CN106046999A - 纳米改性抗老化涂料及其制备方法 - Google Patents
纳米改性抗老化涂料及其制备方法 Download PDFInfo
- Publication number
- CN106046999A CN106046999A CN201610570641.XA CN201610570641A CN106046999A CN 106046999 A CN106046999 A CN 106046999A CN 201610570641 A CN201610570641 A CN 201610570641A CN 106046999 A CN106046999 A CN 106046999A
- Authority
- CN
- China
- Prior art keywords
- weight
- component
- aging resistance
- nano modification
- resistance coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种纳米改性抗老化涂料及其制备方法，所述纳米改性抗老化涂料包括：组分一与组分二；以纳米改性抗老化涂料的总重量为基准，组分一包括：20‐40重量％的甲基丙烯酸乳液、1‐4重量％的胶黏剂、2‐6重量％的抗老化剂、1‐3重量％的甲基纤维素、1‐4重量％的稀释剂、1‐5重量％的防腐剂和2‐5重量％的固色剂；组分二包括：25‐45重量％的有机溶剂和5‐15重量％的水。本发明公开的纳米改性抗老化涂料具有抗老化，耐高温，耐腐蚀等特性。
Description
技术领域
本发明涉及涂料制备，具体涉及纳米改性抗老化涂料及其制备方法。
背景技术
涂料是一种材料，这种材料可以用不同的施工工艺涂覆在被保护或被装饰的物体表面，并能与被涂物形成粘附牢固、具有一定强度、连续的固态薄膜。这样形成的薄膜通称涂膜，又称漆膜或涂层。不论是传统的以天然物质为原料的涂料产品，还是现代发展中以合成化工为原料的涂料产品，都属于有机化工高分子材料。目前现有的涂料种类繁多，而目前常用于室外的涂料往往在使用过程中经历风吹雨淋以及日晒等，使得涂料腐蚀退化以及脱色，出现一系列老化现象。
发明内容
本发明的目的是提供纳米改性抗老化涂料及其制备方法，通过该方法制得的涂料具有抗老化，耐高温，耐腐蚀等特性。
为了实现上述目的，本发明提供了纳米改性抗老化涂料，包括：组分一与组分二；以纳米改性抗老化涂料的总重量为基准，组分一包括：20-40重量％的甲基丙烯酸乳液、1-4重量％的胶黏剂、2-6重量％的抗老化剂、1-3重量％的甲基纤维素、1-4重量％的稀释剂、1-5重量％的防腐剂和2-5重量％的固色剂。组分二包括：25-45重量％的有机溶剂和5-15重量％的水。
本发明还提供了上述纳米改性抗老化涂料的制备方法，该方法包括：
(1)将组分一含有的各物料进行搅拌以形成所述组分一；
(2)将组分二含有的各物料进行搅拌以形成所述组分二；
(3)将所述组分一与组分二搅拌混合得到抗老化涂料。
通过上述技术方案，本发明通过分别搅拌组分一中的各物料和组分二中的各物料以制得组分一和组分二，再将组分一与组分二混合，在反应容器中进行搅拌混合接触和协同作用，从而得到纳米改性抗老化涂料。该方法制得的涂料具有抗老化，耐高温，耐腐蚀等特性。
本发明的其他特征和优点将在随后的具体实施方式部分予以详细说明。
具体实施方式
以下对本发明的具体实施方式进行详细说明。应当理解的是，此处所描述的具体实施方式仅用于说明和解释本发明，并不用于限制本发明。
本发明提供了一种纳米改性抗老化涂料，包括：组分一与组分二；以纳米改性抗老化涂料的总重量为基准，组分一包括：20-40重量％的甲基丙烯酸乳液、1-4重量％的胶黏剂、2-6重量％的抗老化剂、1-3重量％的甲基纤维素、1-4重量％的稀释剂、1-5重量％的防腐剂和2-5重量％的固色剂。组分二包括：25-45重量％的有机溶剂和5-15重量％的水。
在上述纳米改性抗老化涂料中，所用胶黏剂的具体种类可以在宽的范围内选择，但是为了进一步提纳米改性抗老化涂料的抗老化效果，优选地，胶黏剂选自水玻璃、环氧树脂胶黏剂和聚氨酯胶黏剂中的一种或多种。
在上述纳米改性抗老化涂料中，所用抗老化剂的具体种类可以在宽的范围内选择，但是为了进一步提纳米改性抗老化涂料的抗老化效果，优选地，抗老化剂选自受阻酚类、仲芳胺、叔胺类和醌类中的一种或多种。
在上述纳米改性抗老化涂料中，所用稀释剂的具体种类可以在宽的范围内选择，但是为了进一步提纳米改性抗老化涂料的抗老化效果，优选地，稀释剂选自环己酮、苯、甲苯和乙醇中的一种或多种。
在上述纳米改性抗老化涂料中，所用防腐剂的具体种类可以在宽的范围内选择，但是为了进一步提纳米改性抗老化涂料的抗老化效果，优选地，防腐剂选自苯甲酸、苯甲酸钠和对羟基苯甲酸甲酯中的一种或多种。
在上述纳米改性抗老化涂料中，所用固色剂的具体种类可以在宽的范围内选择，但是为了进一步提纳米改性抗老化涂料的抗老化效果，优选地，固色剂选自氯化十六烷基吡啶、胺醛树脂型双氰胺甲醛初缩体、多胺缩合体和酚醛缩合体中的一种或多种。
在上述纳米改性抗老化涂料中，所用有机溶剂的具体种类可以在宽的范围内选择，但是为了进一步提纳米改性抗老化涂料的抗老化效果，优选地，有机溶剂选自甲苯、二甲苯、戊烷、己烷和正丁醇中的一种或多种。
本发明还提供了一种上述纳米改性抗老化涂料的制备方法，该方法包括：
(1)将组分一含有的各物料进行搅拌以形成所述组分一；
(2)将组分二含有的各物料进行搅拌以形成所述组分二；
(3)将所述组分一与组分二搅拌混合得到抗老化涂料。
在上述制备方法中，搅拌的速度和搅拌混合的时间可以在宽的范围内选择，但是为了进一步提高所述纳米改性抗老化涂料的抗老化效果，优选地，所述搅拌的速度均为2000-2800rpm，搅拌混合的时间为25-40h。
在上述制备方法中，搅拌的温度可以在宽的范围内选择，从纳米改性抗老化涂料的抗老化效果和环保角度上考虑，优选地，搅拌的温度为18-35℃。
以下将通过实施例对本发明进行详细描述。
实施例1
在18℃下，选用一反应容器，以纳米改性抗老化涂料的总重量为基准，将32.5重量％的甲基丙烯酸乳液、1重量％的水玻璃、2重量％的受阻酚类、3.5重量％的甲基纤维素、1重量％的环己酮、1重量％的苯甲酸和2重量％的氯化十六烷基吡啶加入其中，搅拌混合制得组分一；选用另一反应容器将45重量％的甲苯和12重量％的水加入其中，搅拌混合制得组分二；将组分一与组分二混合，在2000rpm的转速下，搅拌混合40h，制得纳米改性抗老化涂料A1。
实施例2
在20℃下，选用一反应容器，以纳米改性抗老化涂料的总重量为基准，将25重量％的甲基丙烯酸乳液、4重量％的环氧树脂胶黏剂、6重量％的仲芳胺、2重量％的甲基纤维素、4重量％的苯、3重量％的苯甲酸和4重量％的胺醛树脂型双氰胺甲醛初缩体加入其中，搅拌混合制得组分一；选用另一反应容器将38重量％的二甲苯和14重量％的水加入其中，搅拌混合制得组分二；将组分一与组分二混合，在2200rpm的转速下，搅拌混合35h，制得纳米改性抗老化涂料A2。
实施例3
在25℃下，选用一反应容器，以纳米改性抗老化涂料的总重量为基准，将35重量％的甲基丙烯酸乳液、3重量％的聚氨酯胶黏剂、4重量％的仲芳胺、2重量％的甲基纤维素、2重量％的甲苯、2重量％的苯甲酸钠和5重量％的氯化十六烷基吡啶加入其中，搅拌混合制得组分一；选用另一反应容器将36重量％的戊烷和5重量％的水加入其中，搅拌混合制得组分二；将组分一与组分二混合，在2500rpm的转速下，搅拌混合30h，制得纳米改性抗老化涂料A3。
实施例4
在30℃下，选用一反应容器，以纳米改性抗老化涂料的总重量为基准，将38重量％的甲基丙烯酸乳液、2重量％的聚氨酯胶黏剂、4重量％的叔胺、2重量％的甲基纤维素、4重量％的乙醇、5重量％的对羟基苯甲酸甲酯和2重量％的氯化十六烷基吡啶加入其中，搅拌混合制得组分一；选用另一反应容器将33重量％的己烷和10重量％的水加入其中，搅拌混合制得组分二；将组分一与组分二混合，在2800rpm的转速下，搅拌混合25h，制得纳米改性抗老化涂料A4。
实施例5
在35℃下，选用一反应容器，以纳米改性抗老化涂料的总重量为基准，将40重量％的甲基丙烯酸乳液、2重量％的水玻璃、4重量％的叔胺、2重量％的甲基纤维素、4重量％的乙醇、2重量％的苯甲酸钠和4重量％的氯化十六烷基吡啶加入其中，搅拌混合制得组分一；选用另一反应容器将25重量％的正丁醇和11重量％的水加入其中，搅拌混合制得组分二；将组分一与组分二混合，在2800rpm的转速下，搅拌混合25h，制得纳米改性抗老化涂料A5。
对比例1
相对于实施例1制得涂料B1，所不同的是，以纳米改性抗老化涂料的总重量为基准，受阻酚类的用量为0.5重量％，甲基纤维素的用量为5重量％。
对比例2
相对于实施例2制得涂料B2，所不同的是，以纳米改性抗老化涂料的总重量为基准，甲基丙烯酸乳液的用量为5重量％，环氧树脂胶黏剂的用量为24重量％。
对比例3
相对于实施例3制得涂料B3，所不同的是，以纳米改性抗老化涂料的总重量为基准，甲苯的用量为0.5重量％，苯甲酸钠的用量为3.5重量％。
检测例1
对上述实施例和对比例制得的涂料进行抗老化实验检测，同时将上述实施例和对比例制得的涂料涂抹于金属件上，3个月后观察发现金属件是否出现老化现象，具体结果见表1。
表1
| A1 | A2 | A3 | A4 | A5 | B1 | B2 | B3 | |
| 老化现象 | 无老化 | 无老化 | 无老化 | 无老化 | 无老化 | 老化 | 老化 | 老化 |
通过上述检测例可知，在同一环境下，随着时间的推移，本发明提供的纳米改性抗老化涂料具有抗老化的效果，且制备方法简单，原料易得。
以上详细描述了本发明的优选实施方式，但是，本发明并不限于上述实施方式中的具体细节，在本发明的技术构思范围内，可以对本发明的技术方案进行多种简单变型，这些简单变型均属于本发明的保护范围。
另外需要说明的是，在上述具体实施方式中所描述的各个具体技术特征，在不矛盾的情况下，可以通过任何合适的方式进行组合，为了避免不必要的重复，本发明对各种可能的组合方式不再另行说明。
此外，本发明的各种不同的实施方式之间也可以进行任意组合，只要其不违背本发明的思想，通过将组分一与组分二搅拌混匀在反应容器中进行搅拌混合接触和协同作用，从而得到纳米改性抗老化涂料，其同样应当视为本发明所公开的内容。
Claims (10)
1.一种纳米改性抗老化涂料，其特征在于，包括：组分一与组分二；以纳米改性抗老化涂料的总重量为基准，组分一包括：20‐40重量％的甲基丙烯酸乳液、1‐4重量％的胶黏剂、2‐6重量％的抗老化剂、1‐3重量％的甲基纤维素、1‐4重量％的稀释剂、1‐5重量％的防腐剂和2‐5重量％的固色剂；组分二包括：25‐45重量％的有机溶剂和5‐15重量％的水。
2.根据权利要求1所述的纳米改性抗老化涂料，其中，所述胶黏剂选自水玻璃、环氧树脂胶黏剂和聚氨酯胶黏剂中的一种或多种。
3.根据权利要求1所述的纳米改性抗老化涂料，其中，所述抗老化剂选自受阻酚类/仲芳胺/叔胺类和醌类中的一种或多种。
4.根据权利要求1所述的纳米改性抗老化涂料，其中，所述稀释剂选自环己酮、苯、甲苯和乙醇中的一种或多种。
5.根据权利要求1所述的纳米改性抗老化涂料，其中，所述防腐剂选自苯甲酸、苯甲酸钠和对羟基苯甲酸甲酯中的一种或多种。
6.根据权利要求1所述的纳米改性抗老化涂料，其中，所述固色剂选自氯化十六烷基吡啶、胺醛树脂型双氰胺甲醛初缩体、多胺缩合体和酚醛缩合体中的一种或多种。
7.根据权利要求1所述的纳米改性抗老化涂料，其中，所述有机溶剂选自甲苯、二甲苯、戊烷、己烷和正丁醇中的一种或多种。
8.一种如权利要求1-7中任意一项所述的纳米改性抗老化涂料的制备方法，其特征在于，所述制备方法包括：
(1)将组分一含有的各物料进行搅拌以形成所述组分一；
(2)将组分二含有的各物料进行搅拌以形成所述组分二；
(3)将所述组分一与组分二搅拌混合得到抗老化涂料。
9.根据权利要求8所述的纳米改性抗老化涂料的制备方法，其中，所述搅拌的速度均为2000-2800rpm，搅拌混合的时间为25-40h。
10.根据权利要求8所述的纳米改性抗老化涂料的制备方法，其中，所述搅拌的温度为18-35℃。