CN107260007A - A kind of woody odor silica gel food pad - Google Patents
A kind of woody odor silica gel food pad Download PDFInfo
- Publication number
- CN107260007A CN107260007A CN201610216963.4A CN201610216963A CN107260007A CN 107260007 A CN107260007 A CN 107260007A CN 201610216963 A CN201610216963 A CN 201610216963A CN 107260007 A CN107260007 A CN 107260007A
- Authority
- CN
- China
- Prior art keywords
- silica gel
- powder
- food pad
- weight
- wood powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of woody odor silica gel food pad, the food pad includes footpath and compiles cloth and be coated in the silica gel on footpath Bian Bu surfaces, and silica gel includes the component of following parts by weight：100 parts by weight of silicone rubber, 0.1~20 parts by weight wood powder, 15~40 parts of filler material by weight, 1~4 parts by weight auxiliary agent, 0.4~10 parts by weight pigment；One or more of mixtures of the wood powder in santal wood powder, pine powder, joss powder, fir powder, rosewood powder, cloves wood powder.Compared with prior art, the fragrance of wood powder is dissolved into food product environment by the silica gel food pad product for the wood powder that the present invention is added in digestion process, improve the single deficiency of silica gel chemical products smell, make product in itself closer to field of food, this product is the upgrading of the improvement to original silicagel pad product, the smell impression of wooden delicate fragrance is added, boiling tools production is had more preferable transition and performance boost.
Description
Technical field
The present invention relates to food processing boiling field of tool, and in particular to a kind of woody odor silica gel food pad.
Background technology
It is workable to have gauze, straw mattress and disposable PP cages cloth in food cooking industry, also have many
Retailer works as cage pad with the Polywoven Bag for packing chemical fertilizer or cement.Gauze and straw pad have one and very intractable asked
Topic, i.e. wheaten food and mat adhesion is very serious, and this have impact on the outward appearance of institute's steaming food, while being a kind of waste.Need
To rub repeatedly and wash, rinse and remove viscous dough, time-consuming, laborious, water wasting.The gauze or grass used for a long time
Pad is easy to assemble dirt, especially straw mattress, because many dirts enter inside the grass blade of straw mattress, it is extremely difficult to which cleaning is dry
Only, very easy breed bacteria.Disposable PP cages cloth is commercially not suitable for promoting due to cost reason.Using
Polywoven Bag or plastic cloth can discharge toxin at high temperature, and food is unhygienic, to the health effect of diner
It is very big.
Chinese patent CN102462384A discloses a kind of organosilicon composite material sanitary and does not glue cage pad and its making
Method, is the new product to above-mentioned tradition using the improvement of product, and gradually approved by market.Food items industry
It is required that it is convenient faster, efficiently, it is quick, make silica gel steamer pad many and aluminum food steamer, stainless steel food steamer, stainless
Steel steaming plate is used after being combined with each other turns into the market mainstream, and chemical silica gel product is odorless tasteless, steel, aluminum
Food steamer adds chemical silica gel cage pad and is combined boiling instrument, has lacked the wooden delicate fragrance of traditional wooden food steamer, Bamboo food steamer,
Chemical silica gel cage pad, which is added, from traditional wooden food steamer, Bamboo food steamer to efficiently steel, aluminum food steamer is combined boiling
Instrument has lacked the continuity on smell.
The content of the invention
It is an object of the present invention to overcome the above-mentioned drawbacks of the prior art and provide a kind of and conventional boil
The woody odor silica gel food pad that technique is more nearly.
The purpose of the present invention can be achieved through the following technical solutions：A kind of woody odor silica gel food pad, the food
Product pad includes footpath and compiles cloth and be coated in the silica gel on footpath Bian Bu surfaces, and described silica gel includes the group of following parts by weight
Point：
The wood powder is in santal wood powder, pine powder, joss powder, fir powder, rosewood powder, cloves wood powder
One or more of mixtures.
The particle diameter of the wood powder is 200~1250 mesh.Fragrant natural environmental-protective wood powder is added to silica gel formula
In, the smell impression of food can be increased, steaming prod is contained a marshmarigold-leaved beesia rhizome smell, make the food of boiling more
Uniqueness, the wood powder of addition has santal wood powder, pine powder, joss powder, fir powder, rosewood powder, cloves wood powder,
Santal wood powder discharges pure natural santal original flavor, and smell adds in food product environment, can make one ventilation and direct oneself from boredom,
Promote heart quiet, the gas of the rosin of pine, fir wood, rosewood, cloves wood can send original quiet and beautiful perfume (or spice)
Taste, so add the silica gel food pad of wood powder just with can just have identical or more preferably smell as Bamboo food steamer
Impression.
The silicon rubber is high-temperature silicon disulfide rubber, and its molecular formula is as follows：
Wherein, the one kind of Me in hydroxyl, methyl or vinyl, n, m, p are respectively different Si-O chain links
The degree of polymerization, n is that 10~20, m is that 10~20, p is 10~20, R1、R2It is identical or different, R1、R2Choosing
From methyl, phenyl, vinyl or CH2CH2CHF3One kind in group.
Described filler is white filler, selected from talcum powder, diatomite, mica powder, kaolin, gas-phase silica
Or one or more of mixtures in calcium carbonate, the particle diameter of the filler is 200~3000 mesh.
Described auxiliary agent is silazane analog assistant.
Described silazane analog assistant includes HMDS and octamethylcyclotetrasilazane.
Described pigment is selected from pigment yellow, paratonere, pigment violet, alizarol saphirol, naphthol green, pigment brown, pigment black
Or one kind in Pigment white.
It is by one kind in polyester fiber, vinylon, spandex, cotton, flax that cloth is compiled in described footpath
Or the mesh fabric of a variety of compositions, the mesh of the mesh fabric is 10~40 mesh, the shape of mesh include it is square,
Circle, one kind of ellipse, triangle, quadrangle, pentagon, hexagon；The thickness that cloth is compiled in the footpath is
0.3mm~0.6mm, the grammes per square metre that cloth is compiled in footpath is 50g~110g/m2。
Described silicon rubber, filler, auxiliary agent, wood powder, pigment are mixed, stirred in proportion, high-temperature process, roller
Use, the glue being made is compiled cloth in footpath and is coated, by drying tunnel curing molding, divide after grinding, filtering post-processing
It is cut into required product size.
The edge of described silica gel food pad carries out bound edge processing, and described bound edge processing mode includes carrying out edge
Apply and reheating is carried out after silica gel solidify the mode of bound edge, or processing of directly being lockstitched a border with line mode.
The woody odor silica gel food pad product, silica gel that can be in different colors is ink, passes through bat printing, silk-screen
Mode carry out beating trade mark processing on the product cut.The silica gel ink colors used include pigment yellow,
Paratonere, pigment violet, alizarol saphirol, naphthol green, pigment brown, pigment black, Pigment white, while being different from xylon gas
The color of taste food advance capital for body.
The thickness of described silica gel food pad is 0.65~2mm, and the grammes per square metre of silica gel food pad is 350~800g/m2。
Compared with prior art, beneficial effects of the present invention are embodied in：The silica gel food pad product of the wood powder of addition exists
The fragrance of wood powder is dissolved into food product environment by digestion process, improves the single deficiency of silica gel chemical products smell,
Make product in itself closer to field of food, this product is the upgrading of the improvement to original silicagel pad product, is added wooden
The smell impression of delicate fragrance, makes boiling tools production have more preferable transition and performance boost.
Brief description of the drawings
Fig. 1 is structural representation of the invention.
Embodiment
Embodiments of the invention are elaborated below, the present embodiment enters under premised on technical solution of the present invention
Row is implemented, and gives detailed embodiment and specific operating process, but protection scope of the present invention is not limited to down
The embodiment stated.
Embodiment 1
The parts by weight of high temperature silicone rubber 100, the parts by weight of talcum powder 20, processing aid HMDS 0.5
Parts by weight, the parts by weight of santal wood powder 10, the mesh of wood powder particle diameter 300, the parts by weight of white color 5, mix in proportion,
The glue being made after stirring, high-temperature process, roller grinding, filtering, terylene net is coated in using rolling method by glue
On eye cloth, material selection polyester fiber is 0.3mm from eyelet fabric thickness, and woven dacron mesh is 10 mesh, gram
Focus on 50g/m2, final product thickness 0.65mm, grammes per square metre 350g/m2.A diameter of 40cm circle is cut out,
Edge is coated after silica gel and carries out reheating solidification bound edge, using green silica gel ink, print house mark
On woody odor silica gel food pad, the structure of its final products is as shown in Figure 1.
Embodiment 2
The parts by weight of high temperature silicone rubber 100, the parts by weight of processing aid octamethylcyclotetrasilazane 4, mica powder filler
40 parts by weight, the parts by weight of santal wood powder 20, the mesh of wood powder particle diameter 600, color 10 parts by weight of Huang are mixed in proportion
Glue, is coated in and washed by the glue being made after conjunction, stirring, high-temperature process, roller grinding, filtering using rolling method
It is 0.6mm from eyelet fabric thickness on synthetic fibre eyelet fabric, material selection polyester fiber, vinal is washed
Synthetic fibre cloth mesh is 40 mesh, and grammes per square metre is in 110g/m2, final product thickness 2mm, grammes per square metre 800g/m2.Cut out chi
The very little rectangle for 30*40cm, direct lock seaming processing is carried out to edge, and using red silica gel ink, printing is public
Trade mark is taken charge of on woody odor silica gel food pad.
Embodiment 3
The parts by weight of high temperature silicone rubber 100, the parts by weight of pearl filler 20, processing aid octamethylcyclotetrasilazane
2 parts by weight, the parts by weight of pine powder 5, the mesh of wood powder particle diameter 1250, the parts by weight of white color 5, mix in proportion,
The glue being made after stirring, high-temperature process, roller grinding, filtering, terylene net is coated in using rolling method by glue
On eye cloth, material selection spandex, is 0.5mm from eyelet fabric thickness, and woven dacron mesh is 30 mesh, and grammes per square metre exists
80g/m2, final product thickness 0.8mm, grammes per square metre 400g/m2.The rectangle that size is 50*70cm is cut out,
Edge is coated after silica gel and carries out reheating solidification bound edge, using green silica gel ink, print house mark
On woody odor silica gel food pad.Direct lock seaming processing is carried out to edge, using blue silica gel ink, printing is public
Trade mark is taken charge of on woody odor silica gel food pad.
Embodiment 4
The parts by weight of high temperature silicone rubber 100, the parts by weight of tripolite filling material 25, processing aid octamethylcyclotetrasilazane
0.9 parts by weight, the parts by weight of cloves wood powder 5, the mesh of wood powder particle diameter 300, the parts by weight of white color 3, mix in proportion,
The glue being made after stirring, high-temperature process, roller grinding, filtering, terylene net is coated in using rolling method by glue
On eye cloth, material selection polyester fiber and spandex blended yarn weaved fabric are 0.6mm, woven dacron from eyelet fabric thickness
Mesh is 40 mesh, and grammes per square metre is in 110g/m2, final product thickness 1.1mm, grammes per square metre 450g/m2.Cut out diameter
For 70cm circle, edge is coated after silica gel and carries out reheating solidification bound edge, using green silica gel ink,
House mark is printed on woody odor silica gel food pad.
Embodiment 5
The parts by weight of high temperature silicone rubber 100, the parts by weight of tripolite filling material 10, the parts by weight of pearl filler 10, processing
The parts by weight of auxiliary agent octamethylcyclotetrasilazane 1, the parts by weight of cloves wood powder 5, the mesh of wood powder particle diameter 500, rosewood powder
5 parts by weight, the parts by weight of white color 5 are made after mixing, stirring, high-temperature process, roller grinding, filtering in proportion
Into glue, glue is coated on Dacron mesh cloth using rolling method, from eyelet fabric thickness be 0.3mm,
Woven dacron mesh is 10 mesh, and grammes per square metre is in 50g/m2, final product thickness 0.8mm, grammes per square metre 400g/m2.Cutting
Go out a diameter of 60 circle, edge is coated after silica gel carry out reheating solidification bound edge, use green silica gel
Ink, printing house mark is on woody odor silica gel food pad.
Embodiment 6
The talcum powder of high temperature silicone rubber 100, the parts by weight of talcum powder 5, the talcum powder of tripolite filling material 5, pearl filler
5 talcum powder, 0.6 part of processing aid HMDS, the talcum powder of rosewood powder 0.1, wood powder particle diameter 200
Mesh, 0.4 part of white color, the glue being made in proportion after mixing, stirring, high-temperature process, roller grinding, filtering,
Glue is coated on Dacron mesh cloth using rolling method, is 0.6mm, woven dacron mesh from eyelet fabric thickness
For 40 mesh, grammes per square metre is in 110g/m2, final product thickness 1.0mm, grammes per square metre 440g/m2.Cutting out size is
30*40cm rectangle, is coated after silica gel to product edge and carries out reheating solidification bound edge, use green
Silica gel ink, printing house mark is on woody odor silica gel food pad.
Claims (10)
1. a kind of woody odor silica gel food pad, it is characterised in that the food pad includes footpath and compiles cloth and be coated in
The silica gel on footpath Bian Bu surfaces, described silica gel includes the component of following parts by weight：
The wood powder is in santal wood powder, pine powder, joss powder, fir powder, rosewood powder, cloves wood powder
One or more of mixtures.
2. a kind of woody odor silica gel food pad according to claim 1, it is characterised in that the wood powder
Particle diameter be 200~1250 mesh.
3. a kind of woody odor silica gel food pad according to claim 1, it is characterised in that the silicon rubber
Glue is high-temperature silicon disulfide rubber, and its molecular formula is as follows：
Wherein, the one kind of Me in hydroxyl, methyl or vinyl, n, m, p are respectively different Si-O chain links
The degree of polymerization, n is that 10~20, m is that 10~20, p is 10~20, R1、R2It is identical or different, R1、R2Choosing
From methyl, phenyl, vinyl or CH2CH2CHF3One kind in group.
4. a kind of woody odor silica gel food pad according to claim 1, it is characterised in that described fills out
Expect for white filler, in talcum powder, diatomite, mica powder, kaolin, gas-phase silica or calcium carbonate
One or more of mixtures, the particle diameter of the filler is 200~3000 mesh.
5. a kind of woody odor silica gel food pad according to claim 1, it is characterised in that described helps
Agent is silazane analog assistant.
6. a kind of woody odor silica gel food pad according to claim 5, it is characterised in that described silicon
Azane analog assistant includes HMDS and octamethylcyclotetrasilazane.
7. a kind of woody odor silica gel food pad according to claim 1, it is characterised in that described face
Material is in pigment yellow, paratonere, pigment violet, alizarol saphirol, naphthol green, pigment brown, pigment black or Pigment white
It is a kind of.
8. a kind of woody odor silica gel food pad according to claim 1, it is characterised in that described footpath
Compiling cloth is made up of the one or more in polyester fiber, vinylon, spandex, cotton, flax
Mesh fabric, the mesh of the mesh fabric is 10~40 mesh, the shape of mesh include it is square, circular, oval,
Triangle, quadrangle, pentagon, one kind of hexagon；The thickness that cloth is compiled in the footpath is 0.3mm~0.6mm,
The grammes per square metre that cloth is compiled in footpath is 50g~110g/m2。
9. a kind of woody odor silica gel food pad according to claim 1, it is characterised in that described silicon
The edge of glue food pad carries out bound edge processing, and described bound edge processing mode is laggard including being coated silica gel to edge
Row reheating solidifies the mode of bound edge, or processing of directly being lockstitched a border with line mode.
10. a kind of woody odor silica gel food pad according to claim 1, it is characterised in that described silicon
The thickness of glue food pad is 0.65~2mm, and the grammes per square metre of silica gel food pad is 350~800g/m2。