学性质的情形下，少量添加其他功能助剂，例如添加漂白剂、增色剂或色素可改变窗帘叶片的颜色，添加抗氧化剂或抗紫外线剂可提高窗帘叶片的使用年限，添加紫外线吸收剂可在窗帘叶片附加提供降低室内紫外线的功能，除此之外亦可能添加滑剂、弹性助剂或抗静电剂。
前述环保材料的成分可以使用混炼机在混炼后造粒备用，或以螺杆押出机混炼后直接押出成片状备用，供后续进一步加工制作为所需的造型而成为窗帘叶片或其他制成品。
为确定上述环保材料可符合窗帘叶片的使用需求，本申请的发明人进一步选用数个具体实施例，制成片状的环保材料后测试其物理性质。其测试步骤系先以双螺杆混炼造粒机于170℃至210℃进行混炼造粒，随后以热押成型机于180℃热押成型，并裁切为90mm×12mm×1mm的受测样品，于室温环境下以耐冲击测试器测试受测样品，作为各种比例成分的环保材料机械强度是否适于制作窗帘叶片的参考依据。
受测试的具体实施例及比较例成分以及测试结果，请参考下表1:
表1:受测样品的成分及测试结果比较表
测试结果中，为符合窗帘的一般使用情形，经验证以耐冲击7磅以上为适于制作直立帘窗帘叶片的主要评量基准，可以发现，以上实施例均可通过耐冲击测试，相对的，在比较例1与2中，无机矿盐母粒所占比例较高，其耐冲击测试结果均远低于7磅，可以判断上述比较例均不适于作为窗帘叶片的材料。
此外，由实施例3与4的比较可以发现，采用线性低密度聚乙烯与POE-MA相较于采用高密度聚乙烯与PE-MA可以获得显著优异的耐冲击性质；
由实施例4与5比较以及实施例6与7比较则可以发现，在环保材料中的聚烯烃采用聚丙烯及线性低密度聚乙烯可以获得一定程度的较佳抗冲击性能。
若以实施例1及3两者相较，增加无机矿盐母粒含量，减少PE含量，将降低耐冲击力，由9磅降低到7磅。
若以实施例1及2两者相较，增加接枝弹性体PE-MA含量，可提升耐冲击力，由7磅提升到9磅。
若以实施例7及实施例8两者相较，添加接枝弹性体POE-MA，将提升耐冲击力，由12磅提升到18磅。
若以实施例7及实施例9两者相较，比较添加未接枝弹性体POE及接枝弹性体POE-MA，虽然仍以添加接枝弹性体POE-MA者的表现较佳，但实施例9仍是比实施例8未添加助剂者耐冲击力佳，符合窗帘耐冲击力的标准要求。
若以比较例1及比较例2两者相较，当无机矿盐母粒含量增加到90％，即使添加接枝弹性体POE-MA，提升耐冲击力效果有限，仅由2磅提升到3磅。
在以上说明的测试中，聚烯烃虽然仅测试线性低密度聚乙烯、高密度聚乙烯与聚丙烯，但聚烯烃中的低密度聚乙烯及中密度聚乙烯也具有与高密度聚乙烯相似的材料性质，在合理推测下，在聚烯烃使用低密度聚乙烯及中密度聚乙烯也能使环保材料的材料特性符合制作窗帘叶片的需求。
基于以上结果，可以发现本发明的环保材料确实具有适于制作窗帘的机械性质，不需使用聚氯乙烯而无燃烧排放戴奥辛的环保问题，且成分中含有相当比例的碳酸钙，有助于控制或降低材料成本，当属业界与市场所欢迎的材料。
以上所述的具体实施例，对本发明的目的、技术方案和有益效果进行了进一步详细说明，应理解的是，以上所述仅为本发明的具体实施例而已，并不用于限制本发明，凡在本发明的精神和原则之内，所做的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (10)
1.一种环保材料，包括：
60至80wt％的无机矿盐母粒，所述无机矿盐母粒包含碳酸钙及聚乙烯或聚丙烯，其中碳酸钙与聚乙烯或聚丙烯的重量比为8比2；
15至35wt％的聚合单体的主链碳数为二或三的聚烯烃，所述聚烯烃为线性低密度聚乙烯、低密度聚乙烯、中密度聚乙烯、高密度聚乙烯或聚丙烯；
5至10wt％的助剂，所述助剂为POE、接枝弹性体POE-MA或PE-MA。
2.一种环保材料，包括：
80wt％的无机矿盐母粒，所述无机矿盐母粒包含碳酸钙及聚乙烯或聚丙烯，其中碳酸钙与聚乙烯或聚丙烯的重量比为8比2；
20wt％的聚合单体的主链碳数为二或三的聚烯烃，所述聚烯烃为线性低密度聚乙烯、低密度聚乙烯、中密度聚乙烯、高密度聚乙烯或聚丙烯。
3.一种环保材料，由以下成分所组成：
60至80wt％的无机矿盐母粒，所述无机矿盐母粒包含碳酸钙及聚乙烯或聚丙烯，其中碳酸钙与聚乙烯或聚丙烯的重量比为8比2；
15至35wt％之聚合单体的主链碳数为二或三的聚烯烃，所述聚烯烃为线性低密度聚乙烯、低密度聚乙烯、中密度聚乙烯、高密度聚乙烯或聚丙烯；
5至10wt％的助剂，所述助剂为POE、接枝弹性体POE-MA或PE-MA。
4.根据权利要求1～3任一项所述的环保材料，其中所述聚烯烃为线性低密度聚乙烯、高密度聚乙烯或聚丙烯。
5.根据权利要求1～3任一项所述的环保材料，其中所述聚烯烃为线性低密度聚乙烯或聚丙烯。
6.根据权利要求1或3所述的环保材料，其中所述的助剂为接枝弹性体POE-MA。
7.一种窗帘叶片，使用如权利要求1～3任一项所述的环保材料所制成。
8.根据权利要求7所述的窗帘叶片，其中所述聚烯烃为线性低密度聚乙烯、高密度聚乙烯或聚丙烯。
9.根据权利要求7所述的窗帘叶片，其中所述聚烯烃为线性低密度聚乙烯或聚丙烯。
10.根据权利要求7所述的窗帘叶片，其中所述的助剂为接枝弹性体POE-MA。