CN107814987A - 一种涉水环保防锈丁腈橡胶材料 - Google Patents
一种涉水环保防锈丁腈橡胶材料 Download PDFInfo
- Publication number
- CN107814987A CN107814987A CN201711103458.XA CN201711103458A CN107814987A CN 107814987 A CN107814987 A CN 107814987A CN 201711103458 A CN201711103458 A CN 201711103458A CN 107814987 A CN107814987 A CN 107814987A
- Authority
- CN
- China
- Prior art keywords
- antirust
- environment
- carbon black
- paddled
- nitrile rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种涉水环保防锈丁腈橡胶材料，包括以下重量份的各组分：丁腈胶100‑150、防锈炭黑80‑100、环保增塑剂TP‑95 15‑30、轻质碳酸钙20‑35、石蜡1‑2、氧化锌5‑6、硬脂酸1.5‑2.8、硫磺S 1.5‑1.8、防老剂264 1‑2、促进剂CBS 1.5‑2.2、促进剂TT 1.5‑2。
Description
技术领域
本发明涉及涉水丁腈橡胶技术领域，尤其涉及一种涉水环保防锈丁腈橡胶材料。
背景技术
丁腈橡胶是由丁二烯和丙烯腈经乳液聚合法制得的，简称NBR，丁腈橡胶主要采用低温乳液聚合法生产，耐油性极好，耐磨性较高，耐热性较好，粘接力强，常被用做管道的柔性接口密封，施工方便，污水的收集、输送更加安全。在涉水设备中，橡胶制品经常需要和金属管道一起使用作为密封垫片、橡胶管直接连在金属管口上将金属零部件镶嵌在橡胶上等等。普通橡胶制品在和金属制品接触或一起组合时，橡胶对金属没有防锈保护作用，在涉水环境中受时间、微生物、污染物等因素的共同影响，金属材料不可避免的容易锈蚀，而橡胶之中的添加剂或助剂对金属还有一定的腐蚀性。这些情况导致金属件与橡胶的接头处出现锈蚀，影响密封性能，经常因为锈蚀而报废、更换，造成了一定的经济损失，同时还会污染水资源。
中国专利201110419962.7公开了一种防锈橡胶及其制作方法，主要通过在生胶体系中添加防锈剂达到防锈效果，但是使用的防锈剂主要为气相缓蚀剂，在水环境中容易析出，不适合用于涉水设备中，且亚硝酸钠、苯甲酸钠等物质本身也是一种污染物，不够环保。
发明内容
本发明为了弥补已有技术的缺陷，提供一种涉水环保防锈丁腈橡胶材料。
本发明是通过以下技术方案实现的：
一种涉水环保防锈丁腈橡胶材料，包括以下重量份的各组分：丁腈胶100-150、防锈炭黑80-100、环保增塑剂TP-95 15-30、轻质碳酸钙20-35、石蜡1-2、氧化锌5-6、硬脂酸1.5-2.8、硫磺S 1.5-1.8、防老剂264 1-2、促进剂CBS1.5-2.2、促进剂TT 1.5-2。
所述的一种涉水环保防锈丁腈橡胶材料，所述的防锈炭黑是由羟基化炭黑与含有羧基的环保防锈剂按照1:(0.001-0.01)的重量比反应得到的。
所述的羟基化炭黑是将炭黑经强酸羧化处理5-10h，然后在羧化后的炭黑表面接枝硅烷偶联剂，再将接枝硅烷偶联剂的炭黑投入醇溶液中水解，即得到羟基化的炭黑。
所述的炭黑优选N550炭黑、N770炭黑中的一种或一种以上。
所述的含有羧基的环保防锈剂为有机羧酸醇胺盐、羧基苯丙三氮唑、3-苯甲酰基-α-D-呋喃葡萄糖、3-苄基-α-D-呋喃葡萄糖、3-乙酰基-α-D-呋喃葡萄糖、3-十二酰基-α-D-呋喃葡萄糖、二羧基油酸酰胺中的一种。
所述的羟基化炭黑与含有羧基的环保防锈剂反应具体条件为：以四氢呋喃或水作为反应介质，在50-80℃条件下搅拌反应2-5h，反应结束后所得物料水洗3-5次，热风干燥后过筛。
本发明通过将防锈剂用炭黑包覆的方法将防锈剂引入到丁腈橡胶体系中，选用的防锈剂为羧基化的环保防锈剂，水溶性或油溶性的防锈剂均可，较之传统的防锈剂直接添加方式的优点在于：利用改性处理后炭黑表面的羟基与防锈剂中的羧基反应，将炭黑与防锈剂的牢固结合，提高了防锈剂与橡胶材料的相容性，获得了更为长效的防锈效果，有效的抑制了防锈剂的析出，对橡胶材料本身无不良影响，有效的抑制了结合处金属材料的腐蚀，延长了金属材料的使用寿命，减少了金属制品的维护成本，保证了涉水设备的使用性能。
具体实施方式
一种涉水环保防锈丁腈橡胶材料，包括以下重量份的各组分：丁腈胶100、防锈炭黑80、环保增塑剂TP-95 20、轻质碳酸钙20、石蜡1、氧化锌5、硬脂酸1.5、硫磺S 1.5、防老剂264 1、促进剂CBS 1.5、促进剂TT 1.5。
其中防锈炭黑是由羟基化炭黑与羧基苯丙三氮唑按照1:0.001的重量比反应得到的。
所述的羟基化炭黑是将炭黑经强酸羧化处理5h，然后在羧化后的炭黑表面接枝硅烷偶联剂，再将接枝硅烷偶联剂的炭黑投入醇溶液中水解，即得到羟基化的炭黑，其中炭黑为N550炭黑和N770炭黑按照1:1.5的重量比配制而成。
所述的羟基化炭黑与羧基苯丙三氮唑反应具体条件为：以四氢呋喃作为反应介质，在50℃条件下搅拌反应2h，反应结束后所得物料水洗3次，热风干燥后过筛。
将制得的材料按相应的国家标准进行各项性能测试，实验数据见表1：
表1
Claims (6)
1.一种涉水环保防锈丁腈橡胶材料，其特征在于，包括以下重量份的各组分：丁腈胶100-150、防锈炭黑80-100、环保增塑剂TP-95 15-30、轻质碳酸钙20-35、石蜡1-2、氧化锌5-6、硬脂酸1.5-2.8、硫磺S 1.5-1.8、防老剂264 1-2、促进剂CBS 1.5-2.2、促进剂TT 1.5-2。
2.如权利要求1所述的一种涉水环保防锈丁腈橡胶材料，其特征在于，所述的防锈炭黑是由羟基化炭黑与含有羧基的环保防锈剂按照1:（0.001-0.01）的重量比反应得到的。
3.如权利要求2所述的一种涉水环保防锈丁腈橡胶材料，其特征在于，所述的羟基化炭黑是将炭黑经强酸羧化处理5-10h，然后在羧化后的炭黑表面接枝硅烷偶联剂，再将接枝硅烷偶联剂的炭黑投入醇溶液中水解，即得到羟基化的炭黑。
4.如权利要求3所述的一种涉水环保防锈丁腈橡胶材料，其特征在于，所述的炭黑优选N550炭黑、N770炭黑中的一种或一种以上。
5.如权利要求2所述的一种涉水环保防锈丁腈橡胶材料，其特征在于，所述的含有羧基的环保防锈剂为有机羧酸醇胺盐、羧基苯丙三氮唑、3-苯甲酰基-α-D-呋喃葡萄糖、3-苄基-α-D-呋喃葡萄糖、3-乙酰基-α-D-呋喃葡萄糖、3-十二酰基-α-D-呋喃葡萄糖、二羧基油酸酰胺中的一种。
6.如权利要求2所述的一种涉水环保防锈丁腈橡胶材料，其特征在于，所述的羟基化炭黑与含有羧基的环保防锈剂反应具体条件为：以四氢呋喃或水作为反应介质，在50-80℃条件下搅拌反应2-5h，反应结束后所得物料水洗3-5次，热风干燥后过筛。