CN107163734A - 一种环保涂料及其应用 - Google Patents
一种环保涂料及其应用 Download PDFInfo
- Publication number
- CN107163734A CN107163734A CN201710524823.8A CN201710524823A CN107163734A CN 107163734 A CN107163734 A CN 107163734A CN 201710524823 A CN201710524823 A CN 201710524823A CN 107163734 A CN107163734 A CN 107163734A
- Authority
- CN
- China
- Prior art keywords
- environmental protection
- coating material
- protection coating
- parts
- tio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种环保涂料，包括如下质量份数的组分：丙烯酸乳液10～25份；N掺杂的TiO25～20份；活性炭负载SnO21～5份；纤维素0.1～1份；滑石粉5～20份；助剂5～20份；水80～100份。本发明涂料在可见光照射下除甲醛效率达到88％以上。
Description
技术领域
本发明涉及涂料领域，具体涉及一种环保涂料及其应用。
背景技术
室内装修材料产生的有毒有害物质包括甲醛、微尘，严重影响人类家居健康。有报告显示，长期接触甲醛可引起各种呼吸道、消化道及皮肤癌症。目前，人们通常采用室内通风并延长入住时间、使用甲醛祛除剂等来降低室内甲醛浓度。以上做法很难除去隐蔽不通风部位的甲醛释放点。为了可长期有效将甲醛从室内装修中祛除，人们做了大量的工作。
CN104046062A公开了一种吸收甲醛的建筑涂料，本涂料产生具有强氧化力的氢氧游离基，在分解甲醛、苯、氨、TVOC等有机化合物的作用，同时达到了抗菌、防毒、除臭、防污、亲水自洁等效果。CN101020794B公开了一种环保水性漆的制备方法，主要应用胺基化合物、银氨溶液、两性氧化物组成的除醛功能组合物添加入水性漆中制备的一种水性漆。现有技术中的上述方法改善了涂料对有害气体的吸收作用，但其添加的无机催化剂，例如二氧化钛只能在紫外线照射的情况下发挥光催化降解作用，对于室内或常处于日光照射而非紫外线照射的基体不适用，应用上存在局限性。
发明内容
鉴于现有技术中存在的问题，本发明的目的之一在于提供一种环保涂料，包括如下质量份数的组分：
例如，丙烯酸乳液为10份、12份、15份、18份、20份、22份或25份等。N掺杂的TiO2为5份、6份、8份、10份、12份、14份、15份、16份、18份或20份。活性炭负载SnO2为5份、6份、8份、10份、12份、14份或15份。纤维素为0.1份、0.2份、0.3份、0.5份、0.8份或1份。滑石粉为5份、6份、8份、10份、12份、14份、15份、16份、18份或20份。助剂为5份、6份、8份、10份、12份、14份、15份、16份、18份或20份。水为80份、82份、85份、88份、90份、92份、95份、98份或100份。
本发明所述的环保涂料优选包括如下质量份数的组分：
本发明所述助剂优选包括分散剂、消泡剂、增稠剂和润湿剂。
优选地，所述分散剂包括聚羧酸铵盐和/或聚羧酸钠盐。
优选地，所述消泡剂包括矿物油改性消泡剂。
优选地，所述增稠剂包括邻苯二甲酸二丁酯、碱溶胀型丙烯酸或聚氨酯中的任意一种或至少两种的组合，其中典型但非限制性的组合为：邻苯二甲酸二丁酯和碱溶胀型丙烯酸的组合、碱溶胀型丙烯酸和聚氨酯的组合、邻苯二甲酸二丁酯和聚氨酯的组合。
优选地，所述润湿剂包括烷基聚氧乙烯醚。
优选地，所述分散剂、消泡剂、增稠剂与润湿剂的质量比为(1～3):(1～3):(1～3):(1～3)，例如1:3:3:1、1:2:3:2、1:1:3:3、1:3:1:3或1:1:1:1等，优选(1～2):(1～2):(1～2):(1～2)。
本发明所述N掺杂的TiO2中N与TiO2的质量比优选为(1～8):100，例如1:100、2:100、3:100、5:100、6:100或8:100，优选(3～5):100。
本发明所述N掺杂的TiO2的中值粒径优选为1.3～2.5μm，例如1.3μm、1.5μm、1.6μm、1.8μm、2μm、2.2μm或2.5μm等，优选1.5～2μm。
本发明所述活性炭负载SnO2中SnO2与活性炭的质量比优选为(15～50):100，例如15:100、18:100、20:100、25:100、30:100、25:100、30:100、35:100、40:100或50:100，优选(20～35):100。
本发明所述活性炭负载SnO2的中值粒径优选为1.3～2.5μm，例如1.3μm、1.5μm、1.6μm、1.8μm、2μm、2.2μm或2.5μm等，优选1.5～2μm。
本发明N掺杂的TiO2与活性炭负载SnO2的质量比优选为(1～3):(1～3)，例如1:1、2:1、1:2、1:3、3:1、3:2或2:3等，优选(1～2):(1～2)。
本发明的目的之二在于提供如目的之一所述环保涂料在内饰涂料中的应用。
本发明的目的之三在于提供如目的之一所述环保涂料在室外面漆中的应用。
相对于现有技术，本发明至少具有如下有益效果：
本发明的环保涂料通过按一定比例添加N掺杂的TiO2和活性炭负载SnO2与其他组分协同，实现了对可见光更高的利用率，且在无紫外光的可见光区也可被活化，除甲醛效率达到88％以上。本发明涂料在室内涂料中的应用不受限制，即使在长期得不到紫外光照射的环境下仍能发挥高催化效率，有效催化降低室内空气中的甲醛。
具体实施方式
下面通过具体实施方式来进一步说明本发明的技术方案。
为更好地说明本发明，便于理解本发明的技术方案，本发明列举实施例如下。本领域技术人员应该明了，所述实施例仅仅是帮助理解本发明，不应视为对本发明的具体限制。
实施例1
一种环保涂料，包括如下质量份数的组分：
其中，助剂由聚羧酸铵盐、矿物油改性消泡剂、邻苯二甲酸二丁酯、烷基聚氧乙烯醚按照质量比为1:3:1:3混合组成；
N掺杂的TiO2中值粒径为1.3μm，N与TiO2的质量比为1:100；
活性炭负载SnO2的中值粒径为1.3μm，SnO2与活性炭的质量比为15:100。
实施例2
一种环保涂料，包括如下质量份数的组分：
其中，助剂由聚羧酸钠盐、矿物油改性消泡剂、碱溶胀型丙烯酸、烷基聚氧乙烯醚按照质量比为3:3:1:1混合组成；
N掺杂的TiO2中值粒径为2.5μm，N与TiO2的质量比为8:100；
活性炭负载SnO2的中值粒径为2.5μm，SnO2与活性炭的质量比为50:100。
实施例3
一种环保涂料，包括如下质量份数的组分：
其中，助剂由聚羧酸钠盐、矿物油改性消泡剂、碱溶胀型丙烯酸、烷基聚氧乙烯醚按照质量比为1:2:2:1混合组成；
N掺杂的TiO2中值粒径为1.5μm，N与TiO2的质量比为3:100；
活性炭负载SnO2的中值粒径为2μm，SnO2与活性炭的质量比为35:100。
实施例4
一种环保涂料，包括如下质量份数的组分：
其中，助剂由聚羧酸钠盐、矿物油改性消泡剂、碱溶胀型丙烯酸、烷基聚氧乙烯醚按照质量比为2:1:1:1混合组成；
N掺杂的TiO2中值粒径为2μm，N与TiO2的质量比为5:100；
活性炭负载SnO2的中值粒径为1.5μm，SnO2与活性炭的质量比为20:100。
实施例5
一种环保涂料，包括如下质量份数的组分：
其中，助剂由聚羧酸钠盐、矿物油改性消泡剂、碱溶胀型丙烯酸、烷基聚氧乙烯醚按照质量比为1.5:1:1.5:1混合组成；
N掺杂的TiO2中值粒径为1.8μm，N与TiO2的质量比为4:100；
活性炭负载SnO2的中值粒径为1.7μm，SnO2与活性炭的质量比为30:100。
对比例1
与实施例5的区别仅在于：省去N掺杂的TiO2。
对比例2
与实施例5的区别仅在于：省去活性炭负载SnO2。
将各实施例以及对比例的涂料在100瓦的可见光照射120min后，测试甲醛净化效率S，整理于表1。
表1
| 实施例1 | 实施例2 | 实施例3 | 实施例4 | 实施例5 | 对比例1 | 对比例2 | |
| S | 88％ | 88.2％ | 88.9％ | 89.1％ | 91.2％ | 78％ | 84％ |
从表1可以看出，本发明通过按一定比例添加N掺杂的TiO2和活性炭负载SnO2与其他组分协同得到的环保涂料，实现了不可预期的甲醛去除效率，而实施例5与对比例1～2的结果证实，省略上述两种填料中的任意一种都会降低甲醛去除效率，这说明，两种填料存在协同作用，使得涂料被可见光激发后能催化降解有害气体，尤其扩宽了其在室内涂料中的应用，即使在长期得不到紫外光照射的环境下仍能发挥高催化效率，有效催化降低室内空气中的甲醛。
以上详细描述了本发明的优选实施方式，但是本发明并不限于上述实施方式中的具体细节，在本发明的技术构思范围内，可以对本发明的技术方案进行多种简单变型，这些简单变型均属于本发明的保护范围。
另外需要说明的是，在上述具体实施方式中所描述的各个具体技术特征，在不矛盾的情况下，可以通过任何合适的方式进行组合，为了避免不必要的重复，本发明对各种可能的组合方式不再另行说明。
此外，本发明的各种不同的实施方式之间也可以进行任意组合，只要其不违背本发明的思想，其同样应当视为本发明所公开的内容。
Claims (10)
1.一种环保涂料，其特征在于，包括如下质量份数的组分：
2.如权利要求1所述的环保涂料，其特征在于，所述环保涂料包括如下质量份数的组分：
3.如权利要求1或2所述的环保涂料，其特征在于，所述助剂包括分散剂、消泡剂、增稠剂和润湿剂；
优选地，所述分散剂包括聚羧酸铵盐和/或聚羧酸钠盐；
优选地，所述消泡剂包括矿物油改性消泡剂；
优选地，所述增稠剂包括邻苯二甲酸二丁酯、碱溶胀型丙烯酸或聚氨酯中的任意一种或至少两种的组合；
优选地，所述润湿剂包括烷基聚氧乙烯醚；
优选地，所述分散剂、消泡剂、增稠剂与润湿剂的质量比为(1～3):(1～3):(1～3):(1～3)，优选(1～2):(1～2):(1～2):(1～2)。
4.如权利要求1～3任一项所述的环保涂料，其特征在于，所述N掺杂的TiO2中N与TiO2的质量比为(1～8):100，优选(3～5):100。
5.如权利要求1～4任一项所述的环保涂料，其特征在于，所述N掺杂的TiO2的中值粒径为1.3～2.5μm，优选1.5～2μm。
6.如权利要求1～5任一项所述的环保涂料，其特征在于，所述活性炭负载SnO2中SnO2与活性炭的质量比为(15～50):100，优选(20～35):100。
7.如权利要求1～6任一项所述的环保涂料，其特征在于，所述活性炭负载SnO2的中值粒径为1.3～2.5μm，优选1.5～2μm。
8.如权利要求1～7任一项所述的环保涂料，其特征在于，N掺杂的TiO2与活性炭负载SnO2的质量比为(1～3):(1～3)，优选(1～2):(1～2)。
9.如权利要求1～8任一项所述环保涂料在内饰涂料中的应用。
10.如权利要求1～8任一项所述环保涂料在室外面漆中的应用。