CN106901904A - 纳米银抑菌芯片及其生产方法和具有纳米银抑菌功能的卫生巾 - Google Patents
纳米银抑菌芯片及其生产方法和具有纳米银抑菌功能的卫生巾 Download PDFInfo
- Publication number
- CN106901904A CN106901904A CN201710088029.3A CN201710088029A CN106901904A CN 106901904 A CN106901904 A CN 106901904A CN 201710088029 A CN201710088029 A CN 201710088029A CN 106901904 A CN106901904 A CN 106901904A
- Authority
- CN
- China
- Prior art keywords
- woven fabrics
- nano silver
- antibacterial
- parts
- chip
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种纳米银抑菌芯片及其生产方法和具有纳米银抑菌功能的卫生巾，所述纳米银抑菌芯片的加工方法包括以下步骤：将无纺布在聚氨基酸溶液中浸渍、在抑菌整理液中浸渍、经紫外线照射、汽蒸、洗涤、烘干、分割得到纳米银抑菌芯片。本发明所述具有纳米银抑菌功能的卫生巾，优化了纳米银抑菌芯片的生产工艺，降低了生产成本，具有强效、持久的抑菌功能，可有效缓解经期炎症引起的白带异常、阴部瘙痒等妇科病症。
Description
技术领域
本发明涉及一种具有纳米银抑菌功能的卫生巾，尤其涉及一种纳米银抑菌芯片及其生产方法和具有纳米银抑菌功能的卫生巾。
背景技术
卫生巾作为女性经期直接贴身使用的产品，其质量、舒适度和抑菌性能直接关乎女性的健康。女性在经期期间，抵抗力下降，很容易会发生细菌感染，进而导致一系列的妇科疾病，通常会出现有阴部瘙痒、白带增多等症状，因此开发具高效抑菌功能的卫生巾十分必要。纳米银性质活泼且具有相当高的活性，与细菌接触时，通过破坏细胞合成酶的活性使其丧失增殖能力，从而杀死细菌，这种抗菌方法不会破坏人体的免疫能力，不会损害人体健康。提高纳米银在卫生巾表面的分散性，不但可以提高杀菌效果，还能有效提高银的利用率，降低生产成本。银离子易形成络合物，利用银离子和配体形成络合物，限制银离子在网络结构内还原，控制银离子的迁移，降低还原后银的团聚现象。
本发明提供了一种纳米银抑菌芯片及其生产方法和具有纳米银抑菌功能的卫生巾，抑菌效果好、舒适度高。
发明内容
针对现有技术中存在的上述不足，本发明所要解决的技术问题之一是提供一种纳米银抑菌芯片的加工方法。
本发明所要解决的技术问题之二是提供一种纳米银抑菌芯片。
本发明所要解决的技术问题之三是提供一种具有纳米银抑菌功能的卫生巾。
本发明目的是通过如下技术方案实现的：
一种纳米银抑菌芯片的加工方法，包含以下步骤：
(1)将无纺布在抑菌整理液中浸渍60-150min；
(2)浸渍抑菌整理液后的无纺布在紫外线下照射30-60min；
(3)将紫外线照射后的无纺布用水洗涤1-3次；
(4)将洗涤后的无纺布烘干，卷成合适的厚度、分割成合适的宽度后，得到纳米银抑菌芯片。
一种纳米银抑菌芯片的加工方法，包含以下步骤：
(1)将100-300重量份的无纺布在20℃的抑菌整理液中浸渍60-150min，所述抑菌整理液包含如下重量份的原料：硝酸银10-30份、抗坏血酸钠100-200份、水1000-2000份；
(2)浸渍抑菌整理液后的无纺布在200-350nm波长的紫外线下照射30-60min；
(3)将紫外线照射后的无纺布用水洗涤1-3次；
(4)将洗涤后的无纺布在60-80℃下烘干，卷成合适的厚度、分割成合适的宽度后，得到纳米银抑菌芯片。
一种纳米银抑菌芯片的加工方法，包含以下步骤：
(1)将100-300重量份的无纺布在25℃的聚氨基酸水溶液中浸渍20-50min，所述聚氨基酸水溶液包含如下重量份的原料：聚氨基酸20-40份、水1000-2000份；
(2)将浸渍后的无纺布在20℃的抑菌整理液中浸渍60-150min，所述抑菌整理液包含如下重量份的原料：硝酸银10-30份、抗坏血酸钠100-200份、水1000-2000份；
(3)浸渍抑菌整理液后的无纺布在200-350nm波长的紫外线下照射30-60min；
(4)将紫外线照射后的无纺布用水洗涤1-3次；
(5)将洗涤后的无纺布在60-80℃下烘干，卷成合适的厚度、分割成合适的宽度后，得到纳米银抑菌芯片。
一种纳米银抑菌芯片的加工方法，包含以下步骤：
(1)将100-300重量份的无纺布在25℃的聚氨基酸水溶液中浸渍20-50min，所述聚氨基酸水溶液包含如下重量份的原料：聚氨基酸20-40份、水1000-2000份；
(2)将浸渍后的无纺布在20℃的抑菌整理液中浸渍60-150min，所述抑菌整理液包含如下重量份的原料：硝酸银10-30份、抗坏血酸钠100-200份、水1000-2000份；
(3)浸渍抑菌整理液后的无纺布在温度为110℃、相对湿度为100％的条件下汽蒸35-45min；
(4)将汽蒸后的无纺布用水洗涤1-3次；
(5)将洗涤后的无纺布在60-80℃下烘干，卷成合适的厚度、分割成合适的宽度后，得到纳米银抑菌芯片。
一种纳米银抑菌芯片的加工方法，包含以下步骤：
(1)将100-300重量份的无纺布在25℃的聚氨基酸水溶液中浸渍20-50min，所述聚氨基酸水溶液包含如下重量份的原料：聚氨基酸20-40份、水1000-2000份；
(2)将浸渍后的无纺布在20℃的抑菌整理液中浸渍60-150min，所述抑菌整理液包含如下重量份的原料：硝酸银10-30份、抗坏血酸钠100-200份、水1000-2000份；
(3)浸渍抑菌整理液后的无纺布在200-350nm波长的紫外线下照射40-50min；
(4)将紫外线照射后的无纺布在温度为110℃、相对湿度为100％的条件下汽蒸35-40min；
(5)将汽蒸后的无纺布用水洗涤1-3次；
(6)将洗涤后的无纺布在60-80℃下烘干，卷成合适的厚度、分割成合适的宽度后，得到纳米银抑菌芯片。
优选地，所述聚氨基酸为聚赖氨酸和/或聚谷氨酸。
优选地，所述无纺布为莫代尔纤维和/或棉纤维制备而成。
本发明还提供一种纳米银抑菌芯片。
本发明还提供一种具有纳米银抑菌功能的卫生巾，所述具有纳米银抑菌功能的卫生巾由自上而下依次叠在一起的表层、权利要求1-7中任一项所述的纳米银抑菌芯片、吸收层、底膜、离型纸层、包膜和快易贴组成。
本发明所述一种具有纳米银抑菌功能的卫生巾，优化了纳米银抑菌芯片的生产工艺，降低了生产成本，同时提高了抑菌芯片表面纳米银的分散性，使其具有强效、持久的抑菌功能，可有效缓解经期炎症引起的白带异常、阴部瘙痒等妇科病症。
具体实施方式
抑菌性能测试：参照《中华人民共和国国家标准GB15979-1995，一次性使用卫生用品卫生标准》，检测制得的纳米银抑菌芯片对下述三种微生物的抑菌性能。所测试的微生物：大肠杆菌(Escherichia coli)AS.1.90；金黄色葡萄球菌(Staphylococcus aureus)AS.1.89；白色念珠菌(Candida albicance)AS.2.2086。将制得的纳米银抑菌芯片分别经紫外照射1.5min杀菌后，在每片纳米银抑菌芯片上均匀涂布大肠杆菌1.0×105CFU/片，金黄色葡萄球菌1.0×105CFU/片，金黄色葡萄球菌1.0×105CFU/片，作用30分钟后测试每片纳米银抑菌芯片菌含量。
抗菌持久性能测试：采用国家标准GB/T 20944.3-2008《纺织品抗菌性能的评价第3部分：振荡法》进行抗菌性定量测试，采用耐洗色牢度试验机洗涤方法，测试水洗30次后的纳米银抑菌芯片，以金黄色葡萄球菌ATCC No.6538(革兰氏阳性菌)为试验菌种。
感官评分测试：于某医院妇科门诊招募志愿者，所招募志愿者的条件为：具有阴部发炎病史的女性。向志愿者性派发3个月用量的具有纳米银抑菌功能的卫生巾，共招募志愿者女性320人，随机分成16组，每组20人，16个小组的志愿者分别使用实施例1-16的具有纳米银抑菌功能的卫生巾，同组志愿者使用同一实施例的具有纳米银抑菌功能的卫生巾。志愿者需在每月经期结束后，提供自己的使用感受。使用感受包括：阴部是否瘙痒及白带是否减少两种感官体验进行评分，每项得分的满分为十分，感觉越好评分越高，计算各组志愿者在三个月经期三次评分的平均分。
实施例中各原料介绍：
聚赖氨酸，具体采用江西百盈生物科技有限公司提供的食品级ε-聚赖氨酸。
聚谷氨酸，采用山东康勤生物科技有限公司提供的化妆品级γ-聚谷氨酸。
硝酸银，CAS号：7761-88-8。
抗坏血酸钠，CAS号：134-03-2。
莫代尔纤维，采用奥地利兰精公司生产的莫代尔，产品规格：1.3Dtex×38mm。
棉纤维，采用细绒棉，规格：1.8Dtex×30mm。
实施例1
纳米银抑菌芯片的加工方法，包含以下步骤：
(1)将150重量份的无纺布在1335重量份的20℃的抑菌整理液中浸渍80min，所述抑菌整理液包含如下重量份的原料：硝酸银15份、抗坏血酸钠120份、水1200份；
(2)浸渍抑菌整理液后的无纺布在254nm波长的紫外线下照射30min；
(3)将紫外线照射后的无纺布用水洗涤3次；
(4)将洗涤后的无纺布在75℃下烘干，卷成厚度为0.5cm，并分割成长为15cm，宽为5cm后，得到纳米银抑菌芯片。
所述无纺布由50wt％莫代尔纤维与50wt％棉纤维使用针织纬编大圆机进行针织织造得到，平纹织物，面料克重为125克/平方米。所述紫外线照射可采用市售的紫外线杀菌器。所述抑菌整理液的制备方法如下：将15重量份硝酸银、120重量份抗坏血酸钠溶解于1200重量份的水中，搅拌均匀得到抑菌整理液。
具有纳米银抑菌功能的卫生巾结构为表层(材质为纯棉水刺布，克重100g/m2)，及设置在所述表层下方的纳米银抑菌芯片，及设置在所述纳米银抑菌芯片下方的吸收层(吸收层包括吸收体1(采用邹平阿迪达达婴童用品有限公司提供的货号为NB-001的竹纤维纱布)和设置在所述吸收体1下方的吸收体2(采用广州胜欣化工科技有限公司生产的牌号为胜欣的高分子吸水树脂))，及设置在所述吸收层下方的底膜(采用沧州市亚泰塑胶有限公司生产的PE薄膜，克重50g/m2)，及设置在所述底膜下方的离型纸(采用苏州宇宣纸业有限公司生产的白色格拉辛纸离型纸，克重80g/m2)，及设置在所述离型纸下方的包膜(采用Ethyl公司出品的型号MODEL XP 39385的低密度聚乙烯包膜，厚度为0.025mm)和设置在所述包膜下方的快易贴(采用泉州市天龙卫生用品有限公司提供的快易贴)。将表层、纳米银抑菌芯片、吸收层、底膜、离型纸、包膜和快易贴按卫生巾常规工艺制备得到实施例1的具有纳米银抑菌功能的卫生巾，尺寸为300mm。
实施例2
与实施例1基本相同，区别仅仅在于：所述步骤(2)中紫外线照射时间为40min。
实施例3
与实施例1基本相同，区别仅仅在于：所述步骤(2)中紫外线照射时间为50min。
实施例4
与实施例1基本相同，区别仅仅在于：所述步骤(2)中紫外线照射时间为60min。
实施例5
纳米银抑菌芯片的加工方法，包含以下步骤：
(1)将150重量份的无纺布在25℃的1500重量份的聚氨基酸水溶液中浸渍30min；
(2)将浸渍后的无纺布在20℃的1335重量份的抑菌整理液中浸渍80min，所述抑菌整理液包含如下重量份的原料：硝酸银15份、抗坏血酸钠120份、水1200份；
(3)浸渍抑菌整理液后的无纺布在254nm波长的紫外线下照射50min；
(4)将紫外线照射后的无纺布用水洗涤3次；
(5)将洗涤后的无纺布在75℃下烘干，卷成厚度为0.5cm，并分割成长为15cm，宽为5cm后，得到纳米银抑菌芯片。
所述无纺布由50wt％莫代尔纤维与50wt％棉纤维使用针织纬编大圆机进行针织织造得到，平纹织物，面料克重为125克/平方米。所述紫外线照射可采用市售的紫外线杀菌器。所述抑菌整理液的制备方法如下：将15重量份硝酸银、120重量份抗坏血酸钠溶解于1200重量份的水中，搅拌均匀得到抑菌整理液。所述聚氨基酸水溶液的制备方法如下：将30重量份的ε-聚赖氨酸溶解于1470重量份的水中，搅拌均匀，得到聚氨基酸水溶液。
具有纳米银抑菌功能的卫生巾结构为表层(材质为纯棉水刺布，克重100g/m2)，及设置在所述表层下方的纳米银抑菌芯片，及设置在所述纳米银抑菌芯片下方的吸收层(吸收层包括吸收体1(采用邹平阿迪达达婴童用品有限公司提供的货号为NB-001的竹纤维纱布)和设置在所述吸收体1下方的吸收体2(采用广州胜欣化工科技有限公司生产的牌号为胜欣的高分子吸水树脂))，及设置在所述吸收层下方的底膜(采用沧州市亚泰塑胶有限公司生产的PE薄膜，克重50g/m2)，及设置在所述底膜下方的离型纸(采用苏州宇宣纸业有限公司生产的白色格拉辛纸离型纸，克重80g/m2)，及设置在所述离型纸下方的包膜(采用Ethyl公司出品的型号MODEL XP 39385的低密度聚乙烯包膜，厚度为0.025mm)和设置在所述包膜下方的快易贴(采用泉州市天龙卫生用品有限公司提供的快易贴)。将表层、纳米银抑菌芯片、吸收层、底膜、离型纸、包膜和快易贴按卫生巾常规工艺制备得到实施例1的具有纳米银抑菌功能的卫生巾，尺寸为300mm。
实施例6
与实施例5基本相同，区别仅仅在于：所述聚氨基酸水溶液的制备方法如下：将30重量份的γ-聚谷氨酸溶解于1470重量份的水中，搅拌均匀，得到聚氨基酸水溶液。
实施例7
与实施例5基本相同，区别仅仅在于：所述聚氨基酸水溶液的制备方法如下：将9重量份的ε-聚赖氨酸和21重量份的γ-聚谷氨酸溶解于1470重量份的水中，搅拌均匀，得到聚氨基酸水溶液。抑菌性能测试结果表明，30分钟后纳米银抑菌芯片中检出大肠杆菌1.8×103CFU/片、金黄色葡萄球菌1.9×103CFU/片、白色念珠菌3.3×103CFU/片。抗菌持久性能测试结果表明，水洗30次后的纳米银抑菌芯片对金黄色葡萄球菌的抑菌率为87.6％。感官评分测试结果：阴部是否瘙痒评分8.4分，白带是否减少评分8.6分。
实施例8
与实施例5基本相同，区别仅仅在于：所述聚氨基酸水溶液的制备方法如下：将12重量份的ε-聚赖氨酸和18重量份的γ-聚谷氨酸溶解于1470重量份的水中，搅拌均匀，得到聚氨基酸水溶液。
抑菌性能测试结果表明，30分钟后纳米银抑菌芯片中检出大肠杆菌1.6×103CFU/片、金黄色葡萄球菌1.7×103CFU/片、白色念珠菌2.1×103CFU/片。抗菌持久性能测试结果表明，水洗30次后的纳米银抑菌芯片对金黄色葡萄球菌的抑菌率为91.5％。感官评分测试结果：阴部是否瘙痒评分8.7分，白带是否减少评分8.9分。
实施例9
与实施例5基本相同，区别仅仅在于：所述聚氨基酸水溶液的制备方法如下：将15重量份的ε-聚赖氨酸和15重量份的γ-聚谷氨酸溶解于1470重量份的水中，搅拌均匀，得到聚氨基酸水溶液。抑菌性能测试结果表明，30分钟后纳米银抑菌芯片中检出大肠杆菌1.4×103CFU/片、金黄色葡萄球菌1.5×103CFU/片、白色念珠菌2.0×103CFU/片。抗菌持久性能测试结果表明，水洗30次后的纳米银抑菌芯片对金黄色葡萄球菌的抑菌率为90.2％。感官评分测试结果：阴部是否瘙痒评分8.6分，白带是否减少评分8.8分。
实施例10
纳米银抑菌芯片的加工方法，包含以下步骤：
(1)将150重量份的无纺布在25℃的1500重量份的聚氨基酸水溶液中浸渍30min；
(2)将浸渍后的无纺布在20℃的1335重量份的抑菌整理液中浸渍80min，所述抑菌整理液包含如下重量份的原料：硝酸银15份、抗坏血酸钠120份、水1200份；
(3)将浸渍抑菌整理液后的无纺布在温度为110℃、相对湿度为100％的条件下汽蒸35min；
(4)将汽蒸后的无纺布用水洗涤3次；
(5)将洗涤后的无纺布在75℃下烘干，卷成厚度为0.5cm，并分割成长为15cm，宽为5cm后，得到纳米银抑菌芯片。
所述无纺布由50wt％莫代尔纤维与50wt％棉纤维使用针织纬编大圆机进行针织织造得到，平纹织物，面料克重为125克/平方米。所述的汽蒸过程可采用市售的汽蒸焙烘机进行。所述抑菌整理液的制备方法如下：将15重量份硝酸银、120重量份抗坏血酸钠溶解于1200重量份的水中，搅拌均匀得到抑菌整理液。所述聚氨基酸水溶液的制备方法如下：将12重量份的ε-聚赖氨酸和18重量份的γ-聚谷氨酸溶解于1470重量份的水中，搅拌均匀，得到聚氨基酸水溶液。
具有纳米银抑菌功能的卫生巾结构为表层(材质为纯棉水刺布，克重100g/m2)，及设置在所述表层下方的纳米银抑菌芯片，及设置在所述纳米银抑菌芯片下方的吸收层(吸收层包括吸收体1(采用邹平阿迪达达婴童用品有限公司提供的货号为NB-001的竹纤维纱布)和设置在所述吸收体1下方的吸收体2(采用广州胜欣化工科技有限公司生产的牌号为胜欣的高分子吸水树脂))，及设置在所述吸收层下方的底膜(采用沧州市亚泰塑胶有限公司生产的PE薄膜，克重50g/m2)，及设置在所述底膜下方的离型纸(采用苏州宇宣纸业有限公司生产的白色格拉辛纸离型纸，克重80g/m2)，及设置在所述离型纸下方的包膜(采用Ethyl公司出品的型号MODEL XP 39385的低密度聚乙烯包膜，厚度为0.025mm)和设置在所述包膜下方的快易贴(采用泉州市天龙卫生用品有限公司提供的快易贴)。将表层、纳米银抑菌芯片、吸收层、底膜、离型纸、包膜和快易贴按卫生巾常规工艺制备得到实施例1的具有纳米银抑菌功能的卫生巾，尺寸为300mm。
实施例11
与实施例10基本相同，区别仅仅在于：所述步骤(3)中汽蒸时间为40min。
实施例12
与实施例10基本相同，区别仅仅在于：所述步骤(3)中汽蒸时间为45min。
实施例13
纳米银抑菌芯片的加工方法，包含以下步骤：
(1)将150重量份的无纺布在25℃的1500重量份的聚氨基酸水溶液中浸渍30min；
(2)将浸渍后的无纺布在20℃的1335重量份的抑菌整理液中浸渍80min，所述抑菌整理液包含如下重量份的原料：硝酸银15份、抗坏血酸钠120份、水1200份；
(3)浸渍抑菌整理液后的无纺布在254nm波长的紫外线下照射40min；
(4)将紫外线照射后的无纺布在温度为110℃、相对湿度为100％的条件下汽蒸45min；
(5)将汽蒸后的无纺布用水洗涤3次；
(6)将洗涤后的无纺布在75℃下烘干，卷成厚度为0.5cm，并分割成长为15cm，宽为5cm后，得到纳米银抑菌芯片。
所述无纺布由50wt％莫代尔纤维与50wt％棉纤维使用针织纬编大圆机进行针织织造得到，平纹织物，面料克重为125克/平方米。所述紫外线照射可采用市售的紫外线杀菌器。所述的汽蒸过程可采用市售的汽蒸焙烘机进行。所述抑菌整理液的制备方法如下：将15重量份硝酸银、120重量份抗坏血酸钠溶解于1200重量份的水中，搅拌均匀得到抑菌整理液。所述聚氨基酸水溶液的制备方法如下：将12重量份的ε-聚赖氨酸和18重量份的γ-聚谷氨酸溶解于1470重量份的水中，搅拌均匀，得到聚氨基酸水溶液。
具有纳米银抑菌功能的卫生巾结构为表层(材质为纯棉水刺布，克重100g/m2)，及设置在所述表层下方的纳米银抑菌芯片，及设置在所述纳米银抑菌芯片下方的吸收层(吸收层包括吸收体1(采用邹平阿迪达达婴童用品有限公司提供的货号为NB-001的竹纤维纱布)和设置在所述吸收体1下方的吸收体2(采用广州胜欣化工科技有限公司生产的牌号为胜欣的高分子吸水树脂))，及设置在所述吸收层下方的底膜(采用沧州市亚泰塑胶有限公司生产的PE薄膜，克重50g/m2)，及设置在所述底膜下方的离型纸(采用苏州宇宣纸业有限公司生产的白色格拉辛纸离型纸，克重80g/m2)，及设置在所述离型纸下方的包膜(采用Ethyl公司出品的型号MODEL XP 39385的低密度聚乙烯包膜，厚度为0.025mm)和设置在所述包膜下方的快易贴(采用泉州市天龙卫生用品有限公司提供的快易贴)。将表层、纳米银抑菌芯片、吸收层、底膜、离型纸、包膜和快易贴按卫生巾常规工艺制备得到实施例1的具有纳米银抑菌功能的卫生巾，尺寸为300mm。
实施例14
与实施例13基本相同，区别仅仅在于：所述步骤(3)中紫外线照射时间为45min，所述步骤(4)中汽蒸时间为45min。
实施例15
与实施例13基本相同，区别仅仅在于：所述步骤(3)中紫外线照射时间为50min，所述步骤(4)中汽蒸时间为35min。
实施例16
纳米银抑菌芯片的加工方法，包含以下步骤：
(1)将150重量份的无纺布在25℃的1500重量份的聚氨基酸水溶液中浸渍30min；
(2)将浸渍后的无纺布在20℃的1335重量份的抑菌整理液中浸渍80min，所述抑菌整理液包含如下重量份的原料：硝酸银15份、抗坏血酸钠120份、水1200份；
(3)浸渍抑菌整理液后的无纺布在254nm波长的紫外线下照射45min；
(4)将紫外线照射后的无纺布在温度为110℃、相对湿度为100％的条件下汽蒸40min；
(5)将汽蒸后的无纺布用水洗涤3次；
(6)将洗涤后的无纺布在75℃下烘干，卷成厚度为0.5cm，并分割成长为15cm，宽为5cm后，得到纳米银抑菌芯片。
所述无纺布由50wt％莫代尔纤维与50wt％棉纤维使用针织纬编大圆机进行针织织造得到，平纹织物，面料克重为125克/平方米。所述紫外线照射可采用市售的紫外线杀菌器。所述的汽蒸过程可采用市售的汽蒸焙烘机进行。所述抑菌整理液的制备方法如下：将15重量份硝酸银、120重量份抗坏血酸钠溶解于1200重量份的水中，搅拌均匀得到抑菌整理液。所述聚氨基酸水溶液的制备方法如下：将12重量份的ε-聚赖氨酸和18重量份的γ-聚谷氨酸溶解于1470重量份的水中，搅拌均匀，得到聚氨基酸水溶液。
具有纳米银抑菌功能的卫生巾制备：将上述纳米银抑菌芯片添加到卫生巾(采用护舒宝卫生巾，商品编号：420598，产地：广州，材质：棉柔亲肤，尺寸：300mm)表层下面，得到实施例16的具有纳米银抑菌功能的卫生巾。
抑菌性能测试结果表明，30分钟后纳米银抑菌芯片中未检出大肠杆菌、金黄色葡萄球菌和白色念珠菌。抗菌持久性能测试结果表明，水洗30次后的纳米银抑菌芯片对金黄色葡萄球菌的抑菌率为99.8％。感官评分测试结果：阴部是否瘙痒评分9.7分，白带是否减少评分9.8分。
测试例1
对制备得到的纳米银抑菌芯片进行抑菌性能测试，具体测试结果见表1。
表1：纳米银抑菌芯片抑菌性能结果表单位：CFU/片
比较实施例5-6与实施例1-4，将无纺布预先在聚氨基酸水溶液中浸渍，无纺布表面吸附的聚氨基酸分子具有大量的氨基和羧基，能和随后吸附的银离子形成络合物，限制了银离子的迁移，再经过紫外光化学还原，使无纺布表面均匀的生成银纳米粒子，无团聚，提高纳米银抑菌芯片的抑菌效果。实施例10-12将无纺布预先在聚氨基酸水溶液中浸渍，然后采用汽蒸法缓慢还原吸附在无纺布表面的银离子，提高纳米银在无纺布表面的分散性，增强纳米银抑菌芯片的抑菌性能。实施例13-15采用紫外光化学还原和汽蒸还原相结合的方法，制得的纳米银抑菌芯片取得了最佳的抑菌效果。
测试例2
将制得的纳米银抑菌芯片进行抗菌持久性能测试，具体测试结果见表2。
表2：纳米银抑菌芯片抗菌持久性能测试结果表
比较实施例5-6与实施例1-4，将无纺布预先在聚氨基酸水溶液中浸渍，再经过紫外光化学还原银离子的方法能提高纳米银抑菌芯片的抑菌持久性。实施例10-12采用汽蒸法缓慢还原法，能增强纳米银抑菌芯片的抑菌持久性。实施例13-15采用紫外光化学还原和汽蒸还原相结合的方法，制得的纳米银抑菌芯片具有最佳的抑菌持久性。
测试例3
对制得的具有纳米银抑菌功能的卫生巾进行感官评分测试，具体测试结果见表3。
表3：感官评分测试结果表
实施例13-15采用紫外光化学还原和汽蒸还原相结合的方法，制得的纳米银抑菌芯片的感官评分最好，能有效地缓解经期炎症引起的白带增多、阴部瘙痒等症状，整体舒适度较高。
Claims (9)
1.一种纳米银抑菌芯片的加工方法，其特征在于，包含以下步骤：
(1)将无纺布在抑菌整理液中浸渍60-150min；
(2)浸渍抑菌整理液后的无纺布在紫外线下照射30-60min；
(3)将紫外线照射后的无纺布用水洗涤1-3次；
(4)将洗涤后的无纺布烘干，卷成合适的厚度、分割成合适的宽度后，得到纳米银抑菌芯片。
2.如权利要求1所述的纳米银抑菌芯片的加工方法，其特征在于，包含以下步骤：
(1)将100-300重量份的无纺布在20℃的抑菌整理液中浸渍60-150min，所述抑菌整理液包含如下重量份的原料：硝酸银10-30份、抗坏血酸钠100-200份、水1000-2000份；
(2)浸渍抑菌整理液后的无纺布在200-350nm波长的紫外线下照射30-60min；
(3)将紫外线照射后的无纺布用水洗涤1-3次；
(4)将洗涤后的无纺布在60-80℃下烘干，卷成合适的厚度、分割成合适的宽度后，得到纳米银抑菌芯片。
3.如权利要求1所述的纳米银抑菌芯片的加工方法，其特征在于，包含以下步骤：
(1)将100-300重量份的无纺布在25℃的聚氨基酸水溶液中浸渍20-50min，所述聚氨基酸水溶液包含如下重量份的原料：聚氨基酸20-40份、水1000-2000份；
(2)将浸渍后的无纺布在20℃的抑菌整理液中浸渍60-150min，所述抑菌整理液包含如下重量份的原料：硝酸银10-30份、抗坏血酸钠100-200份、水1000-2000份；
(3)浸渍抑菌整理液后的无纺布在200-350nm波长的紫外线下照射30-60min；
(4)将紫外线照射后的无纺布用水洗涤1-3次；
(5)将洗涤后的无纺布在60-80℃下烘干，卷成合适的厚度、分割成合适的宽度后，得到纳米银抑菌芯片。
4.如权利要求1所述的纳米银抑菌芯片的加工方法，其特征在于，包含以下步骤：
(1)将100-300重量份的无纺布在25℃的聚氨基酸水溶液中浸渍20-50min，所述聚氨基酸水溶液包含如下重量份的原料：聚氨基酸20-40份、水1000-2000份；
(2)将浸渍后的无纺布在20℃的抑菌整理液中浸渍60-150min，所述抑菌整理液包含如下重量份的原料：硝酸银10-30份、抗坏血酸钠100-200份、水1000-2000份；
(3)浸渍抑菌整理液后的无纺布在温度为110℃、相对湿度为100％的条件下汽蒸35-45min；
(4)将汽蒸后的无纺布用水洗涤1-3次；
(5)将洗涤后的无纺布在60-80℃下烘干，卷成合适的厚度、分割成合适的宽度后，得到纳米银抑菌芯片。
5.如权利要求1所述的纳米银抑菌芯片的加工方法，其特征在于，包含以下步骤：
(1)将100-300重量份的无纺布在25℃的聚氨基酸水溶液中浸渍20-50min，所述聚氨基酸水溶液包含如下重量份的原料：聚氨基酸20-40份、水1000-2000份；
(2)将浸渍后的无纺布在20℃的抑菌整理液中浸渍60-150min，所述抑菌整理液包含如下重量份的原料：硝酸银10-30份、抗坏血酸钠100-200份、水1000-2000份；
(3)浸渍抑菌整理液后的无纺布在200-350nm波长的紫外线下照射40-50min；
(4)将紫外线照射后的无纺布在温度为110℃、相对湿度为100％的条件下汽蒸35-40min；
(5)将汽蒸后的无纺布用水洗涤1-3次；
(6)将洗涤后的无纺布在60-80℃下烘干，卷成合适的厚度、分割成合适的宽度后，得到纳米银抑菌芯片。
6.如权利要求3或4或5所述的纳米银抑菌芯片的加工方法，其特征在于，所述聚氨基酸为聚赖氨酸和/或聚谷氨酸。
7.如权利要求1-7任一项所述的纳米银抑菌芯片的加工方法，其特征在于所述无纺布为莫代尔纤维和/或棉纤维制备而成。
8.一种纳米银抑菌芯片，其特征在于，采用权利要求1-8中任一项所述方法加工而成。
9.一种具有纳米银抑菌功能的卫生巾，其特征在于，由自上而下依次叠在一起的表层、权利要求1-7中任一项所述的纳米银抑菌芯片、吸收层、底膜、离型纸层、包膜和快易贴组成。