CN106186808A - 一种内墙环保装饰材料及其制备方法 - Google Patents
一种内墙环保装饰材料及其制备方法 Download PDFInfo
- Publication number
- CN106186808A CN106186808A CN201610501631.0A CN201610501631A CN106186808A CN 106186808 A CN106186808 A CN 106186808A CN 201610501631 A CN201610501631 A CN 201610501631A CN 106186808 A CN106186808 A CN 106186808A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- ornament materials
- kieselguhr
- green
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种内墙环保装饰材料，其主要由硅藻土250‑320份，乳胶粉20‑35份，重质碳酸钙460‑560份，灰钙150‑200份，木质纤维素1‑5份，纤维素醚6‑20份，煅烧高岭土8‑15份，贵金属催化剂5‑8份，二氧化钛8‑15份，硅灰石粉5‑20份，白云石粉5‑20份，膨润土2‑10份，纳米活性炭5‑10份，防霉剂0.1‑1份，酞菁绿0.5‑1.2份，抗碱剂5‑8份，凹凸棒粘土粉2‑6份，防裂纤维1‑5份，乳酸菌粉2‑5份组成。本发明还提供了该内墙环保装饰材料的制备方法。上述配方结合制备方法能够解决人们在室内活动时间太久导致吸入如苯、甲醛等有害物质，同时降低有害气体的累积量。
Description
技术领域
本发明属于墙面装饰材料技术领域，具体涉及一种内墙环保装饰材料及其制备方法。
背景技术
随着生产和生活方式的更加现代化，更多的工作和文娱体育活动都可在室内进行，购物也不必每天上街，合适的室内微小气候使人们不必经常到户外去调节热效应，这样，人们的室内活动时间就更多，甚至高达90%以上，室内空气质量对人体健康的关系就显得更加密切更加重要，因装潢使用建材工艺及材料的特性，一般都会释放如苯、甲醛等有害物质，虽然室内污染物的浓度较低，但由于接触时间很长，故其累积接触量很高，特别是老幼病残等体弱人群，抵抗力较低、户外活动机会更少，因此，室内空气质量的好坏直接关系到人们的健康。硅藻土是一种硅质沉积岩，由硅藻遗体沉积而成，主要矿物成分为蛋白石，白色或浅黄色，它性能稳定，耐酸，孔容大、孔径大，比表面积大，吸附性强，能吸附等于自身质量1.5～4倍的液体，能吸附自身质量1.1～1.5倍的油分，它的电位为负，绝对值大，吸附正电荷能力强，含有硅藻土材料对水份的吸收和释放能够产生瀑布效果，将水分子分解成正负离子，正负离子群在空气中四处浮游，有杀菌能力。
发明内容
为了解决人们在室内活动时间太久导致吸入如苯、甲醛等有害物质，降低有害气体的累积量，本发明从墙面材料污染物释放以及外部污染物的分解进行同步治理，提供了一种内墙环保装饰材料及其制备方法。
一种内墙环保装饰材料及其制备方法，按重量份计，其主要由硅藻土250-320份，乳胶粉20-35份，重质碳酸钙460-560份，灰钙150-200份，木质纤维素1-5份，纤维素醚6-20份，煅烧高岭土8-15份，贵金属催化剂5-8份，二氧化钛8-15份，硅灰石粉5-20份，白云石粉5-20份，膨润土2-10份，纳米活性炭5-10份，防霉剂0.1-1份，酞菁绿0.5-1.2份，抗碱剂5-8份，凹凸棒粘土粉2-6份，防裂纤维1-5份，乳酸菌粉2-5份组成。
进一步的，所述重质碳酸钙为300目，白度恳求：95%，碳酸钙含量：99%；
进一步的，所述二氧化钛，其含量大于98..5%；
进一步的，所述硅藻土为天然硅藻土，其中主要成分是二氧化硅，白色，其中二氧化硅含量不小于91％；
进一步的，所述内墙环保装饰材料制备方法如下：
（1）、首先按照比例称量合适比例的装饰材料各组分原料，分别放置在无尘的密闭容器；
（2）、将硅藻土、乳胶粉、重质碳酸钙、灰钙组分原料混合加入洁净的搅拌机进行充分搅拌，搅拌时间为50分钟，然后按照组分比例依次加入木质纤维素、纤维素醚、煅烧高岭土、贵金属催化剂、二氧化钛、硅灰石粉、白云石粉、膨润土、纳米活性炭、防霉剂、酞菁绿、抗碱剂、凹凸棒粘土粉、防裂纤维、乳酸菌粉，然后根据搅拌的均匀度判断，1-3小时后即可关闭搅拌机；
（3）、将上述搅拌均匀后的材料容器盛放后置入干燥箱进行干燥，60-80℃干燥10-20小时，采用聚乙烯包装袋进行分装，密封包装即可。
本发明的有益之处在于：
墙体材料具有消除异味的功能，保持室内清洁，同时能够长时间消除异味和吸收、分解有害化学物质，并能够长期保持室内墙面清洁，此外，墙体材料还能够吸收和分解引起人过敏的物质，产生医疗效果，其对水分的吸收和释放能够产生瀑布效果，将水分子分解成正负离子，由于水分子被包裹，形成正负离子群，然后以水分子为载体，在空气中四处浮游，拥有杀菌能力，正负离子群中性能最活跃的氢氧根离子与有害物质进行剧烈的化学反应，最后将它们彻底分解成水分子等无害物，起到健康和环保的作用。
具体实施方式
下面将结合具体实施例来详细说明本发明，在此本发明的示意性实施例以及说明用来解释本发明，但并不作为对本发明的限定。
实施例1
一种内墙环保装饰材料，按重量份计，其主要由硅藻土260份，乳胶粉22份，重质碳酸钙500份，灰钙150份，木质纤维素2份，纤维素醚7份，煅烧高岭土9份，贵金属催化剂6份，二氧化钛9份，硅灰石粉15份，白云石粉16份，膨润土4份，纳米活性炭6份，防霉剂0.5份，酞菁绿0.8份，抗碱剂6份，凹凸棒粘土粉3份，防裂纤维2份，乳酸菌粉3份组成；所述重质碳酸钙为300目，白度恳求：95%，碳酸钙含量：99%；所述二氧化钛，其含量大于98.5%；所述硅藻土为天然硅藻土，其中主要成分是二氧化硅，白色，其中二氧化硅含量不小于91％。
该内墙环保装饰材料制备方法，包括以下步骤：
（1）、首先按照比例称量合适比例的装饰材料各组分原料，分别放置在无尘的密闭容器；
（2）、将硅藻土、乳胶粉、重质碳酸钙、灰钙组分原料混合加入洁净的搅拌机进行充分搅拌，搅拌时间为50分钟，然后按照组分比例依次加入木质纤维素、纤维素醚、煅烧高岭土、贵金属催化剂、二氧化钛、硅灰石粉、白云石粉、膨润土、纳米活性炭、防霉剂、酞菁绿、抗碱剂、凹凸棒粘土粉、防裂纤维、乳酸菌粉，然后根据搅拌的均匀度判断，1.5小时后即可关闭搅拌机；
（3）、将上述搅拌均匀后的材料容器盛放后置入干燥箱进行干燥，65℃干燥12小时，采用聚乙烯包装袋进行分装，密封包装即可。
实施例2
一种内墙环保装饰材料，按重量份计，其主要由硅藻土280份，乳胶粉28份，重质碳酸钙520份，灰钙180份，木质纤维素3份，纤维素醚15份，煅烧高岭土10份，贵金属催化剂6份，二氧化钛12份，硅灰石粉18份，白云石粉16份，膨润土8份，纳米活性炭7份，防霉剂0.8份，酞菁绿1份，抗碱剂6份，凹凸棒粘土粉5份，防裂纤维3份，乳酸菌粉4份组成；所述重质碳酸钙为300目，白度恳求：95%，碳酸钙含量：99%；所述二氧化钛，其含量大于98.5%；所述硅藻土为天然硅藻土，其中主要成分是二氧化硅，白色，其中二氧化硅含量不小于91％。
该内墙环保装饰材料制备方法，包括以下步骤：
（1）、首先按照比例称量合适比例的装饰材料各组分原料，分别放置在无尘的密闭容器；
（2）、将硅藻土、乳胶粉、重质碳酸钙、灰钙组分原料混合加入洁净的搅拌机进行充分搅拌，搅拌时间为50分钟，然后按照组分比例依次加入木质纤维素、纤维素醚、煅烧高岭土、贵金属催化剂、二氧化钛、硅灰石粉、白云石粉、膨润土、纳米活性炭、防霉剂、酞菁绿、抗碱剂、凹凸棒粘土粉、防裂纤维、乳酸菌粉，然后根据搅拌的均匀度判断，2.5小时后即可关闭搅拌机；
（3）、将上述搅拌均匀后的材料容器盛放后置入干燥箱进行干燥，60-80℃干燥18小时，采用聚乙烯包装袋进行分装，密封包装即可。
实施例3
一种内墙环保装饰材料，按重量份计，其主要由硅藻土320份，乳胶粉35份，重质碳酸钙460份，灰钙150份，木质纤维素5份，纤维素醚18份，煅烧高岭土12份，贵金属催化剂7份，二氧化钛12份，硅灰石粉16份，白云石粉15份，膨润土8份，纳米活性炭8份，防霉剂1份，酞菁绿1份，抗碱剂6份，凹凸棒粘土粉5份，防裂纤维4份，乳酸菌粉3份组成；所述重质碳酸钙为300目，白度恳求：95%，碳酸钙含量：99%；所述二氧化钛，其含量大于98.5%；所述硅藻土为天然硅藻土，其中主要成分是二氧化硅，白色，其中二氧化硅含量不小于91％。
该内墙环保装饰材料制备方法，包括以下步骤：
（1）、首先按照比例称量合适比例的装饰材料各组分原料，分别放置在无尘的密闭容器；
（2）、将硅藻土、乳胶粉、重质碳酸钙、灰钙组分原料混合加入洁净的搅拌机进行充分搅拌，搅拌时间为50分钟，然后按照组分比例依次加入木质纤维素、纤维素醚、煅烧高岭土、贵金属催化剂、二氧化钛、硅灰石粉、白云石粉、膨润土、纳米活性炭、防霉剂、酞菁绿、抗碱剂、凹凸棒粘土粉、防裂纤维、乳酸菌粉，然后根据搅拌的均匀度判断，2小时后即可关闭搅拌机；
（3）、将上述搅拌均匀后的材料容器盛放后置入干燥箱进行干燥，75℃干燥15小时，采用聚乙烯包装袋进行分装，密封包装即可。
上述实施例仅例示性说明本发明的原理及其功效，而非用于限制本发明。任何熟悉此技术的人士皆可在不违背本发明的精神及范畴下，对上述实施例进行修饰或改变。因此，举凡所属技术领域中具有通常知识者在未脱离本发明所揭示的精神与技术思想下所完成的一切等效修饰或改变，仍应由本发明的权利要求所涵盖。
Claims (2)
1.一种内墙环保装饰材料及其制备方法，按重量份计，其特征在于，其主要由硅藻土250-320份，乳胶粉20-35份，重质碳酸钙460-560份，灰钙150-200份，木质纤维素1-5份，纤维素醚6-20份，煅烧高岭土8-15份，贵金属催化剂5-8份，二氧化钛8-15份，硅灰石粉5-20份，白云石粉5-20份，膨润土2-10份，纳米活性炭5-10份，防霉剂0.1-1份，酞菁绿0.5-1.2份，抗碱剂5-8份，凹凸棒粘土粉2-6份，防裂纤维1-5份，乳酸菌粉2-5份组成；所述重质碳酸钙为300目，白度恳求：95%，碳酸钙含量：99%；所述二氧化钛，其含量大于98.5%；所述硅藻土为天然硅藻土，其中主要成分是二氧化硅，白色，其中二氧化硅含量不小于91％。
2.根据权利要求1所述的内墙环保装饰材料制备方法，其特征在于，包括以下步骤：
（1）、首先按照比例称量合适比例的装饰材料各组分原料，分别放置在无尘的密闭容器；
（2）、将硅藻土、乳胶粉、重质碳酸钙、灰钙组分原料混合加入洁净的搅拌机进行充分搅拌，搅拌时间为50分钟，然后按照组分比例依次加入木质纤维素、纤维素醚、煅烧高岭土、贵金属催化剂、二氧化钛、硅灰石粉、白云石粉、膨润土、纳米活性炭、防霉剂、酞菁绿、抗碱剂、凹凸棒粘土粉、防裂纤维、乳酸菌粉，然后根据搅拌的均匀度判断，1-3小时后即可关闭搅拌机；
（3）、将上述搅拌均匀后的材料容器盛放后置入干燥箱进行干燥，60-80℃干燥10-20小时，采用聚乙烯包装袋进行分装，密封包装即可。