CN1077972A - Imitation ceramic interior wall paint - Google Patents
Imitation ceramic interior wall paint Download PDFInfo
- Publication number
- CN1077972A CN1077972A CN 92102794 CN92102794A CN1077972A CN 1077972 A CN1077972 A CN 1077972A CN 92102794 CN92102794 CN 92102794 CN 92102794 A CN92102794 A CN 92102794A CN 1077972 A CN1077972 A CN 1077972A
- Authority
- CN
- China
- Prior art keywords
- parts
- interior wall
- wall paint
- imitation ceramic
- ceramic interior
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of imitation ceramic interior wall paint, its proportioning (weight) is:
Water: 100 parts of polyvinyl alcohol: 0.5 part of formaldehyde: 0.8～1.2 part of hydrochloric acid: 0.3～0.4 part of caustic soda (concentration 30%): 0.5 part of urea: 0.5～1.2 part of silica powder: 100～200 parts of titanium dioxides: 50 parts.
Have the cohesive strength height, do not come off, not scaling, bright and clean is porcelain, not reflective, nontoxic, odorlessness such as can wash at excellent performance, are a kind of novel replacement coating.
Description
The invention belongs to interior wall coating for building
Existing interior wall has WALL CLOTH, wallpaper and various coating with finishing material.WALL CLOTH is wrinkling easily after making moist, go mouldy and the edge turnup; The poor durability of wallpaper is made moist, damaged and come off easily; Various coating are all non-moistureproof, can not wipe examination to stain and remove.Along with the raising of living standards of the people, the decoration of living indoor wall is required more and more high, the various materials of above-mentioned existing interior wall all can not be satisfied the demand.
A kind of imitation ceramic interior wall paint that the objective of the invention is to overcome the deficiency of above-mentioned technology and provide.
The objective of the invention is to realize by following technical measures.
A kind of imitation ceramic interior wall paint comprises solvent, neutralizing agent, frostproofer, water and coating, it is characterized in that the proportioning (weight) of each composition is:
Water: 100 parts
Polyvinyl alcohol: 0.5 part
Formaldehyde: 0.8～1.2 part
Hydrochloric acid: 0.3～0.4 part
Caustic soda (concentration 30%): about 0.5 part (is 7～8 to be as the criterion with pH value)
Urea: 0.5～1.2 part
Silica powder: 100～200 parts
Blending process:
When 1, getting 100 parts of water and put into reactor and heat, add 5 parts of polyvinyl alcohol, stirred 15～20 minutes to 50～80 ℃;
2, add 0.3～0.5 part in formaldehyde, continue to stir;
3, when temperature rises to 90～94 ℃, be incubated 40～50 minutes, filter with 80 mesh sieves and put into the cooling pool cooling;
4, when being cooled to 85～90 ℃, add 0.3～0.4 part of hydrochloric acid, require in 5～10 minutes, slowly to add, and ceaselessly stir, need after adding to continue to stir 10 minutes;
5, add 0.5～0.7 part in formaldehyde, require slowly to add in 15 minutes, temperature should not be lower than 80 ℃ when adding, and continues to stir 40 minutes, when temperature drops to below 80 ℃, stirs 60 minutes;
6, adding concentration is about 0.5 part in 30% caustic soda (is 7～8 to be as the criterion with pH value);
7, add frostproofer (urea), add 1～1.2 part winter, add 0.5～0.7 part summer, stirred 10～20 minutes;
8, filled (silica powder, titanium dioxide): add 100 parts of silica powders summer, 50 parts of titanium dioxides add 200 parts of silica powders winter, and 50 parts of titanium dioxides are till stirring;
9, be filtered into bucket with 80 mesh sieves and be finished product.
Embodiment: its proportioning (weight) is specially:
Water: 100kg
Polyvinyl alcohol: 0.5kg
Formaldehyde: 0.3kg
Caustic soda (concentration 30%): about 0.5kg (is 7～8 to be as the criterion with pH value)
Urea: 1kg
Silica powder: 150kg
Titanium dioxide: 50kg
Its blending process is the same.
The present invention compares existing decorative paint and has following remarkable advantage:
1, has the adhesion strength height, do not come off;
2, fineness is good, any surface finish such as porcelain;
3, the life-span long, not peeling, breach, aging;
4, nontoxic, odorlessness, "dead";
5, waterproof and dampproof performance is good, but effects on surface is cleaned.
Claims (1)
1, a kind of imitation ceramic interior wall paint comprises: solvent, neutralizing agent, frostproofer, water and filler is characterized in that the proportioning (weight) of each composition is:
Water: 100 parts
Polyvinyl alcohol: 0.5 part
Formaldehyde: 0.8～1.2 part
Hydrochloric acid: 0.3～0.4 part
Caustic soda (concentration 30%): about 0.5 (is 7～8 to be as the criterion with pH value)
Urea: 0.5～1.2 part
Silica powder: 100～200 parts
Titanium dioxide: 50 parts.