CN106007600A - Imitated-marble table board and preparing method thereof - Google Patents
Imitated-marble table board and preparing method thereof Download PDFInfo
- Publication number
- CN106007600A CN106007600A CN201610343120.0A CN201610343120A CN106007600A CN 106007600 A CN106007600 A CN 106007600A CN 201610343120 A CN201610343120 A CN 201610343120A CN 106007600 A CN106007600 A CN 106007600A
- Authority
- CN
- China
- Prior art keywords
- idiosome
- parts
- parian
- marble
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an imitated-marble table board and a preparing method thereof. The imitated-marble table board comprises a base body and marble figures coated on the surface of the base body. The base body comprises the ingredients in parts by mass: 100 parts of magnesium sulfate solution, 110 parts of magnesium oxide, 45-55 parts of silica sand, 1-3 parts of modifying agent and 0-3 parts of reinforcing agent. The invention further discloses the preparing method of the imitated-marble table board. According to the imitated-marble board, the base body is made of fireproof and waterproof materials of magnesium oxide and silica sand. Thus, the imitated-marble table board has an A1 level fireproof function and can protect a main body structure from being destroyed when fire happens. The imitated-marble table board overcomes the defects that natural marble has radiation and is less in resources and also has the advantages of being attractive in appearance and good in mechanical property like the marble. The imitated-marble table board is simple in manufacturing technique, can be designed into corresponding shapes, sizes and figures according to application occasions, can meet the using requirements of occasions such as wash basins, kitchen range tops, floors and television walls and is a green and environmental-friendly novel building material.
Description
Technical field
The invention belongs to decorative building material field, be specifically related to a kind of parian deck plate and preparation method thereof.
Background technology
Marble, also known as marble, is the limestone of recrystallization, and main component is CaCO3.At present, marble master
It is used for being processed into various shape material, sheet material, makees the metope of building, ground, platform, post.Marmorean matter
Feel soft attractive in appearance solemnly, elegant style, in a great variety, be the ideal material decorating luxurious building, be also skill
The traditional material of art engraving.In interior decoration, television set table top, windowsill, the kitchen range top, flooring etc. are also
It is suitable for using marble.
Owing to natural marble growth cycle is long, expensive, therefore on market generally with artificial marble,
Resin panel, bluestone board replace, although but these materials are worth cheap, but there is also various
Not enough.If artificial marble is to be processed by stone powder, there is radiation in various degree, and this
Radiate more higher than natural marble；Resin panel is easily deformed and content of formaldehyde is high；Bluestone board easy fracture, add
Work difficulty is big and outward appearance is the most attractive in appearance, can only do low-end product and use.
Summary of the invention
It is an object of the invention to overcome the problems referred to above of the prior art, it is provided that a kind of elegant in appearance, green
Environmental protection, radiationless and there is the parian deck plate of A1 level fire-proof function.
For solve above-mentioned technical problem, the present invention by the following technical solutions:
A kind of parian deck plate, including idiosome and the imitation marble being coated on idiosome surface, wherein,
Each component and the mass fraction thereof of preparing idiosome be: Adlerika: 100 parts, magnesium oxide: 110 parts, stone
Ying Fen: 45～55 parts, modifying agent: 1～3 part, reinforcing agent: 0～3 part.
Further, each component and the mass fraction thereof of preparing this parian panel idiosome be: magnesium sulfate is molten
Liquid: 100 parts, magnesium oxide: 110 parts, silica flour: 50 parts, modifying agent: 1 part.
Further, each component and the mass fraction thereof of preparing this parian panel idiosome be: magnesium sulfate is molten
Liquid: 100 parts, magnesium oxide: 110 parts, silica flour: 50 parts, modifying agent: 1 part, reinforcing agent: 1 part.
Further, component and the quality proportioning thereof of described modifying agent be, polyvinyl alcohol: hydrochloric acid: hydroxide
Sodium: allylamine=80:1:1:12.
Further, the reinforcing agent used can be glass fibre, asbestos fibre, cellulose fibre, people
Make one or more in fiber.
In order to improve idiosome intensity, improve the produced area of monolithic deck plate, the ripple of described Adlerika
U.S.'s degree is 28 degree.
Another object of the present invention is to provide the preparation method of a kind of parian deck plate, specifically includes following
Step:
S1: the preparation of parian deck plate idiosome:
S11: weigh each component by material mixture ratio and deposit；
S12: by the silica flour weighed, Adlerika, magnesium oxide, modifying agent and reinforcing agent mix homogeneously
Prepare idiosome castable；
S13: the idiosome castable that S12 prepares is poured into mould and pours into a mould；
S14: the mould being cast with idiosome castable is placed in room of resting, is dried at room temperature for；
S15: by dry idiosome excision forming；
The preparation of S2: imitation marble:
S21: transferred by water or the method for thermal transfer is at the surface printing imitation marble of S15 gained idiosome
And the decorative pattern of printing is carried out UV light oil processing, the most both obtained parian deck plate.
Further, when being dried, temperature control is: 20～30 DEG C, be at least 5 days drying time.
Compared with prior art, the parian deck plate of the present invention has an advantage highlighted below:
(1) the parian deck plate of the present invention uses fire-proof and water-proof material oxidation magnesium, silica flour to make embryo
Body, thus there is A1 level fire-proof function, when fire occurs, it is possible to protection agent structure is not destroyed；
(2) the parian deck plate of the present invention successfully overcomes natural marble has radiation, resource few
Deficiency, but possesses the advantages such as marmorean elegant in appearance, good mechanical property, and market potential is huge；
(3) the parian deck plate processing technology of the present invention is easy, can be corresponding according to applicable situation design
Shape, size and decorative pattern, the use of the occasions such as wash platform, the kitchen range top, ground, video wall can be met
Requirement；
(4) compared with natural marble, the parian deck plate of the present invention is inexpensive, it is simple to promote
Application.
Accompanying drawing explanation
Fig. 1 is the parian deck plate preparation technology flow chart in the embodiment of the present invention.
Detailed description of the invention
In order to make the purpose of the present invention, technical scheme and advantage clearer, below in conjunction with accompanying drawing and reality
Execute example, the present invention is further elaborated.Only should be appreciated that specific embodiment described herein
In order to explain the present invention, it is not intended to limit the present invention.
Embodiment
Parian deck plate in the present embodiment includes idiosome and is coated on the parian flower on idiosome surface
Stricture of vagina, wherein, each component and the mass fraction thereof of preparing idiosome be: Baume degrees is the Adlerika of 28 degree:
100 parts, magnesium oxide: 110 parts, silica flour: 50 parts, modifying agent: 1 part, reinforcing agent: 1 part.Wherein,
The modifying agent used be polyvinyl alcohol 160 grams, hydrochloric acid 2 grams, sodium hydroxide 2 grams, allylamine 24 grams equal
Even mixture；Reinforcing agent can be in glass fibre, asbestos fibre, cellulose fibre, staple fibre
Kind or several mixture, as preferably, use in neutral glass fibre.
The preparation method also disclosing parian deck plate in the present embodiment, as it is shown in figure 1, specifically wrap
Include following steps:
S1: the preparation of parian deck plate idiosome:
S11: weigh each component by material mixture ratio and deposit；
S12: by the silica flour weighed, Adlerika, magnesium oxide, modifying agent and reinforcing agent mix homogeneously
Prepare idiosome castable；
S13: the idiosome castable that S12 prepares is poured into mould and pours into a mould；
S14: the mould being cast with idiosome castable is placed in room of resting, is dried at room temperature for；
S15: by dry idiosome excision forming；
The preparation of S2: imitation marble:
S21: transferred by water or the method for thermal transfer is at the surface printing imitation marble of S15 gained idiosome
And the decorative pattern of printing is carried out UV light oil processing, the most i.e. obtain parian deck plate.
As further preferred version, described step S12 is additionally included in made idiosome castable addition
Foaming agent, for alleviating the weight of idiosome material.
Further, described foaming agent is included by the mass fraction of component: A agent mother solution 5-16 part, B catalysis
Agent 1-3 part；
Wherein, A agent mother solution includes following composition by weight: hydrogen peroxide 4-12 part of 30% concentration, cleaning agent 1-4
Part；
Cleaning agent includes following composition by weight: sodium alkyl benzene sulfonate 0.1-0.4 part, fatty alcohol-polyoxyethylene ether
0.2-0.5 part, coconut oil diethanolamine 0.2-0.6 part, triethanolamine 0.5-2.5 part；Described B catalyst is
Manganese dioxide granule.
It should be noted that and mostly use physical foaming technology, physical blowing to need special foaming machine at present,
The CBA of the present invention can directly add and in the slurry it be carried out foaming process.
Additionally, the present invention also provides for the preparation method of a kind of above-mentioned foaming agent, comprise the following steps:
A: weigh proportioning, raw material is carried out according to a certain percentage weighing and takes；
B: catalyst grinds, and load weighted catalyst manganese dioxide is placed in milling apparatus and is ground,
The ambient temperature ground is 10-30 degree Celsius, and milling time is 2-6 minute, the manganese dioxide after grinding
The a diameter of 50-200 micron of grain；
C: make cleaning agent, by load weighted sodium alkyl benzene sulfonate, fatty alcohol-polyoxyethylene ether, coconut oil
Diethanolamine and triethanolamine are put into respectively in mixing plant and are stirred mixing, and mixing time is that 5-15 divides
Clock, reaction temperature is 5-16 degree Celsius, makes cleaning agent；
D: make mother solution, the cleaning agent completed proportionally is mixed with load weighted hydrogen peroxide
And stir, mixing time is 2-7 minute, and whipping temp is 10-22 degree Celsius；
E: in magnesium oxide: the ratio of mother solution=100:5 adds after magnesium oxysulfide slurry and mother solution are stirred
Catalyst is the most expandable, catalyst additional proportion: mother solution: catalyst=30:1.
Those of ordinary skill in the art is it will be appreciated that embodiment described here is to aid in reader's reason
Solve the present invention principle, it should be understood that protection scope of the present invention be not limited to such special statement and
Embodiment.Those of ordinary skill in the art can make various according to these technology disclosed by the invention enlightenment
Without departing from other various concrete deformation and combination of essence of the present invention, these deformation and combination are still in the present invention
Protection domain in.
Claims (7)
1. a parian deck plate, it is characterised in that: include idiosome and be coated on the imitative of idiosome surface
Marbling, wherein, each component and the mass fraction thereof of preparing idiosome be:
Baume degrees is the Adlerika of 28 degree: 100 parts；
Magnesium oxide powder: 110 parts；
Silica flour: 45～55 parts；
Modifying agent: 1～3 part, component and the quality proportioning thereof of described modifying agent be, polyvinyl alcohol: hydrochloric acid:
Sodium hydroxide: allylamine=80:1:1:12.
Parian deck plate the most according to claim 1, it is characterised in that: prepare its idiosome
Each component and mass fraction thereof be:
Adlerika: 100 parts；
Magnesium oxide: 110 parts；
Silica flour: 50 parts；
Modifying agent: 1 part.
Parian deck plate the most according to claim 1, it is characterised in that: prepare its idiosome
Each component and mass fraction thereof be:
Adlerika: 100 parts；
Magnesium oxide: 110 parts；
Silica flour: 50 parts；
Modifying agent: 1 part；
Reinforcing agent: 1 part, described reinforcing agent is in neutral glass fibre.
4. the preparation method of the parian deck plate described in a claim 1 or 2, it is characterised in that:
Comprise the following steps:
S1: the preparation of parian deck plate idiosome:
S11: weigh each component by material mixture ratio and deposit；
S12: the silica flour weighed, Adlerika, magnesium oxide and modifying agent mix homogeneously are prepared idiosome
Castable；
S13: the idiosome castable that S12 prepares is poured into mould and pours into a mould；
S14: the mould being cast with idiosome castable is placed in room of resting, is dried at room temperature for；
S15: by dry idiosome excision forming；
The preparation of S2: imitation marble:
S21: transferred by water or thermal transfer method S15 gained idiosome surface printing imitation marble also
The decorative pattern of printing is carried out UV light oil processing, the most i.e. obtains parian deck plate.
The preparation method of parian deck plate the most according to claim 4, it is characterised in that: institute
State the cast of the idiosome in step S12 and also include the reinforcing agent for strengthening the idiosome strength of materials, described reinforcing agent
For glass fibre.
The preparation method of parian deck plate the most according to claim 5, it is characterised in that: institute
State step S12 and be additionally included in made idiosome castable addition foaming agent, for alleviating the weight of idiosome material
Amount.
The preparation method of parian deck plate the most according to claim 6, it is characterised in that: institute
State foaming agent to include by the mass fraction of component: A agent mother solution 5-16 part, B catalyst 1-3 part；
Wherein, A agent mother solution includes following composition by weight: hydrogen peroxide 4-12 part of 30% concentration, cleaning agent 1-4
Part；
Cleaning agent includes following composition by weight: sodium alkyl benzene sulfonate 0.1-0.4 part, fatty alcohol-polyoxyethylene ether
0.2-0.5 part, coconut oil diethanolamine 0.2-0.6 part, triethanolamine 0.5-2.5 part；
Described B catalyst is manganese dioxide granule.