CN106626859A - 热升华转印纸 - Google Patents
热升华转印纸 Download PDFInfo
- Publication number
- CN106626859A CN106626859A CN201611159012.4A CN201611159012A CN106626859A CN 106626859 A CN106626859 A CN 106626859A CN 201611159012 A CN201611159012 A CN 201611159012A CN 106626859 A CN106626859 A CN 106626859A
- Authority
- CN
- China
- Prior art keywords
- parts
- layer
- sublimation transfer
- thermal dye
- dye sublimation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种热升华转印纸，包括托墨层、纸纤维粘结层、基纸层和背涂层，所述托墨层包括聚阴离子纤维素和干燥填料，所述纸纤维粘结层采用粘结剂，所述粘结剂为水性树脂，所述涂层包括蔗糖1‑10份、季戊四醇1‑15份、淀粉1‑10份、纤维素2‑15份、气相二氧化硅2‑10份、聚乙烯醇2‑16份、甘油2‑18份、硫酸钡2‑9份、羟甲基纤维素2‑15份、杀菌剂1‑10份、有机溶剂2‑15份、表面活性剂2‑15份、无极氧化物1‑10份、增稠剂1‑15份、中和剂1‑10份、松浆油脂肪酸2‑15份、聚丙烯酰胺1‑15份、多糖衍生物1‑10份、缓蚀剂1‑15份、油墨介质吸附剂1‑10份，本发明制备工艺简单，制得油墨具有良好的托墨能力、耐腐性、耐磨性、抗氧化性、耐水性和附着能力。
Description
技术领域
本发明涉及油墨技术领域，具体为一种热升华转印纸。
背景技术
热升华转印是一种无水印染工艺，具有较高的环保效应，对目前国家倡导的高能耗行业节能减排改造工程具有重要价值，目前已成为研究热点。热升华转印的原理是在高温下(通常为220℃以上)，热升华转印介质上的分散染料升华至化纤面料上并直接被面料纤维固定，印染好的化纤面料可以免水洗。可以认为，热升华转印工艺，尤其是数码热升华转印工艺，是一种高度环保并且实用可靠的工艺，有希望替代传统印染工艺。
而升华转印纸提升了印刷精致度，更重要的是能够便捷地实现了纺织品的无水印染，喷墨打印机在电脑的控制下可以直接在喷墨热升华转印纸上打印出色彩艳丽、形象逼真的效果而无需制版等工序，再经过简单加热工序即可使被转印物得到精致的印刷效果。然而，由于升华转移印刷过程需要加热到较高的温度，因此高温转移时油墨的连接料必须具备一定的耐热性此外，现有的转印纸墨水的托墨能力比较差，需要涂布的量比较多，目前国内外对于热升华转移印纸及其制备方法较少。
发明内容
本发明的目的在于提供一种热升华转印纸，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：一种热升华转印纸，包括托墨层、纸纤维粘结层、基纸层和背涂层，所述托墨层包括聚阴离子纤维素和干燥填料，所述纸纤维粘结层采用粘结剂，所述粘结剂为水性树脂，所述涂层包括蔗糖1-10份、季戊四醇1-15份、淀粉1-10份、纤维素2-15份、气相二氧化硅2-10份、聚乙烯醇2-16份、甘油2-18份、硫酸钡2-9份、羟甲基纤维素2-15份、杀菌剂1-10份、有机溶剂2-15份、表面活性剂2-15份、无极氧化物1-10份、增稠剂1-15份、中和剂1-10份、松浆油脂肪酸2-15份、聚丙烯酰胺1-15份、多糖衍生物1-10份、缓蚀剂1-15份、油墨介质吸附剂1-10份。
较佳的，所述多糖衍生物包括：聚葡萄糖、葡聚糖、阿拉伯胶、琼脂、糖元、透明质酸。
较佳的，所述干燥填料是疏水淀粉、S iO2、CaCO3中的一种或几种的混合物。
较佳的，所述托墨层可以一层涂布，也可以分多层涂布。
较佳的，所述粘结剂为水性树脂，采用乙二醛、聚酰胺类树脂、碳酸锆钾、苯乙烯系热塑性弹性体中的任意一种或几种的混合物。
较佳的，所述涂层最佳配比为蔗糖4份、季戊四醇8份、淀粉5份、纤维素7份、气相二氧化硅3份、聚乙烯醇8份、甘油5份、硫酸钡3份、羟甲基纤维素9份、杀菌剂3份、有机溶剂7份、表面活性剂5份、无极氧化物9份、增稠剂3份、中和剂2份、松浆油脂肪酸3份、聚丙烯酰胺2份、多糖衍生物3份、缓蚀剂2份、油墨介质吸附剂3份。
与现有技术相比，本发明的有益效果是：
(1)本发明制备工艺简单，制得热升华转印纸具有良好的托墨能力、耐磨性、抗氧化性、耐水性和附着能力；
(2)本发明中增加有防腐蚀剂，能够使涂层具有良好的防腐蚀性。
具体实施方式
下面对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
本发明提供一种技术方案：一种热升华转印纸，包括托墨层、纸纤维粘结层、基纸层和背涂层，所述托墨层包括聚阴离子纤维素和干燥填料，所述纸纤维粘结层采用粘结剂，所述粘结剂为水性树脂，所述涂层包括蔗糖1-10份、季戊四醇1-15份、淀粉1-10份、纤维素2-15份、气相二氧化硅2-10份、聚乙烯醇2-16份、甘油2-18份、硫酸钡2-9份、羟甲基纤维素2-15份、杀菌剂1-10份、有机溶剂2-15份、表面活性剂2-15份、无极氧化物1-10份、增稠剂1-15份、中和剂1-10份、松浆油脂肪酸2-15份、聚丙烯酰胺1-15份、多糖衍生物1-10份、缓蚀剂1-15份、油墨介质吸附剂1-10份。
实施例一：
于本实施例中，所述涂层最佳配比为蔗糖4份、季戊四醇8份、淀粉5份、纤维素7份、气相二氧化硅3份、聚乙烯醇8份、甘油5份、硫酸钡3份、羟甲基纤维素9份、杀菌剂3份、有机溶剂7份、表面活性剂5份、无极氧化物9份、增稠剂3份、中和剂2份、松浆油脂肪酸3份、聚丙烯酰胺2份、多糖衍生物3份、缓蚀剂2份、油墨介质吸附剂3份。
于本实施例中，所述多糖衍生物包括：聚葡萄糖、葡聚糖、阿拉伯胶、琼脂、糖元、透明质酸。
于本实施例中，所述干燥填料是疏水淀粉、SiO2、CaCO3中的一种或几种的混合物。
于本实施例中，所述托墨层可以一层涂布，也可以分多层涂布。
于本实施例中，所述粘结剂为水性树脂，采用乙二醛、聚酰胺类树脂、碳酸锆钾、苯乙烯系热塑性弹性体中的任意一种或几种的混合物。
实施例二：
于本实施例中，所述涂层最佳配比为蔗糖5份、季戊四醇8份、淀粉5份、纤维素7份、气相二氧化硅3份、聚乙烯醇8份、甘油5份、硫酸钡3份、羟甲基纤维素9份、杀菌剂5份、有机溶剂10份、表面活性剂5份、无极氧化物9份、增稠剂3份、中和剂2份、松浆油脂肪酸3份、聚丙烯酰胺2份、多糖衍生物3份、缓蚀剂2份、油墨介质吸附剂3份。
于本实施例中，所述多糖衍生物包括：聚葡萄糖、葡聚糖、阿拉伯胶、琼脂、糖元、透明质酸。
于本实施例中，所述干燥填料是疏水淀粉、SiO2、CaCO3中的一种或几种的混合物。
于本实施例中，所述托墨层可以一层涂布，也可以分多层涂布。
于本实施例中，所述粘结剂为水性树脂，采用乙二醛、聚酰胺类树脂、碳酸锆钾、苯乙烯系热塑性弹性体中的任意一种或几种的混合物。
实施例三：
于本实施例中，所述涂层最佳配比为蔗糖4份、季戊四醇10份、淀粉6份、纤维素7份、气相二氧化硅3份、聚乙烯醇10份、甘油5份、硫酸钡3份、羟甲基纤维素9份、杀菌剂3份、有机溶剂7份、表面活性剂4份、无极氧化物9份、增稠剂5份、中和剂2份、松浆油脂肪酸3份、聚丙烯酰胺2份、多糖衍生物3份、缓蚀剂2份、油墨介质吸附剂3份。
于本实施例中，所述多糖衍生物包括：聚葡萄糖、葡聚糖、阿拉伯胶、琼脂、糖元、透明质酸。
于本实施例中，所述干燥填料是疏水淀粉、SiO2、CaCO3中的一种或几种的混合物。
于本实施例中，所述托墨层可以一层涂布，也可以分多层涂布。
于本实施例中，所述粘结剂为水性树脂，采用乙二醛、聚酰胺类树脂、碳酸锆钾、苯乙烯系热塑性弹性体中的任意一种或几种的混合物。
实施例四：
于本实施例中，所述涂层最佳配比为蔗糖4份、季戊四醇8份、淀粉10份、纤维素2份、气相二氧化硅10份、聚乙烯醇8份、甘油5份、硫酸钡3份、羟甲基纤维素9份、杀菌剂3份、有机溶剂10份、表面活性剂5份、无极氧化物9份、增稠剂3份、中和剂2份、松浆油脂肪酸3份、聚丙烯酰胺2份、多糖衍生物3份、缓蚀剂2份、油墨介质吸附剂3份。
于本实施例中，所述多糖衍生物包括：聚葡萄糖、葡聚糖、阿拉伯胶、琼脂、糖元、透明质酸。
于本实施例中，所述干燥填料是疏水淀粉、SiO2、CaCO3中的一种或几种的混合物。
于本实施例中，所述托墨层可以一层涂布，也可以分多层涂布。
于本实施例中，所述粘结剂为水性树脂，采用乙二醛、聚酰胺类树脂、碳酸锆钾、苯乙烯系热塑性弹性体中的任意一种或几种的混合物。
本发明制备工艺简单，制得热升华转印纸具有良好的托墨能力、防腐性、耐磨性、抗氧化性、耐水性和附着能力；本发明中添加防腐蚀剂，能使油墨具有良好的防腐蚀性。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (6)
1.一种热升华转印纸，其特征在于：包括托墨层、纸纤维粘结层、基纸层和背涂层，所述托墨层包括聚阴离子纤维素和干燥填料，所述纸纤维粘结层采用粘结剂，所述粘结剂为水性树脂，所述涂层包括蔗糖1-10份、季戊四醇1-15份、淀粉1-10份、纤维素2-15份、气相二氧化硅2-10份、聚乙烯醇2-16份、甘油2-18份、硫酸钡2-9份、羟甲基纤维素2-15份、杀菌剂1-10份、有机溶剂2-15份、表面活性剂2-15份、无极氧化物1-10份、增稠剂1-15份、中和剂1-10份、松浆油脂肪酸2-15份、聚丙烯酰胺1-15份、多糖衍生物1-10份、缓蚀剂1-15份、油墨介质吸附剂1-10份。
2.根据权利要求1所述的热升华转印纸,其特征在于：所述多糖衍生物包括：聚葡萄糖、葡聚糖、阿拉伯胶、琼脂、糖元、透明质酸。
3.根据权利要求1所述的热升华转印纸,其特征在于：所述干燥填料是疏水淀粉、SiO2、CaCO3中的一种或几种的混合物。
4.根据权利要求1所述的热升华转印纸,其特征在于：所述托墨层可以一层涂布，也可以分多层涂布。
5.根据权利要求1所述的热升华转印纸,其特征在于：所述粘结剂为水性树脂，采用乙二醛、聚酰胺类树脂、碳酸锆钾、苯乙烯系热塑性弹性体中的任意一种或几种的混合物。
6.根据权利要求1所述的热升华转印纸,其特征在于：所述涂层最佳配比为蔗糖4份、季戊四醇8份、淀粉5份、纤维素7份、气相二氧化硅3份、聚乙烯醇8份、甘油5份、硫酸钡3份、羟甲基纤维素9份、杀菌剂3份、有机溶剂7份、表面活性剂5份、无极氧化物9份、增稠剂3份、中和剂2份、松浆油脂肪酸3份、聚丙烯酰胺2份、多糖衍生物3份、缓蚀剂2份、油墨介质吸附剂3份。