CN107700004A - A kind of antimicrobial form feather dress fabric and preparation method thereof - Google Patents
A kind of antimicrobial form feather dress fabric and preparation method thereof Download PDFInfo
- Publication number
- CN107700004A CN107700004A CN201710913851.9A CN201710913851A CN107700004A CN 107700004 A CN107700004 A CN 107700004A CN 201710913851 A CN201710913851 A CN 201710913851A CN 107700004 A CN107700004 A CN 107700004A
- Authority
- CN
- China
- Prior art keywords
- parts
- fiber
- fabric
- washing
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of antimicrobial form feather dress fabric and preparation method thereof, belongs to fabric technology and preparing technical field, in order to solve in the prior art the problem of the type Product Process is complicated, and cost is higher, and function is single：A kind of antimicrobial form feather dress fabric, including llowing group of materials parts by weights are mixed：8 12 parts of chitin fiber, 58 parts of sodium hypophosphite, 35 parts of pearl fiber, 12 18 parts of antibacterial finishing agent, 40 55 parts of duck's down fiber, 35 50 parts of coffee carbon fiber, 65 80 parts of Fypro, 10 15 parts of bleeding agent, 35 parts of toluene, 24 parts of butanone；Present invention simultaneously provides the preparation method of above-mentioned fabric, including braiding fabric, immersion, drying three steps of ironing.And cost of the present invention is low, preparation technology is simple, plays an important roll to the performance and low-carbon environment-friendly for improving feather dress fabric.
Description
Technical field
The present invention relates to a kind of feather dress fabric and preparation method thereof, belongs to fabric technology and preparing technical field, mainly
It is related to a kind of antimicrobial form feather dress fabric and preparation method thereof.
Background technology
As the improvement of people's living standards, people are increasingly paid close attention to the fabric composition of clothes, to the various of its function
Change and require also more and more higher.Low-carbon environment-friendly, green fabric nuisanceless, vdiverse in function gradually receive the concern of people, market
Have a extensive future.However, the type Product Process is complicated in the market, cost is higher, it is impossible to meets that environmental protection takes into account the need of production
Ask.
The content of the invention
In order to solve the above problems, the present invention discloses a kind of antimicrobial form feather dress fabric and preparation method thereof, energy-conserving and environment-protective,
Technique is simple, vdiverse in function.
The object of the present invention is achieved like this：
A kind of antimicrobial form feather dress fabric, including llowing group of materials parts by weights are mixed：Chitin fiber 8-12 parts, secondary phosphorous
Sour sodium 5-8 parts, pearl fiber 3-5 parts, antibacterial finishing agent 12-18 parts, duck's down fiber 40-55 parts, coffee carbon fiber 35-50 parts,
Fypro 65-80 parts, bleeding agent 10-15 parts, toluene 3-5 parts, butanone 2-4 parts.
Further, the antibacterial finishing agent includes refining agent 5-8 parts, hydrogen peroxide 10-16 parts, sodium metasilicate 8-12 parts, carbon
Sour sodium 8-12 parts, sodium hydroxide 1-2 parts.
Further, the bath raio 1 of the antibiotic downy jackets fabric and antibacterial finishing agent:50.
Present invention simultaneously provides the preparation method of above-mentioned fabric, comprise the following steps：
Step 1, chitin fiber, pearl fiber, duck's down fiber, coffee carbon fiber and Fypro are passed through into warp thread respectively
And weft yarns, form semi-finished product fabric.
Warp thread described in step 1 includes chitin fiber 25, pearl fiber 15 and duck's down fiber 50, weaves respectively
Into yarn, then three kinds of yarns are formed；The weft yarn includes coffee carbon fiber 18 and Fypro 50, respectively
Yarn is made into, then forms two kinds of yarns, then by recombing, chain grilling, retraction, combing and arranging process,
Form semi-finished product fabric.
Preferably, semi-finished product fabric described in step 1 is twill-weave structure, through it is close be 500/10 centimetres, filling density change
Respectively 220,240,260,280,300/10 centimetres.
Step 2, the semi-finished product fabric that step 1 is formed, is put into sodium hypophosphite, antibiotic finish after warm water soaks
Soaked in agent, bleeding agent, toluene and butanone mixed liquor.
The warm water temperature described in step 2 is 45-55 degrees Celsius, and soak time is 45-60 minutes.
Step 3, by the fabric soaked through washing, drying, final ironing obtains finished product fabric.
Further, the water-washing process includes first time washing, second of washing and third time washing.
Preferably, the first time washing water temperature is 80-95 degrees Celsius, and it is 65-80 degrees Celsius that second, which is washed water temperature, the
It is 45-60 degrees Celsius to wash water temperature three times, and the first time washing, second of washing and third time washing time are 15 points
Clock.
The present invention compared with prior art, has the advantages that：According to proportioning disclosed by the invention and experiment step
Rapid a kind of antimicrobial form feather dress fabric of gained and preparation method thereof, has good occlusion characteristic, does not contain any chemistry addition
The addition of agent, chitin fiber and pearl fiber improves the antibiotic property of fabric, and the addition of duck's down fiber is greatly improved again
The comfortableness of fabric, soft texture.And cost of the present invention is low, preparation technology is simple, to making the life better and low-carbon ring
Guarantor plays an important roll, suitable for promoting.
Embodiment
Embodiment 1
A kind of antimicrobial form feather dress fabric, including llowing group of materials parts by weights are mixed：8 parts of chitin fiber, ortho phosphorous acid
5 parts of sodium, 3 parts of pearl fiber, 12 parts of antibacterial finishing agent, 40 parts of duck's down fiber, 35 parts of coffee carbon fiber, 65 parts of Fypro,
10 parts of bleeding agent, 3 parts of toluene, 2 parts of butanone.
Further, the antibacterial finishing agent include 5 parts of refining agent, 10 parts of hydrogen peroxide, 8 parts of sodium metasilicate, 8 parts of sodium carbonate,
1 part of sodium hydroxide.
Further, the bath raio 1 of the antibiotic downy jackets fabric and antibacterial finishing agent:50.
Present invention simultaneously provides the preparation method of above-mentioned fabric, comprise the following steps：
Step 1, chitin fiber, pearl fiber, duck's down fiber, coffee carbon fiber and Fypro are passed through into warp thread respectively
And weft yarns, form semi-finished product fabric；
Step 2, the semi-finished product fabric that step 1 is formed, be put into after warm water soaks sodium hypophosphite, antibacterial finishing agent,
Soaked in bleeding agent, toluene and butanone mixed liquor.
Step 3, by the fabric soaked through washing, drying, final ironing obtains finished product fabric.
Warp thread described in step 1 forms including chitin fiber, pearl fiber and duck's down fiber blend, and the weft yarn includes
Coffee carbon fiber and Fypro blending form.
Semi-finished product fabric described in step 1 is twill-weave structure.
The warm water temperature described in step 2 is 45 degrees Celsius, and soak time is 45 minutes.
Water-washing process described in step 3 includes washing for the first time, second of washing and third time and washed.
The first time washing water temperature is 80 degrees Celsius, and it is 65 degrees Celsius that second, which is washed water temperature, and third time washes water temperature
For 45 degrees Celsius.
The first time washing, second of washing and third time washing time are 15 minutes.
Embodiment 2
A kind of antimicrobial form feather dress fabric, including llowing group of materials parts by weights are mixed：9 parts of chitin fiber, ortho phosphorous acid
5.5 parts of sodium, 3.5 parts of pearl fiber, 13 parts of antibacterial finishing agent, 45 parts of duck's down fiber, 38 parts of coffee carbon fiber, Fypro 70
Part, 11 parts of bleeding agent, 3.5 parts of toluene, 2.5 parts of butanone.
Further, the antibacterial finishing agent include 6 parts of refining agent, 12 parts of hydrogen peroxide, 9 parts of sodium metasilicate, 9 parts of sodium carbonate,
1.2 parts of sodium hydroxide.
Further, the bath raio 1 of the antibiotic downy jackets fabric and antibacterial finishing agent:50.
Present invention simultaneously provides the preparation method of above-mentioned fabric, comprise the following steps：
Step 1, chitin fiber, pearl fiber, duck's down fiber, coffee carbon fiber and Fypro are passed through into warp thread respectively
And weft yarns, form semi-finished product fabric；
Step 2, the semi-finished product fabric that step 1 is formed, be put into after warm water soaks sodium hypophosphite, antibacterial finishing agent,
Soaked in bleeding agent, toluene and butanone mixed liquor.
Step 3, by the fabric soaked through washing, drying, final ironing obtains finished product fabric.
Warp thread described in step 1 forms including chitin fiber, pearl fiber and duck's down fiber blend, and the weft yarn includes
Coffee carbon fiber and Fypro blending form.
Semi-finished product fabric described in step 1 is twill-weave structure.
The warm water temperature described in step 2 is 48 degrees Celsius, and soak time is 50 minutes.
Water-washing process described in step 3 includes washing for the first time, second of washing and third time and washed.
The first time washing water temperature is 85 degrees Celsius, and it is 70 degrees Celsius that second, which is washed water temperature, and third time washes water temperature
For 50 degrees Celsius.
The first time washing, second of washing and third time washing time are 15 minutes.
Embodiment 3
A kind of antimicrobial form feather dress fabric, including llowing group of materials parts by weights are mixed：10 parts of chitin fiber, ortho phosphorous acid
6 parts of sodium, 4 parts of pearl fiber, 15 parts of antibacterial finishing agent, 48 parts of duck's down fiber, 42 parts of coffee carbon fiber, 73 parts of Fypro,
13 parts of bleeding agent, 4 parts of toluene, 3 parts of butanone.
Further, the antibacterial finishing agent includes 6.8 parts of refining agent, 14 parts of hydrogen peroxide, 10 parts of sodium metasilicate, sodium carbonate 10
Part, 1.4 parts of sodium hydroxide.
Further, the bath raio 1 of the antibiotic downy jackets fabric and antibacterial finishing agent:50.
Present invention simultaneously provides the preparation method of above-mentioned fabric, comprise the following steps：
Step 1, chitin fiber, pearl fiber, duck's down fiber, coffee carbon fiber and Fypro are passed through into warp thread respectively
And weft yarns, form semi-finished product fabric；
Step 2, the semi-finished product fabric that step 1 is formed, be put into after warm water soaks sodium hypophosphite, antibacterial finishing agent,
Soaked in bleeding agent, toluene and butanone mixed liquor.
Step 3, by the fabric soaked through washing, drying, final ironing obtains finished product fabric.
Warp thread described in step 1 forms including chitin fiber, pearl fiber and duck's down fiber blend, and the weft yarn includes
Coffee carbon fiber and Fypro blending form.
Semi-finished product fabric described in step 1 is twill-weave structure.
The warm water temperature described in step 2 is 50 degrees Celsius, and soak time is 54 minutes.
Water-washing process described in step 3 includes washing for the first time, second of washing and third time and washed.
The first time washing water temperature is 87 degrees Celsius, and it is 73 degrees Celsius that second, which is washed water temperature, and third time washes water temperature
For 52 degrees Celsius.
The first time washing, second of washing and third time washing time are 15 minutes.
Embodiment 4
A kind of antimicrobial form feather dress fabric, including llowing group of materials parts by weights are mixed：11 parts of chitin fiber, ortho phosphorous acid
7 parts of sodium, 4.5 parts of pearl fiber, 17 parts of antibacterial finishing agent, 52 parts of duck's down fiber, 46 parts of coffee carbon fiber, Fypro 77
Part, 14 parts of bleeding agent, 4.5 parts of toluene, 3.5 parts of butanone.
Further, the antibacterial finishing agent includes 7 parts of refining agent, 15 parts of hydrogen peroxide, 11 parts of sodium metasilicate, sodium carbonate 11
Part, 1.8 parts of sodium hydroxide.
Further, the bath raio 1 of the antibiotic downy jackets fabric and antibacterial finishing agent:50.
Present invention simultaneously provides the preparation method of above-mentioned fabric, comprise the following steps：
Step 1, chitin fiber, pearl fiber, duck's down fiber, coffee carbon fiber and Fypro are passed through into warp thread respectively
And weft yarns, form semi-finished product fabric；
Step 2, the semi-finished product fabric that step 1 is formed, be put into after warm water soaks sodium hypophosphite, antibacterial finishing agent,
Soaked in bleeding agent, toluene and butanone mixed liquor.
Step 3, by the fabric soaked through washing, drying, final ironing obtains finished product fabric.
Warp thread described in step 1 forms including chitin fiber, pearl fiber and duck's down fiber blend, and the weft yarn includes
Coffee carbon fiber and Fypro blending form.
Semi-finished product fabric described in step 1 is twill-weave structure.
The warm water temperature described in step 2 is 50 degrees Celsius, and soak time is 58 minutes.
Water-washing process described in step 3 includes washing for the first time, second of washing and third time and washed.
The first time washing water temperature is 90 degrees Celsius, and it is 75 degrees Celsius that second, which is washed water temperature, and third time washes water temperature
For 55 degrees Celsius.
The first time washing, second of washing and third time washing time are 15 minutes.
Embodiment 5
A kind of antimicrobial form feather dress fabric, including llowing group of materials parts by weights are mixed：12 parts of chitin fiber, ortho phosphorous acid
8 parts of sodium, 5 parts of pearl fiber, 18 parts of antibacterial finishing agent, 55 parts of duck's down fiber, 50 parts of coffee carbon fiber, 80 parts of Fypro,
15 parts of bleeding agent, 5 parts of toluene, 4 parts of butanone.
Further, the antibacterial finishing agent includes 8 parts of refining agent, 16 parts of hydrogen peroxide, 12 parts of sodium metasilicate, sodium carbonate 12
Part, 2 parts of sodium hydroxide.
Further, the bath raio 1 of the antibiotic downy jackets fabric and antibacterial finishing agent:50.
Present invention simultaneously provides the preparation method of above-mentioned fabric, comprise the following steps：
Step 1, chitin fiber, pearl fiber, duck's down fiber, coffee carbon fiber and Fypro are passed through into warp thread respectively
And weft yarns, form semi-finished product fabric；
Step 2, the semi-finished product fabric that step 1 is formed, be put into after warm water soaks sodium hypophosphite, antibacterial finishing agent,
Soaked in bleeding agent, toluene and butanone mixed liquor.
Step 3, by the fabric soaked through washing, drying, final ironing obtains finished product fabric.
Warp thread described in step 1 forms including chitin fiber, pearl fiber and duck's down fiber blend, and the weft yarn includes
Coffee carbon fiber and Fypro blending form.
Semi-finished product fabric described in step 1 is twill-weave structure.
The warm water temperature described in step 2 is 55 degrees Celsius, and soak time is 60 minutes.
Water-washing process described in step 3 includes washing for the first time, second of washing and third time and washed.
The first time washing water temperature is 95 degrees Celsius, and it is 80 degrees Celsius that second, which is washed water temperature, and third time washes water temperature
For 60 degrees Celsius.
The first time washing, second of washing and third time washing time are 15 minutes.
Embodiment 1-5 is anti-microbial property test of the present invention, and method of testing is：Using standard cotton lining cloth as control sample,
Feather dress fabric disclosed by the invention and control sample are cut into 5mm*5mm square fragment, weigh 0.75g as sample.Will
Sample and control sample after sterilizing are respectively put into the triangle of certain density staphylococcus aureus bacterium solution and Escherichia coli bacteria liquid
In beaker, vibrated 30 hours under conditions of 25 degrees Celsius, 200 revs/min, the viable bacteria concentration before measurement vibration and after vibration,
Bacteriostasis rate is calculated, calculation formula is as follows：
It is the bacteriostasis rate of sample in formula, is the present invention for the average value of the viable bacteria concentration after control sample oscillating contact
The average value of viable bacteria concentration after disclosed feather dress fabric oscillating contact, test result are as shown in table 1.
| Embodiment test parameter | Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Embodiment 5 | Comparative example |
| Y/% | 12.41 | 13.49 | 15.89 | 16.53 | 18.21 | 10.44 |
From table 1 it follows that a kind of antimicrobial form feather dress fabric provided by embodiment 1-5 has good biocidal property
Can, compared with prior art, temperature fall time constant improves 18.9% in embodiment 1, and temperature fall time constant improves in embodiment 2
29.2%, temperature fall time constant improves 52.2% in embodiment 3, and temperature fall time constant improves 58.3% in embodiment 4, real
Apply the temperature fall time constant of example 5 and improve 74.4%.
It should be understood that above description is to illustrate rather than to be limited.By reading foregoing description,
Many embodiments and many applications outside the example provided all will be apparent for a person skilled in the art.
Therefore, the scope of the present invention should not determine with reference to foregoing description, but should be with reference to preceding claims and these power
Profit requires the four corner of possessed equivalent to determine.For comprehensive purpose, all articles and reference include patent Shen
The disclosure that please and announce is all by reference to being incorporated herein.Any of theme disclosed herein is omitted in preceding claims
Aspect is not intended to abandon the body matter, also should not be considered as applicant and the theme is not thought of as to disclosed application
A part for theme.
Those listed above it is a series of describe in detail only for the application feasibility embodiment specifically
Bright, they are simultaneously not used to limit the protection domain of the application, all equivalent implementations made without departing from the application skill spirit
Or change should be included within the protection domain of the application.
Claims (10)
- A kind of 1. antimicrobial form feather dress fabric, it is characterised in that：It is mixed including llowing group of materials parts by weights：Chitin fiber 8-12 parts, sodium hypophosphite 5-8 parts, pearl fiber 3-5 parts, antibacterial finishing agent 12-18 parts, duck's down fiber 40-55 parts, coffee carbon Fiber 35-50 parts, Fypro 65-80 parts, bleeding agent 10-15 parts, toluene 3-5 parts, butanone 2-4 parts.
- A kind of 2. antimicrobial form feather dress fabric according to claim 1, it is characterised in that：The antibacterial finishing agent includes essence Refine agent 5-8 parts, hydrogen peroxide 10-16 parts, sodium metasilicate 8-12 parts, sodium carbonate 8-12 parts, sodium hydroxide 1-2 parts.
- A kind of 3. antimicrobial form feather dress fabric according to claim 2, it is characterised in that：The antibiotic downy jackets fabric with The bath raio 1 of antibacterial finishing agent:50.
- A kind of 4. preparation method of antimicrobial form feather dress fabric according to claim 1, it is characterised in that：Including following step Suddenly：Step 1, chitin fiber, pearl fiber, duck's down fiber, coffee carbon fiber and Fypro are passed through into warp thread respectively And weft yarns, form semi-finished product fabric；Step 2, the semi-finished product fabric that step 1 is formed, be put into after warm water soaks sodium hypophosphite, antibacterial finishing agent, Soaked in bleeding agent, toluene and butanone mixed liquor；Step 3, by the fabric soaked through washing, drying, final ironing obtains finished product fabric.
- A kind of 5. preparation method of antimicrobial form feather dress fabric according to claim 4, it is characterised in that：Described in step 1 Warp thread forms including chitin fiber, pearl fiber and duck's down fiber blend, and the weft yarn includes coffee carbon fiber and polyamide Fiber blend forms.
- A kind of 6. preparation method of antimicrobial form feather dress fabric according to claim 4, it is characterised in that：Described in step 1 Semi-finished product fabric is twill-weave structure.
- A kind of 7. preparation method of antimicrobial form feather dress fabric according to claim 4, it is characterised in that：Described in step 2 The warm water temperature is 45-55 degrees Celsius, and soak time is 45-60 minutes.
- A kind of 8. preparation method of antimicrobial form feather dress fabric according to claim 4, it is characterised in that：Described in step 3 Water-washing process includes washing for the first time, second of washing and third time and washed.
- A kind of 9. preparation method of antimicrobial form feather dress fabric according to claim 8, it is characterised in that：The first time It is 80-95 degrees Celsius to wash water temperature, and it is 65-80 degrees Celsius that second, which is washed water temperature, and it is that 45-60 is Celsius that third time, which washes water temperature, Degree.
- A kind of 10. preparation method of antimicrobial form feather dress fabric according to claim 8, it is characterised in that：Described first Secondary washing, second of washing and third time washing time are 15 minutes.