CN107177056A - A kind of high anti-tear tire glue - Google Patents
A kind of high anti-tear tire glue Download PDFInfo
- Publication number
- CN107177056A CN107177056A CN201710447704.7A CN201710447704A CN107177056A CN 107177056 A CN107177056 A CN 107177056A CN 201710447704 A CN201710447704 A CN 201710447704A CN 107177056 A CN107177056 A CN 107177056A
- Authority
- CN
- China
- Prior art keywords
- parts
- tire
- tire glue
- glue
- tear
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the high anti-tear tire glue of one kind, the tire glue by mass component by being constituted as follows：60 80 parts of natural rubber, 20 30 parts of neoprene, 10 15 parts of EP rubbers, 36 parts of zinc oxide, 13 parts of stearic acid, 23 parts of age resistor, 0.4 0.6 parts of Sulfur, 45 parts of accelerator, 60 70 parts of carbon black, 68 parts of coumarone indene resin, 1.5 1.8 parts of polyethylene glycol, 12 parts of rosin, 68 parts of hydrogenated rosin.The invention provides the high anti-tear tire glue of one kind, the tire glue has the performance of excellent tear-proof, applied on automobile tire, can prevent blowing out for tire moment from causing serious potential safety hazard, be also the service life for extending tire on the one hand.
Description
Technical field
The present invention relates to automobile tire technical field, more particularly to a kind of high anti-tear tire glue.
Background technology
Tire is one of most important building block on automobile, and it supports the total weight of vehicle, bears the load of automobile,
Ensure the adhesive force on wheel and road surface, mitigate and absorb automobile vibrations in motion and impulsive force, prevent auto parts and components by
To strenuous vibration and earlier period damage, noise when adapting to the high speed performance of vehicle and reducing traveling, it is ensured that the security of traveling, behaviour
Handing stability, comfortableness and energy saving economy.
With the development of technology, existing tire is still good on the whole in many performances, but existing wheel
Tire is in terms of tear-proof or not ideal enough, so causes automobile to produce potential safety hazard in the process of moving.Particularly in automobile
During high-speed cruising, if tear resistance is poor, when automobile tire is received in extraneous sharp object thorn, tire will be broken moment
Split, cause car crash, the security of the lives and property to user causes great infringement.
The content of the invention
In view of this, the invention provides the high anti-tear tire glue of one kind, the tire glue has the performance of excellent tear-proof, applies
On automobile tire, it can prevent blowing out for tire moment from causing serious potential safety hazard, be also to extend tire on the one hand
Service life.
A kind of high anti-tear tire glue, the tire glue by mass component by being constituted as follows：
Preferably, the tire glue by mass component by being constituted below：
Preferably, the tire glue by mass component by being constituted below：
Preferably, the age resistor is at least one of anti-aging agent RD or antioxidant 4020.
Preferably, the age resistor is the mixture of anti-aging agent RD and antioxidant 4020, and its mass ratio is 1:2.
Preferably, the carbon black is at least one of carbon black N220 or white carbon.
Preferably, the mixture for carbon black N220 and white carbon, its mass ratio is 7:4.
Preferably, the accelerator is at least two in captax DB, accelerant NOBS and accelerator TBTD.
Preferably, the accelerator is captax DB, accelerant NOBS and accelerator TBTD mixing, its mass ratio
For 1:1:0.1.
The beneficial effects of the present invention are：The invention provides the high anti-tear tire glue of one kind, the tire glue has excellent anti-tear
The performance split, is applied on automobile tire, can prevent blowing out for tire moment from causing serious potential safety hazard, on the one hand
It is the service life for extending tire.
Embodiment：
To illustrate the thought and purpose of the present invention, below in conjunction with specific embodiment, the present invention is described further.
Embodiment 1
A kind of high anti-tear tire glue, tire glue by mass component by being constituted as follows：
After natural rubber, neoprene and EP rubbers are plasticated using banbury, fraction time adds zinc oxide, hard
Resin acid, age resistor, carbon black, coumarone indene resin, polyethylene glycol, rosin and hydrogenated rosin etc., mixing time is after addition every time
25-55s, melting temperature scope heats up at 40-110 DEG C and controls temperature to be heat-treated in the range of 115-145 DEG C, heat
Processing time in 3-8min, back glue add accelerator and Sulfur on a mill, then vulcanize on vulcanizing press, sulphur
Change condition is 155 DEG C × T90, obtains tire glue.
Determined by GB-T529-1999
Tearing strength (KN/m)：102.2
Embodiment 2
A kind of high anti-tear tire glue, tire glue by mass component by being constituted as follows：
After natural rubber, neoprene and EP rubbers are plasticated using banbury, fraction time addition zinc oxide,
Stearic acid, age resistor, carbon black, coumarone indene resin, polyethylene glycol, rosin and hydrogenated rosin etc., mixing time after adding every time
For 25-55s, melting temperature scope heats up at 40-110 DEG C and controls temperature to be heat-treated in the range of 115-145 DEG C,
Heat treatment time in 3-8min, back glue add accelerator and Sulfur on a mill, then vulcanize on vulcanizing press,
Conditions of vulcanization is 155 DEG C × T90, obtains tire glue.
Determined by GB-T529-1999
Tearing strength (KN/m)：105.8
Embodiment 3
A kind of high anti-tear tire glue, tire glue by mass component by being constituted as follows：
After natural rubber, neoprene and EP rubbers are plasticated using banbury, fraction time adds zinc oxide, hard
Resin acid, age resistor, carbon black, coumarone indene resin, polyethylene glycol, rosin and hydrogenated rosin etc., mixing time is after addition every time
25-55s, melting temperature scope heats up at 40-110 DEG C and controls temperature to be heat-treated in the range of 115-145 DEG C, heat
Processing time in 3-8min, back glue add accelerator and Sulfur on a mill, then vulcanize on vulcanizing press, sulphur
Change condition is 155 DEG C × T90, obtains tire glue.
Determined by GB-T529-1999
Tearing strength (KN/m)：113.4
Embodiment 4
A kind of high anti-tear tire glue, tire glue by mass component by being constituted as follows：
After natural rubber, neoprene and EP rubbers are plasticated using banbury, fraction time adds zinc oxide, hard
Resin acid, age resistor, carbon black, coumarone indene resin, polyethylene glycol, rosin and hydrogenated rosin etc., mixing time is after addition every time
25-55s, melting temperature scope heats up at 40-110 DEG C and controls temperature to be heat-treated in the range of 115-145 DEG C, heat
Processing time in 3-8min, back glue add accelerator and Sulfur on a mill, then vulcanize on vulcanizing press, sulphur
Change condition is 155 DEG C × T90, obtains tire glue.
Determined by GB-T529-1999
Tearing strength (KN/m)：117.8
Embodiment 5
A kind of high anti-tear tire glue, tire glue by mass component by being constituted as follows：
After natural rubber, neoprene and EP rubbers are plasticated using banbury, fraction time adds zinc oxide, hard
Resin acid, age resistor, carbon black, coumarone indene resin, polyethylene glycol, rosin and hydrogenated rosin etc., mixing time is after addition every time
25-55s, melting temperature scope heats up at 40-110 DEG C and controls temperature to be heat-treated in the range of 115-145 DEG C, heat
Processing time in 3-8min, back glue add accelerator and Sulfur on a mill, then vulcanize on vulcanizing press, sulphur
Change condition is 155 DEG C × T90, obtains tire glue.
Determined by GB-T529-1999
Tearing strength (KN/m)：120.4
Above is to specific embodiment provided by the present invention.
The present invention is described in detail specification, and specific case used herein is former to the structure of the present invention
Reason and embodiment are set forth, and above example is only intended to the method and its core concept for helping to understand the present invention；Together
When, for those of ordinary skill in the art, according to the thought of the present invention, have in specific embodiments and applications
Change part, in summary, this specification content should not be construed as limiting the invention.
Claims (9)
1. a kind of high anti-tear tire glue, it is characterised in that the tire glue by mass component by being constituted as follows：
。
2. tire glue according to claim 1, it is characterised in that the tire glue by mass component by being constituted below：
。
3. tire glue according to claim 1, it is characterised in that the tire glue by mass component by being constituted below：
。
4. according to any described tire glue of claims 1 to 3, it is characterised in that：The age resistor is anti-aging agent RD or anti-old
At least one of agent 4020.
5. tire glue according to claim 4, it is characterised in that：The age resistor is the mixed of anti-aging agent RD and antioxidant 4020
Compound, its mass ratio is 1:2.
6. according to any described tire glue of claims 1 to 3, it is characterised in that：The carbon black is carbon black N220 or white carbon
At least one of.
7. tire glue according to claim 6, it is characterised in that：Described is the mixture of carbon black N220 and white carbon, its matter
Amount is than being 7:4.
8. according to any described tire glue of claims 1 to 3, it is characterised in that：The accelerator is captax DB, accelerator
At least two in NOBS and accelerator TBTD.
9. tire glue according to claim 8, it is characterised in that：The accelerator be captax DB, accelerant NOBS and
Accelerator TBTD mixing, its mass ratio is 1:1:0.1.