CN107699087A - 一种水性纳米改性丙烯酸酯杀虫抗菌涂料及其制备方法 - Google Patents
一种水性纳米改性丙烯酸酯杀虫抗菌涂料及其制备方法 Download PDFInfo
- Publication number
- CN107699087A CN107699087A CN201710968579.4A CN201710968579A CN107699087A CN 107699087 A CN107699087 A CN 107699087A CN 201710968579 A CN201710968579 A CN 201710968579A CN 107699087 A CN107699087 A CN 107699087A
- Authority
- CN
- China
- Prior art keywords
- parts
- insecticidal
- acrylic acid
- nano
- defoamer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种水性纳米改性丙烯酸酯杀虫抗菌涂料，其原料按重量份包括以下组分：丙烯酸酯乳液35‑50 份、钛白粉15‑30份、纳米二氧化钛浆料10‑15份、抗菌纳米二氧化钛3‑6份、低聚丙烯酸钠溶液6‑9份、重质碳酸钙5‑9份、甲基丙烯酸甲酯‑笨乙烯‑丙烯酸丁酯共聚物微球3‑5份、高效氯氰菊酯0.5‑0.8份、植物提取艾草提取液0.2‑0.5份、负离子抗菌添加剂0.1‑0.3份、滑石粉2‑5份、成膜助剂0.3‑0.9份、分散剂0.2‑0.6份、增稠剂0.3‑0.6份、消泡剂0.3‑0.6份、去离子水30‑50份。本发明还提供其制备方法，本发明的涂料具有良好的施工性、耐人工气候老化、牢固不变形、健康环保、耐虫卵滋生、耐虫蛀、缓释杀虫、抗菌防霉等优点。
Description
技术领域
本发明涉及一种涂料，具体地说涉及一种水性纳米改性丙烯酸酯杀虫抗菌涂料及其制备方法。
背景技术
目前建筑装饰材料特别是房屋内墙的装饰材料，主要起到美化室内外的作用，使人感觉舒适温暖，房屋更加牢固，使用的材料一般是高岭土、硅石灰粉、滑石粉、云母粉、钛白粉等原料加入分散剂、润湿剂、丙二醇、乳液、水调和而成，起到了美化效果和保护墙体的作用但是人们对环保的要求越来越高，对墙面装饰材料提出来新的希望——杀虫抗菌涂料。现在饰材料虽然能够使室内墙面美观整洁，从而使居住和生活环境更舒适，但是很多现有的建筑装饰材料在使用中易在墙体表层滋生霉菌和虫卵，尤其是沿海等潮湿地区，霉菌能在20-38℃、相对湿度85％左右的适宜条件下大量繁殖，侵蚀建筑物表面，破坏底材，同时建筑内墙涂料表面由于暴露面积大，也是真菌、细菌、虫卵滋生的主要位置。这些霉菌、细菌、真菌、虫卵一方面破坏了涂料表面的美观和冲刷性，另一方面还严重影响人们的健康和对家居环境的破坏。
发明内容
为此，本发明所要解决的是提供一种水性纳米改性丙烯酸酯杀虫抗菌涂料及其制备方法，本发明的涂料具有良好的施工性、耐人工气候老化、牢固不变形、健康环保、耐虫卵滋生、耐虫蛀、缓释杀虫、抗菌防霉等优点。
为解决上述技术问题，本发明的技术方案为：一种水性纳米改性丙烯酸酯杀虫抗菌涂料，其原料按重量份包括以下组分：丙烯酸酯乳液35-50 份、钛白粉15-30份、纳米二氧化钛浆料10-15份、抗菌纳米二氧化钛3-6份、低聚丙烯酸钠溶液6-9份、重质碳酸钙5-9份、甲基丙烯酸甲酯-笨乙烯-丙烯酸丁酯共聚物微球3-5份、高效氯氰菊酯0.5-0.8份、植物提取艾草提取液0.2-0.5份、负离子抗菌添加剂0.1-0.3份、滑石粉2-5份、成膜助剂0.3-0.9份、分散剂0.2-0.6份、增稠剂0.3-0.6份、消泡剂0.3-0.6份、去离子水30-50份。
进一步地，所述的一种水性纳米改性丙烯酸酯杀虫抗菌涂料，其原料按重量份包括以下组分：丙烯酸酯乳液35份、钛白粉15份、纳米二氧化钛浆料10份、抗菌纳米二氧化钛3份、低聚丙烯酸钠溶液6份、重质碳酸钙5份、甲基丙烯酸甲酯-笨乙烯-丙烯酸丁酯共聚物微球3份、高效氯氰菊酯0.5份、植物提取艾草提取液0.2份、负离子抗菌添加剂0.1份、滑石粉2份、成膜助剂0.3份、分散剂0.2份、增稠剂0.3份、消泡剂0.3份、去离子水30份。
进一步地，所述的一种水性纳米改性丙烯酸酯杀虫抗菌涂料，其原料按重量份包括以下组分：丙烯酸酯乳液50 份、钛白粉30份、纳米二氧化钛浆料15份、抗菌纳米二氧化钛6份、低聚丙烯酸钠溶液9份、重质碳酸钙9份、甲基丙烯酸甲酯-笨乙烯-丙烯酸丁酯共聚物微球5份、高效氯氰菊酯0.8份、植物提取艾草提取液0.5份、负离子抗菌添加剂0.3份、滑石粉5份、成膜助剂0.9份、分散剂0.6份、增稠剂0.6份、消泡剂0.6份、去离子水50份。
进一步地，所述的一种水性纳米改性丙烯酸酯杀虫抗菌涂料，其原料按重量份包括以下组分：丙烯酸酯乳液45份、钛白粉22份、纳米二氧化钛浆料13份、抗菌纳米二氧化钛5份、低聚丙烯酸钠溶液7份、重质碳酸钙6份、甲基丙烯酸甲酯-笨乙烯-丙烯酸丁酯共聚物微球4份、高效氯氰菊酯0.6份、植物提取艾草提取液0.4份、负离子抗菌添加剂0.2份、滑石粉4份、成膜助剂0.6份、分散剂0.4份、增稠剂0.4份、消泡剂0.4份、去离子水35份。
进一步地，所述的一种水性纳米改性丙烯酸酯杀虫抗菌涂料，其制备方法包括以下步骤：
S10、缓释载体和复合杀虫添加剂预吸附：在甲基丙烯酸甲酯-笨乙烯-丙烯酸丁酯共聚物微球粉末中，低速分散下先后加入配方中定量的高效氯氰菊酯、植物提取艾草提取液，混合均匀后静置24h充分预吸附得预吸附液；
S11、增稠剂预溶解：将需要添加的增稠剂与15倍去离子水混合均匀，密封待用即预制浆；
S12、按顺序准确向分散缸加入去离子水（预留一部分可用于调整黏度、冲洗缸壁、溶解残留预制浆），底转速下依次投入各纳米材料至完全溶解，随后加入分散剂、成膜助剂、一半消泡剂、滑石粉、钛白粉、重质碳酸钙等和准备好的杀虫粉体和负离子抗菌添加剂，调快转速分散30-40min至浆料细度小于或等于50微米；
S13、降低转速，按顺序加入丙烯酸酯乳液、低聚丙烯酸钠溶液、另一半消泡剂，搅拌10-20min后，缓慢投入预制浆、预吸附液及余下的去离子水低速分散混合既得所需的一种水性纳米改性丙烯酸酯杀虫抗菌涂料。
进一步地，所述的钛白粉为为锐钛型钛白粉或金红石型钛白粉中的任何一种或其任意配比的混合物。
进一步地，所述的重质碳酸钙为过1500目筛超细粉。
进一步地，所述分散剂为丙烯酸氨盐分散剂1124 或ACSODIUM5045。
进一步地，所述的所述所述的消泡剂为有机硅类消泡剂、矿物油类消泡剂或其组合。
本发明的作用效果：
1、本发明中加入纳米二氧化钛后，纳米材料的光散射性好，粒度小且分布均匀，涂料遮盖力有明显的提高，遮盖力增长率约为27.5%，改善了涂料的施工性能；
2、本发明中添加复合纳米二氧化钛的水性建筑涂料具有杀菌功能，含纳米二氧化钛的涂料在紫外线照射30min后，对金黄色葡萄球菌、大肠杆菌杀菌均较好，抑菌率分别为82.2%\79.2%，但在无紫外线照射下，无明显的杀菌效果；
3、本发明的特点是采用新型甲基丙烯酸甲酯-苯乙烯-丙烯酸丁酯共聚物微球近饱和吸附高效高效氯氰菊酯和植物提取艾草提取液的复配杀虫组分，加入到丙烯酸酯乳液的基础涂料中，制备得到的水性纳米改性丙烯酸酯杀虫抗菌涂料能够迅速持久地驱逐、触杀各种害虫，具有抗菌防霉效果好、耐人工气候老化、良好的施工性、耐虫卵滋生、耐虫蛀、缓释杀虫效果、耐冲刷、对人体无毒无害、环保美观的高装饰性装饰的涂料，本装饰涂料不但具有绿色环保，缓释杀虫、抗菌防霉作用效果，而且该装饰涂料能够渗透到水泥墙面内与水泥构成一个整体，附着力特别强，硬度大；装饰后的墙面还具有耐老化，耐虫蛀、耐冲刷、牢固不变形、高装饰性强的特点。
具体实施方式
为了使本发明的内容更容易被清楚的理解，下面根据本发明的具体实施例，对本发明作进一步详细的说明。
实施例1
一种水性纳米改性丙烯酸酯杀虫抗菌涂料，其原料按重量份包括以下组分：丙烯酸酯乳液35份、钛白粉15份、纳米二氧化钛浆料10份、抗菌纳米二氧化钛3份、低聚丙烯酸钠溶液6份、重质碳酸钙5份、甲基丙烯酸甲酯-笨乙烯-丙烯酸丁酯共聚物微球3份、高效氯氰菊酯0.5份、植物提取艾草提取液0.2份、负离子抗菌添加剂0.1份、滑石粉2份、成膜助剂0.3份、分散剂0.2份、增稠剂0.3份、消泡剂0.3份、去离子水30份。
其制备方法包括以下步骤：
S10、缓释载体和复合杀虫添加剂预吸附：在甲基丙烯酸甲酯-笨乙烯-丙烯酸丁酯共聚物微球粉末中，低速分散下先后加入配方中定量的高效氯氰菊酯、植物提取艾草提取液，混合均匀后静置24h充分预吸附得预吸附液；
S11、增稠剂预溶解：将需要添加的增稠剂与15倍去离子水混合均匀，密封待用即预制浆；
S12、按顺序准确向分散缸加入去离子水（预留一部分可用于调整黏度、冲洗缸壁、溶解残留预制浆），底转速下依次投入各纳米材料至完全溶解，随后加入分散剂、成膜助剂、一半消泡剂、滑石粉、钛白粉、重质碳酸钙等和准备好的杀虫粉体和负离子抗菌添加剂，调快转速分散30min至浆料细度小于或等于50微米；
S13、降低转速，按顺序加入丙烯酸酯乳液、低聚丙烯酸钠溶液、另一半消泡剂，搅拌10min后，缓慢投入预制浆、预吸附液及余下的去离子水低速分散混合既得所需的一种水性纳米改性丙烯酸酯杀虫抗菌涂料。
所述的钛白粉为为锐钛型钛白粉。
所述的重质碳酸钙为过1500目筛超细粉。
所述分散剂为丙烯酸氨盐分散剂1124 。
所述的所述所述的消泡剂为有机硅类消泡剂。
实施例2
一种水性纳米改性丙烯酸酯杀虫抗菌涂料，其原料按重量份包括以下组分：丙烯酸酯乳液50 份、钛白粉30份、纳米二氧化钛浆料15份、抗菌纳米二氧化钛6份、低聚丙烯酸钠溶液9份、重质碳酸钙9份、甲基丙烯酸甲酯-笨乙烯-丙烯酸丁酯共聚物微球5份、高效氯氰菊酯0.8份、植物提取艾草提取液0.5份、负离子抗菌添加剂0.3份、滑石粉5份、成膜助剂0.9份、分散剂0.6份、增稠剂0.6份、消泡剂0.6份、去离子水50份。
其制备方法包括以下步骤：
S10、缓释载体和复合杀虫添加剂预吸附：在甲基丙烯酸甲酯-笨乙烯-丙烯酸丁酯共聚物微球粉末中，低速分散下先后加入配方中定量的高效氯氰菊酯、植物提取艾草提取液，混合均匀后静置24h充分预吸附得预吸附液；
S11、增稠剂预溶解：将需要添加的增稠剂与15倍去离子水混合均匀，密封待用即预制浆；
S12、按顺序准确向分散缸加入去离子水（预留一部分可用于调整黏度、冲洗缸壁、溶解残留预制浆），底转速下依次投入各纳米材料至完全溶解，随后加入分散剂、成膜助剂、一半消泡剂、滑石粉、钛白粉、重质碳酸钙等和准备好的杀虫粉体和负离子抗菌添加剂，调快转速分散40min至浆料细度小于或等于50微米；
S13、降低转速，按顺序加入丙烯酸酯乳液、低聚丙烯酸钠溶液、另一半消泡剂，搅拌20min后，缓慢投入预制浆、预吸附液及余下的去离子水低速分散混合既得所需的一种水性纳米改性丙烯酸酯杀虫抗菌涂料。
所述的钛白粉为为金红石型钛白粉。
所述的重质碳酸钙为过1500目筛超细粉。
所述分散剂为ACSODIUM5045。
所述的所述所述的消泡剂为矿物油类消泡剂。
实施例3
一种水性纳米改性丙烯酸酯杀虫抗菌涂料，其原料按重量份包括以下组分：丙烯酸酯乳液45份、钛白粉22份、纳米二氧化钛浆料13份、抗菌纳米二氧化钛5份、低聚丙烯酸钠溶液7份、重质碳酸钙6份、甲基丙烯酸甲酯-笨乙烯-丙烯酸丁酯共聚物微球4份、高效氯氰菊酯0.6份、植物提取艾草提取液0.4份、负离子抗菌添加剂0.2份、滑石粉4份、成膜助剂0.6份、分散剂0.4份、增稠剂0.4份、消泡剂0.4份、去离子水35份。
其制备方法包括以下步骤：
S10、缓释载体和复合杀虫添加剂预吸附：在甲基丙烯酸甲酯-笨乙烯-丙烯酸丁酯共聚物微球粉末中，低速分散下先后加入配方中定量的高效氯氰菊酯、植物提取艾草提取液，混合均匀后静置24h充分预吸附得预吸附液；
S11、增稠剂预溶解：将需要添加的增稠剂与15倍去离子水混合均匀，密封待用即预制浆；
S12、按顺序准确向分散缸加入去离子水（预留一部分可用于调整黏度、冲洗缸壁、溶解残留预制浆），底转速下依次投入各纳米材料至完全溶解，随后加入分散剂、成膜助剂、一半消泡剂、滑石粉、钛白粉、重质碳酸钙等和准备好的杀虫粉体和负离子抗菌添加剂，调快转速分散35min至浆料细度小于或等于50微米；
S13、降低转速，按顺序加入丙烯酸酯乳液、低聚丙烯酸钠溶液、另一半消泡剂，搅拌15min后，缓慢投入预制浆、预吸附液及余下的去离子水低速分散混合既得所需的一种水性纳米改性丙烯酸酯杀虫抗菌涂料。
所述的钛白粉为为锐钛型钛白粉或金红石型钛白粉中的任意配比的混合物。
所述的重质碳酸钙为过1500目筛超细粉。
所述分散剂为丙烯酸氨盐分散剂1124 。
所述的所述所述的消泡剂为有机硅类消泡剂、矿物油类消泡剂的任意配比的混合物。
本发明的一种水性纳米改性丙烯酸酯杀虫抗菌涂料性能检测结果如下表1所示
表2为本发明一种水性纳米改性丙烯酸酯杀虫抗菌涂料遮盖力对比检测结果表
表3为本发明一种水性纳米改性丙烯酸酯杀虫抗菌涂料抗菌性能检测表
| 供试微生物菌株 | 待测涂料菌落数 | 对照涂料菌落数 | 抑菌率/% |
| 金黄色葡萄球菌 | 30 | 168 | 82．18 |
| 大肠杆菌 | 47 | 216 | 78．24 |
表4为本发明一种水性纳米改性丙烯酸酯杀虫抗菌涂料在杀虫效果评价
通过表1、表2、表3表4可以看出本发明的一种水性纳米改性丙烯酸酯杀虫抗菌涂料能够迅速持久地驱逐、触杀各种害虫，具有抗菌防霉效果好、耐人工气候老化、耐虫卵滋生、耐虫蛀、缓释杀虫效果、耐冲刷、良好的施工性、对人体无毒无害、环保美观的高装饰性装饰的涂料，本装饰涂料不但具有绿色环保，缓释杀虫、抗菌防霉作用效果，而且该装饰涂料能够渗透到水泥墙面内与水泥构成一个整体，附着力特别强，硬度大；装饰后的墙面还具有耐老化，耐虫蛀、耐冲刷、牢固不变形、高装饰性强的特点。
Claims (9)
1.一种水性纳米改性丙烯酸酯杀虫抗菌涂料，其特征在于，其原料按重量份包括以下组分：丙烯酸酯乳液35-50 份、钛白粉15-30份、纳米二氧化钛浆料10-15份、抗菌纳米二氧化钛3-6份、低聚丙烯酸钠溶液6-9份、重质碳酸钙5-9份、甲基丙烯酸甲酯-笨乙烯-丙烯酸丁酯共聚物微球3-5份、高效氯氰菊酯0.5-0.8份、植物提取艾草提取液0.2-0.5份、负离子抗菌添加剂0.1-0.3份、滑石粉2-5份、成膜助剂0.3-0.9份、分散剂0.2-0.6份、增稠剂0.3-0.6份、消泡剂0.3-0.6份、去离子水30-50份。
2.根据权利要求1所述的一种水性纳米改性丙烯酸酯杀虫抗菌涂料，其特征在于，其原料按重量份包括以下组分：丙烯酸酯乳液35份、钛白粉15份、纳米二氧化钛浆料10份、抗菌纳米二氧化钛3份、低聚丙烯酸钠溶液6份、重质碳酸钙5份、甲基丙烯酸甲酯-笨乙烯-丙烯酸丁酯共聚物微球3份、高效氯氰菊酯0.5份、植物提取艾草提取液0.2份、负离子抗菌添加剂0.1份、滑石粉2份、成膜助剂0.3份、分散剂0.2份、增稠剂0.3份、消泡剂0.3份、去离子水30份。
3.根据权利要求1所述的一种水性纳米改性丙烯酸酯杀虫抗菌涂料，其特征在于，其原料按重量份包括以下组分：丙烯酸酯乳液50 份、钛白粉30份、纳米二氧化钛浆料15份、抗菌纳米二氧化钛6份、低聚丙烯酸钠溶液9份、重质碳酸钙9份、甲基丙烯酸甲酯-笨乙烯-丙烯酸丁酯共聚物微球5份、高效氯氰菊酯0.8份、植物提取艾草提取液0.5份、负离子抗菌添加剂0.3份、滑石粉5份、成膜助剂0.9份、分散剂0.6份、增稠剂0.6份、消泡剂0.6份、去离子水50份。
4.根据权利要求1所述的一种水性纳米改性丙烯酸酯杀虫抗菌涂料，其特征在于，其原料按重量份包括以下组分：丙烯酸酯乳液45份、钛白粉22份、纳米二氧化钛浆料13份、抗菌纳米二氧化钛5份、低聚丙烯酸钠溶液7份、重质碳酸钙6份、甲基丙烯酸甲酯-笨乙烯-丙烯酸丁酯共聚物微球4份、高效氯氰菊酯0.6份、植物提取艾草提取液0.4份、负离子抗菌添加剂0.2份、滑石粉4份、成膜助剂0.6份、分散剂0.4份、增稠剂0.4份、消泡剂0.4份、去离子水35份。
5.根据权利要求1-4任一所述的一种水性纳米改性丙烯酸酯杀虫抗菌涂料，其特征在于，其制备方法包括以下步骤：
S10、缓释载体和复合杀虫添加剂预吸附：在甲基丙烯酸甲酯-笨乙烯-丙烯酸丁酯共聚物微球粉末中，低速分散下先后加入配方中定量的高效氯氰菊酯、植物提取艾草提取液，混合均匀后静置24h充分预吸附得预吸附液；
S11、增稠剂预溶解：将需要添加的增稠剂与15倍去离子水混合均匀，密封待用即预制浆；
S12、按顺序准确向分散缸加入去离子水（预留一部分可用于调整黏度、冲洗缸壁、溶解残留预制浆），底转速下依次投入各纳米材料至完全溶解，随后加入分散剂、成膜助剂、一半消泡剂、滑石粉、钛白粉、重质碳酸钙等和准备好的杀虫粉体和负离子抗菌添加剂，调快转速分散30-40min至浆料细度小于或等于50微米；
S13、降低转速，按顺序加入丙烯酸酯乳液、低聚丙烯酸钠溶液、另一半消泡剂，搅拌10-20min后，缓慢投入预制浆、预吸附液及余下的去离子水低速分散混合既得所需的一种水性纳米改性丙烯酸酯杀虫抗菌涂料。
6.根据权利要求1-4任一所述的一种水性纳米改性丙烯酸酯杀虫抗菌涂料，其特征在于，所述的钛白粉为为锐钛型钛白粉或金红石型钛白粉中的任何一种或其任意配比的混合物。
7.根据权利要求1-4任一所述的一种水性纳米改性丙烯酸酯杀虫抗菌涂料，其特征在于，所述的重质碳酸钙为过1500目筛超细粉。
8.根据权利要求1-4任一所述的一种水性纳米改性丙烯酸酯杀虫抗菌涂料，其特征在于，所述分散剂为丙烯酸氨盐分散剂1124 或ACSODIUM5045。
9.根据权利要求1-4任一所述的一种水性纳米改性丙烯酸酯杀虫抗菌涂料，其特征在于，所述的所述所述的消泡剂为有机硅类消泡剂、矿物油类消泡剂或其组合。