CN106221000A - 一种高强度耐撕裂聚丙烯薄膜配方 - Google Patents
一种高强度耐撕裂聚丙烯薄膜配方 Download PDFInfo
- Publication number
- CN106221000A CN106221000A CN201610613544.4A CN201610613544A CN106221000A CN 106221000 A CN106221000 A CN 106221000A CN 201610613544 A CN201610613544 A CN 201610613544A CN 106221000 A CN106221000 A CN 106221000A
- Authority
- CN
- China
- Prior art keywords
- parts
- high intensity
- tear
- polypropylene film
- pelopon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种高强度耐撕裂聚丙烯薄膜配方，包括以下重量份的原料：聚丙烯80‑90份、丁醚化树脂10‑15份、三烯丙基异氰酸酯4‑8份、羟丙基纤维素12‑18份、普鲁兰多糖7‑15份、纳米二氧化硅13‑16份、十二烷基苯磺酸钠盐2‑7份、乙酸龙脑酯2‑5份、木粉11‑13份、甘油30‑40份。本发明高强度耐撕裂聚丙烯薄膜大大提高了薄膜的耐撕裂强度，提高了薄膜的稳定性，大大增强了薄膜的使用寿命。
Description
技术领域
本发明属于高分子材料领域，具体涉及一种高强度耐撕裂聚丙烯薄膜配方。
背景技术
中国塑料薄膜的产量约占塑料制品总产量的20％，是塑料制品中产量增长较快的类别之一。从中国塑料薄膜(厚度为0.06mm～0.26mm)的应用领域看，用量最大、品种最多、应用最广的是包装工业，其消费约占2/3，其次是农业约占30％，再有就是功能膜，如微孔膜、屏蔽膜、土工膜等。若在树脂基体中添加适宜的塑料助剂，就可以制备出所需的各种功能性薄膜。塑料薄膜工业上的生产方法有压延法和挤出法，其中挤出法又分为挤出吹膜、挤出流延、挤出拉伸(又称二次成型)等。
随着中国经济的发展以及农村产业结构的调整，中国各行各业对塑料薄膜的市场需求不断上升。预测2015年全球塑料薄膜和板材市场消费量有望达到5070万吨，其中亚太地区预计将成为增长最快的区域市场。中国塑料薄膜产业当前正处于一个蓬勃发展的阶段，2001-2011年市场规模年均增速达到18％以上，预计2012年将达到3500亿元。
中国塑料薄膜行业正处于一个蓬勃发展的阶段，据悉，中国塑料薄膜的需求量每年将以9％以上的速度增长。而且随着各种新材料、新设备和新工艺不断地涌现，将促使中国的塑料薄膜朝着品种多样化、专用化以及具备多功能的复合膜方向发展。
塑料薄膜，用于包装,以及用作覆膜层。塑料包装及塑料包装产品在市场上所占的份额越来越大，特别是复合塑料软包装，已经广泛地应用于食品、医药、化工等领域，其中又以食品包装所占比例最大，比如饮料包装、速冻食品包装、蒸煮食品包装、快餐食品包装等，这些产品都给人们生活带来了极大的便利。
聚丙烯薄膜有良好的光泽和很好的透明度，耐热酸碱、耐溶剂、耐摩擦、耐撕裂、能透气，低于160℃时不能热封。双向拉伸聚丙烯薄膜具有质轻、无毒、无臭、防潮、机械强度高，尺寸稳定性好、印刷性能良好、透明性好等优点。具有高透明度、光泽好、阻隔性好、抗冲强度高、耐低温等优点。其缺点是热合时易发生薄膜收缩(热收缩烟膜利用其热收缩性能除外)。它的综合性能优于防潮。广泛应用于食品、糖果、香烟、茶叶、果汁、牛奶、纺织品等的包装，有“包装皇后”的美称。在某些贵重产品的运输中，尤其是出口产品的运输，因运输路途较长且可能会存在较恶劣的运输条件，这些产品往往要求包装物具有非常高的强度，以保证这类产品的安全运输。但现有的聚丙烯薄膜存在强度低、耐撕裂性能不好的问题。
综上所述，解决现有技术存在的不足已成为本领域亟待解决的技术问题。
发明内容
本发明的目的在于提供一种高强度耐撕裂聚丙烯薄膜配方。
为了实现上述目的，本发明提供了一种高强度耐撕裂聚丙烯薄膜配方，由以下重量份的原料制得：聚丙烯80-90份、丁醚化树脂10-15份、三烯丙基异氰酸酯4-8份、羟丙基纤维素12-18份、普鲁兰多糖7-15份、纳米二氧化硅13-16份、十二烷基苯磺酸钠盐2-7份、乙酸龙脑酯2-5份、木粉11-13份、甘油30-40份。
优选方案为由以下重量份的原料制得：聚丙烯80份、丁醚化树脂10份、三烯丙基异氰酸酯4份、羟丙基纤维素12份、普鲁兰多糖7份、纳米二氧化硅13份、十二烷基苯磺酸钠盐2份、乙酸龙脑酯2份、木粉11份、甘油30份。
优选方案为由以下重量份的原料制得：聚丙烯90份、丁醚化树脂15份、三烯丙基异氰酸酯8份、羟丙基纤维素18份、普鲁兰多糖15份、纳米二氧化硅16份、十二烷基苯磺酸钠盐7份、乙酸龙脑酯5份、木粉13份、甘油40份。
优选方案为由以下重量份的原料制得：聚丙烯82份、丁醚化树脂12份、三烯丙基异氰酸酯5份、羟丙基纤维素13份、普鲁兰多糖8份、纳米二氧化硅14份、十二烷基苯磺酸钠盐3份、乙酸龙脑酯3份、木粉12份、甘油32份。
优选方案为由以下重量份的原料制得：聚丙烯88份、丁醚化树脂14份、三烯丙基异氰酸酯7份、羟丙基纤维素17份、普鲁兰多糖13份、纳米二氧化硅15份、十二烷基苯磺酸钠盐6份、乙酸龙脑酯4份、木粉12份、甘油38份。
其制备方法为：按重量份配比称取各组分，投入到反应釜中，在氮气气氛中加热反应，然后送入双螺杆挤出机，双螺杆挤出样条经水冷、风干、切粒，得到母粒，最后将母粒放入塑料吹膜机挤出吹膜，即得到成品。
本发明具有以下有益效果：本发明高强度耐撕裂聚丙烯薄膜大大提高了薄膜的耐撕裂强度，提高了薄膜的稳定性，大大增强了薄膜的使用寿命。
具体实施方式
实施例1
本实施例的一种高强度耐撕裂聚丙烯薄膜配方，由以下重量份的原料制得：聚丙烯90份、丁醚化树脂15份、三烯丙基异氰酸酯8份、羟丙基纤维素18份、普鲁兰多糖15份、纳米二氧化硅16份、十二烷基苯磺酸钠盐7份、乙酸龙脑酯5份、木粉13份、甘油40份。
制备方法为：按重量份配比称取各组分，投入到反应釜中，在氮气气氛中加热反应，然后送入双螺杆挤出机，双螺杆挤出样条经水冷、风干、切粒，得到母粒，最后将母粒放入塑料吹膜机挤出吹膜，即得到成品。
实施例2
本实施例的一种高强度耐撕裂聚丙烯薄膜配方，由以下重量份的原料制得：聚丙烯80份、丁醚化树脂10份、三烯丙基异氰酸酯4份、羟丙基纤维素12份、普鲁兰多糖7份、纳米二氧化硅13份、十二烷基苯磺酸钠盐2份、乙酸龙脑酯2份、木粉11份、甘油30份。制备方法为：按重量份配比称取各组分，投入到反应釜中，在氮气气氛中加热反应，然后送入双螺杆挤出机，双螺杆挤出样条经水冷、风干、切粒，得到母粒，最后将母粒放入塑料吹膜机挤出吹膜，即得到成品。
实施例3
本实施例的一种高强度耐撕裂聚丙烯薄膜配方，由以下重量份的原料制得：聚丙烯82份、丁醚化树脂12份、三烯丙基异氰酸酯5份、羟丙基纤维素13份、普鲁兰多糖8份、纳米二氧化硅14份、十二烷基苯磺酸钠盐3份、乙酸龙脑酯3份、木粉12份、甘油32份。所述强碱为氢氧化锂。制备方法为：按重量份配比称取各组分，投入到反应釜中，在氮气气氛中加热反应，然后送入双螺杆挤出机，双螺杆挤出样条经水冷、风干、切粒，得到母粒，最后将母粒放入塑料吹膜机挤出吹膜，即得到成品。
实施例4
本实施例的一种高强度耐撕裂聚丙烯薄膜配方，由以下重量份的原料制得：聚丙烯82份、丁醚化树脂12份、三烯丙基异氰酸酯5份、羟丙基纤维素13份、普鲁兰多糖8份、纳米二氧化硅14份、十二烷基苯磺酸钠盐3份、乙酸龙脑酯3份、木粉12份、甘油32份。制备方法为：按重量份配比称取各组分，投入到反应釜中，在氮气气氛中加热反应，然后送入双螺杆挤出机，双螺杆挤出样条经水冷、风干、切粒，得到母粒，最后将母粒放入塑料吹膜机挤出吹膜，即得到成品。
Claims (5)
1.一种高强度耐撕裂聚丙烯薄膜配方，其特征在于包括以下重量份的原料：聚丙烯80-90份、丁醚化树脂10-15份、三烯丙基异氰酸酯4-8份、羟丙基纤维素12-18份、普鲁兰多糖7-15份、纳米二氧化硅13-16份、十二烷基苯磺酸钠盐2-7份、乙酸龙脑酯2-5份、木粉11-13份、甘油30-40份。
2.根据权利要求1所述的一种高强度耐撕裂聚丙烯薄膜配方，其特征在于由以下重量份的原料制得：聚丙烯80份、丁醚化树脂10份、三烯丙基异氰酸酯4份、羟丙基纤维素12份、普鲁兰多糖7份、纳米二氧化硅13份、十二烷基苯磺酸钠盐2份、乙酸龙脑酯2份、木粉11份、甘油30份。
3.根据权利要求1所述的一种高强度耐撕裂聚丙烯薄膜配方，其特征在于由以下重量份的原料制得：聚丙烯90份、丁醚化树脂15份、三烯丙基异氰酸酯8份、羟丙基纤维素18份、普鲁兰多糖15份、纳米二氧化硅16份、十二烷基苯磺酸钠盐7份、乙酸龙脑酯5份、木粉13份、甘油40份。
4.根据权利要求1所述的一种高强度耐撕裂聚丙烯薄膜配方，其特征在于由以下重量份的原料制得：聚丙烯82份、丁醚化树脂12份、三烯丙基异氰酸酯5份、羟丙基纤维素13份、普鲁兰多糖8份、纳米二氧化硅14份、十二烷基苯磺酸钠盐3份、乙酸龙脑酯3份、木粉12份、甘油32份。
5.根据权利要求1所述的一种高强度耐撕裂聚丙烯薄膜配方，其特征在于由以下重量份的原料制得：聚丙烯88份、丁醚化树脂14份、三烯丙基异氰酸酯7份、羟丙基纤维素17份、普鲁兰多糖13份、纳米二氧化硅15份、十二烷基苯磺酸钠盐6份、乙酸龙脑酯4份、木粉12份、甘油38份。