CN106734860A - 一种基于磷酸盐的有机铸造粘结剂 - Google Patents
一种基于磷酸盐的有机铸造粘结剂 Download PDFInfo
- Publication number
- CN106734860A CN106734860A CN201611097044.6A CN201611097044A CN106734860A CN 106734860 A CN106734860 A CN 106734860A CN 201611097044 A CN201611097044 A CN 201611097044A CN 106734860 A CN106734860 A CN 106734860A
- Authority
- CN
- China
- Prior art keywords
- parts
- sand
- epoxy resin
- weight
- core
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及到一种铸造用有机粘结剂，即应用于热芯工艺的一种基于磷酸盐的有机铸造粘结剂。所述磷酸盐铸造有机粘结剂由磷酸盐溶液、具有乙烯基团的酚醛树脂、三乙酸甘油酯及金属氧化物固化剂组成；用于制备砂型或砂芯时以新砂重量份数为参照，即新砂100份，金属氧化物固化剂1～5份、具有乙烯基团的酚醛树脂2～10份、三乙酸甘油酯3～12份及磷酸盐溶液3～5份，所述磷酸盐溶液按重量份数计算：磷酸100份、氢氧化铝10～40份、氢氧化钡1～6份及水80～150份，将上述组分在80～150度混合均匀制成磷酸盐溶液。
Description
技术领域
本发明涉及到一种铸造用有机粘结剂，即应用于热芯工艺的一种基于磷酸盐的有机铸造粘结剂。
背景技术
作为制造业的基础，铸造工业随着中国制造、尤其是汽车产业的高速增长而进入了一个前所未有的快速发展时期。
目前，高品位铸件的生产过程中需要使用大批量的树脂粘结剂，热法固化的覆膜砂生产过程中会产生大量的游离甲醛和游离苯酚；冷芯盒法则需要有毒的三乙胺气体催化的作用实现酚醛树脂中的羟甲基(-CH2OH)和聚异氰酸酯中的(-N＝C＝O)基团之间生成固态尿烷酚醛的反应；无论是热法、还是冷法，在铸件浇注后树脂完全或不完全燃烧都会产生大量的有害废气；环境的日益恶化，环保意识的增强，迫使人们不断寻找新型的低发气、无污染的绿色铸造粘结剂。
采用CO2固化的水玻璃系列无机粘结剂无毒、无味、铸造过程无废气排放，但是残留强度过高、不易再生等缺陷导致其产生污染，因而，具有良好溃散性的磷酸盐基无机粘结剂成为绿色铸造粘结剂的首选材料。
虽然早在1978年，美国专利US4127157就提出基于磷酸盐的铸造粘结剂；但是，磷酸盐粘结剂的最大缺点，即具有明显的易吸湿性，吸湿问题一方面导致固化形成的磷酸盐空间网格节点断开而失去强度，无法保证砂型或砂芯的外形，影响了砂芯的可存放时间；另一方面砂芯内的水气在浇注过程中汽化而导致铸件气孔缺陷，给铸件质量带来危害。为了解决吸湿性问题，可以采用添加各种氧化物的方法，增强磷酸盐的键合强度来改善耐湿性，但是效果并不理想，更是给旧砂的再生带来困难。
发明内容
针对上述的磷酸盐粘结剂的吸湿性问题，确保使用磷酸盐粘结剂的砂型或砂芯具有更长的可存放时间，减少铸件气孔报废的几率，本发明是在磷酸盐铸造无机粘结剂基础上，通过在缩聚的磷酸盐空间网格增加憎水节点从而减少接触水分的几率，显著改善其耐湿性；以磷酸盐为铸造粘结剂主体而制备的砂型或砂芯，在铸造生产过程中较之有机树脂粘结剂，不会产生任何有害的产物；为改善耐湿性而添加的聚乙烯醇不会像含苯的有机树脂一样，因不完全燃烧而产生有害的气体。
本发明参照了生物学中常见的磷脂分子的结构，即具有亲水特性的磷酸根和憎水特性的乙烯基团的双重特性，满足复杂的亲水及憎水要求。
所述有机铸造粘结剂由磷酸盐溶液、具有乙烯基团的酚醛树脂、三乙酸甘油酯及金属氧化物固化剂组成；用于制备砂型或砂芯时以新砂重量份数为参照，即新砂100份，金属氧化物固化剂1～5份、具有乙烯基团的酚醛树脂2～10份、三乙酸甘油酯3～12份及磷酸盐溶液3～5份，所述磷酸盐溶液按重量份数计算：磷酸100份、氢氧化铝10～40份、氢氧化钡1～6份及水80～150份，将上述组分在80～150度混合均匀制成磷酸盐溶液。
进一步包括液态环氧树脂，所述液态环氧树脂选自由双酚A环氧树脂、双酚F环氧树脂、三官能团或更多官能团环氧树脂、橡胶改性的环氧树脂、氨基甲酸乙酯改性的环氧树脂、丙烯酸类化合物改性的环氧树脂、光敏环氧树脂和它们的混合物组成的组中
所述酚醛树脂具有50000～5000000g/mol的重均分子量。
所述金属氧化物固化剂为纯氧化镁粉。
基于磷酸盐的有机铸造粘结剂用于制备砂型或砂芯的方法为：新砂质量以100重量份计算，先后加入金属氧化物固化剂0.1～1重量份、具有乙烯基团的酚醛树脂2～10重量份、三乙酸甘油酯3～12重量份及磷酸盐溶液3～5份，并均匀混合；混匀的型砂或芯砂用手动或机械的方式加入芯盒并紧实，加热至80～150℃固化或采用相同温度的热气流固化，形成铸造所需的砂芯或砂型。
热固化过程使得磷酸盐发生缩聚反应，形成空间网格包覆于铸造砂的表面，并把这些铸造砂紧密联系起来，形成铸造砂芯或砂型所需的强度；由于空间网格部分节点上具有憎水特性的乙烯基团，显著减少吸水几率，使得铸造砂芯或砂型具有良好的耐湿性；乙烯基团在铸造浇注后的燃烧过程不会因类似苯环的不完全燃烧而产生任何有毒的气体排放，因而是一种绿色环保的铸造粘结剂。
具体实施方式
为了评价铸造粘结剂的吸湿性，通常是把固化后的型砂试样放置于特定湿度(如相对湿度85±5％)条件下，测定试样抗拉强度或抗压强度随时间的衰减关系，易吸湿的粘结剂试样可能在一小时或数小时内失去强度而溃散，严重影响铸造砂型或砂芯的可存放时间。
下面结合实例进一步说明本发明的实际使用方法，它是对本发明的解释而不限于以下实例。
实例1
磷酸盐溶液按照按重量份数计算：质量百分浓度为85％的工业磷酸100份+氢氧化铝25份+氢氧化钡2份+水100份，将上述组分在90度混合均匀制成磷酸盐溶液；
新砂质量以100重量份计算，先后加入金属氧化物固化剂0.1重量份、具有乙烯基团的酚醛树脂2重量份、三乙酸甘油酯3重量份及磷酸盐溶液3份，并均匀混合；混匀的型砂或芯砂用手动或机械的方式加入芯盒并紧实，加热至80～150℃固化或采用相同温度的热气流固化，形成铸造所需的砂型，取出试样并测试其抗拉强度，即时强度0.38MPa；85±5％湿度条件下，24小时后的强度0.32Mpa，这个强度意味着型砂试样的可存放时间至少24小时。
实例2
磷酸盐溶液按照按重量份数计算：质量百分浓度为85％的工业磷酸100份+氢氧化铝25份+氢氧化钡2.5份，混合并加热搅拌制备磷酸铝溶液；
新砂质量以100重量份计算，先后加入金属氧化物固化剂1重量份、具有乙烯基团的酚醛树脂10重量份、三乙酸甘油酯12重量份及磷酸盐溶液5份，并均匀混合；混匀的型砂或芯砂用手动或机械的方式加入芯盒并紧实，加热至80～150℃固化或采用相同温度的热气流固化，形成铸造所需的砂型，取出试样并测试其抗拉强度；即时强度0.33MPa；85±5％湿度条件下，24小时后的强度0.29Mpa，这个强度意味着型砂试样的可存放时间至少24小时。
实例3
磷酸盐溶液按照按重量份数计算：质量百分浓度为85％的工业磷酸100份+氢氧化铝25份+氢氧化钡2.5份，混合并加热搅拌制备磷酸铝溶液；
新砂质量以100重量份计算，先后加入金属氧化物固化剂0.5重量份、具有乙烯基团的酚醛树脂8重量份、三乙酸甘油酯8重量份及磷酸盐溶液4份，并均匀混合；混匀的型砂或芯砂用手动或机械的方式加入芯盒并紧实，加热至80～150℃固化或采用相同温度的热气流固化，形成铸造所需的砂型，取出试样并测试其抗拉强度；即时强度0.32MPa；85±5％湿度条件下，24小时后的强度0.30Mpa，这个强度意味着型砂试样的可存放时间至少24小时。
对所公开的实施例的上述说明，使本领域专业技术人员能够实现或使用本发明。对这些实施例的多种修改对本领域的专业技术人员来说将是显而易见的，本文中所定义的一般原理可以在不脱离本发明的精神或范围的情况下，在其它实施例中实现。因此，本发明将不会被限制于本文所示的实施例，而是要符合与本文所公开的原理和新颖特点相一致的最宽的范围。
Claims (5)
1.一种基于磷酸盐的有机铸造粘结剂，其特征在于：所述有机铸造粘结剂由磷酸盐溶液、具有乙烯基团的酚醛树脂、三乙酸甘油酯及金属氧化物固化剂组成；用于制备砂型或砂芯时以新砂重量份数为参照，即新砂100份，金属氧化物固化剂1～5份、具有乙烯基团的酚醛树脂2～10份、三乙酸甘油酯3～12份及磷酸盐溶液3～5份，所述磷酸盐溶液按重量份数计算：磷酸100份、氢氧化铝10～40份、氢氧化钡1～6份及水80～150份，将上述组分在80～150度混合均匀制成磷酸盐溶液。
2.如权利要求1所述的一种基于磷酸盐的有机铸造粘结剂，其特征在于：进一步包括液态环氧树脂，所述液态环氧树脂选自由双酚A环氧树脂、双酚F环氧树脂、三官能团或更多官能团环氧树脂、橡胶改性的环氧树脂、氨基甲酸乙酯改性的环氧树脂、丙烯酸类化合物改性的环氧树脂、光敏环氧树脂和它们的混合物组成的组中。
3.如权利要求1所述的一种基于磷酸盐的有机铸造粘结剂，其特征在于：所述酚醛树脂具有50000～5000000g/mol的重均分子量。
4.如权利要求1所述的一种基于磷酸盐的有机铸造粘结剂，其特征在于：所述金属氧化物固化剂为纯氧化镁粉。
5.将权利要求1所述的一种基于磷酸盐的有机铸造粘结剂用于制备砂型或砂芯的方法为：新砂质量以100重量份计算，先后加入金属氧化物固化剂0.1～1重量份、具有乙烯基团的酚醛树脂2～10重量份、三乙酸甘油酯3～12重量份及磷酸盐溶液3～5份，并均匀混合；混匀的型砂或芯砂用手动或机械的方式加入芯盒并紧实，加热至80～150℃固化或采用相同温度的热气流固化，形成铸造所需的砂芯或砂型。