CN106543815A - A kind of wood plastic decorative construction material - Google Patents
A kind of wood plastic decorative construction material Download PDFInfo
- Publication number
- CN106543815A CN106543815A CN201611055380.4A CN201611055380A CN106543815A CN 106543815 A CN106543815 A CN 106543815A CN 201611055380 A CN201611055380 A CN 201611055380A CN 106543815 A CN106543815 A CN 106543815A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- styrene
- construction material
- wood
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of wood plastic decorative construction material, which is composed of the following components by weight：100 105 parts of polrvinyl chloride、15 18 parts of Kaolin、30 35 parts of wood powder、57 parts of carbonyl iron dust、0.8 1.2 parts of copper sulphate pentahydrate、46 parts of nitrile rubber、25 30 parts of furfuryl alcohol resin、11 32 parts of hydroxyethyl cellulose、39 parts of expanded perlite、49 parts of tourmaline powder、Heptan 2.3 4.5 parts of 2 alkene, 2 methanol、8 15 parts of styrene-acrylic emulsion、46 parts of butyl acetate、5 10 parts of magnesium chloride、28 parts of mica powder、37 parts of methyl styrene、10 15 parts of titanium dioxide、35 45 parts of white glue with vinyl、2.5 4.6 parts of sodium hexameta phosphate、60 70 parts of acrylic acid ester emulsion、0.1 0.3 parts of hexafluoroacetylacetone calcium、1.5 3 parts of lithium magnesium silicate、12 parts of phenothiazine、12 parts of benzotriazole、13 parts of mill base.The coating of the present invention has the function such as water-fast, acidproof, alkaline-resisting, freeze thawing resistance, dirt-resisting dustproof, ageing-resistant, fire prevention, is a kind of coating for possessing and having several functions, applied widely, meets requirement of the people to decorative paint.
Description
Technical field
The present invention relates to a kind of construction material, specially a kind of wood plastic decorative construction material.
Background technology
Wall acrylic acid gloss emulsion paint, is all thin coating, it with high-molecular organic material as main film forming substance, plus
Upper different pigment, filler and aggregate and made by thin coat, the features such as with water-fast, acidproof, alkaline-resisting, freeze thawing resistance, current city
The function imperfection that coating on face has, existing defects, the major defect of this coating are that film elasticity is easily aging, cause
Extensibility declines, is unable to the intensity of effective protection wall plaster bottom, so as to producing metope cracking, coming off, not only affects building
Thing is attractive in appearance, and metope cracking, causes metope leak.
The content of the invention
It is an object of the invention to provide a kind of wood plastic decorative construction material.
The purpose of the present invention can be achieved through the following technical solutions：
A kind of wood plastic decorative construction material, which is composed of the following components by weight：Polrvinyl chloride 100-105 parts, height
Ridge soil 15-18 parts, wood powder 30-35 parts, carbonyl iron dust 5-7 parts, copper sulphate pentahydrate 0.8-1.2 parts, nitrile rubber 4-6 parts, furfuryl alcohol
Resin 25-30 parts, hydroxyethyl cellulose 11-32 parts, expanded perlite 3-9 parts, tourmaline powder 4-9 parts, hept-2-ene" -2- methanol
2.3-4.5 parts, styrene-acrylic emulsion 8-15 parts, butyl acetate 4-6 parts, magnesium chloride 5-10 parts, mica powder 2-8 parts, methyl styrene 3-7
Part, titanium dioxide 10-15 parts, white glue with vinyl 35-45 part, sodium hexameta phosphate 2.5-4.6 parts, acrylic acid ester emulsion 60-70 parts, hexafluoro second
Acyl acetone calcium 0.1-0.3 parts, lithium magnesium silicate 1.5-3 parts, phenothiazine 1-2 parts, benzotriazole 1-2 parts, mill base 1-3 parts.
Preferably, a kind of wood plastic decorative construction material, which is composed of the following components by weight：Polrvinyl chloride
100 parts, 18 parts of Kaolin, 30 parts of wood powder, 5 parts of carbonyl iron dust, 1.2 parts of copper sulphate pentahydrate, 4 parts of nitrile rubber, furfuryl alcohol resin 25
Part, 32 parts of hydroxyethyl cellulose, -9 parts of expanded perlite, 9 parts of tourmaline powder, 2.3 parts of hept-2-ene" -2- methanol, styrene-acrylic emulsion 8
It is part, 4 parts of butyl acetate, 10 parts of magnesium chloride, 8 parts of mica powder, 7 parts of methyl styrene, 15 parts of titanium dioxide, 45 parts of white glue with vinyl, six inclined
2.5 parts of sodium phosphate, 60 parts of acrylic acid ester emulsion, 0.3 part of hexafluoroacetylacetone calcium, 1.5 parts of lithium magnesium silicate, 2 parts of phenothiazine, benzene a pair of horses going side by side
1 part of triazole, 3 parts of mill base.
Preferably, a kind of wood plastic decorative construction material, which is composed of the following components by weight：Polrvinyl chloride
100 parts, 16 parts of Kaolin, 32 parts of wood powder, 6 parts of carbonyl iron dust, 1 part of copper sulphate pentahydrate, 5 parts of nitrile rubber, 28 parts of furfuryl alcohol resin,
22 parts of hydroxyethyl cellulose, 6 parts of expanded perlite, 6 parts of tourmaline powder, 3.5 parts of hept-2-ene" -2- methanol, 10 parts of styrene-acrylic emulsion,
5 parts of butyl acetate, 8 parts of magnesium chloride, 6 parts of mica powder, 4 parts of methyl styrene, 12 parts of titanium dioxide, 40 parts of white glue with vinyl, hexa metaphosphoric acid
4 parts of sodium, 65 parts of acrylic acid ester emulsion, 0.2 part of hexafluoroacetylacetone calcium, 2 parts of lithium magnesium silicate, 2 parts of phenothiazine, benzotriazole 2
Part, 2 parts of mill base..
Beneficial effects of the present invention：The coating of the present invention has water-fast, acidproof, alkaline-resisting, freeze thawing resistance, dirt-resisting dustproof, resistance to old
The functions such as change, fire prevention, are a kind of coating for possessing and having several functions, applied widely, meet the requirement of people's External Wall coating.
Specific embodiment
The present invention is described further with reference to embodiment.
Embodiment 1
A kind of wood plastic decorative construction material, which is composed of the following components by weight：100 parts of polrvinyl chloride, Kaolin
15 parts, 30 parts of wood powder, 5 parts of carbonyl iron dust, 0.8 part of copper sulphate pentahydrate, 4 parts of nitrile rubber, 25 parts of furfuryl alcohol resin, hydroxy ethyl fiber
Element 11 parts, 3 parts of expanded perlite, 4 parts of tourmaline powder, 2.3 parts of hept-2-ene" -2- methanol, 8 parts of styrene-acrylic emulsion, 4 parts of butyl acetate,
5 parts of magnesium chloride, 2 parts of mica powder, 3 parts of methyl styrene, 10 parts of titanium dioxide, 35 parts of white glue with vinyl, 2.5 parts of sodium hexameta phosphate, propylene
60 parts of acid esters emulsion, 0.1 part of hexafluoroacetylacetone calcium, 1.5 parts of lithium magnesium silicate, 1 part of phenothiazine, 1 part of benzotriazole, mill base 1
Part.
Embodiment 2
A kind of wood plastic decorative construction material, which is composed of the following components by weight：105 parts of polrvinyl chloride, Kaolin
18 parts, 35 parts of wood powder, 7 parts of carbonyl iron dust, 1.2 parts of copper sulphate pentahydrate, 6 parts of nitrile rubber, 30 parts of furfuryl alcohol resin, hydroxy ethyl fiber
32 parts of element, 9 parts of expanded perlite, 9 parts of tourmaline powder, 4.5 parts of hept-2-ene" -2- methanol, 15 parts of styrene-acrylic emulsion, butyl acetate 6
Part, 10 parts of magnesium chloride, 8 parts of mica powder, 7 parts of methyl styrene, 15 parts of titanium dioxide, 45 parts of white glue with vinyl, 4.6 parts of sodium hexameta phosphate,
70 parts of acrylic acid ester emulsion, 0.3 part of hexafluoroacetylacetone calcium, 3 parts of lithium magnesium silicate, 2 parts of phenothiazine, 2 parts of benzotriazole, mill base
3 parts.
Embodiment 3
A kind of wood plastic decorative construction material, which is composed of the following components by weight：100 parts of polrvinyl chloride, Kaolin
18 parts, 30 parts of wood powder, 5 parts of carbonyl iron dust, 1.2 parts of copper sulphate pentahydrate, 4 parts of nitrile rubber, 25 parts of furfuryl alcohol resin, hydroxy ethyl fiber
32 parts of element, -9 parts of expanded perlite, 9 parts of tourmaline powder, 2.3 parts of hept-2-ene" -2- methanol, 8 parts of styrene-acrylic emulsion, butyl acetate 4
Part, 10 parts of magnesium chloride, 8 parts of mica powder, 7 parts of methyl styrene, 15 parts of titanium dioxide, 45 parts of white glue with vinyl, 2.5 parts of sodium hexameta phosphate,
60 parts of acrylic acid ester emulsion, 0.3 part of hexafluoroacetylacetone calcium, 1.5 parts of lithium magnesium silicate, 2 parts of phenothiazine, 1 part of benzotriazole, color
3 parts of slurry.
Embodiment 4
A kind of wood plastic decorative construction material, which is composed of the following components by weight：100 parts of polrvinyl chloride, Kaolin
16 parts, 32 parts of wood powder, 6 parts of carbonyl iron dust, 1 part of copper sulphate pentahydrate, 5 parts of nitrile rubber, 28 parts of furfuryl alcohol resin, hydroxyethyl cellulose
22 parts, 6 parts of expanded perlite, 6 parts of tourmaline powder, 3.5 parts of hept-2-ene" -2- methanol, 10 parts of styrene-acrylic emulsion, 5 parts of butyl acetate,
8 parts of magnesium chloride, 6 parts of mica powder, 4 parts of methyl styrene, 12 parts of titanium dioxide, 40 parts of white glue with vinyl, 4 parts of sodium hexameta phosphate, acrylic acid
65 parts of ester emulsion, 0.2 part of hexafluoroacetylacetone calcium, 2 parts of lithium magnesium silicate, 2 parts of phenothiazine, 2 parts of benzotriazole, 2 parts of mill base.
Above content is only to present configuration example and explanation, affiliated those skilled in the art couple
Described instantiation is made various modifications or supplements or substituted using similar mode, as long as will not past this right
Scope defined in book is sought, the protection domain of invention all should be belonged to.
Claims (3)
1. a kind of wood plastic decorative construction material, it is characterised in which is composed of the following components by weight：Polrvinyl chloride 100-
105 parts, Kaolin 15-18 parts, wood powder 30-35 parts, carbonyl iron dust 5-7 parts, copper sulphate pentahydrate 0.8-1.2 parts, nitrile rubber 4-6
Part, furfuryl alcohol resin 25-30 parts, hydroxyethyl cellulose 11-32 parts, expanded perlite 3-9 parts, tourmaline powder 4-9 parts, hept-2-ene"-
2- methanol 2.3-4.5 parts, styrene-acrylic emulsion 8-15 parts, butyl acetate 4-6 parts, magnesium chloride 5-10 parts, mica powder 2-8 parts, methylbenzene
Ethylene 3-7 parts, titanium dioxide 10-15 parts, white glue with vinyl 35-45 part, sodium hexameta phosphate 2.5-4.6 parts, acrylic acid ester emulsion 60-70
Part, hexafluoroacetylacetone calcium 0.1-0.3 parts, lithium magnesium silicate 1.5-3 parts, phenothiazine 1-2 parts, benzotriazole 1-2 parts, mill base 1-
3 parts.
2. a kind of wood plastic decorative construction material according to claim 1, it is characterised in which is by following components by weight
Composition：100 parts of polrvinyl chloride, 18 parts of Kaolin, 30 parts of wood powder, 5 parts of carbonyl iron dust, 1.2 parts of copper sulphate pentahydrate, nitrile rubber 4
Part, 25 parts of furfuryl alcohol resin, 32 parts of hydroxyethyl cellulose, -9 parts of expanded perlite, 9 parts of tourmaline powder, hept-2-ene" -2- methanol 2.3
Part, 8 parts of styrene-acrylic emulsion, 4 parts of butyl acetate, 10 parts of magnesium chloride, 8 parts of mica powder, 7 parts of methyl styrene, 15 parts of titanium dioxide, Virgin's milk
45 parts of glue, 2.5 parts of sodium hexameta phosphate, 60 parts of acrylic acid ester emulsion, 0.3 part of hexafluoroacetylacetone calcium, 1.5 parts of lithium magnesium silicate, fen
2 parts of thiazine, 1 part of benzotriazole, 3 parts of mill base.
3. a kind of wood plastic decorative construction material according to claim 1, it is characterised in which is by following components by weight
Composition：100 parts of polrvinyl chloride, 16 parts of Kaolin, 32 parts of wood powder, 6 parts of carbonyl iron dust, 1 part of copper sulphate pentahydrate, 5 parts of nitrile rubber,
28 parts of furfuryl alcohol resin, 22 parts of hydroxyethyl cellulose, 6 parts of expanded perlite, 6 parts of tourmaline powder, 3.5 parts of hept-2-ene" -2- methanol,
10 parts of styrene-acrylic emulsion, 5 parts of butyl acetate, 8 parts of magnesium chloride, 6 parts of mica powder, 4 parts of methyl styrene, 12 parts of titanium dioxide, white glue with vinyl
40 parts, 4 parts of sodium hexameta phosphate, 65 parts of acrylic acid ester emulsion, 0.2 part of hexafluoroacetylacetone calcium, 2 parts of lithium magnesium silicate, phenothiazine 2
Part, 2 parts of benzotriazole, 2 parts of mill base.