CN106928875A - 一种高耐侯性光学胶薄膜胶片及其制作工艺 - Google Patents
一种高耐侯性光学胶薄膜胶片及其制作工艺 Download PDFInfo
- Publication number
- CN106928875A CN106928875A CN201710296725.3A CN201710296725A CN106928875A CN 106928875 A CN106928875 A CN 106928875A CN 201710296725 A CN201710296725 A CN 201710296725A CN 106928875 A CN106928875 A CN 106928875A
- Authority
- CN
- China
- Prior art keywords
- optical cement
- parts
- weight
- film
- weather resisteant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及液晶显示屏技术领域，具体涉及一种高耐侯性光学胶薄膜胶片及其制作工艺，包括从下往上依次贴合的轻离型膜、光学胶层和重离型膜，所述光学胶层包括以下重量份的原料：丙烯酸酯单体80‑120份、增稠剂4‑8份、固化剂2‑6份、引发剂1‑5份、偶联剂1‑3份、消泡剂1‑2份、抗紫外线剂0.5‑1.5份、抗氧化剂0.8‑1.2份。本发明的高耐侯性光学胶薄膜胶片通过在光学胶中加入UV固化剂，经过高温消泡、UV固化制程，可以很好的压制气泡反弹，且模切良率可以达到94%以上。
Description
技术领域
本发明涉及液晶显示屏技术领域，具体涉及一种高耐侯性光学胶薄膜胶片及其制作工艺。
背景技术
现有光学胶与偏光片贴后经过高温高湿测试存在汽泡。高温高湿测试：温度：60度，湿度：90%，工作时间：72H。投入产品100片经测试后有63片有汽泡反弹，63%比例。
液晶屏在使用过程中发热会出现汽泡风险，偏光片属于树质材料天生有5%水分导致汽泡产生，现有光学胶无法压制汽 。
光学胶因使用在可视显示范围内对外观要求非常高不可有溢胶、异物、变型等等，模切良率可以达到60%。
发明内容
为了克服现有技术中存在的缺点和不足，本发明的目的在于提供一种高耐侯性光学胶薄膜胶片，该高耐侯性光学胶薄膜胶片通过在光学胶中加入UV固化剂，经过高温消泡、UV固化制程，可以很好的压制气泡反弹，且模切良率可以达到94%以上。
本发明的另一目的在于提供一种高耐侯性光学胶薄膜胶片的制作工艺，该制作工艺步骤简单，操作控制方便，质量稳定，生产效率高，生产成本低，可大规模工业化生产。
本发明的目的通过下述技术方案实现：一种高耐侯性光学胶薄膜胶片，包括从下往上依次贴合的轻离型膜、光学胶层和重离型膜，所述光学胶层包括以下重量份的原料：
丙烯酸酯单体 80-120份
增稠剂 4-8份
固化剂 2-6份
引发剂 1-5份
偶联剂 1-3份
消泡剂 1-2份
抗紫外线剂 0.5-1.5份
抗氧化剂 0.8-1.2份。
本发明的光学胶通过采用上述原料，并严格控制各原料的重量配比，制得的光学胶粘结力强，耐候性好，综合性能优异。
优选的，所述丙烯酸单体是由丙烯酸丁酯、氰基丙烯酸酯、甲基丙烯酸羟丙酯和三羧甲基丙烷三丙烯酸酯以重量比2-4:1.5-2.5:0.5-1.5:1组成的混合物。
本发明通过严格控制丙烯酸单体的种类、复配及配比，制得的光学胶粘结力强，综合性能优异。
优选的，所述增稠剂是由羧甲基纤维素、羟乙基纤维素和羟丙基甲基纤维素以重量比1:1.5-2.5:0.5-1.5组成的混合物。
本发明通过严格控制增稠剂的种类、复配及配比，其增稠效果好，制得的光学胶粘结力强。
优选的，所述固化剂是由异氰酸酯、亚甲基双环己烷胺和甲基丙烯酸缩水甘油酯以重量比1:0.8-1.2:1.4-2.2组成的混合物。
本发明通过严格控制固化剂的种类、复配及配比，其固化效果好，可以很好的压制气泡反弹。
优选的，所述引发剂是由2-羟基-2-苯基苯乙酮、2-甲基-2-(4-吗啉基)-1-[4-(甲硫基)苯基]-1-丙酮和2,4,6-三甲基苯甲酰基-二苯基氧化膦以重量比0.8-1.2:1:1.5-2.5组成的混合物。
本发明通过严格控制引发剂的种类、复配及配比，其引发效果好，可以很好的压制气泡反弹。
优选的，所述偶联剂是由乙烯基三乙酰氧基硅烷、乙烯基三过氧化叔丁基硅烷和乙烯基三(β-甲氧基乙氧基)硅烷以重量比1.4-2.2:1:2-4组成的混合物。
本发明通过严格控制偶联剂的种类、复配及配比，其偶联效果好，可以很好的压制气泡反弹。
优选的，所述消泡剂是由壬基酚聚氧乙烯醚、羧甲基纤维素钠和二氧化硅以重量比4-6:2-3:1组成的混合物。
本发明通过严格控制消泡剂的种类、复配及配比，其消泡效果好，制得的光学胶具有较好的稳定性。
优选的，所述抗紫外线剂是由2- 羟基-4-甲氧基二苯甲酮、2-羟基-4-正辛氧基二苯甲酮和4-苯甲酰氧基-2，2，6，6-四甲基哌啶以重量比1：1.8-2.6：0.8-1.2组成的混合物。
本发明通过严格控制紫外线吸收剂的种类、复配及重量配比，能强烈吸收紫外线，具有优良的协同效应。
优选的，所述抗氧化剂是由N-苯基-N’-异丙基-对苯二胺、N-（1,3-二甲基丁基）-N’-苯基对苯二胺和N，N’-苯基对苯二胺以重量比1:0.4-0.8:0.8-1.2组成的混合物。
本发明通过严格控制抗氧剂的种类、复配及重量配比，可以延缓或抑制材料氧化过程的进行，从而阻止材料的老化并延长其使用寿命。
一种高耐侯性光学胶薄膜胶片的制备方法，包括以下步骤：
（1）取一轻离型膜，在轻离型膜的一面进行电晕处理；
（2）在轻离型膜的电晕处理面涂布一层光学胶，压印后形成光学胶层；
（3）在光学胶层的表面贴合一层重离型膜，制得所述高耐侯性光学胶薄膜胶片。
本发明的有益效果在于：本发明的高耐侯性光学胶薄膜胶片通过在光学胶中加入UV固化剂，经过高温消泡、UV固化制程，可以很好的压制气泡反弹，且模切良率可以达到94%以上。
本发明的制作工艺步骤简单，操作控制方便，质量稳定，生产效率高，生产成本低，可大规模工业化生产。
具体实施方式
为了便于本领域技术人员的理解，下面结合实施例对本发明作进一步的说明，实施方式提及的内容并非对本发明的限定。
实施例1
一种高耐侯性光学胶薄膜胶片，包括从下往上依次贴合的轻离型膜、光学胶层和重离型膜，所述光学胶层包括以下重量份的原料：
丙烯酸酯单体 80份
增稠剂 4份
固化剂 2份
引发剂 1份
偶联剂 1份
消泡剂 1份
抗紫外线剂 0.5份
抗氧化剂 0.8份。
所述丙烯酸单体是由丙烯酸丁酯、氰基丙烯酸酯、甲基丙烯酸羟丙酯和三羧甲基丙烷三丙烯酸酯以重量比2:1.5:0.5:1组成的混合物。
所述增稠剂是由羧甲基纤维素、羟乙基纤维素和羟丙基甲基纤维素以重量比1:1.5:0.5组成的混合物。
所述固化剂是由异氰酸酯、亚甲基双环己烷胺和甲基丙烯酸缩水甘油酯以重量比1:0.8:1.4组成的混合物。
所述引发剂是由2-羟基-2-苯基苯乙酮、2-甲基-2-(4-吗啉基)-1-[4-(甲硫基)苯基]-1-丙酮和2,4,6-三甲基苯甲酰基-二苯基氧化膦以重量比0.8:1:1.5组成的混合物。
所述偶联剂是由乙烯基三乙酰氧基硅烷、乙烯基三过氧化叔丁基硅烷和乙烯基三(β-甲氧基乙氧基)硅烷以重量比1.4:1:2组成的混合物。
所述消泡剂是由壬基酚聚氧乙烯醚、羧甲基纤维素钠和二氧化硅以重量比4:2:1组成的混合物。
所述抗紫外线剂是由2- 羟基-4-甲氧基二苯甲酮、2-羟基-4-正辛氧基二苯甲酮和4-苯甲酰氧基-2，2，6，6-四甲基哌啶以重量比1：1.8：0.8组成的混合物。
所述抗氧化剂是由N-苯基-N’-异丙基-对苯二胺、N-（1,3-二甲基丁基）-N’-苯基对苯二胺和N，N’-苯基对苯二胺以重量比1:0.4:0.8组成的混合物。
一种高耐侯性光学胶薄膜胶片的制备方法，包括以下步骤：
（1）取一轻离型膜，在轻离型膜的一面进行电晕处理；
（2）在轻离型膜的电晕处理面涂布一层光学胶，压印后形成光学胶层；
（3）在光学胶层的表面贴合一层重离型膜，制得所述高耐侯性光学胶薄膜胶片。
实施例2
一种高耐侯性光学胶薄膜胶片，包括从下往上依次贴合的轻离型膜、光学胶层和重离型膜，所述光学胶层包括以下重量份的原料：
丙烯酸酯单体 90份
增稠剂 5份
固化剂 3份
引发剂 2份
偶联剂 1.5份
消泡剂 1.2份
抗紫外线剂 0.8份
抗氧化剂 0.9份。
所述丙烯酸单体是由丙烯酸丁酯、氰基丙烯酸酯、甲基丙烯酸羟丙酯和三羧甲基丙烷三丙烯酸酯以重量比2.5:1.8:0.8:1组成的混合物。
所述增稠剂是由羧甲基纤维素、羟乙基纤维素和羟丙基甲基纤维素以重量比1:1.8:0.8组成的混合物。
所述固化剂是由异氰酸酯、亚甲基双环己烷胺和甲基丙烯酸缩水甘油酯以重量比1:0.9:1.6组成的混合物。
所述引发剂是由2-羟基-2-苯基苯乙酮、2-甲基-2-(4-吗啉基)-1-[4-(甲硫基)苯基]-1-丙酮和2,4,6-三甲基苯甲酰基-二苯基氧化膦以重量比0.9:1:1.8组成的混合物。
所述偶联剂是由乙烯基三乙酰氧基硅烷、乙烯基三过氧化叔丁基硅烷和乙烯基三(β-甲氧基乙氧基)硅烷以重量比1.6:1:2.5组成的混合物。
所述消泡剂是由壬基酚聚氧乙烯醚、羧甲基纤维素钠和二氧化硅以重量比4.5:2.2:1组成的混合物。
所述抗紫外线剂是由2- 羟基-4-甲氧基二苯甲酮、2-羟基-4-正辛氧基二苯甲酮和4-苯甲酰氧基-2，2，6，6-四甲基哌啶以重量比1：2：0.9组成的混合物。
所述抗氧化剂是由N-苯基-N’-异丙基-对苯二胺、N-（1,3-二甲基丁基）-N’-苯基对苯二胺和N，N’-苯基对苯二胺以重量比1:0.5:0.9组成的混合物。
一种高耐侯性光学胶薄膜胶片的制备方法，包括以下步骤：
（1）取一轻离型膜，在轻离型膜的一面进行电晕处理；
（2）在轻离型膜的电晕处理面涂布一层光学胶，压印后形成光学胶层；
（3）在光学胶层的表面贴合一层重离型膜，制得所述高耐侯性光学胶薄膜胶片。
实施例3
一种高耐侯性光学胶薄膜胶片，包括从下往上依次贴合的轻离型膜、光学胶层和重离型膜，所述光学胶层包括以下重量份的原料：
丙烯酸酯单体 100份
增稠剂 6份
固化剂 3份
引发剂 3份
偶联剂 2份
消泡剂 1.5份
抗紫外线剂 1份
抗氧化剂 1份。
所述丙烯酸单体是由丙烯酸丁酯、氰基丙烯酸酯、甲基丙烯酸羟丙酯和三羧甲基丙烷三丙烯酸酯以重量比3:2:1:1组成的混合物。
所述增稠剂是由羧甲基纤维素、羟乙基纤维素和羟丙基甲基纤维素以重量比1:2:1组成的混合物。
所述固化剂是由异氰酸酯、亚甲基双环己烷胺和甲基丙烯酸缩水甘油酯以重量比1:1:1.8组成的混合物。
所述引发剂是由2-羟基-2-苯基苯乙酮、2-甲基-2-(4-吗啉基)-1-[4-(甲硫基)苯基]-1-丙酮和2,4,6-三甲基苯甲酰基-二苯基氧化膦以重量比1:1:2组成的混合物。
所述偶联剂是由乙烯基三乙酰氧基硅烷、乙烯基三过氧化叔丁基硅烷和乙烯基三(β-甲氧基乙氧基)硅烷以重量比1.8:1:3组成的混合物。
所述消泡剂是由壬基酚聚氧乙烯醚、羧甲基纤维素钠和二氧化硅以重量比5:2.5:1组成的混合物。
所述抗紫外线剂是由2- 羟基-4-甲氧基二苯甲酮、2-羟基-4-正辛氧基二苯甲酮和4-苯甲酰氧基-2，2，6，6-四甲基哌啶以重量比1：2.2：1组成的混合物。
所述抗氧化剂是由N-苯基-N’-异丙基-对苯二胺、N-（1,3-二甲基丁基）-N’-苯基对苯二胺和N，N’-苯基对苯二胺以重量比1:0.6:1组成的混合物。
一种高耐侯性光学胶薄膜胶片的制备方法，包括以下步骤：
（1）取一轻离型膜，在轻离型膜的一面进行电晕处理；
（2）在轻离型膜的电晕处理面涂布一层光学胶，压印后形成光学胶层；
（3）在光学胶层的表面贴合一层重离型膜，制得所述高耐侯性光学胶薄膜胶片。
实施例4
一种高耐侯性光学胶薄膜胶片，包括从下往上依次贴合的轻离型膜、光学胶层和重离型膜，所述光学胶层包括以下重量份的原料：
丙烯酸酯单体 110份
增稠剂 7份
固化剂 5份
引发剂 4份
偶联剂 2.5份
消泡剂 1.8份
抗紫外线剂 1.2份
抗氧化剂 1.1份。
所述丙烯酸单体是由丙烯酸丁酯、氰基丙烯酸酯、甲基丙烯酸羟丙酯和三羧甲基丙烷三丙烯酸酯以重量比3.5:2.2:1.2:1组成的混合物。
所述增稠剂是由羧甲基纤维素、羟乙基纤维素和羟丙基甲基纤维素以重量比1:2.2:1.2组成的混合物。
所述固化剂是由异氰酸酯、亚甲基双环己烷胺和甲基丙烯酸缩水甘油酯以重量比1:1.1:2组成的混合物。
所述引发剂是由2-羟基-2-苯基苯乙酮、2-甲基-2-(4-吗啉基)-1-[4-(甲硫基)苯基]-1-丙酮和2,4,6-三甲基苯甲酰基-二苯基氧化膦以重量比1.1:1:2.2组成的混合物。
所述偶联剂是由乙烯基三乙酰氧基硅烷、乙烯基三过氧化叔丁基硅烷和乙烯基三(β-甲氧基乙氧基)硅烷以重量比2:1:3.5组成的混合物。
所述消泡剂是由壬基酚聚氧乙烯醚、羧甲基纤维素钠和二氧化硅以重量比5.5:2.8:1组成的混合物。
所述抗紫外线剂是由2- 羟基-4-甲氧基二苯甲酮、2-羟基-4-正辛氧基二苯甲酮和4-苯甲酰氧基-2，2，6，6-四甲基哌啶以重量比1：2.4：1.1组成的混合物。
所述抗氧化剂是由N-苯基-N’-异丙基-对苯二胺、N-（1,3-二甲基丁基）-N’-苯基对苯二胺和N，N’-苯基对苯二胺以重量比1:0.7:1.1组成的混合物。
一种高耐侯性光学胶薄膜胶片的制备方法，包括以下步骤：
（1）取一轻离型膜，在轻离型膜的一面进行电晕处理；
（2）在轻离型膜的电晕处理面涂布一层光学胶，压印后形成光学胶层；
（3）在光学胶层的表面贴合一层重离型膜，制得所述高耐侯性光学胶薄膜胶片。
实施例5
一种高耐侯性光学胶薄膜胶片，包括从下往上依次贴合的轻离型膜、光学胶层和重离型膜，所述光学胶层包括以下重量份的原料：
丙烯酸酯单体 120份
增稠剂 8份
固化剂 6份
引发剂 5份
偶联剂 3份
消泡剂 2份
抗紫外线剂 1.5份
抗氧化剂 1.2份。
所述丙烯酸单体是由丙烯酸丁酯、氰基丙烯酸酯、甲基丙烯酸羟丙酯和三羧甲基丙烷三丙烯酸酯以重量比4:2.5:1.5:1组成的混合物。
所述增稠剂是由羧甲基纤维素、羟乙基纤维素和羟丙基甲基纤维素以重量比1:2.5:1.5组成的混合物。
所述固化剂是由异氰酸酯、亚甲基双环己烷胺和甲基丙烯酸缩水甘油酯以重量比1:1.2:2.2组成的混合物。
所述引发剂是由2-羟基-2-苯基苯乙酮、2-甲基-2-(4-吗啉基)-1-[4-(甲硫基)苯基]-1-丙酮和2,4,6-三甲基苯甲酰基-二苯基氧化膦以重量比1.2:1:2.5组成的混合物。
所述偶联剂是由乙烯基三乙酰氧基硅烷、乙烯基三过氧化叔丁基硅烷和乙烯基三(β-甲氧基乙氧基)硅烷以重量比2.2:1:4组成的混合物。
所述消泡剂是由壬基酚聚氧乙烯醚、羧甲基纤维素钠和二氧化硅以重量比6:3:1组成的混合物。
所述抗紫外线剂是由2- 羟基-4-甲氧基二苯甲酮、2-羟基-4-正辛氧基二苯甲酮和4-苯甲酰氧基-2，2，6，6-四甲基哌啶以重量比1：2.6：1.2组成的混合物。
所述抗氧化剂是由N-苯基-N’-异丙基-对苯二胺、N-（1,3-二甲基丁基）-N’-苯基对苯二胺和N，N’-苯基对苯二胺以重量比1:0.8:1.2组成的混合物。
一种高耐侯性光学胶薄膜胶片的制备方法，包括以下步骤：
（1）取一轻离型膜，在轻离型膜的一面进行电晕处理；
（2）在轻离型膜的电晕处理面涂布一层光学胶，压印后形成光学胶层；
（3）在光学胶层的表面贴合一层重离型膜，制得所述高耐侯性光学胶薄膜胶片。
本发明制得的高耐侯性光学胶薄膜胶片通过在光学胶中加入UV固化剂，经过高温消泡、UV固化制程，可以很好的压制气泡反弹，且模切良率可以达到94%以上。
上述实施例为本发明较佳的实现方案，除此之外，本发明还可以其它方式实现，在不脱离本发明构思的前提下任何显而易见的替换均在本发明的保护范围之内。
Claims (10)
1.一种高耐侯性光学胶薄膜胶片，其特征在于：包括从下往上依次贴合的轻离型膜、光学胶层和重离型膜，所述光学胶层包括以下重量份的原料：
丙烯酸酯单体 80-120份
增稠剂 4-8份
固化剂 2-6份
引发剂 1-5份
偶联剂 1-3份
消泡剂 1-2份
抗紫外线剂 0.5-1.5份
抗氧化剂 0.8-1.2份。
2.根据权利要求1所述的一种高耐侯性光学胶薄膜胶片，其特征在于：所述丙烯酸单体是由丙烯酸丁酯、氰基丙烯酸酯、甲基丙烯酸羟丙酯和三羧甲基丙烷三丙烯酸酯以重量比2-4:1.5-2.5:0.5-1.5:1组成的混合物。
3.根据权利要求1所述的一种高耐侯性光学胶薄膜胶片，其特征在于：所述增稠剂是由羧甲基纤维素、羟乙基纤维素和羟丙基甲基纤维素以重量比1:1.5-2.5:0.5-1.5组成的混合物。
4.根据权利要求1所述的一种高耐侯性光学胶薄膜胶片，其特征在于：所述固化剂是由异氰酸酯、亚甲基双环己烷胺和甲基丙烯酸缩水甘油酯以重量比1:0.8-1.2:1.4-2.2组成的混合物。
5.根据权利要求1所述的一种高耐侯性光学胶薄膜胶片，其特征在于：所述引发剂是由2-羟基-2-苯基苯乙酮、2-甲基-2-(4-吗啉基)-1-[4-(甲硫基)苯基]-1-丙酮和2,4,6-三甲基苯甲酰基-二苯基氧化膦以重量比0.8-1.2:1:1.5-2.5组成的混合物。
6.根据权利要求1所述的一种高耐侯性光学胶薄膜胶片，其特征在于：所述偶联剂是由乙烯基三乙酰氧基硅烷、乙烯基三过氧化叔丁基硅烷和乙烯基三(β-甲氧基乙氧基)硅烷以重量比1.4-2.2:1:2-4组成的混合物。
7.根据权利要求1所述的一种高耐侯性光学胶薄膜胶片，其特征在于：所述消泡剂是由壬基酚聚氧乙烯醚、羧甲基纤维素钠和二氧化硅以重量比4-6:2-3:1组成的混合物。
8.根据权利要求1所述的一种高耐侯性光学胶薄膜胶片，其特征在于：所述抗紫外线剂是由2- 羟基-4-甲氧基二苯甲酮、2-羟基-4-正辛氧基二苯甲酮和4-苯甲酰氧基-2，2，6，6-四甲基哌啶以重量比1：1.8-2.6：0.8-1.2组成的混合物。
9.根据权利要求1所述的一种高耐侯性光学胶薄膜胶片，其特征在于：所述抗氧化剂是由N-苯基-N’-异丙基-对苯二胺、N-（1,3-二甲基丁基）-N’-苯基对苯二胺和N，N’-苯基对苯二胺以重量比1:0.4-0.8:0.8-1.2组成的混合物。
10.如权利要求1-9任一项所述的一种高耐侯性光学胶薄膜胶片的制备方法，其特征在于：包括如下步骤：
（1）取一轻离型膜，在轻离型膜的一面进行电晕处理；
（2）在轻离型膜的电晕处理面涂布一层光学胶，压印后形成光学胶层；
（3）在光学胶层的表面贴合一层重离型膜，制得所述高耐侯性光学胶薄膜胶片。