CN107801523B - 生态覆盖卷制造方法 - Google Patents

生态覆盖卷制造方法 Download PDF

Info

Publication number
CN107801523B
CN107801523B CN201710819272.8A CN201710819272A CN107801523B CN 107801523 B CN107801523 B CN 107801523B CN 201710819272 A CN201710819272 A CN 201710819272A CN 107801523 B CN107801523 B CN 107801523B
Authority
CN
China
Prior art keywords
layer
water absorption
polyester film
parts
ecological
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201710819272.8A
Other languages
English (en)
Other versions
CN107801523A (zh
Inventor
李绍才
孙海龙
李付斌
张华德
张洪波
李广辉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chengdu Mingfu Horticulture Co ltd
Original Assignee
Sichuan Allvery Environmental Protection Technology Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sichuan Allvery Environmental Protection Technology Co ltd filed Critical Sichuan Allvery Environmental Protection Technology Co ltd
Priority to CN201710819272.8A priority Critical patent/CN107801523B/zh
Publication of CN107801523A publication Critical patent/CN107801523A/zh
Application granted granted Critical
Publication of CN107801523B publication Critical patent/CN107801523B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属于绿化环保工程技术领域，提供了一种生态覆盖卷制造方法。该方法包括：将第一聚酯薄膜层放卷，开设第一通孔；向第一聚酯薄膜层铺设一层第一吸水层；对植物种子进行包衣，将包衣植物种子与肥料混合，经旋转填料形成混合层后铺设在第一吸水层上；向混合层铺设一层第二吸水层；将第二聚酯薄膜层放卷，开设第二通孔，对位铺设在第二吸水层上；向第一聚酯薄膜层、第一吸水层、混合层、第二吸水层和第二聚酯薄膜层之间填充热熔针棉，加压复合形成生态覆盖膜；对生态覆盖膜进行卷绕包装。该方法设计科学合理，操作简单易行，可实现大规模制造，采用该方法制备得到的生态覆盖卷具有优异的防治裸露地表扬尘的效果，且绿色环保、成本低。

Description

生态覆盖卷制造方法
技术领域
本发明属于绿化环保工程技术领域，具体地说，涉及一种生态覆盖卷制造方法。
背景技术
扬尘污染危及环境和人体健康，已成为世界污染难题。随着我国工业化程度加深，扬尘污染问题越发严重，扬尘问题不仅造成大量资源损失，而且污染周边环境，影响人们正常生产和生活。随着环保意思的增强，人们对扬尘污染治理日益重视。现在大多数裸露地表采取的措施是通过苫盖孔径较小的绿网从而达到抑制扬尘的目的，但是这样做既不环保又浪费资源，成本比较高不经济，而且抑制扬尘的效果一般。
发明内容
针对现有技术中上述的不足，本发明提供一种生态覆盖卷制造方法，该制造方法设计科学合理，操作简单易行，可实现大规模制造，采用该方法制备得到的生态覆盖卷能有效提高植物种子的发芽存活率，具有优异的防治裸露地表扬尘的效果，且绿色环保、成本低。
为了达到上述目的，本发明采用的解决方案是：
一种生态覆盖卷制造方法，其特征在于：包括以下制备步骤：将第一聚酯薄膜层放卷，开设直径为2-3mm 的第一通孔；向第一聚酯薄膜层铺设一层第一吸水层，第一吸水层由无机吸水材料经旋转填料制成；对植物种子进行包衣，将包衣植物种子与肥料混合，经旋转填料形成混合层后铺设在第一吸水层上；向混合层铺设一层第二吸水层，第二吸水层由无机吸水材料经旋转填料制成；将第二聚酯薄膜层放卷，开设直径为1-2mm 的第二通孔，对位铺设在第二吸水层上；对第一聚酯薄膜层、第一吸水层、混合层、第二吸水层和第二聚酯薄膜层之间填充热熔针棉，加压复合形成生态覆盖膜；对生态覆盖膜进行卷绕包装。
本发明提供的生态覆盖卷制造方法的有益效果是：
本发明提供的生态覆盖卷制造方法包括：将第一聚酯薄膜层放卷，开设直径为2-3mm 的第一通孔；其中，聚酯薄膜具有较好的耐寒性、耐热性、刚性好、强度高，使生态覆盖卷能在较冷或较热的环境下使用，提高其使用的范围；第一聚酯薄膜层表面开设有多个直径为2-3mm的第一通孔，便于雨水等通过第一通孔进入第一吸水层，从而进入混合层使种子在薄膜之间生长；
向第一聚酯薄膜层铺设一层第一吸水层，第一吸水层由无机吸水材料经旋转填料制成；第一吸水层能够起到很好的保水的作用；旋转填料有利于无机吸水材料快速成型，且制备得到的第一吸水层密实紧凑；
对植物种子进行包衣，将包衣植物种子与肥料混合，经旋转填料形成混合层后铺设在第一吸水层上；包衣植物种子具有较好的抗逆性、抗病性，复合肥能为包衣植物种子提供生长养分；
向混合层铺设一层第二吸水层，第二吸水层由无机吸水材料经旋转填料制成；混合层置于两层吸水层之间，为植物种子的生长提供充足的水分；
将第二聚酯薄膜层放卷，开设直径为1-2mm 的第二通孔，对位铺设在第二吸水层上；第二聚酯薄膜层表面开设有多个直径为1-2mm的第二通孔，目的是为了在雨水等量很大时，使多余的雨水通过第二聚酯薄膜层的通孔流入地表，在使用时可以通过浇水或自然雨水，使植物种子发芽；
在第一聚酯薄膜层、第一吸水层、混合层、第二吸水层和第二聚酯薄膜层之间填充热熔针棉，加压复合形成生态覆盖膜；热熔针棉具有透气性好，保暖性佳，轻质，回弹力强，耐老化，耐水洗，不霉变等特点，加压复合能够使得制得的生态覆盖膜更加紧凑密实；
对生态覆盖膜进行卷绕包装得到生态覆盖卷。
附图说明
为了更清楚地说明本发明实施例的技术方案，下面将对实施例中所需要使用的附图作简单地介绍，应当理解，以下附图仅示出了本发明的某些实施例，因此不应被看作是对范围的限定，对于本领域普通技术人员来讲，在不付出创造性劳动的前提下，还可以根据这些附图获得其他相关的附图。
图1为本发明的生态覆盖卷的结构示意图；
图2为对比例3提供的生态覆盖卷的结构示意图。
图标：100-生态覆盖卷；200-第一聚酯薄膜层；210-第一通孔；300-第一吸水层；400-混合物层；500-第二吸水层；600-第二聚酯薄膜层；610-第二通孔；700-生态覆盖卷；710-第一聚酯薄膜层；711-第一通孔；720-混合层；730-第二聚酯薄膜层；731-第二通孔。
具体实施方式
为使本发明实施例的目的、技术方案和优点更加清楚，下面将对本发明实施例中的技术方案进行清楚、完整地描述。实施例中未注明具体条件者，按照常规条件或制造商建议的条件进行。所用试剂或仪器未注明生产厂商者，均为可以通过市售购买获得的常规产品。
下面对本发明实施例提供的一种生态覆盖卷制造方法进行具体说明。
请参照图1，一种生态覆盖卷100，从上至下依次为第一聚酯薄膜层200、第一吸水层300、混合物层400、第二吸水层500及第二聚酯薄膜层600。
该生态覆盖卷100是的制造方法如下：
首先将第一聚酯薄膜层200放卷，开设直径为2-3mm 的第一通孔210，在该直径范围内有利于雨水顺利通过；优选的，第一聚酯薄膜层200表面的开孔率为15-20%；
接着向第一聚酯薄膜层200铺设一层第一吸水层300，第一吸水层300由无机吸水材料经旋转填料制成，优选地，无机吸水材料为膨胀蛭石；膨胀蛭石具有良好的阳离子交换性和吸附性，储水保墒，提高生态覆盖卷100的透气性和含水性；膨胀蛭石还可起到缓冲作用，使肥料在作物生长介质中缓慢释放，且允许稍过量地使用肥料而对植物没有危害；膨胀蛭石还可向作物提供自身含有的K、Mg、Ca、Fe以及微量的Mn、Cu、Zn等元素。
然后，对植物种子进行包衣，将包衣植物种子与肥料混合，经旋转填料形成混合层400后铺设在第一吸水层300上；包衣植物种子由包覆材料包覆植物种子制得，包覆材料按重量份计包括：膨润土10-18份、腐殖酸10-15份、赤霉素1-3份、海藻酸钠8-12份、杀虫剂5-8份、杀菌剂5-8份、水70-100份，其中，海藻酸钠为粘合剂，腐殖酸和膨润土为保水剂，赤霉素为生长剂，杀虫剂优选为可尼丁，杀菌剂优选为多菌灵。该包衣植物种子具有较好的抗逆性、抗病性，能很好的促进植物种子发芽。复合肥按重量份计，包括尿素12-20份、微量元素0.5-1份、磷酸二氢钾5-8份、氨基酸0.5-1份，其中，尿素为种子提供氮素，氮是蛋白质（包括一些酶和辅酶）、核酸、磷脂的主要成分，他们是原生质、细胞核和生物膜的重要组成部分，在植物生命活动中具有特殊的作用，微量元素对植物的生长发育有着至关重要的作用，是植物体内酶或辅酶的组成成分，具有很强的专一性，本发明中微量元素有效成分包括钼、铜、铁和锌；磷酸二氢钾是磷钾肥，为无色结晶或白色颗粒状粉末；既能为种子提供磷P、K，又能作为种子的生长调节剂，促进种子发芽。
接着，向混合层400铺设一层第二吸水层500，第二吸水层500由无机吸水材料经旋转填料制成，作为优选地，第一吸水层300和第二吸水层500的厚度太薄吸水保水的效果太差，厚度太厚会影响植物种子的吸收，优选的，第一吸水层300和第二吸水层500的厚度均为0.4-0.5mm。
再将第二聚酯薄膜层600放卷，开设直径为1-2mm 的第二通孔610，对位铺设在第二吸水层500上，目的是为了在雨水等量很大时，使多余的雨水通过第二通孔610流入地表，避免淹死种子；优选地，第二聚酯薄膜层600表面的开孔率为10-15%，第二聚酯薄膜层600的开孔率小于第一聚酯薄膜层200，目的是为了保障能为植物种子提供充足的水分，供植物种子生长。
接着，对第一聚酯薄膜层200、第一吸水层300、混合层400、第二吸水层500和第二聚酯薄膜层600之间填充热熔针棉，加压复合形成生态覆盖膜；对生态覆盖膜进行卷绕包装。
该生态覆盖卷100制造方法设计科学合理，操作简单易行，可实现大规模制造，采用该方法制备得到的生态覆盖卷100能有效提高植物种子的发芽存活率，具有优异的防治裸露地表扬尘的效果，且绿色环保、成本低。
实施例1
本实施例提供了一种生态覆盖卷100制造方法，包括以下制备步骤：
将第一聚酯薄膜层200放卷，以开孔率为15%开设直径为2mm 的第一通孔210；
再向第一聚酯薄膜层200铺设一层0.4mm厚的第一吸水层300，第一吸水层300由膨胀蛭石经旋转填料制成；
接着对植物种子进行包衣，包衣植物种子由包覆材料包覆植物种子制得，包覆材料按重量份计包括：膨润土10份、腐殖酸10份、赤霉素1份、海藻酸钠8份、可尼丁5份、多菌灵5份、水70份；将包衣植物种子与肥料混合，肥料按重量份计，其原料包括尿素12份、钼0.2份、铜0.1份、铁0.1份、锌0.1份、磷酸二氢钾5份、氨基酸0.5份；经旋转填料形成混合层400后铺设在第一吸水层300上；
接着向混合层铺设一层0.4mm厚的第二吸水层500，第二吸水层500由膨胀蛭石经旋转填料制成；
然后将第二聚酯薄膜层600放卷，以开孔率为10%开设直径为1mm 的第二通孔610，对位铺设在第二吸水层500上；
对第一聚酯薄膜层、第一吸水层、混合层、第二吸水层和第二聚酯薄膜层之间填充热熔针棉，加压复合形成生态覆盖膜；对生态覆盖膜进行卷绕包装。
实施例2
本实施例提供了一种生态覆盖卷100制造方法，包括以下制备步骤：
将第一聚酯薄膜层200放卷，以开孔率为20%开设直径为3mm 的第一通孔210；
再向第一聚酯薄膜层200铺设一层0.5mm厚的第一吸水层300，第一吸水层300由膨胀蛭石经旋转填料制成；
接着对植物种子进行包衣，包衣植物种子由包覆材料包覆植物种子制得，包覆材料按重量份计包括：膨润土18份、腐殖酸15份、赤霉素3份、海藻酸钠12份、可尼丁8份、多菌灵8份、水100份；将包衣植物种子与肥料混合，肥料按重量份计，其原料包括尿素20份、钼0.4份、铜0.2份、铁0.2份、锌0.2份、磷酸二氢钾8份、氨基酸1份；经旋转填料形成混合层400后铺设在第一吸水层300上；
接着向混合层铺设一层0.5mm厚的第二吸水层500，第二吸水层500由膨胀蛭石经旋转填料制成；
然后将第二聚酯薄膜层600放卷，以开孔率为15%开设直径为2mm 的第二通孔610，对位铺设在第二吸水层500上；
对第一聚酯薄膜层、第一吸水层、混合层、第二吸水层和第二聚酯薄膜层之间填充热熔针棉，加压复合形成生态覆盖膜；对生态覆盖膜进行卷绕包装。
实施例3
本实施例提供了一种生态覆盖卷100制造方法，包括以下制备步骤：
将第一聚酯薄膜层200放卷，以开孔率为18%开设直径为2.5mm 的第一通孔210；
再向第一聚酯薄膜层200铺设一层0.5mm厚的第一吸水层300，第一吸水层300由膨胀蛭石经旋转填料制成；
接着对植物种子进行包衣，包衣植物种子由包覆材料包覆植物种子制得，包覆材料按重量份计包括：膨润土15份、腐殖酸12份、赤霉素2份、海藻酸钠10份、可尼丁6份、多菌灵6份、水80份；将包衣植物种子与肥料混合，肥料按重量份计，其原料包括尿素20份、钼0.3份、铜0.1份、铁0.2份、锌0.1份、磷酸二氢钾6份、氨基酸0.8份；经旋转填料形成混合层400后铺设在第一吸水层300上；
接着向混合层铺设一层0.5mm厚的第二吸水层500，第二吸水层500由膨胀蛭石经旋转填料制成；
然后将第二聚酯薄膜层600放卷，以开孔率为13%开设直径为1.5mm 的第二通孔610，对位铺设在第二吸水层500上；
对第一聚酯薄膜层、第一吸水层、混合层、第二吸水层和第二聚酯薄膜层之间填充热熔针棉，加压复合形成生态覆盖膜；对生态覆盖膜进行卷绕包装。
对比例1
本对比例提供了一种生态覆盖卷100制造方法，包括以下制备步骤：
将第一聚酯薄膜层200放卷，以开孔率为18%开设直径为1.5mm 的第一通孔210；
再向第一聚酯薄膜层200铺设一层0.5mm厚的第一吸水层300，第一吸水层300由膨胀蛭石经旋转填料制成；
接着对植物种子进行包衣，包衣植物种子由包覆材料包覆植物种子制得，包覆材料按重量份计包括：膨润土15份、腐殖酸12份、赤霉素2份、海藻酸钠10份、可尼丁6份、多菌灵6份、水80份；经旋转填料形成混合层400后铺设在第一吸水层300上；
接着向混合层铺设一层0.5mm厚的第二吸水层500，第二吸水层500由膨胀蛭石经旋转填料制成；
然后将第二聚酯薄膜层600放卷，以开孔率为13%开设直径为1.5mm 的第二通孔610，对位铺设在第二吸水层500上；
对第一聚酯薄膜层、第一吸水层、混合层、第二吸水层和第二聚酯薄膜层之间填充热熔针棉，加压复合形成生态覆盖膜；对生态覆盖膜进行卷绕包装。
对比例2
本对比例提供了一种生态覆盖卷100制造方法，包括以下制备步骤：
将第一聚酯薄膜层200放卷，以开孔率为18%开设直径为1.5mm 的第一通孔210；
再向第一聚酯薄膜层200铺设一层0.5mm厚的第一吸水层300，第一吸水层300由膨胀蛭石经旋转填料制成；
接着将肥料混合，肥料的原料按重量份计，包括尿素20份、钼0.3份、铜0.1份、铁0.2份、锌0.1份、磷酸二氢钾6份、氨基酸0.8份；经旋转填料形成混合层400后铺设在第一吸水层300上；
接着向混合层铺设一层0.5mm厚的第二吸水层500，第二吸水层500由膨胀蛭石经旋转填料制成；
然后将第二聚酯薄膜层600放卷，以开孔率为13%开设直径为1.5mm 的第二通孔610，对位铺设在第二吸水层500上；
对第一聚酯薄膜层、第一吸水层、混合层、第二吸水层和第二聚酯薄膜层之间填充热熔针棉，加压复合形成生态覆盖膜；对生态覆盖膜进行卷绕包装。
对比例3
本对比例提供了一种生态覆盖卷700制造方法，包括以下制备步骤：
将第一聚酯薄膜层710放卷，以开孔率为18%开设直径为2.5mm 的第一通孔711；
接着对植物种子进行包衣，包衣植物种子由包覆材料包覆植物种子制得，包覆材料按重量份计包括：膨润土15份、腐殖酸12份、赤霉素2份、海藻酸钠10份、可尼丁6份、多菌灵6份、水80份；将包衣植物种子与肥料混合，肥料按重量份计，其原料包括尿素20份、钼0.3份、铜0.1份、铁0.2份、锌0.1份、磷酸二氢钾6份、氨基酸0.8份；经旋转填料形成混合层720后铺设在第一聚酯薄膜层710上；
然后将第二聚酯薄膜层730放卷，以开孔率为13%开设直径为1.5mm 的第二通孔731，对位铺设在混合层720上；
对第一聚酯薄膜层710、混合层720和第二聚酯薄膜层730之间填充热熔针棉，加压复合形成生态覆盖膜；对生态覆盖膜进行卷绕包装。
按实施例1-3，对比例1-3制备生态覆盖卷，10天以后观察种子的发芽率，结果如表1所示。
表1实施例1-3和对比例1-3的种子发芽率
实施例1 实施例2 实施例3 对比例1 对比例2 对比例3
发芽率（%） 93% 93% 95% 55% 65% 61%
从表1中可以看出，实施例1-3制备得到的生态覆盖卷的植物种子的发芽率较高，均在93%及以上，对比例1-3制备得到的生态覆盖卷的种子的发芽率较低，对比例1中混合层不包括肥料，对比例2中混合层中植物种子不是包衣植物种子，对比例3中不包括吸水层。该结果表明，通过本发明实施例的制造方法制备得到的生态覆盖卷，植物种子具有较高的发芽率，可以大面积的生长，通过薄膜与植物能达到很好的治理裸露地表扬尘的效果，而且环保、成本低，使用方便，需要移动时只需要提起生态覆盖卷即可。
以上所述仅为本发明的优选实施例而已，并不用于限制本发明，对于本领域的技术人员来说，本发明可以有各种更改和变化。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (9)

1.一种生态覆盖卷制造方法，其特征在于：包括以下制备步骤：
将第一聚酯薄膜层放卷，开设直径为2-3mm 的第一通孔；向所述第一聚酯薄膜层铺设一层第一吸水层，第一吸水层由无机吸水材料经旋转填料制成；对植物种子进行包衣，将包衣植物种子与肥料混合，经旋转填料形成混合层后铺设在所述第一吸水层上；向所述混合层铺设一层第二吸水层，所述第二吸水层由无机吸水材料经旋转填料制成；将第二聚酯薄膜层放卷，开设直径为1-2mm 的第二通孔，对位铺设在所述第二吸水层上；对所述第一聚酯薄膜层、第一吸水层、所述混合层、所述第二吸水层和第二聚酯薄膜层之间填充热熔针棉，加压复合形成生态覆盖膜；对所述生态覆盖膜进行卷绕包装。
2.根据权利要求1所述的生态覆盖卷制造方法，其特征在于：所述第一聚酯薄膜层的开孔率为15-20%，所述第二聚酯薄膜层的开孔率为10-15%。
3.根据权利要求1所述的生态覆盖卷制造方法，其特征在于：所述第一吸水层和第二吸水层的无机吸水材料均为膨胀蛭石。
4.根据权利要求3所述的生态覆盖卷制造方法，其特征在于：所述第一吸水层和所述第二吸水层的厚度均为0.4-0.5mm。
5.根据权利要求1所述的生态覆盖卷制造方法，其特征在于：所述包衣植物种子由包覆材料包覆植物种子制得，所述包覆材料按重量份计包括：膨润土10-18份、腐殖酸10-15份、赤霉素1-3份、海藻酸钠8-12份、杀虫剂5-8份、杀菌剂5-8份和水70-100份。
6.根据权利要求5所述的生态覆盖卷制造方法，其特征在于：所述杀虫剂为可尼丁。
7.根据权利要求5所述的生态覆盖卷制造方法，其特征在于：所述杀菌剂为多菌灵。
8.根据权利要求1所述的生态覆盖卷制造方法，其特征在于：所述肥料按重量份计，包括：尿素12-20份、微量元素0.5-1份、磷酸二氢钾5-8份和氨基酸0.5-1份。
9.根据权利要求8所述的生态覆盖卷制造方法，其特征在于：所述微量元素包括钼、铜、铁和锌中的至少一种。
CN201710819272.8A 2017-09-12 2017-09-12 生态覆盖卷制造方法 Expired - Fee Related CN107801523B (zh)