CN106181054A - 一种表面光滑的铁氧体产品激光成型方法 - Google Patents
一种表面光滑的铁氧体产品激光成型方法 Download PDFInfo
- Publication number
- CN106181054A CN106181054A CN201510216027.9A CN201510216027A CN106181054A CN 106181054 A CN106181054 A CN 106181054A CN 201510216027 A CN201510216027 A CN 201510216027A CN 106181054 A CN106181054 A CN 106181054A
- Authority
- CN
- China
- Prior art keywords
- ferrite
- protection film
- pet protection
- ganoid
- ferrite material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种表面光滑的铁氧体产品激光成型方法，用激光切割铁氧体材料，成型出铁氧体产品，在激光切割前，在铁氧体材料表面粘贴一层PET保护膜；PET保护膜上表面为光滑面，下表面为粘性面，PET保护膜下表面的粘度为17-27g，PET保护膜为蓝色保护膜，PET保护膜厚度为0.05～0.07mm，PET保护膜与铁氧体材料表面之间无气泡。与现有技术相比，本发明在激光切割前在铁氧体材料表面粘贴一层蓝色的PET保护膜，使得切割后铁氧体表面无脏污、划伤、漏铁、颗粒、焦边等外观不良现象，在揭掉PET保护膜后，铁氧体产品的表面与切割前铁氧体材料表面没有任何变化，因此，采用本发明方法切割成型的铁氧体产品表面光滑，良品率高；有效的降低的在制作过程中产生的外观不良.同时本发明方法大大提高生产效率，降低生产成本。
Description
技术领域
本发明涉及一种铁氧体产品成型方法，尤其是涉及一种表面光滑的铁氧体产品激光成型方法。
背景技术
铁氧体是一种具有铁磁性的金属磁性材料，因其具有较大的电阻率，较高的介电性能，铁氧体材料可以隔离金属材料对天线磁场的吸收，增加天线的磁场强度，有效增加通信感应距离，而且铁氧体材料具有成本低、温度稳定性好、硬度强、耐腐蚀性好等特点，因此，近年来在近距离无线通信领域得到广泛应用。
现有的铁氧体材料结构如图1所示，包括铁氧体层3，固结在铁氧体层3上表面的表面PET薄膜4，铁氧体层3下表面设置胶层2，胶层2的下方为单面胶保护膜1。铁氧体材料在使用时需要根据待安装铁氧体产品的要求切割成不同的形状。
对铁氧体材料进行切割一般采用激光切割方法。中国专利CN 104107983A公布了一种新型铁氧体激光切割方法。但是包括对比专利中公开的方法在内的常规激光切割铁氧体产品时，铁氧体材质在激光切割后，由于激光的超高温度，在铁氧体表面会留下铁屑、异物与脏污等，需要人工拿无尘布或毛刷擦拭表面的异物及脏污，一方面容易造成铁氧体表面划伤、漏铁、颗粒异物处理不干净等外观不良的现象，造成不良率提高，另一方面需要在切割后增加表面处理工艺，生产效率太低，增加生产环节与生产成本。
发明内容
本发明的目的就是为了克服上述现有技术存在的缺陷而提供一种减少工序、提高生产效率、提高产品外观品质的表面光滑的铁氧体产品激光成型方法。
本发明的目的可以通过以下技术方案来实现：
一种表面光滑的铁氧体产品激光成型方法，用激光切割铁氧体材料，成型出铁氧体产品，在激光切割前，在铁氧体材料表面粘结一层PET保护膜。
所述的PET保护膜上表面为光滑面，下表面为粘性面。
所述的PET保护膜下表面的粘度为17-27g，优选为20g，粘度太大的话不易从铁氧体材料表面揭下来，粘度太小的话粘结性较差。
采用光纤激光机对铁氧体材料进行激光切割，由于采用的是光纤激光机，透明的保护膜不能起到保护作用，会使得激光穿透透明膜后对铁氧体材料表面造成伤害，因此所述的PET保护膜为蓝色保护膜。
所述的PET保护膜厚度为0.05～0.07mm。厚度太小的话，保护效果较差，厚度太高的话会影响切割效果。
所述的PET保护膜与铁氧体材料表面之间无气泡，如果有气泡产生会影响切割效果。
激光切割后，所述的PET保护膜粘结在成型的铁氧体产品上，在出货时，表面的PET保护膜可以不揭掉，防止运输过程中造成的铁氧体表面外观不良。
与现有技术相比，本发明具有以下优点及有益效果：
1、本发明在激光切割前在铁氧体材料表面粘结一层蓝色的PET保护膜，使得切割后铁氧体表面无脏污、划伤、漏铁、颗粒、焦边等外观不良现象，在揭掉PET保护膜后，铁氧体产品的表面与切割前铁氧体材料表面没有任何变化，因此，采用本发明方法切割成型的铁氧体产品表面光滑，良品率高；
2、本发明的方法适用性强，不管什么颜色的铁氧体，只要按照本发明的方法都可达到在激光切割后表面无脏污、划伤、漏铁、焦边、颗粒等外观不良现象；
3、本发明的方法工艺简单，易于操作，且仅需要使用PET保护膜，成本很低，但是节约了切割后对铁氧体产品表面的清洁处理工序，因此，本发明方法大大提高生产效率，降低生产成本。
4、在激光切割时，根据需要可以将铁氧体材料的单面胶保护膜切穿或选择不切穿，切穿的话，使得单面胶保护膜黏贴在铁氧体产品上，不切穿的话，使得多个铁氧体产品粘结在一个单面胶保护膜上，使用时再将铁氧体产品从单面胶保护膜上剥离下来。
附图说明
图1为铁氧体材料的分解结构示意图。
图2为铁氧体材料激光切割前分解结构示意图。
具体实施方式
下面结合附图和具体实施例对本发明进行详细说明。
实施例
一种表面光滑的铁氧体产品激光成型方法，用激光切割铁氧体材料，成型出铁氧体产品，在激光切割前，在铁氧体材料表面粘结一层PET保护膜5，如图2所示，这样铁氧体材料由上到下依次为：PET保护膜5、PET薄膜4、铁氧体层3、胶层2及单面胶保护膜1。
其中，PET保护膜上表面为光滑面，下表面为粘性面。PET保护膜下表面的粘度为17-27g，优选为20g，粘度太大的话不易从铁氧体材料表面揭下来，粘度太小的话粘结性较差。PET保护膜厚度为0.05～0.07mm。厚度太小的话，保护效果较差，厚度太高的话会影响切割效果。PET保护膜与铁氧体材料表面之间无气泡，如果有气泡产生会影响切割效果。
本实施例采用光纤激光机对铁氧体材料进行激光切割，由于采用的是光纤激光机，透明的保护膜不能起到保护作用，会使得激光穿透透明膜后对铁氧体材料表面造成伤害，因此PET保护膜为蓝色保护膜。
激光切割后，PET保护膜粘结在成型的铁氧体产品上，在出货时，表面的PET保护膜可以不揭掉，防止运输过程中造成的铁氧体表面外观不良。
在激光切割前在铁氧体材料表面粘结一层蓝色的PET保护膜，使得切割后铁氧体表面无脏污、划伤、漏铁、颗粒、焦边等外观不良现象，在揭掉PET保护膜后，铁氧体产品的表面与切割前铁氧体材料表面没有任何变化，因此，采用本发明方法切割成型的铁氧体产品表面光滑，良品率高。
上述的对实施例的描述是为便于该技术领域的普通技术人员能理解和使用发明。熟悉本领域技术的人员显然可以容易地对这些实施例做出各种修改，并把在此说明的一般原理应用到其他实施例中而不必经过创造性的劳动。因此，本发明不限于上述实施例，本领域技术人员根据本发明的揭示，不脱离本发明范畴所做出的改进和修改都应该在本发明的保护范围之内。
Claims (7)
1.一种表面光滑的铁氧体产品激光成型方法，用激光切割铁氧体材料，成型出铁氧体产品，其特征在于，在激光切割前，在铁氧体材料表面粘结一层PET保护膜。
2.根据权利要求1所述的一种表面光滑的铁氧体产品激光成型方法，其特征在于，所述的PET保护膜上表面为光滑面，下表面为粘性面。
3.根据权利要求2所述的一种表面光滑的铁氧体产品激光成型方法，其特征在于，所述的PET保护膜下表面的粘度为17-27g。
4.根据权利要求1所述的一种表面光滑的铁氧体产品激光成型方法，其特征在于，采用光纤激光机对铁氧体材料进行激光切割，所述的PET保护膜为蓝色保护膜。
5.根据权利要求1所述的一种表面光滑的铁氧体产品激光成型方法，其特征在于，所述的PET保护膜厚度为0.05～0.07mm。
6.根据权利要求1所述的一种表面光滑的铁氧体产品激光成型方法，其特征在于，所述的PET保护膜与铁氧体材料表面之间无气泡。
7.根据权利要求1所述的一种表面光滑的铁氧体产品激光成型方法，其特征在于，激光切割后，所述的PET保护膜粘贴在成型的铁氧体产品上。