CN106654957A - 一种低压抽出式开关柜及其防腐工艺 - Google Patents
一种低压抽出式开关柜及其防腐工艺 Download PDFInfo
- Publication number
- CN106654957A CN106654957A CN201611152707.XA CN201611152707A CN106654957A CN 106654957 A CN106654957 A CN 106654957A CN 201611152707 A CN201611152707 A CN 201611152707A CN 106654957 A CN106654957 A CN 106654957A
- Authority
- CN
- China
- Prior art keywords
- parts
- following components
- rare earth
- remaining
- earth element
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种低压抽出式开关柜，该开关柜按质量百分比计包括以下组分：Zn：3‑6%，Mo：1 ‑1.5%，Ti：1‑1.2%，N：0.02‑0.03%，Cr：8‑11%，C：0.01‑0.03%，Mn：0.5‑0.7%，Nb：0.3‑0.6%，Mg：0.7‑0.9%，Cu：0.3‑0.4 %，W：0.5‑0.7%，Si：0.3‑0.5%，P：0.025‑0.030%，S：0.008‑0.010%，稀土元素：0.1‑0.3%，其余为Fe及不可避免的杂质；本发明还涉及一种低压抽出式开关柜的防腐工艺，该防腐工艺简单易行，能有效的提高开关柜的防腐性能，延长其使用寿命，降低成本。
Description
技术领域
本发明涉及一种开关柜，具体涉及一种低压抽出式开关柜及其防腐工艺。
背景技术
开关柜是一种电气设备，开关柜外线先进入柜内主控开关，然后进入分控开关，各分路按其需要设置，如仪表，自控，电动机磁力开关，各种交流接触器等，有的还设高压室与低压室开关柜，设有高压母线，如发电厂等，有的还设有为保主要设备的低周减载。
开关柜的主要作用是在电力系统进行发电、输电、配电和电能转换的过程中，进行开合、控制和保护用电设备，开关柜内的部件主要有断路器、隔离开关、负荷开关、操作机构、互感器以及各种保护装置等组成，高低压开关柜是开关柜的一种，现有的高低压开关柜可以在室内使用，也可以在户外使用，但是在较恶劣情况下开关柜在使用时，容易遭受侵蚀，或在温度较高情况下不够耐高温，缩短开关柜的使用寿命。
发明内容
本发明所要解决的技术问题是，针对以上现有技术存在的缺点，提出一种低压抽出式开关柜及其防腐工艺，该防腐工艺简单易行，能有效的提高开关柜的防腐性能，延长其使用寿命，降低成本。
本发明解决以上技术问题的技术方案是：
一种低压抽出式开关柜，该开关柜按质量百分比计包括以下组分：
Zn：3-6%，Mo：1 -1.5%，Ti：1-1.2%，N：0.02-0.03%，Cr：8-11%，C：0.01-0.03%，Mn：0.5-0.7%，Nb：0.3-0.6%，Mg：0.7-0.9%，Cu：0.3-0.4 %，W：0.5-0.7%，Si：0.3-0.5%，P：0.025-0.030%，S：0.008-0.010%，稀土元素：0.1-0.3%，其余为Fe及不可避免的杂质；
所述的稀土元素按质量百分比计包括以下组分：镧：5-7 %，铈：5-8%，钪：6-7%，钇：3-7%， 钆：5-7%，镨：15-18 %，其余为其它镧系元素，以上各组分之和为100%。
本发明进一步限定的技术方案为：
前述低压抽出式开关柜中，该开关柜按质量百分比计包括以下组分：
Zn：3%，Mo：1 %，Ti：1%，N：0.02%，Cr：8%，C：0.01%，Mn：0.5%，Nb：0.3%，Mg：0.7%，Cu：0.3%，W：0.5%，Si：0.3%，P：0.025%，S：0.008%，稀土元素：0.1-0.3%，其余为Fe及不可避免的杂质；
稀土元素按质量百分比计包括以下组分：镧：5%，铈：5%，钪：6%，钇：3%， 钆：5%，镨：15%，其余为其它镧系元素，以上各组分之和为100%。
前述低压抽出式开关柜中，该开关柜按质量百分比计包括以下组分：
Zn：6%，Mo：1.5%，Ti：1.2%，N：0.03%，Cr：11%，C：0.03%，Mn：0.7%，Nb：0.6%，Mg：0.9%，Cu：0.4 %，W：0.7%，Si：0.5%，P：0.030%，S：0.010%，稀土元素：0.3%，其余为Fe及不可避免的杂质；
稀土元素按质量百分比计包括以下组分：镧：7 %，铈：8%，钪：7%，钇：7%， 钆：7%，镨：18%，其余为其它镧系元素，以上各组分之和为100%。
前述低压抽出式开关柜中，该开关柜按质量百分比计包括以下组分：
Zn：4%，Mo：1.2%，Ti：1.1%，N：0.025%，Cr：9%，C：0.02%，Mn：0.6%，Nb：0.4%，Mg：0.8%，Cu：0.35 %，W：0.6%，Si：0.4%，P：0.028%，S：0.009%，稀土元素：0.2%，其余为Fe及不可避免的杂质；
稀土元素按质量百分比计包括以下组分：镧：6 %，铈：6%，钪：6%，钇：5%， 钆：6%，镨：16%，其余为其它镧系元素，以上各组分之和为100%。
本发明还涉及一种低压抽出式开关柜的防腐工艺，在开关柜的外表面涂覆一层防腐层，所述的防腐层按按质量分数计包括以下组分：
双酚A型聚醚醚酮树脂：40-60份，石墨浆：5-9份，消泡剂：9-14份，流平剂：2-5份，溶剂：10-20份，助溶剂：8-12份；触变剂： 4-8份，表面活性剂：3-5份，防霉剂：2-4份；
所述的消泡剂为有机硅氧烷；所述流平剂为N-甲基吡咯烷酮；所述溶剂为三氯甲烷、二氯甲烷、氮甲基吡咯烷酮或二甲基亚砜中的一种；所述助溶剂为甲醇或乙醇；所述触变剂为有机蒙脱土；所述表面活性剂为十二烷基苯磺酸钠；所述防霉剂为为取代芳烃类、杂环化合物或胺类化合物。
前述低压抽出式开关柜的防腐工艺，防腐层按以下步骤制备：
取双酚A型聚醚醚酮树脂、石墨浆及溶剂和助溶剂投入到分散缸中搅拌，搅拌速度为120-200转/min，搅拌10-18min制得均匀的预混物，然后加入消泡剂、流平剂、、防霉剂、触变剂以及表面活性剂，续搅拌，搅拌速度为250-300转/min，搅拌15-22min后经过滤得到防腐涂层，将防腐涂料喷涂在开关柜的表面，固化干燥得到防腐层。
本发明的有益效果是：
在本发明的防腐层中加入了发泡剂有效的提高了透气性，改善了粉料粒子的粘结状态，提高了抗磨性，使得表面微溶粗化，明显改善了涂料的涂挂性。
本发明中采用填料为石墨浆替换已有的玻璃鳞片，防止涂层脆性带来的脱落问题，同时，与主体树脂材料搭配使用改变材料硬度，使材料产生韧性，在脱硝装置使用震动时可与装置保持一致的方向，也就起到抗脱落的作用，也增强了耐蚀性。
具体实施方式
实施例1
本实施例提供一种低压抽出式开关柜，该开关柜按质量百分比计包括以下组分：
Zn：3%，Mo：1 %，Ti：1%，N：0.02%，Cr：8%，C：0.01%，Mn：0.5%，Nb：0.3%，Mg：0.7%，Cu：0.3%，W：0.5%，Si：0.3%，P：0.025%，S：0.008%，稀土元素：0.1-0.3%，其余为Fe及不可避免的杂质；
稀土元素按质量百分比计包括以下组分：镧：5%，铈：5%，钪：6%，钇：3%， 钆：5%，镨：15%，其余为其它镧系元素，以上各组分之和为100%；
上述低压抽出式开关柜的防腐工艺，在开关柜的外表面涂覆一层防腐层，所述的防腐层按按质量分数计包括以下组分：
双酚A型聚醚醚酮树脂：40-60份，石墨浆：5-9份，消泡剂：9-14份，流平剂：2-5份，溶剂：10-20份，助溶剂：8-12份；触变剂： 4-8份，表面活性剂：3-5份，防霉剂：2-4份；
消泡剂为有机硅氧烷；流平剂为N-甲基吡咯烷酮；溶剂为三氯甲烷；助溶剂为甲醇；触变剂为有机蒙脱土；表面活性剂为十二烷基苯磺酸钠；所霉剂为取代芳烃类化合物；
防腐层按以下步骤制备：
取双酚A型聚醚醚酮树脂、石墨浆及溶剂和助溶剂投入到分散缸中搅拌，搅拌速度为120-200转/min，搅拌10-18min制得均匀的预混物，然后加入消泡剂、流平剂、、防霉剂、触变剂以及表面活性剂，续搅拌，搅拌速度为250-300转/min，搅拌15-22min后经过滤得到防腐涂层，将防腐涂料喷涂在开关柜的表面，固化干燥得到防腐层。
实施例2
本实施例提供一种低压抽出式开关柜，该开关柜按质量百分比计包括以下组分：
Zn：6%，Mo：1.5%，Ti：1.2%，N：0.03%，Cr：11%，C：0.03%，Mn：0.7%，Nb：0.6%，Mg：0.9%，Cu：0.4 %，W：0.7%，Si：0.5%，P：0.030%，S：0.010%，稀土元素：0.3%，其余为Fe及不可避免的杂质；
稀土元素按质量百分比计包括以下组分：镧：7 %，铈：8%，钪：7%，钇：7%， 钆：7%，镨：18%，其余为其它镧系元素，以上各组分之和为100%；
上述低压抽出式开关柜的防腐工艺，在开关柜的外表面涂覆一层防腐层，所述的防腐层按按质量分数计包括以下组分：
双酚A型聚醚醚酮树脂：40-60份，石墨浆：5-9份，消泡剂：9-14份，流平剂：2-5份，溶剂：10-20份，助溶剂：8-12份；触变剂： 4-8份，表面活性剂：3-5份，防霉剂：2-4份；
消泡剂为有机硅氧烷；流平剂为N-甲基吡咯烷酮；溶剂为二氯甲烷；助溶剂为乙醇；触变剂为有机蒙脱土；表面活性剂为十二烷基苯磺酸钠；防霉剂为杂环化合物类化合物；
防腐层按以下步骤制备：
取双酚A型聚醚醚酮树脂、石墨浆及溶剂和助溶剂投入到分散缸中搅拌，搅拌速度为120-200转/min，搅拌10-18min制得均匀的预混物，然后加入消泡剂、流平剂、、防霉剂、触变剂以及表面活性剂，续搅拌，搅拌速度为250-300转/min，搅拌15-22min后经过滤得到防腐涂层，将防腐涂料喷涂在开关柜的表面，固化干燥得到防腐层。
实施例3
本实施例提供一种低压抽出式开关柜，该开关柜按质量百分比计包括以下组分：
Zn：4%，Mo：1.2%，Ti：1.1%，N：0.025%，Cr：9%，C：0.02%，Mn：0.6%，Nb：0.4%，Mg：0.8%，Cu：0.35 %，W：0.6%，Si：0.4%，P：0.028%，S：0.009%，稀土元素：0.2%，其余为Fe及不可避免的杂质；
稀土元素按质量百分比计包括以下组分：镧：6 %，铈：6%，钪：6%，钇：5%， 钆：6%，镨：16%，其余为其它镧系元素，以上各组分之和为100%；
上述低压抽出式开关柜的防腐工艺，在开关柜的外表面涂覆一层防腐层，所述的防腐层按按质量分数计包括以下组分：
双酚A型聚醚醚酮树脂：40-60份，石墨浆：5-9份，消泡剂：9-14份，流平剂：2-5份，溶剂：10-20份，助溶剂：8-12份；触变剂： 4-8份，表面活性剂：3-5份，防霉剂：2-4份；
消泡剂为有机硅氧烷；流平剂为N-甲基吡咯烷酮；溶剂为氮甲基吡咯烷酮；助溶剂为甲醇或乙醇；触变剂为有机蒙脱土；表面活性剂为十二烷基苯磺酸钠；防霉剂为胺类化合物；
防腐层按以下步骤制备：
取双酚A型聚醚醚酮树脂、石墨浆及溶剂和助溶剂投入到分散缸中搅拌，搅拌速度为120-200转/min，搅拌10-18min制得均匀的预混物，然后加入消泡剂、流平剂、、防霉剂、触变剂以及表面活性剂，续搅拌，搅拌速度为250-300转/min，搅拌15-22min后经过滤得到防腐涂层，将防腐涂料喷涂在开关柜的表面，固化干燥得到防腐层。
除上述实施例外，本发明还可以有其他实施方式。凡采用等同替换或等效变换形成的技术方案，均落在本发明要求的保护范围。
Claims (6)
1.一种低压抽出式开关柜，其特征在于，该开关柜按质量百分比计包括以下组分：
Zn：3-6%，Mo：1 -1.5%，Ti：1-1.2%，N：0.02-0.03%，Cr：8-11%，C：0.01-0.03%，Mn：0.5-0.7%，Nb：0.3-0.6%，Mg：0.7-0.9%，Cu：0.3-0.4 %，W：0.5-0.7%，Si：0.3-0.5%，P：0.025-0.030%，S：0.008-0.010%，稀土元素：0.1-0.3%，其余为Fe及不可避免的杂质；
所述的稀土元素按质量百分比计包括以下组分：镧：5-7 %，铈：5-8%，钪：6-7%，钇：3-7%， 钆：5-7%，镨：15-18 %，其余为其它镧系元素，以上各组分之和为100%。
2.根据权利要求1所述的低压抽出式开关柜，其特征在于，该开关柜按质量百分比计包括以下组分：
Zn：3%，Mo：1 %，Ti：1%，N：0.02%，Cr：8%，C：0.01%，Mn：0.5%，Nb：0.3%，Mg：0.7%，Cu：0.3%，W：0.5%，Si：0.3%，P：0.025%，S：0.008%，稀土元素：0.1-0.3%，其余为Fe及不可避免的杂质；
所述的稀土元素按质量百分比计包括以下组分：镧：5%，铈：5%，钪：6%，钇：3%， 钆：5%，镨：15%，其余为其它镧系元素，以上各组分之和为100%。
3.根据权利要求1所述的低压抽出式开关柜，其特征在于，该开关柜按质量百分比计包括以下组分：
Zn：6%，Mo：1.5%，Ti：1.2%，N：0.03%，Cr：11%，C：0.03%，Mn：0.7%，Nb：0.6%，Mg：0.9%，Cu：0.4 %，W：0.7%，Si：0.5%，P：0.030%，S：0.010%，稀土元素：0.3%，其余为Fe及不可避免的杂质；
所述的稀土元素按质量百分比计包括以下组分：镧：7 %，铈：8%，钪：7%，钇：7%， 钆：7%，镨：18 %，其余为其它镧系元素，以上各组分之和为100%。
4.根据权利要求1所述的低压抽出式开关柜，其特征在于，该开关柜按质量百分比计包括以下组分：
Zn：4%，Mo：1.2%，Ti：1.1%，N：0.025%，Cr：9%，C：0.02%，Mn：0.6%，Nb：0.4%，Mg：0.8%，Cu：0.35 %，W：0.6%，Si：0.4%，P：0.028%，S：0.009%，稀土元素：0.2%，其余为Fe及不可避免的杂质；
所述的稀土元素按质量百分比计包括以下组分：镧：6 %，铈：6%，钪：6%，钇：5%， 钆：6%，镨：16 %，其余为其它镧系元素，以上各组分之和为100%。
5.如权利要求1所述的低压抽出式开关柜的防腐工艺，其特征在于，在开关柜的外表面涂覆一层防腐层，所述的防腐层按按质量分数计包括以下组分：
双酚A型聚醚醚酮树脂：40-60份，石墨浆：5-9份，消泡剂：9-14份，流平剂：2-5份，溶剂：10-20份，助溶剂：8-12份；触变剂： 4-8份，表面活性剂：3-5份，防霉剂：2-4份；
所述的消泡剂为有机硅氧烷；所述流平剂为N-甲基吡咯烷酮；所述溶剂为三氯甲烷、二氯甲烷、氮甲基吡咯烷酮或二甲基亚砜中的一种；所述助溶剂为甲醇或乙醇；所述触变剂为有机蒙脱土；所述表面活性剂为十二烷基苯磺酸钠；所述防霉剂为为取代芳烃类、杂环化合物或胺类化合物。
6.根据权利要求1所述的低压抽出式开关柜的防腐工艺，其特征在于，所述防腐层按以下步骤制备：
取双酚A型聚醚醚酮树脂、石墨浆及溶剂和助溶剂投入到分散缸中搅拌，搅拌速度为120-200转/min，搅拌10-18min制得均匀的预混物，然后加入消泡剂、流平剂、、防霉剂、触变剂以及表面活性剂，续搅拌，搅拌速度为250-300转/min，搅拌15-22min后经过滤得到防腐涂层，将防腐涂料喷涂在开关柜的表面，固化干燥得到防腐层。