CN106243828A - 一种水性油墨 - Google Patents
一种水性油墨 Download PDFInfo
- Publication number
- CN106243828A CN106243828A CN201610749366.8A CN201610749366A CN106243828A CN 106243828 A CN106243828 A CN 106243828A CN 201610749366 A CN201610749366 A CN 201610749366A CN 106243828 A CN106243828 A CN 106243828A
- Authority
- CN
- China
- Prior art keywords
- parts
- color ink
- water
- water color
- weight ratio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种水性油墨，包括以下重量份的材料：颜料10‑25份，连结料25‑40份，溶剂35‑70份，消泡剂1‑3份，流平剂1‑3份，5A分子筛2‑5份，气相二氧化硅1‑2份，分散剂2‑5份，附着力促进剂0.5‑1.5份，乙醇胺1‑3份,三乙胺3‑5份，2‑氨基‑2‑甲基‑1‑丙醇1‑3份，反干燥剂2‑3份，胶质油1‑2份。本发明中可以增强油墨的附着力，防止油墨出现渗墨、化墨等现象，稳定性强，存储时间长，具有一定的防干燥能力，污染小。
Description
技术领域
本发明涉及油墨技术领域，尤其涉及一种水性油墨。
背景技术
水性油墨是由连结料、颜料、助剂等物质组成的均匀浆状物质。连结料提供油墨必要的转移性能，颜料赋予油墨以色彩。水性油墨的连结料主要分为两种类型：水稀释型和水分散型。前者可以使用的树脂类型有很多种。水分散型的连结料是在水中通过乳化的单体聚合所得，它是两相体系，其中油相以颗粒状在水相中分散，虽不能够被水溶解，但能够被水稀释，所以也可以认为是水包油乳液型，水性油墨以水为溶剂，挥发性有机化合物含量极低，对环境污染小；油性油墨以有机溶剂为溶剂，对环境污染大。因此，水性油墨越来越受到欢迎；但目前，水性油墨普遍在分散性、光泽度、抗水性上性能不足，在固化时时间较长，降低了使用效率，增加了成本，同时油墨的储存效果也是值得关注的问题，同时油墨的储存效果也是值得关注的问题。
发明内容
基于背景技术存在的技术问题，本发明提出了一种水性油墨。
本发明提出的一种水性油墨，包括以下重量份的材料：颜料10-25份，连结料25-40份，溶剂35-70份，消泡剂1-3份，流平剂1-3份，5A分子筛2-5份，气相二氧化硅1-2份，分散剂2-5份，附着力促进剂0.5-1.5份，乙醇胺1-3份,三乙胺3-5份，2-氨基-2-甲基-1-丙醇1-3份，反干燥剂2-3份，胶质油1-2份。
优选地，所述连结料是水溶性丙烯酸树脂、顺丁烯二酸树脂和水性氨基树脂按照重量比为4:1:1混合组成。
优选地，所述溶剂包括去离子水、乙醇和乙二醇丁醚并按照重量比为3:1:1混合组成。
优选地，所述消泡剂为聚醚改性硅。
优选地，所述流平剂是聚二甲基硅氧烷和氟化硅氧烷按照重量比为2:1混合组成。
优选地，所述附着力促进剂是氨基硅烷和环氧基硅烷按照重量比为1:2混合组成。
优选地，所述分散剂为油酸酰胺。
优选地，所述反干燥剂是对苯二胺、邻苯二酚和β-萘酚按照重量比为1:2:1混合组成。
优选地，所述颜料为有机颜料或无机颜料。
本发明与现有技术相比较，具有的有益技术效果：
本发明中，选用油酸酰胺作为分散剂可以降低树脂颗粒成型熔融黏度，分散那些难于溶解于液体的无机、有机颜料的固体及液体颗粒，同时也能防止颗粒的沉降和凝聚、改进流动性同时兼具增滑剂的功能可降低油墨表面摩擦系数；由于油墨在使用过程中容易起泡会影响印刷的质量，消泡剂聚醚改性硅结合了聚醚跟有机硅消泡剂二者的优点，耐酸、碱和无机盐，可用于苛刻条件下的消泡，可降低体系表面张力，使自己易于在液体的表面铺展和吸附，从而降低液体表面膜强度来达到消泡目的；流平剂可以使油墨在干燥成膜过程中形成一个平整、光滑、均匀的涂膜，采用聚二甲基硅氧烷和氟化硅氧烷按照重量比为2:1混合组成，聚二甲基硅氧烷具备良好的表面状态控制能力，但会经常出现缩孔，加入氟化硅氧烷后则可以改善基材的润湿性，提高防缩孔能力；加入气相二氧化硅能在油墨体系中起到较好的防沉降作用，但是较多的气相二氧化硅会使油墨的流平性变差，此时添加5A分子筛可以提高油墨的稳定性，5A分子筛孔壁上的硅羟基的极性可以使5A分子筛与带有极性基团的连结料之间具有很好的相容性，使得分子筛的存在能够使连结料通过化学键与分子筛连接起来，使油墨的网链结构更加完善，提高油墨的储存时间；连结料采用水溶性丙烯酸树脂、顺丁烯二酸树脂和水性氨基树脂按照重量比为4:1:1混合组成，水溶性丙烯酸树脂价格低、使用安全，能节省资源和能源，减少环境污染和公害，水性氨基树脂为无色透明粘性液体，水溶性好，可以无限稀释，具有较高的活性；溶剂包括去离子水、乙醇和乙二醇丁醚并按照重量比为3:1:1混合组成，相互之间融合性好，较单一溶剂来说，对连结料树脂具有很强的溶解力，将大部分有机挥发溶剂替代为去离子水，从而达到大幅度降低大气污染的目的；附着力促进剂是氨基硅烷和环氧基硅烷按照重量比为1:2混合组成，环氧基硅烷为新型的环氧基偶联剂，具有反应活性基团，具有良好的耐黄变性特性，氨基硅烷具有两种功能团，即氨基和乙氧基，其中三个可水解基团(乙氧基)，在反应中先水解生成硅醇，由于硅醇不稳定，极易与无机物或金属表面的羟基结合脱水，从而与无机物或金属结合起来，氨基上带有两个活泼氢可以和各种聚合物发生反应，从而通过化学键将两种性质完全不同的材料紧密的结合起来，两者配合使用可以进一步提高树脂连结料的附着力，防止油墨出现渗墨、化墨等现象；胶质油可以提高油墨的固着速度，稳定性佳，可用来调整油墨身骨及光泽；反干燥剂是对苯二胺、邻苯二酚和β-萘酚按照重量比为1:2:1混合组成，较单一的反干燥剂来说，其具有更加广泛的抗氧化性能，可避免油墨干燥过快而导致印刷机器上的油墨干燥起皮；由于pH值的大小对油墨的稳定性和粘度有很大的影响，加入乙醇胺、三乙胺和2-氨基-2-甲基-1-丙醇可调节水性油墨的pH值使其维持在8.0-9.5之间，其中2-氨基-2-甲基-1-丙醇和乙醇胺与水性树脂发生的是酰胺化反应达到中和，而三乙胺与水性树脂发生的是酯化反应达到中和。
具体实施方式
下面结合具体实施例对本发明作进一步解说。
实施例1
本实施例中，一种水性油墨，包括以下重量份的材料：颜料10份，连结料25份，溶剂35份，消泡剂1份，流平剂1份，5A分子筛2份，气相二氧化硅1份，分散剂2份，附着力促进剂0.5份，乙醇胺1份,三乙胺3份，2-氨基-2-甲基-1-丙醇1份，反干燥剂2份，胶质油1份。
连结料是水溶性丙烯酸树脂、顺丁烯二酸树脂和水性氨基树脂按照重量比为4:1:1混合组成，溶剂包括去离子水、乙醇和乙二醇丁醚并按照重量比为3:1:1混合组成，消泡剂为聚醚改性硅，流平剂是聚二甲基硅氧烷和氟化硅氧烷按照重量比为2:1混合组成，附着力促进剂是氨基硅烷和环氧基硅烷按照重量比为1:2混合组成，分散剂为油酸酰胺，反干燥剂是对苯二胺、邻苯二酚和β-萘酚按照重量比为1:2:1混合组成，颜料为有机颜料中的酞菁蓝。
实施例2
本实施例中，一种水性油墨，包括以下重量份的材料：颜料17.5份，连结料32.5份，溶剂52.5份，消泡剂2份，流平剂2份，5A分子筛3.5份，气相二氧化硅1.5份，分散剂3.5份，附着力促进剂1份，乙醇胺2份,三乙胺4份，2-氨基-2-甲基-1-丙醇2份，反干燥剂2.5份，胶质油1.5份。
连结料是水溶性丙烯酸树脂、顺丁烯二酸树脂和水性氨基树脂按照重量比为4:1:1混合组成，溶剂包括去离子水、乙醇和乙二醇丁醚并按照重量比为3:1:1混合组成，消泡剂为聚醚改性硅，流平剂是聚二甲基硅氧烷和氟化硅氧烷按照重量比为2:1混合组成，附着力促进剂是氨基硅烷和环氧基硅烷按照重量比为1:2混合组成，分散剂为油酸酰胺，反干燥剂是对苯二胺、邻苯二酚和β-萘酚按照重量比为1:2:1混合组成，颜料为有机颜料中的立索尔红。
实施例3
本实施例中，一种水性油墨，包括以下重量份的材料：颜料25份，连结料40份，溶剂70份，消泡剂3份，流平剂3份，5A分子筛5份，气相二氧化硅2份，分散剂5份，附着力促进剂1.5份，乙醇胺3份,三乙胺5份，2-氨基-2-甲基-1-丙醇3份，反干燥剂3份，胶质油2份。
连结料是水溶性丙烯酸树脂、顺丁烯二酸树脂和水性氨基树脂按照重量比为4:1:1混合组成，溶剂包括去离子水、乙醇和乙二醇丁醚并按照重量比为3:1:1混合组成，消泡剂为聚醚改性硅，流平剂是聚二甲基硅氧烷和氟化硅氧烷按照重量比为2:1混合组成，附着力促进剂是氨基硅烷和环氧基硅烷按照重量比为1:2混合组成，分散剂为油酸酰胺，反干燥剂是对苯二胺、邻苯二酚和β-萘酚按照重量比为1:2:1混合组成，颜料为无机颜料中的钛白粉。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。
Claims (9)
1.一种水性油墨，其特征在于，包括以下重量份的材料：颜料10-25份，连结料25-40份，溶剂35-70份，消泡剂1-3份，流平剂1-3份，5A分子筛2-5份，气相二氧化硅1-2份，分散剂2-5份，附着力促进剂0.5-1.5份，乙醇胺1-3份,三乙胺3-5份，2-氨基-2-甲基-1-丙醇1-3份，反干燥剂2-3份，胶质油1-2份。
2.根据权利要求1所述的一种水性油墨，其特征在于：所述连结料是水溶性丙烯酸树脂、顺丁烯二酸树脂和水性氨基树脂按照重量比为4:1:1混合组成。
3.根据权利要求1所述的一种水性油墨，其特征在于：所述溶剂包括去离子水、乙醇和乙二醇丁醚并按照重量比为3:1:1混合组成。
4.根据权利要求1所述的一种水性油墨，其特征在于：所述消泡剂为聚醚改性硅。
5.根据权利要求1所述的一种水性油墨，其特征在于：所述流平剂是聚二甲基硅氧烷和氟化硅氧烷按照重量比为2:1混合组成。
6.根据权利要求1所述的一种水性油墨，其特征在于：所述附着力促进剂是氨基硅烷和环氧基硅烷按照重量比为1:2混合组成。
7.根据权利要求1所述的一种水性油墨，其特征在于：所述分散剂为油酸酰胺。
8.根据权利要求1所述的一种水性油墨，其特征在于：所述反干燥剂是对苯二胺、邻苯二酚和β-萘酚按照重量比为1:2:1混合组成。
9.根据权利要求1所述的一种水性油墨，其特征在于：所述颜料为有机颜料或无机颜料。